CN104231878B - A kind of communication equipment electrically conducting coating and preparation method thereof - Google Patents
A kind of communication equipment electrically conducting coating and preparation method thereof Download PDFInfo
- Publication number
- CN104231878B CN104231878B CN201410480887.9A CN201410480887A CN104231878B CN 104231878 B CN104231878 B CN 104231878B CN 201410480887 A CN201410480887 A CN 201410480887A CN 104231878 B CN104231878 B CN 104231878B
- Authority
- CN
- China
- Prior art keywords
- parts
- communication equipment
- electrically conducting
- conducting coating
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of communication equipment electrically conducting coating and preparation method thereof, this coating in mass parts containing following composition: 5 ~ 15 parts, graphite, potassium stannate 0.5 ~ 3 part, 0.3 ~ 0.7 part, aluminium hydroxide, titanium dioxide 2 ~ 5 parts, quartz sand 0.6 ~ 1.5 part, 13 ~ 20 parts, vibrin, polyvinylpyrrolidone 0.5 ~ 1.5 part, ethyl cellosolve 18 ~ 26 parts, st-yrax 0.05 ~ 0.15 part, titanic acid ester 0.02 ~ 0.04 part.Coating provided by the invention has excellent conductivity, and it is shock-resistant simultaneously, water resistance good, and time of drying is fast, also has the ability getting rid of accumulate static charge.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of communication equipment electrically conducting coating and preparation method thereof.
Background technology
At the society of information develop rapidly, communication equipment is the requisite daily necessitiess of people.Communication equipment has mobile phone, computer, network interface card, receiving set etc.Communication equipment coating must possess excellent conductivity, impact resistance, water resistance and snappiness.But the conductivity of existing communication equipment coating is not high, shock-resistant poor with water resistance, effectively can not improve the functional quality of communication equipment.
Summary of the invention
The technical problem solved: for conduction, the shortcoming that shock-resistant and water resistance is poor of existing communication equipment coating, the invention provides a kind of communication equipment electrically conducting coating and preparation method thereof.
Technical scheme: a kind of communication equipment electrically conducting coating, in mass parts containing following composition: 5 ~ 15 parts, graphite, potassium stannate 0.5 ~ 3 part, 0.3 ~ 0.7 part, aluminium hydroxide, titanium dioxide 2 ~ 5 parts, quartz sand 0.6 ~ 1.5 part, 13 ~ 20 parts, vibrin, polyvinylpyrrolidone 0.5 ~ 1.5 part, ethyl cellosolve 18 ~ 26 parts, st-yrax 0.05 ~ 0.15 part, titanic acid ester 0.02 ~ 0.04 part.
A kind of communication equipment electrically conducting coating described above, in mass parts containing following composition: 8 ~ 12 parts, graphite, potassium stannate 1.5 ~ 2.3 parts, 0.4 ~ 0.6 part, aluminium hydroxide, titanium dioxide 3 ~ 4 parts, quartz sand 0.9 ~ 1.2 part, 15 ~ 18 parts, vibrin, polyvinylpyrrolidone 0.9 ~ 1.2 part, ethyl cellosolve 20 ~ 23 parts, st-yrax 0.08 ~ 0.11 part, titanic acid ester 0.025 ~ 0.03 part.
The preparation process of a kind of communication equipment electrically conducting coating described above is as follows: graphite, titanium dioxide, aluminium hydroxide and quartz sand are mixed, then vibrin is added, mix, finally add potassium stannate, polyvinylpyrrolidone, ethyl cellosolve, st-yrax and titanic acid ester, mix and get product.
Beneficial effect: a kind of communication equipment electrically conducting coating provided by the invention and preparation method thereof, this coating has excellent conductivity, and it is shock-resistant simultaneously, water resistance good, and time of drying is fast, also has the ability getting rid of accumulate static charge.
Embodiment
Describe the present invention below in conjunction with embodiment.
embodiment 1
The present embodiment provides a kind of communication equipment electrically conducting coating, in mass parts containing following composition: 5 parts, graphite, potassium stannate 0.5 part, 0.3 part, aluminium hydroxide, titanium dioxide 2 parts, quartz sand 0.6 part, 13 parts, vibrin, polyvinylpyrrolidone 0.5 part, ethyl cellosolve 18 parts, st-yrax 0.05 part, titanic acid ester 0.02 part.
A kind of preparation process of communication equipment electrically conducting coating is as follows: graphite, titanium dioxide, aluminium hydroxide and quartz sand are mixed, then vibrin is added, mix, finally add potassium stannate, polyvinylpyrrolidone, ethyl cellosolve, st-yrax and titanic acid ester, mix and get product.
The resistance of the coating that the present embodiment provides is 55 Ω, snappiness 6 grades, and impact strength is 60N/m, and water tolerance is good, and time of drying is fast.
embodiment 2
The present embodiment provides a kind of communication equipment electrically conducting coating, in mass parts containing following composition: 8 parts, graphite, potassium stannate 1.5 parts, 0.4 part, aluminium hydroxide, titanium dioxide 3 parts, quartz sand 0.9 part, 15 parts, vibrin, polyvinylpyrrolidone 0.9 part, ethyl cellosolve 20 parts, st-yrax 0.08 part, titanic acid ester 0.025 part.
A kind of preparation process of communication equipment electrically conducting coating is as follows: graphite, titanium dioxide, aluminium hydroxide and quartz sand are mixed, then vibrin is added, mix, finally add potassium stannate, polyvinylpyrrolidone, ethyl cellosolve, st-yrax and titanic acid ester, mix and get product.
The resistance of the coating that the present embodiment provides is 52 Ω, snappiness 6 grades, and impact strength is 62N/m, and water tolerance is good, and time of drying is fast.
embodiment 3
The present embodiment provides a kind of communication equipment electrically conducting coating, in mass parts containing following composition: 12 parts, graphite, potassium stannate 2.3 parts, 0.6 part, aluminium hydroxide, titanium dioxide 4 parts, quartz sand 1.2 parts, 18 parts, vibrin, polyvinylpyrrolidone 1.2 parts, ethyl cellosolve 23 parts, st-yrax 0.11 part, titanic acid ester 0.03 part.
A kind of preparation process of communication equipment electrically conducting coating is as follows: graphite, titanium dioxide, aluminium hydroxide and quartz sand are mixed, then vibrin is added, mix, finally add potassium stannate, polyvinylpyrrolidone, ethyl cellosolve, st-yrax and titanic acid ester, mix and get product.
The resistance of the coating that the present embodiment provides is 48 Ω, snappiness 6 grades, and impact strength is 65N/m, and water tolerance is good, and time of drying is fast.
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (1)
1. a communication equipment electrically conducting coating, it is characterized in that, in mass parts containing following composition: 8 ~ 12 parts, graphite, potassium stannate 1.5 ~ 2.3 parts, 0.4 ~ 0.6 part, aluminium hydroxide, titanium dioxide 3 ~ 4 parts, quartz sand 0.9 ~ 1.2 part, 15 ~ 18 parts, vibrin, polyvinylpyrrolidone 0.9 ~ 1.2 part, ethyl cellosolve 20 ~ 23 parts, st-yrax 0.08 ~ 0.11 part, titanic acid ester 0.025 ~ 0.03 part;
Described a kind of communication equipment electrically conducting coating is prepared by following preparation method: graphite, titanium dioxide, aluminium hydroxide and quartz sand are mixed, then vibrin is added, mix, finally add potassium stannate, polyvinylpyrrolidone, ethyl cellosolve, st-yrax and titanic acid ester, mix and get product.