CN104278564A - Dyeing agent and method for dyeing nylon fabric by using dyeing agent - Google Patents
Dyeing agent and method for dyeing nylon fabric by using dyeing agent Download PDFInfo
- Publication number
- CN104278564A CN104278564A CN201410498887.1A CN201410498887A CN104278564A CN 104278564 A CN104278564 A CN 104278564A CN 201410498887 A CN201410498887 A CN 201410498887A CN 104278564 A CN104278564 A CN 104278564A
- Authority
- CN
- China
- Prior art keywords
- parts
- coloring agent
- dyeing
- facing material
- dyeing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a dyeing agent. The dyeing agent comprises the following components in parts by mass: 5-8 parts of butyl methacrylate, 3-5 parts of sodium stearate, 1-2 parts of dibutyl phthalate, 3-4 parts of triglyceride, 2-3 parts of styrene, 0.2-0.5 part of polyethylene glycol, 1.2-1.5 parts of sodium persulfate and 120-130 parts of distilled water. The invention also provides a method for dyeing the nylon fabric by using the dyeing agent. The preparation method of the dyeing agent is simple; after the nylon fabric is dyed by the dyeing agent, the soaping fastness reaches a grade between VI and V; the dyeing agent is firm in adhesion; the K/S value is 9.074-9.135; the dyeing agent is high in dyeing performance.
Description
Technical field
A kind of method that the present invention relates to coloring agent and use this coloring agent to dye to nylon facing material.
Background technology
Nylon is a kind of saying of polyamide fiber, can be made into long fine or short fiber.Nylon 6 is polycaprolactam, and nylon66 fiber is polyhexamethylene adipamide.Nylon66 fiber harder than nylon 6 12%, and in theory, hardness is higher, the fragility of fiber is larger, thus more easily ruptures.Conventional colouring method is not easily painted and easily fades.
Summary of the invention
The invention provides a kind of coloring agent; For this reason, the present invention also provides the method using this coloring agent to dye to nylon facing material.Coloring agent of the present invention is easily painted and not fugitive color.
The invention provides a kind of coloring agent, described coloring agent is made up of each component of following mass fraction: butyl methacrylate 5-8 part, odium stearate 3-5 part, dibutyl phthalate 1-2 part, triglycerides 3-4 part, styrene 2-3 part, polyethylene glycol 0.2-0.5 part, sodium peroxydisulfate 1.2-1.5 part, distilled water 120-130 part.
Preferably, described coloring agent is made up of each component of following mass fraction: butyl methacrylate 6 parts, odium stearate 4 parts, dibutyl phthalate 1.5 parts, triglycerides 3.5 parts, styrene 2.5 parts, polyethylene glycol 0.4 part, sodium peroxydisulfate 1.3 parts, distilled water 125 parts.
The present invention also provides the preparation method of above-mentioned coloring agent, step is as follows: the butyl methacrylate of proportional quantity, dibutyl phthalate, sodium peroxydisulfate and water are mixed, be heated to 70-80 DEG C, stir lower reaction 2-3 hour, remaining ingredient is added by proportional quantity, stir lower reaction 1-2 hour, obtained finished product after cooling.
The present invention also provides the method using above-mentioned coloring agent to dye to nylon facing material, step is as follows: the coloring agent described in claim 1 or 2 is heated to 35-40 DEG C, nylon facing material is put into, 65 DEG C are warming up to the heat up speed of 1 DEG C of every 2-3min, insulation 70-90min, clean nylon facing material after cooling, dry.
Coloring agent preparation method of the present invention is simple.And after applying staining reagent of the present invention, the soaping fastness of nylon facing material is 4-5 level, coloring agent combines firmly, and K/S value is 9.074-9.135, and dyeability is good.
Detailed description of the invention
Following embodiment is convenient to understand the present invention better, but does not limit the present invention.Experimental technique in following embodiment, if no special instructions, is conventional method.
embodiment 1
The formula of coloring agent of the present invention is as follows:
Butyl methacrylate 6kg, odium stearate 4kg, dibutyl phthalate 1.5kg, triglycerides 3.5kg, styrene 2.5kg, polyethylene glycol 0.4kg, sodium peroxydisulfate 1.3kg, distilled water 125kg.
The preparation method of coloring agent of the present invention is:
The butyl methacrylate of proportional quantity, dibutyl phthalate, sodium peroxydisulfate and water are mixed, is heated to 75 DEG C, stir lower reaction 2.5 hours, remaining ingredient is added by proportional quantity, stir lower reaction 1.5 hours, obtained finished product after cooling.
Coloring agent of the present invention is used to the method that nylon facing material dyes to be:
Coloring agent is heated to 38 DEG C, is put into by nylon facing material, and be warming up to 65 DEG C with the heat up speed of 1 DEG C of every 2min, insulation 80min, cleans nylon facing material after cooling, dries.
After staining reagent prepared by application the present embodiment, the soaping fastness of nylon facing material is 5 grades, and K/S value is 9.135.
embodiment 2
The formula of coloring agent of the present invention is as follows:
Butyl methacrylate 8kg, odium stearate 3kg, dibutyl phthalate 1kg, triglycerides 3kg, styrene 2kg, polyethylene glycol 0.5kg, sodium peroxydisulfate 1.5kg, distilled water 120kg.
The preparation method of coloring agent of the present invention is:
The butyl methacrylate of proportional quantity, dibutyl phthalate, sodium peroxydisulfate and water are mixed, is heated to 70 DEG C, stir lower reaction 2 hours, remaining ingredient is added by proportional quantity, stir lower reaction 1 hour, obtained finished product after cooling.
Coloring agent of the present invention is used to the method that nylon facing material dyes to be:
Coloring agent is heated to 40 DEG C, is put into by nylon facing material, and be warming up to 65 DEG C with the heat up speed of 1 DEG C of every 3min, insulation 90min, cleans nylon facing material after cooling, dries.
After staining reagent prepared by application the present embodiment, the soaping fastness of nylon facing material is 5 grades, and K/S value is 9.807.
embodiment 3
The formula of coloring agent of the present invention is as follows:
Butyl methacrylate 5kg, odium stearate 5kg, dibutyl phthalate 2kg, triglycerides 4kg, styrene 3kg, polyethylene glycol 0.2kg, sodium peroxydisulfate 1.2kg, distilled water 130kg.
The preparation method of coloring agent of the present invention is:
The butyl methacrylate of proportional quantity, dibutyl phthalate, sodium peroxydisulfate and water are mixed, is heated to 80 DEG C, stir lower reaction 3 hours, remaining ingredient is added by proportional quantity, stir lower reaction 2 hours, obtained finished product after cooling.
Coloring agent of the present invention is used to the method that nylon facing material dyes to be:
Coloring agent is heated to 35 DEG C, is put into by nylon facing material, and be warming up to 65 DEG C with the heat up speed of 1 DEG C of every 3min, insulation 70min, cleans nylon facing material after cooling, dries.
After staining reagent prepared by application the present embodiment, the soaping fastness of nylon facing material is 4 grades, and K/S value is 9.074.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. a coloring agent, is characterized in that: described coloring agent is made up of each component of following mass fraction: butyl methacrylate 5-8 part, odium stearate 3-5 part, dibutyl phthalate 1-2 part, triglycerides 3-4 part, styrene 2-3 part, polyethylene glycol 0.2-0.5 part, sodium peroxydisulfate 1.2-1.5 part, distilled water 120-130 part.
2. coloring agent according to claim 1, is characterized in that: described coloring agent is made up of each component of following mass fraction: butyl methacrylate 6 parts, odium stearate 4 parts, dibutyl phthalate 1.5 parts, triglycerides 3.5 parts, styrene 2.5 parts, polyethylene glycol 0.4 part, sodium peroxydisulfate 1.3 parts, distilled water 125 parts.
3. the preparation method of the coloring agent described in claim 1 or 2, it is characterized in that: step is as follows: the butyl methacrylate of proportional quantity, dibutyl phthalate, sodium peroxydisulfate and water are mixed, be heated to 70-80 DEG C, stir lower reaction 2-3 hour, remaining ingredient is added by proportional quantity, stir lower reaction 1-2 hour, obtained finished product after cooling.
4. use the method that the coloring agent described in claim 1 or 2 dyes to nylon facing material, it is characterized in that: step is as follows: the coloring agent described in claim 1 or 2 is heated to 35-40 DEG C, nylon facing material is put into, 65 DEG C are warming up to the heat up speed of 1 DEG C of every 2-3min, insulation 70-90min, clean nylon facing material after cooling, dry.