CN104277558A - Anti-UV (anti-ultraviolet) aluminum pigment and preparation method thereof - Google Patents
Anti-UV (anti-ultraviolet) aluminum pigment and preparation method thereof Download PDFInfo
- Publication number
- CN104277558A CN104277558A CN201410509325.2A CN201410509325A CN104277558A CN 104277558 A CN104277558 A CN 104277558A CN 201410509325 A CN201410509325 A CN 201410509325A CN 104277558 A CN104277558 A CN 104277558A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethanol
- component
- drying
- stirred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-UV (anti-ultraviolet) aluminum pigment. The invention is characterized in that the aluminum pigment is prepared from the following raw materials in parts by weight: 30-40 parts of micron-scale flake aluminum powder, 4-6 parts of nano zinc oxide, 6-8 parts of ethyl orthosilicate, 0.5-0.8 part of silane coupling agent KH-550, 1-2 parts of cassia oil, 2-4 parts of oleic acid, 0.01-0.03 part of chlorogenic acid, 3-6 parts of ethyl acetate, 0.5-1 part of epoxy soybean oil, 1-2 parts of diethyl phthalate, 0.2-0.4 part of phenyl o-hydroxybenzoate, 0.1-0.2 part of glycerin monostearate, 0.1-0.2 part of silane coupling agent A-151 and 1-2 parts of composite assistant. The aluminum pigment has favorable anti-UV effect and antibacterial auxiliary effect, and has the advantages of favorable compatibility with organic resins and high practicality.
Description
Technical field
The present invention relates to metallic pigment field, be specifically related to a kind of uv-resistant aluminium pigment and preparation method thereof.
Background technology
Metallic pigment are the metallicss with lamellar morphology, its role is to decorate or special process performance gives goods with a kind of metallic color outward appearance for target or feature.The purposes of metallic pigment can be roughly divided into top coat (coating, ink, powder coating etc.) and plastics.In these purposes, make use of the characteristic that metallic pigment are total: high metal luster, high covering power and even thin layers film can be formed.Aluminium powder, Cu-Zn alloy powder and zinc powder are current most widely used metallic pigment.
Nano zine oxide is a kind of polyfunctional new inorganic material, crystal is hexagonal structure, and its granular size, about 1-100 nanometer, has much special character, as non-migratory, fluorescence, piezoelectricity, absorption and scatters ultraviolet ability etc., its UV-preventing rate is up to 98%; Meanwhile, the performance that it also has antibacterial bacteriostatic, the anti-enzyme of taste of dispelling etc. is unique.
Summary of the invention
The object of this invention is to provide a kind of uv-resistant aluminium pigment.
The present invention is achieved by the following technical solutions:
A kind of uv-resistant aluminium pigment, it is made up of the raw material of following weight parts:
Micron-sized flake aluminum 30-40, nano zine oxide 4-6, tetraethoxy 6-8, silane resin acceptor kh-550 0.5-0.8, Oleum Cinnamomi 1-2, oleic acid 2-4, chlorogenic acid 0.01-0.03, ethyl acetate 3-6, epoxy soybean oil 0.5-1, diethyl phthalate 1-2, salicylic acid phenyl ester 0.2-0.4, glyceryl monostearate 0.1-0.2, silane coupling A-151 0.1-0.2, composite assistant 1-2;
Composite assistant is made up of the raw material of following weight part:
Nano-calcium carbonate 30-40, nano silicon 5-10, titanate coupling agent 0.5-1, white mineral oil 1-2, linseed oil 1-2, alizarin assistant 0.5-1, Tenox PG 0.5-1;
The preparation method of composite assistant:
Nano-calcium carbonate and nano silicon are added suitable quantity of water, add titanate coupling agent after mixing, 60-80 DEG C is fully stirred 0.5-1h, adds the mixed solution of white mineral oil, linseed oil, Tenox PG and alizarin assistant after drying, 110-130 DEG C is fully stirred 0.5-1h, to obtain final product.
A preparation method for uv-resistant aluminium pigment, comprises the following steps:
(1) mixed solvent of ammoniacal liquor, distilled water and ethanol is prepared as component A, with alcohol dilution tetraethoxy as B component; Micron-sized flake aluminum is added in appropriate dehydrated alcohol, add silane coupling A-151, after stirred under nitrogen atmosphere 0.5-1h, with 1-2 drip/rate of addition of s drips component A and B component simultaneously respectively, dropping limit, limit is stirred, dropwise rear 40-45 DEG C of reaction 6-8h, with absolute ethanol washing after suction filtration, vacuum-drying, weight ratio=the 1:2:5 of ammoniacal liquor, distilled water and ethanol in described component A, described ammonia concn is 25%, the weight ratio=1:2 of ethanol and tetraethoxy in described B component;
(2) in reaction vessel, add aluminium powder, nano zine oxide and ethanol in proper amount after process in (1), silane resin acceptor kh-550 is added after being uniformly mixed, 60-80 DEG C of heated and stirred back flow reaction 3-6h, rear drying is repeatedly washed with ethanol, add oleic acid, Oleum Cinnamomi and q. s. toluene again, 30-40 DEG C of stirring reaction 1-2h, repeatedly washs after centrifugal, vacuum-drying;
(3) after mixing with all the other raw materials, 50-60 DEG C is stirred 1-2h, takes out final vacuum and is drying to obtain.
Advantage of the present invention is:
1., by the improvement of recipe optimization, make aluminium pigment have good anti-ultraviolet function, be applicable to the fields such as roof coatings; Also has certain antibacterial and mouldproof effect simultaneously.
2., by the surface modification of aluminium powder, improve the hydrophobicity of aluminium pigment and the dispersing property in resin, good, practical with the consistency of resin.
Embodiment
Non-limiting examples of the present invention is as follows:
Embodiment 1
A kind of uv-resistant aluminium pigment, is prepared from by the component raw material of following weight (kg):
Micron-sized flake aluminum 35, nano zine oxide 5, tetraethoxy 7, silane resin acceptor kh-550 0.6, Oleum Cinnamomi 1.5, oleic acid 3, chlorogenic acid 0.02, ethyl acetate 5, epoxy soybean oil 0.6, diethyl phthalate 1.5, salicylic acid phenyl ester 0.3, glyceryl monostearate 0.15, silane coupling A-151 0.15, composite assistant 1.5;
Wherein, composite assistant is made up of the raw material of following weight (kg):
Nano-calcium carbonate 35, nano silicon 8, titanate coupling agent 0.8, white mineral oil 1.5, linseed oil 1.5, alizarin assistant 0.8, Tenox PG 0.8;
The preparation method of composite assistant:
Nano-calcium carbonate and nano silicon are added suitable quantity of water, add titanate coupling agent after mixing, 80 DEG C are fully stirred 0.5h, add the mixed solution of white mineral oil, linseed oil, Tenox PG and alizarin assistant after drying, 120 DEG C are fully stirred 0.5h, to obtain final product.
Its preparation method comprises the following steps:
(1) mixed solvent of ammoniacal liquor, distilled water and ethanol is prepared as component A, with alcohol dilution tetraethoxy as B component; Micron-sized flake aluminum is added in appropriate dehydrated alcohol, add silane coupling A-151, after stirred under nitrogen atmosphere 0.5h, drip component A and B component respectively with the rate of addition of 1/s, dropping limit, limit is stirred simultaneously, dropwise rear 40 DEG C of reaction 8h, with absolute ethanol washing after suction filtration, vacuum-drying, the weight ratio=1:2:5 of ammoniacal liquor, distilled water and ethanol in described component A, described ammonia concn is 25%, the weight ratio=1:2 of ethanol and tetraethoxy in described B component;
(2) in reaction vessel, add aluminium powder, nano zine oxide and ethanol in proper amount after process in (1), silane resin acceptor kh-550 is added after being uniformly mixed, 70 DEG C of heated and stirred back flow reaction 5h, rear drying is repeatedly washed with ethanol, add oleic acid, Oleum Cinnamomi and q. s. toluene again, 30 DEG C of stirring reaction 2h, repeatedly wash after centrifugal, vacuum-drying;
(3) mix latter 60 DEG C with all the other raw materials and stir 1h, take out final vacuum and be drying to obtain.
Through inspection, the pigment coated surfacing of aluminium of the present embodiment is smooth, and glossiness is good, and feel is good.
Claims (2)
1. a uv-resistant aluminium pigment, is characterized in that it is made up of the raw material of following weight parts:
Micron-sized flake aluminum 30-40, nano zine oxide 4-6, tetraethoxy 6-8, silane resin acceptor kh-550 0.5-0.8, Oleum Cinnamomi 1-2, oleic acid 2-4, chlorogenic acid 0.01-0.03, ethyl acetate 3-6, epoxy soybean oil 0.5-1, diethyl phthalate 1-2, salicylic acid phenyl ester 0.2-0.4, glyceryl monostearate 0.1-0.2, silane coupling A-151 0.1-0.2, composite assistant 1-2;
Described composite assistant is made up of the raw material of following weight part:
Nano-calcium carbonate 30-40, nano silicon 5-10, titanate coupling agent 0.5-1, white mineral oil 1-2, linseed oil 1-2, alizarin assistant 0.5-1, Tenox PG 0.5-1;
The preparation method of described composite assistant is:
Nano-calcium carbonate and nano silicon are added suitable quantity of water, add titanate coupling agent after mixing, 60-80 DEG C is fully stirred 0.5-1h, adds the mixed solution of white mineral oil, linseed oil, Tenox PG and alizarin assistant after drying, 110-130 DEG C is fully stirred 0.5-1h, to obtain final product.
2. the preparation method of uv-resistant aluminium pigment according to claim 1, is characterized in that, comprise the following steps:
(1) mixed solvent of ammoniacal liquor, distilled water and ethanol is prepared as component A, with alcohol dilution tetraethoxy as B component; Micron-sized flake aluminum is added in appropriate dehydrated alcohol, add silane coupling A-151, after stirred under nitrogen atmosphere 0.5-1h, with 1-2 drip/rate of addition of s drips component A and B component simultaneously respectively, dropping limit, limit is stirred, dropwise rear 40-45 DEG C of reaction 6-8h, with absolute ethanol washing after suction filtration, vacuum-drying, weight ratio=the 1:2:5 of ammoniacal liquor, distilled water and ethanol in described component A, described ammonia concn is 25%, the weight ratio=1:2 of ethanol and tetraethoxy in described B component;
(2) in reaction vessel, add aluminium powder, nano zine oxide and ethanol in proper amount after process in (1), silane resin acceptor kh-550 is added after being uniformly mixed, 60-80 DEG C of heated and stirred back flow reaction 3-6h, rear drying is repeatedly washed with ethanol, add oleic acid, Oleum Cinnamomi and q. s. toluene again, 30-40 DEG C of stirring reaction 1-2h, repeatedly washs after centrifugal, vacuum-drying;
(3) after mixing with all the other raw materials, 50-60 DEG C is stirred 1-2h, takes out final vacuum and is drying to obtain.