CN104264233A - Refining method for wet frison - Google Patents
Refining method for wet frison Download PDFInfo
- Publication number
- CN104264233A CN104264233A CN201410604946.9A CN201410604946A CN104264233A CN 104264233 A CN104264233 A CN 104264233A CN 201410604946 A CN201410604946 A CN 201410604946A CN 104264233 A CN104264233 A CN 104264233A
- Authority
- CN
- China
- Prior art keywords
- told
- wet bar
- refining
- wet
- bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a refining method for wet frison, which comprises the following steps: (1) oil and glue removal; (2) primary scouring; (3) second scouring; and (4) drying or airing. The refining method for wet frison enables a refining period to be short and the process to be normative, so that a dried product of refined and processed wet frison is stable in quality.
Description
Technical field
The present invention relates to a kind of concise processing method, more particularly, particularly relate to the method for refining that a kind of wet bar is told.
Background technology
The main raw material of silk spinning is that bar is told, and it is the leftover bits and pieces in reeling silk production process.Bar tell concise be most of silk gum, grease, impurity etc. in order to remove in raw material, give full play of the intrinsic gloss of silk fiber and feel, also will keep the original physical and mechanical properties of silk fiber simultaneously as far as possible.Bar is told and is comprised the dry bar Tuhe bar that wets and tell two kinds, and it is exactly that the direct dry bar of airing that do not have got off from filature production line is told that wet bar is told, and bar is told concise these two kinds of methods concise comprising concise and wet bar that dry bar tells and tell.Conventional wet bar is told after under filature production line, first will be placed in soda ash solution to soak after 20 days to one month to carry out multiple white silk again, and the activity time cycle is long, and the wet bar after soaking for a long time is told and attached strong smell, the very difficult elimination of this smell.Therefore, the concise cycle that the method for refining urgently providing a kind of wet bar newly to tell makes wet bar tell is shorter, quality is more stable,
Summary of the invention
The object of the present invention is to provide the method for refining that a kind of wet bar is told, this kind of method for refining makes short, process specification of concise cycle, practices the wet bar refined silk steady quality of system processing.
The technical solution used in the present invention is as follows:
The method for refining that wet bar is told, wherein, comprises the steps:
(1) de-oiling glue: wet bar is told to deoil and comes unstuck;
(2) first white silk: the wet bar after coming unstuck deoiling is told, and puts into the water being added with additive and soaks, then pull out and rinse with clear water, spin-dry;
(3) multiple white silk: tell the water boiling of putting into and with the addition of chemical industry soda ash and sodium hydrosulfite by completing the wet bar after just practicing, clean and spin-dry in clear water reserviors after taking the dish out of the pot, then the wet bar after drying is told and put into the water being added with additive and soak, then pull drying out.
(4) to dry or airing: the wet bar after multiple white silk is told and puts in drying room or under the sun after dryness in the sun, form wet bar refined silk.
Preferably, in step (2), additive comprises chemical industry K6, hydrogen peroxide and soda ash, and additional proportion is that every 100kg bar that wets is told and added 1.5kg chemical industry K6,15kg hydrogen peroxide and 1.5kg soda ash respectively.
Preferably, in step (2), the coolant-temperature gage scope of immersion is 85 DEG C ~ 90 DEG C.
Preferably, in step (2), soak time is 9 ~ 12 hours.
Preferably, in step (3), the temperature range of the water of boiling is 80 DEG C ~ 90 DEG C, and digestion time is 15 ~ 25 minutes.
Preferably, in step (3), spun silk softener and glacial acetic acid, additional proportion is that the dry bar of every 100kg tells the glacial acetic acid adding 0.9kg spun silk softener and 0.8kg respectively.
Preferably, in step (3), the time of immersion is 15 ~ 25 minutes.
Compared with prior art, the beneficial effect that the present invention has is:
The method for refining that a kind of wet bar of the present invention is told, refinery practice first the wet bar got off from filature production line is told it through the process of de-oiling glue, then wet bar is told and to clean after soaking certain hour in the water being positioned over and being placed with additive and to dry, just can carry out multiple experienced step, like this, the refinery practice cycle that wet bar is told is shorter, and the smell that the wet bar after just practicing is told easily is removed.The refinery practice specification more that method for refining of the present invention makes wet bar tell, the wet bar refined silk quality practicing system processing is more stable.
Detailed description of the invention
Below in conjunction with detailed description of the invention, technical scheme of the present invention is described in further detail, but does not form any limitation of the invention.
The method for refining that a kind of wet bar of the present invention is told, wherein, comprises the steps:
(1) de-oiling glue: wet bar is told the degumming process that deoils, removes the factice that wet bar tells self attachment.
(2) first white silk: the wet bar after coming unstuck deoiling is told, and puts into the water being added with additive and soaks, then pull out and rinse with clear water, spin-dry.After wet bar is told and soak certain hour in the water that placed additive, just can reach and reply effect that is active and oxidation.The method for refining that traditional wet bar is told is that wet bar is told to be placed in soda ash solution and soaked 20 days to one month, and process period is long, and the wet bar after soaking for a long time is told and attached strong taste, and this taste is difficult to elimination.Refinery practice time in first white silk step that wet bar of the present invention is told shortens greatly, makes the whole concise cycle shorter.Because the time of just practicing is short, what the wet bar after just practicing was told can not produce strong smell.
Additive comprises chemical industry K6, hydrogen peroxide and soda ash, and additional proportion is that every 100kg bar that wets is told and added 1.5kg chemical industry K6,15kg hydrogen peroxide and 1.5kg soda ash respectively, and the coolant-temperature gage scope of immersion is 85 DEG C ~ 90 DEG C, and soak time is 9 ~ 12 hours.The water dissolved by utilizing such concentration ratio additive and temperature value control to soak in certain limit value, it can be made to reply active and oxidation effectiveness is better.
(3) multiple white silk: tell the water boiling of putting into and with the addition of chemical industry soda ash and sodium hydrosulfite by completing the wet bar after just practicing, clean and spin-dry in clear water reserviors after taking the dish out of the pot, then the wet bar after drying is told and put into the water being added with additive and soak, then pull drying out.
The temperature range of the water of boiling is 80 DEG C ~ 90 DEG C, and digestion time is 15 ~ 25 minutes.Spun silk softener and glacial acetic acid, additional proportion is that the dry bar of every 100kg tells the glacial acetic acid adding 0.9kg spun silk softener and 0.8kg respectively, and the time of immersion is 15 ~ 25 minutes, and by boiling again and the immersion of multiple white silk, the quality that the bar that can wet is told is more stable.
(4) to dry or airing: the wet bar after multiple white silk is told and puts in drying room or under the sun after dryness in the sun, form wet bar refined silk.
The refinery practice specification more that method for refining of the present invention makes wet bar tell, it is more stable that the bar practicing system processing tells refined silk quality.
The foregoing is only better embodiment of the present invention, all do within the scope of the spirit and principles in the present invention any amendment, equivalent to replace and improvement etc., all should be included within protection scope of the present invention.
Claims (7)
1. the method for refining told of wet bar, is characterized in that, comprise the steps:
(1) de-oiling glue: wet bar is told to deoil and comes unstuck;
(2) first white silk: the wet bar after coming unstuck deoiling is told, and puts into the water being added with additive and soaks, then pull out and rinse with clear water, spin-dry;
(3) multiple white silk: tell the water boiling of putting into and with the addition of chemical industry soda ash and sodium hydrosulfite by completing the wet bar after just practicing, clean and spin-dry in clear water reserviors after taking the dish out of the pot, then the wet bar after drying is told and put into the water being added with additive and soak, then pull drying out;
(4) to dry or airing: the wet bar after multiple white silk is told and puts in drying room or under the sun after dryness in the sun, form wet bar refined silk.
2. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (2), additive comprises chemical industry K6, hydrogen peroxide and soda ash, and additional proportion is that every 100kg bar that wets is told and added 1.5kg chemical industry K6,15kg hydrogen peroxide and 1.5kg soda ash respectively.
3. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (2), the coolant-temperature gage scope of immersion is 85 DEG C ~ 90 DEG C.
4. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (2), soak time is 9 ~ 12 hours.
5. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (3), the temperature range of the water of boiling is 80 DEG C ~ 90 DEG C, and digestion time is 15 ~ 25 minutes.
6. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (3), spun silk softener and glacial acetic acid, additional proportion is that the dry bar of every 100kg tells the glacial acetic acid adding 0.9kg spun silk softener and 0.8kg respectively.
7. the method for refining told of a kind of wet bar according to claim 1, it is characterized in that, in step (3), the time of immersion is 15 ~ 25 minutes.