CN104263236A - Anticorrosive protective layer for chemical equipment - Google Patents
Anticorrosive protective layer for chemical equipment Download PDFInfo
- Publication number
- CN104263236A CN104263236A CN201410477952.2A CN201410477952A CN104263236A CN 104263236 A CN104263236 A CN 104263236A CN 201410477952 A CN201410477952 A CN 201410477952A CN 104263236 A CN104263236 A CN 104263236A
- Authority
- CN
- China
- Prior art keywords
- parts
- favorable
- tert
- chemical industry
- yttrium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive protective layer for chemical equipment, which is composed of the following components in percentage by weight: 1-2 parts of polyethyleneglycol bis stearate, 2-3 parts of polydimethylsiloxane, 1-2 parts of yttrium oxide, 1-2 parts of sodium pyrophosphate, 1-2 parts of selenium acetylacetonate, 4-5 parts of chromium chloride, 1-2 parts of nano magnesium hydroxide, 2-5 parts of ammonium molybdate, 3-7 parts of perchloroethylene, 7-8 parts of decabromodiphenyl oxide, 2-3 parts of polyamide resin, 1-2 parts of p-tert-butyl benzoic acid, 1-2 parts of vinyl trimethoxy silane, 1-2 parts of allyl heptanoate and 5-6 parts of isomerized tridecyl alcohol polyethenoxy ether. The anticorrosive protective layer has the advantages of favorable brushing property, favorable wettability for object surfaces, high drying speed of the paint film, favorable mechanical property, favorable acid/alkali resistance, favorable water resistance and favorable organic solvent resistance.
Description
Technical field
The present invention relates to chemical industry equipment corrosion protective covering.
Background technology
Existing chemical industry equipment corrosion protective covering, performance is not also very desirable.
Summary of the invention
The object of the present invention is to provide a kind of chemical industry equipment corrosion protective covering, its brushing property is good, good to the wettability of object plane, and drying varniss is fast, better mechanical property, resistance to acids and bases, water tolerance and organic solvent resistance are better.
For achieving the above object, technical scheme of the present invention is a kind of chemical industry equipment corrosion protective covering of design, consists of the following composition by weight percentage:
1 ~ 2 part of Triglycol distearate,
2 ~ 3 parts of polydimethylsiloxanes,
1 ~ 2 part of yttrium oxide,
1 ~ 2 part of trisodium phosphate,
1 ~ 2 part of methyl ethyl diketone selenium,
4 ~ 5 parts of chromium chlorides,
1 ~ 2 part of nanometric magnesium hydroxide,
2 ~ 5 parts of ammonium molybdates,
3 ~ 7 parts of chlorinated polyvinyl chloride,
7 ~ 8 parts of decabromodiphynly oxides,
2 ~ 3 parts of polyamide resins,
1 ~ 2 part of p-tert-butyl benzoic acid,
1 ~ 2 part of vinyltrimethoxy silane,
1 ~ 2 part of allyl oenanthate,
5 ~ 6 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
1.2 parts of Triglycol distearates,
2.3 parts of polydimethylsiloxanes,
1.2 parts of yttrium oxide,
1.2 parts of trisodium phosphates,
1.2 parts of methyl ethyl diketone selenium,
4.5 parts of chromium chlorides,
1.2 parts of nanometric magnesium hydroxides,
2.5 parts of ammonium molybdates,
3.7 parts of chlorinated polyvinyl chloride,
7.8 parts of decabromodiphynly oxides,
2.3 parts of polyamide resins,
1.2 parts of p-tert-butyl benzoic acids,
1.2 parts of vinyltrimethoxy silanes,
1.2 parts of allyl oenanthates,
5.6 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
2 parts of Triglycol distearates,
3 parts of polydimethylsiloxanes,
2 parts of yttrium oxide,
2 parts of trisodium phosphates,
2 parts of methyl ethyl diketone selenium,
5 parts of chromium chlorides,
2 parts of nanometric magnesium hydroxides,
5 parts of ammonium molybdates,
7 parts of chlorinated polyvinyl chloride,
8 parts of decabromodiphynly oxides,
3 parts of polyamide resins,
2 parts of p-tert-butyl benzoic acids,
2 parts of vinyltrimethoxy silanes,
2 parts of allyl oenanthates,
6 parts of isomerous tridecanol polyoxyethylene ethers.
Preferably, chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
1 part of Triglycol distearate,
2 parts of polydimethylsiloxanes,
1 part of yttrium oxide,
1 part of trisodium phosphate,
1 part of methyl ethyl diketone selenium,
4 parts of chromium chlorides,
1 part of nanometric magnesium hydroxide,
2 parts of ammonium molybdates,
3 parts of chlorinated polyvinyl chloride,
7 parts of decabromodiphynly oxides,
2 parts of polyamide resins,
1 part of p-tert-butyl benzoic acid,
1 part of vinyltrimethoxy silane,
1 part of allyl oenanthate,
5 parts of isomerous tridecanol polyoxyethylene ethers.
Advantage of the present invention and beneficial effect are: provide a kind of chemical industry equipment corrosion protective covering, its brushing property is good, good to the wettability of object plane, and drying varniss is fast, better mechanical property, resistance to acids and bases, water tolerance and organic solvent resistance are better.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
1.2 parts of Triglycol distearates,
2.3 parts of polydimethylsiloxanes,
1.2 parts of yttrium oxide,
1.2 parts of trisodium phosphates,
1.2 parts of methyl ethyl diketone selenium,
4.5 parts of chromium chlorides,
1.2 parts of nanometric magnesium hydroxides,
2.5 parts of ammonium molybdates,
3.7 parts of chlorinated polyvinyl chloride,
7.8 parts of decabromodiphynly oxides,
2.3 parts of polyamide resins,
1.2 parts of p-tert-butyl benzoic acids,
1.2 parts of vinyltrimethoxy silanes,
1.2 parts of allyl oenanthates,
5.6 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 2
Chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
2 parts of Triglycol distearates,
3 parts of polydimethylsiloxanes,
2 parts of yttrium oxide,
2 parts of trisodium phosphates,
2 parts of methyl ethyl diketone selenium,
5 parts of chromium chlorides,
2 parts of nanometric magnesium hydroxides,
5 parts of ammonium molybdates,
7 parts of chlorinated polyvinyl chloride,
8 parts of decabromodiphynly oxides,
3 parts of polyamide resins,
2 parts of p-tert-butyl benzoic acids,
2 parts of vinyltrimethoxy silanes,
2 parts of allyl oenanthates,
6 parts of isomerous tridecanol polyoxyethylene ethers.
Embodiment 3
Chemical industry equipment corrosion protective covering, consists of the following composition by weight percentage:
1 part of Triglycol distearate,
2 parts of polydimethylsiloxanes,
1 part of yttrium oxide,
1 part of trisodium phosphate,
1 part of methyl ethyl diketone selenium,
4 parts of chromium chlorides,
1 part of nanometric magnesium hydroxide,
2 parts of ammonium molybdates,
3 parts of chlorinated polyvinyl chloride,
7 parts of decabromodiphynly oxides,
2 parts of polyamide resins,
1 part of p-tert-butyl benzoic acid,
1 part of vinyltrimethoxy silane,
1 part of allyl oenanthate,
5 parts of isomerous tridecanol polyoxyethylene ethers.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. chemical industry equipment corrosion protective covering, is characterized in that, consists of the following composition by weight percentage:
1 ~ 2 part of Triglycol distearate,
2 ~ 3 parts of polydimethylsiloxanes,
1 ~ 2 part of yttrium oxide,
1 ~ 2 part of trisodium phosphate,
1 ~ 2 part of methyl ethyl diketone selenium,
4 ~ 5 parts of chromium chlorides,
1 ~ 2 part of nanometric magnesium hydroxide,
2 ~ 5 parts of ammonium molybdates,
3 ~ 7 parts of chlorinated polyvinyl chloride,
7 ~ 8 parts of decabromodiphynly oxides,
2 ~ 3 parts of polyamide resins,
1 ~ 2 part of p-tert-butyl benzoic acid,
1 ~ 2 part of vinyltrimethoxy silane,
1 ~ 2 part of allyl oenanthate,
5 ~ 6 parts of isomerous tridecanol polyoxyethylene ethers.
2. chemical industry equipment corrosion protective covering according to claim 1, is characterized in that, consist of the following composition by weight percentage:
1.2 parts of Triglycol distearates,
2.3 parts of polydimethylsiloxanes,
1.2 parts of yttrium oxide,
1.2 parts of trisodium phosphates,
1.2 parts of methyl ethyl diketone selenium,
4.5 parts of chromium chlorides,
1.2 parts of nanometric magnesium hydroxides,
2.5 parts of ammonium molybdates,
3.7 parts of chlorinated polyvinyl chloride,
7.8 parts of decabromodiphynly oxides,
2.3 parts of polyamide resins,
1.2 parts of p-tert-butyl benzoic acids,
1.2 parts of vinyltrimethoxy silanes,
1.2 parts of allyl oenanthates,
5.6 parts of isomerous tridecanol polyoxyethylene ethers.
3. chemical industry equipment corrosion protective covering according to claim 1, is characterized in that, consist of the following composition by weight percentage:
2 parts of Triglycol distearates,
3 parts of polydimethylsiloxanes,
2 parts of yttrium oxide,
2 parts of trisodium phosphates,
2 parts of methyl ethyl diketone selenium,
5 parts of chromium chlorides,
2 parts of nanometric magnesium hydroxides,
5 parts of ammonium molybdates,
7 parts of chlorinated polyvinyl chloride,
8 parts of decabromodiphynly oxides,
3 parts of polyamide resins,
2 parts of p-tert-butyl benzoic acids,
2 parts of vinyltrimethoxy silanes,
2 parts of allyl oenanthates,
6 parts of isomerous tridecanol polyoxyethylene ethers.
4. chemical industry equipment corrosion protective covering according to claim 1, is characterized in that, consist of the following composition by weight percentage:
1 part of Triglycol distearate,
2 parts of polydimethylsiloxanes,
1 part of yttrium oxide,
1 part of trisodium phosphate,
1 part of methyl ethyl diketone selenium,
4 parts of chromium chlorides,
1 part of nanometric magnesium hydroxide,
2 parts of ammonium molybdates,
3 parts of chlorinated polyvinyl chloride,
7 parts of decabromodiphynly oxides,
2 parts of polyamide resins,
1 part of p-tert-butyl benzoic acid,
1 part of vinyltrimethoxy silane,
1 part of allyl oenanthate,
5 parts of isomerous tridecanol polyoxyethylene ethers.