CN104262939A - TPU (Thermoplastic Poly Urethane) thin film smooth anti-blocking masterbatch - Google Patents
TPU (Thermoplastic Poly Urethane) thin film smooth anti-blocking masterbatch Download PDFInfo
- Publication number
- CN104262939A CN104262939A CN201410532183.1A CN201410532183A CN104262939A CN 104262939 A CN104262939 A CN 104262939A CN 201410532183 A CN201410532183 A CN 201410532183A CN 104262939 A CN104262939 A CN 104262939A
- Authority
- CN
- China
- Prior art keywords
- master batch
- smooth
- tpu
- antiblocking
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a TPU (Thermoplastic Poly Urethane) thin film smooth anti-blocking masterbatch which is characterized in that the masterbatch comprises the following components in percentage by weight: 70-90 percent of TPU, 2-10 percent of an anti-blocking agent, 2-10 percent of a smooth agent, 1-5 percent of a compatibilizer and 0.5-2 percent of an antioxidant; the total percentage by weight of the above components is 100 percent; a carrier of the masterbatch is an polyurethane elastomer; the anti-blocking agent is a Halloysite nanotube with a diameter of 30-50 nanometers; the smooth agent is one or more of organic stearate and silicon resin; the compatibilizer is one or more of silane coupling agent; the antioxidant is an antioxidant 1010 or an antioxidant 245 or an antioxidant 20N; the masterbatch is obtained by pelleting by adopting a traditional double screw blending process. The TPU thin film smooth anti-blocking masterbatch has the benefits that with the adoption of the TPU masterbatch provided by the invention, a TPU thin film has an excellent opening smoothness effect; the masterbatch is simple in production process and low in price, and the strength of the TPU thin film can be enhanced to a certain degree.
Description
Technical field
The present invention relates to the smooth antiblocking master batch of a kind of TPU film, belong to plastics functional agent technical field.
Background technology
TPU film, in production and use procedure, due to capillary existence, when pressurized or when being heated, to be easily bonded together and not easily separated.The adhesion of plastics film is many-sided reason, may be to form vacuum closed state because film closes between caudacoria, not easily separates; Also may be that after film forming, its surface has and a large amount of exposes molecular chain, after two panels film closes, create the mutual winding between macromolecular chain, make it open.In order to prevent the generation of this phenomenon, usually add a certain amount of opening slipping agent when producing plastics film.Common opening agent is inorganic talcum powder, diatomite etc., develops into organic amine hydroxybenzene, erucicamide and EBS derivative etc. afterwards, and at present synthetic silica to do slipping agent application in the film also comparatively extensive.
But there is side effect all to some extent in current used slipping agent, the problems such as main manifestations slipping agent is easily separated out, the dispersion of inorganic opening agent.Therefore, develop a kind of efficient, environmental protection, cheap TPU co-extruded films slipping agent is TPU membrane field problem demanding prompt solution.
Summary of the invention
The present invention, for solving above-mentioned the deficiencies in the prior art, its objective is that to provide a kind of opening smooth effective, and production technique is simple, and efficiently, environmental protection, the smooth antiblocking master batch of cheap novel TPU film.
For achieving the above object, the present invention solves the technical scheme that its technical problem adopts:
The smooth antiblocking master batch of a kind of TPU film, is characterized in that: this master batch comprises following component:
TPU：70-90％
Antiblocking agent: 2-10%
Slipping agent: 2-10%
Expanding material: 1-5%
Oxidation inhibitor: 0.5-2%
Above-mentioned each component concentration sum is 100%.
The carrier of this master batch is polyurethane elastomer.
Described antiblocking agent is the halloysite nanotubes of diameter 30-50nm.
Described slipping agent is one or more in organic stearate, silicone resin.
Described organic stearate is Zinic stearas or calcium stearate.
Described expanding material is one or more in silane coupling agent.
Described silane coupling agent is γ-methacryloxypropyl trimethoxy silane or vinyltriethoxysilane.
Described oxidation inhibitor is antioxidant 1010, oxidation inhibitor 245 or oxidation inhibitor 20N.
This master batch adopts traditional twin screw blending technology granulation to obtain.
The invention has the beneficial effects as follows: adopt the TPU master batch in the present invention, prepared TPU film has the excellent smooth effect of opening, and the production technique of master batch is simple, low price, and can the intensity of enhancement TPU film to a certain degree.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
The smooth antiblocking master batch of a kind of TPU film, is characterized in that: this master batch comprises following component:
TPU：70-90％
Antiblocking agent: 2-10%
Slipping agent: 2-10%
Expanding material: 1-5%
Oxidation inhibitor: 0.5-2%
Above-mentioned each component concentration sum is 100%.
The carrier of this master batch is polyurethane elastomer.
Described antiblocking agent is the halloysite nanotubes of diameter 30-50nm.
Described slipping agent is one or more in organic stearate, silicone resin.
Described organic stearate is Zinic stearas or calcium stearate.
Described expanding material is one or more in silane coupling agent.
Described silane coupling agent is γ-methacryloxypropyl trimethoxy silane or vinyltriethoxysilane.
Described oxidation inhibitor is antioxidant 1010, oxidation inhibitor 245 or oxidation inhibitor 20N.
This master batch adopts traditional twin screw blending technology granulation to obtain.
Protection scope of the present invention is not limited to following embodiment, and therefore, every technical scheme of being replaced by simple numerical value, being equal to the formation such as replacement or equivalent transformation, is all formed specific embodiments of the invention, and form protection scope of the present invention.
Embodiment 1: the smooth antiblocking master batch of a kind of TPU film, each composition weight of master batch is composed as follows: TPU:83%, halloysite nanotubes: 6%, silicone resin powder: 6%, silane coupling agent γ-methacryloxypropyl trimethoxy silane: 4%, oxidation inhibitor: 1%.
After being mixed by said components homogenizer, utilize twin screw extruder granulation, obtain the smooth antiblocking master batch of TPU film.
Embodiment 2: the smooth antiblocking master batch of a kind of TPU film, each composition weight of master batch is composed as follows: TPU:80%, halloysite nanotubes: 10%, Zinic stearas: 4%, silane coupling agent vinyl triethoxyl silane: 5%, oxidation inhibitor: 1%.
After being mixed by said components homogenizer, utilize twin screw extruder granulation, obtain the smooth antiblocking master batch of TPU film.
Embodiment 3: the smooth antiblocking master batch of a kind of TPU film, each composition weight of master batch is composed as follows: TPU:90%, halloysite nanotubes: 4%, calcium stearate: 10%, silane coupling agent vinyl Trimethoxy silane: 5%, oxidation inhibitor: 1%.
After being mixed by said components homogenizer, utilize twin screw extruder granulation, obtain the smooth antiblocking master batch of TPU film.
Embodiment 4: the smooth antiblocking master batch of a kind of TPU film, each composition weight of master batch is composed as follows: TPU:70%, halloysite nanotubes: 2%, calcium stearate: 2%, silane coupling agent vinyl Trimethoxy silane: 1%, oxidation inhibitor: 0.5%.
After being mixed by said components homogenizer, utilize twin screw extruder granulation, obtain the smooth antiblocking master batch of TPU film.
Claims (9)
1. the smooth antiblocking master batch of TPU film, is characterized in that: this master batch comprises following component:
TPU：70-90％
Antiblocking agent: 2-10%
Slipping agent: 2-10%
Expanding material: 1-5%
Oxidation inhibitor: 0.5-2%
Above-mentioned each component concentration sum is 100%.
2. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: the carrier of this master batch is polyurethane elastomer.
3. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: described antiblocking agent is the halloysite nanotubes of diameter 30-50nm.
4. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: described slipping agent is one or more in organic stearate, silicone resin.
5. the smooth antiblocking master batch of TPU film according to claim 4, is characterized in that: described organic stearate is Zinic stearas or calcium stearate.
6. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: described expanding material is one or more in silane coupling agent.
7. the smooth antiblocking master batch of TPU film according to claim 6, is characterized in that: described silane coupling agent is γ-methacryloxypropyl trimethoxy silane or vinyltriethoxysilane.
8. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: described oxidation inhibitor is antioxidant 1010, oxidation inhibitor 245 or oxidation inhibitor 20N.
9. the smooth antiblocking master batch of TPU film according to claim 1, is characterized in that: this master batch adopts traditional twin screw blending technology granulation to obtain.