CN1042464C - Aluminium-nickel base contained conductor and making method thereof - Google Patents
Aluminium-nickel base contained conductor and making method thereof Download PDFInfo
- Publication number
- CN1042464C CN1042464C CN93104472A CN93104472A CN1042464C CN 1042464 C CN1042464 C CN 1042464C CN 93104472 A CN93104472 A CN 93104472A CN 93104472 A CN93104472 A CN 93104472A CN 1042464 C CN1042464 C CN 1042464C
- Authority
- CN
- China
- Prior art keywords
- aluminium
- powder
- nickel
- base contained
- nickel base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to an aluminium-nickel base contained conductor and a preparation method thereof. The aluminium-nickel base contained conductor comprises the components of 1.0 to 8.0 wt% of aluminium powder, 1.0 to 8.0 wt% of boron powder, and the equilibrium amount of nickel powder, and the sum of all the components is equal to 100. The preparation method is a powder metallurgy method; in the method, materials are ground, mixed, pressed, sintered in vacuum, pulverized and fine ground after being blended; thereby, powders which can be prepared into conductive slurry and burnt into a nickel aluminum boron conductor in the air are obtained. The powders can be printed on a thermistor electrode substrate so as to manufacture a thermistor electrode, and the aging rate thereof meets the requirements.
Description
A kind of aluminium-nickel base contained conductor and preparation method.The present invention relates to a kind of aluminium-nickel base contained conductor and preparation method thereof, particularly a kind of aluminium-nickel base contained conductor that electrocondution slurry uses and preparation method thereof for preparing.
The present invention is the improvement invention of CN87100475.Ni-based conductor of CN87100475-kind boracic and preparation method thereof has been invented and has been added with a small amount of aluminium powder, boron-the aluminium of zinc powder-zinc-Ni-based conductor, providing with common metal replaces noble metal to prepare the approach of conductor, can make plasma display panel, also can make the thermistor electrode, reduce the conductor cost.But, on the one hand with boron-aluminium-zinc-when Ni-based conductor is made the thermistor electrode, aging coefficient higher (>100%), desirable not enough, burn till the temperature requirement higher (900-110 ℃) of conductor on the other hand.
The objective of the invention is to improve the prescription of the Ni-based conductor of boracic, the aging coefficient reduction meets the requirements when using conductor to make the thermistor electrode; To reduce the temperature of burning till conductor in addition, reduce energy consumption.
The aluminium-nickel base contained conductor of being invented is a base-material with the nickel powder, contains small amount of aluminum, it is characterized in that also containing small amount of boron and compositional range is:
Aluminium powder 1.0-8.0 weight portion
Boron powder 1.0-8.0 weight portion and
Aequum nickel powder granularity 0.075mm
Each component sum is 100 weight portions.
Its preferred component is:
(1) aluminium powder 3.0 weight portions
Boron powder 4.0 weight portions
Nickel powder 93.0 weight portion granularity 0.075mm
(2) aluminium powder 5.0 weight portions
Boron powder 4.0 weight portions
Nickel powder 91.0 weight portion granularity 0.075mm
Aluminium-nickel base contained conductor with the powder metallurgic method preparation is invented comprises:
1, with nearly 1 hour of nickel, aluminium, boron powder mix grinding in agate mortar of working good, mix grinding was even.
2, compound pressure 2.5-4.5 ton/centimetre
2Condition presses down knot.
3, press caking in vacuum degree about 1.33 * 10
-1Handkerchief, sintering under the temperature 600-1100 ℃ of condition is incubated nearly 1 hour.
4, the caking of the pressure behind the sintering is pulverized and is the superfines of particle diameter<0.5 μ m.
With the thermistor electrode of the aluminium-nickel base contained conductor made of being invented, measure its aging coefficient, aging coefficient<30%.
Advantage of the present invention is: (1) aluminium-nickel base contained conductor is used to make the thermistor electrode, and aging coefficient<30% meets the requirements.(2) its preparation method sintering temperature reduces, and helps reducing energy consumption.
Embodiment:
Nickel powder 93.0 gram+boron powder 4.0 gram+aluminium powders 3.0 grams of example 1,0.075mm mix, with 3.0 tons/centimetre
2Pressure is pressed knot, in vacuum degree 1.33 * 10
-1Pa, sintering under 700 ℃ of conditions of temperature is incubated 1 hour.Agglomerate cooling back is pulverized and is the superfines of particle diameter<0.5 μ m.
Nickel powder 91.0 gram+boron powder 4.0 gram+aluminium powders 5.0 grams of example 2,0.075mm mix, with 3.0 tons/centimetre
2Pressure is pressed knot, in vacuum degree 1.33 * 10
-1Pa, sintering under 750 ℃ of conditions of temperature is incubated 1 hour.Agglomerate cooling back is pulverized and is the superfines of particle diameter<0.5 μ m.
Superfines 94.0 grams that use-case 1, example 2 are made, each adds and contains boron-silicon-aluminum glass 6.0 grams, and each mix grinding is even; Each adds the ethyl cellulose organic carrier with the terpinol dissolving, and ratio accounts for the 15-20% of slurry total weight; Rolling evenly after, be that the silk screen printing of 0.045-0.075mm is on the thermistor electrode base sheet with the aperture respectively; Respectively 150 ℃ of oven dry 10 minutes; Respectively in continuous tunnel furnace sintering 25-40 minute then, nickel aluminium boron electrode; Each is ohmic contact with the thermistor electrode base sheet.After each measured the thermistor initial value, heat ageing was 1000 hours when load is arranged, and measures its resistance variations, and aging front and back resistance change rate all<30%.
Claims (5)
1, a kind ofly prepare the aluminium-nickel base contained conductor that electrocondution slurry is used, it is characterized in that also containing the small amount of boron powder and compositional range is:
Aluminium powder 1.0-8.0 weight portion
Boron powder 1.0-8.0 weight portion and
Aequum nickel powder granularity 0.075mm
Each component sum is 100 weight portions.
2,, it is characterized in that component is according to the described aluminium-nickel base contained conductor of claim 1:
Aluminium powder 3.0 weight portions
Boron powder 4.0 weight portions
Nickel powder 93.0 weight portion granularity 0.075mm
3,, it is characterized in that component is according to the described aluminium-nickel base contained conductor of claim 1:
Aluminium powder 5.0 weight portions
Boron powder 4.0 weight portions
Nickel powder 91.0 weight portion granularity 0.075mm
4, the preparation method of the described aluminium-nickel base contained conductor of claim 1 is characterized in that:
(1) with nearly 1 hour of nickel, aluminium, boron powder mix grinding in agate mortar of working good, mix grinding was even.
(2) compound presses down knot in pressure 2.5-4.5 ton/centimetre 2 conditions.
(3) press caking in vacuum degree nearly 1.33 * 10
-1Handkerchief, temperature 600-110 ℃ of condition sintering is incubated nearly 1 hour.
(4) caking of the pressure behind the sintering is pulverized and is the superfines of particle diameter<0.5 μ m.
5, application rights requires 1 described aluminium-nickel base contained conductor, it is characterized in that it is made as the thermistor electrode, measures the aging coefficient of thermistor electrode, aging coefficient<30%.