CN104212333A - Corrosion-resistant paint for chemical equipment - Google Patents
Corrosion-resistant paint for chemical equipment Download PDFInfo
- Publication number
- CN104212333A CN104212333A CN201410477954.1A CN201410477954A CN104212333A CN 104212333 A CN104212333 A CN 104212333A CN 201410477954 A CN201410477954 A CN 201410477954A CN 104212333 A CN104212333 A CN 104212333A
- Authority
- CN
- China
- Prior art keywords
- parts
- favorable
- methylphenol
- tetra
- fatty alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a corrosion-resistant paint for chemical equipment, which is composed of the following components in parts by weight: 2-3 parts of fatty alcohol polyethenoxy ether, 1-2 parts of tetra-n-butyl amino bromide, 1-2 parts of decabromodiphenyl oxide, 1-2 parts of methyltrimethoxy silane, 1-2 parts of perchloroethylene, 3-4 parts of nano aluminum hydroxide, 4-5 parts of molybdenum trioxide, 1-2 parts of 2-methoxy-4-methylphenol, 3-4 parts of selenium acetylacetonate, 2-3 parts of polyamide resin, 6-7 parts of triazine polycarboxylic acid compound and 1-2 parts of allyl heptanoate. The corrosion-resistant paint is convenient to use and easy to manufacture, and has the advantages of favorable brushing property and favorable wettability for object planes; and the paint film has the advantages of high drying speed, favorable mechanical properties, favorable acid/alkali resistance, favorable water resistance and favorable organic solvent resistance.
Description
Technical field
The present invention relates to chemical industry equipment anticorrosive coating.
Background technology
Existing chemical industry equipment anticorrosive coating, performance is not also very desirable.
Summary of the invention
The object of the present invention is to provide a kind of chemical industry equipment anticorrosive coating, it is easy to use, be easy to manufacture, brushing property is good, good to the wettability of object plane, and drying varniss is fast, better mechanical property, resistance to acids and bases, water tolerance and organic solvent resistance are better.
For achieving the above object, technical scheme of the present invention is a kind of chemical industry equipment anticorrosive coating of design, consists of the following composition by weight:
2-3 part fatty alcohol-polyoxyethylene ether,
The amino bromide of 1-2 part tetra-n-butyl,
1-2 part decabromodiphynly oxide,
1-2 part methyltrimethoxy silane,
1-2 part chlorinated polyvinyl chloride,
3-4 part nano level aluminium hydroxide,
4-5 part molybdic oxide,
2-methoxyl group-4-the methylphenol of 1-2 part,
3-4 part methyl ethyl diketone selenium,
2-3 part polyamide resin,
6-7 part triazines multi-carboxylic acid compounds,
1-2 part allyl oenanthate.
Preferably, chemical industry equipment anticorrosive coating, consists of the following composition by weight:
2.3 parts of fatty alcohol-polyoxyethylene ether,
1.2 parts of amino bromides of tetra-n-butyl,
1.2 parts of decabromodiphynly oxides,
1.2 parts of methyltrimethoxy silanes,
1.2 parts of chlorinated polyvinyl chloride,
3.4 parts of nano level aluminium hydroxides,
4.5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1.2 parts,
3.4 parts of methyl ethyl diketone selenium,
2.3 parts of polyamide resins,
6.7 parts of triazines multi-carboxylic acid compounds,
1.2 parts of allyl oenanthates.
Preferably, chemical industry equipment anticorrosive coating, consists of the following composition by weight:
2 parts of fatty alcohol-polyoxyethylene ether,
1 part of amino bromide of tetra-n-butyl,
1 part of decabromodiphynly oxide,
1 part of methyltrimethoxy silane,
1 part of chlorinated polyvinyl chloride,
3 parts of nano level aluminium hydroxides,
4 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1 part,
3 parts of methyl ethyl diketone selenium,
2 parts of polyamide resins,
6 parts of triazines multi-carboxylic acid compounds,
1 part of allyl oenanthate.
Preferably, chemical industry equipment anticorrosive coating, consists of the following composition by weight:
3 parts of fatty alcohol-polyoxyethylene ether,
2 parts of amino bromides of tetra-n-butyl,
2 parts of decabromodiphynly oxides,
2 parts of methyltrimethoxy silanes,
2 parts of chlorinated polyvinyl chloride,
4 parts of nano level aluminium hydroxides,
5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 2 parts,
4 parts of methyl ethyl diketone selenium,
3 parts of polyamide resins,
7 parts of triazines multi-carboxylic acid compounds,
2 parts of allyl oenanthates.
Advantage of the present invention and beneficial effect are: provide a kind of chemical industry equipment anticorrosive coating, it is easy to use, be easy to manufacture, brushing property is good, good to the wettability of object plane, and drying varniss is fast, better mechanical property, resistance to acids and bases, water tolerance and organic solvent resistance are better.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Chemical industry equipment anticorrosive coating, consists of the following composition by weight:
2.3 parts of fatty alcohol-polyoxyethylene ether,
1.2 parts of amino bromides of tetra-n-butyl,
1.2 parts of decabromodiphynly oxides,
1.2 parts of methyltrimethoxy silanes,
1.2 parts of chlorinated polyvinyl chloride,
3.4 parts of nano level aluminium hydroxides,
4.5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1.2 parts,
3.4 parts of methyl ethyl diketone selenium,
2.3 parts of polyamide resins,
6.7 parts of triazines multi-carboxylic acid compounds,
1.2 parts of allyl oenanthates.
Embodiment 2
Chemical industry equipment anticorrosive coating, consists of the following composition by weight:
2 parts of fatty alcohol-polyoxyethylene ether,
1 part of amino bromide of tetra-n-butyl,
1 part of decabromodiphynly oxide,
1 part of methyltrimethoxy silane,
1 part of chlorinated polyvinyl chloride,
3 parts of nano level aluminium hydroxides,
4 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1 part,
3 parts of methyl ethyl diketone selenium,
2 parts of polyamide resins,
6 parts of triazines multi-carboxylic acid compounds,
1 part of allyl oenanthate.
Embodiment 3
Chemical industry equipment anticorrosive coating, consists of the following composition by weight:
3 parts of fatty alcohol-polyoxyethylene ether,
2 parts of amino bromides of tetra-n-butyl,
2 parts of decabromodiphynly oxides,
2 parts of methyltrimethoxy silanes,
2 parts of chlorinated polyvinyl chloride,
4 parts of nano level aluminium hydroxides,
5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 2 parts,
4 parts of methyl ethyl diketone selenium,
3 parts of polyamide resins,
7 parts of triazines multi-carboxylic acid compounds,
2 parts of allyl oenanthates.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. chemical industry equipment anticorrosive coating, is characterized in that, consists of the following composition by weight:
2-3 part fatty alcohol-polyoxyethylene ether,
The amino bromide of 1-2 part tetra-n-butyl,
1-2 part decabromodiphynly oxide,
1-2 part methyltrimethoxy silane,
1-2 part chlorinated polyvinyl chloride,
3-4 part nano level aluminium hydroxide,
4-5 part molybdic oxide,
2-methoxyl group-4-the methylphenol of 1-2 part,
3-4 part methyl ethyl diketone selenium,
2-3 part polyamide resin,
6-7 part triazines multi-carboxylic acid compounds,
1-2 part allyl oenanthate.
2. chemical industry equipment anticorrosive coating according to claim 1, is characterized in that, consist of the following composition by weight:
2.3 parts of fatty alcohol-polyoxyethylene ether,
1.2 parts of amino bromides of tetra-n-butyl,
1.2 parts of decabromodiphynly oxides,
1.2 parts of methyltrimethoxy silanes,
1.2 parts of chlorinated polyvinyl chloride,
3.4 parts of nano level aluminium hydroxides,
4.5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1.2 parts,
3.4 parts of methyl ethyl diketone selenium,
2.3 parts of polyamide resins,
6.7 parts of triazines multi-carboxylic acid compounds,
1.2 parts of allyl oenanthates.
3. chemical industry equipment anticorrosive coating according to claim 1, is characterized in that, consist of the following composition by weight:
2 parts of fatty alcohol-polyoxyethylene ether,
1 part of amino bromide of tetra-n-butyl,
1 part of decabromodiphynly oxide,
1 part of methyltrimethoxy silane,
1 part of chlorinated polyvinyl chloride,
3 parts of nano level aluminium hydroxides,
4 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 1 part,
3 parts of methyl ethyl diketone selenium,
2 parts of polyamide resins,
6 parts of triazines multi-carboxylic acid compounds,
1 part of allyl oenanthate.
4. chemical industry equipment anticorrosive coating according to claim 1, is characterized in that, consist of the following composition by weight:
3 parts of fatty alcohol-polyoxyethylene ether,
2 parts of amino bromides of tetra-n-butyl,
2 parts of decabromodiphynly oxides,
2 parts of methyltrimethoxy silanes,
2 parts of chlorinated polyvinyl chloride,
4 parts of nano level aluminium hydroxides,
5 parts of molybdic oxides,
2-methoxyl group-4-the methylphenol of 2 parts,
4 parts of methyl ethyl diketone selenium,
3 parts of polyamide resins,
7 parts of triazines multi-carboxylic acid compounds,
2 parts of allyl oenanthates.