CN104231788A - High-grade polyvinyl acetate paint for interior decoration - Google Patents
High-grade polyvinyl acetate paint for interior decoration Download PDFInfo
- Publication number
- CN104231788A CN104231788A CN201410403192.0A CN201410403192A CN104231788A CN 104231788 A CN104231788 A CN 104231788A CN 201410403192 A CN201410403192 A CN 201410403192A CN 104231788 A CN104231788 A CN 104231788A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- water
- polyvinyl acetate
- kathon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-grade polyvinyl acetate paint for interior decoration. The paint is prepared from the following ingredients in parts by weight: 3-5 parts of ethoxylated alkyl sodium sulfide, 120-180 parts of polyvinyl acetate latex, 0.3-0.6 part of Kathon, 0.1-0.5 part of potassium tripolyphosphate, 4-8 parts of sodium silicate, 2-6 parts of fatty alcohol sodium sulfate, 20-30 parts of ethylene glycol, 20-30 parts of calcium silicate, 5-8 parts of alcohol ester-12, 100-200 parts of rutile, 50-80 parts of aluminum silicate, 100-200 parts of calcium carbonate and 400-500 parts of water. The paint has the beneficial effects that the water resistance is good, and no blistering and shedding phenomena occur after the paint is soaked in water for 24 hours; the adhesion is good, and no spallation exists; the appearance of a coating film is flat and uniform, and the heat resistance and scrub resistance are good.
Description
Technical field
The invention belongs to technical field of coatings, more specifically relate to a kind of high-grade Vinyl Acetate Copolymer ester paint for upholstery.
Background technology
Interior wall coating is exactly the emulsion paint generally fitted up.Interior wall paint also makes interior wall coating comprise liquid coating and powder coating, and common emulsion paint, wall paint belong to liquid coating.Emulsion paint is thinner with water, be a kind of easy construction, safe, water-fastness, good permeability coating, it can mix different color and lusters according to different scheme of colo(u)r.Kind: water-based inner wall paint, oiliness interior wall paint, dry powder type interior wall paint, belongs to water-borne coatings, and primarily of water, emulsion, pigment, filler, additive five kinds of compositions are formed.And popularizing along with humanity concept, and the formation of novel harmonious society, the interior wall coating designing a kind of water tolerance and erasibility excellence is very important.
Summary of the invention
The object of the invention is to the deficiency overcoming prior art existence, a kind of high-grade Vinyl Acetate Copolymer ester paint for upholstery is provided.
For achieving the above object, this invention takes following technical scheme:
For a high-grade Vinyl Acetate Copolymer ester paint for upholstery, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 3 ~ 5, polyvinyl acetate emulsion: 120 ~ 180,
Kathon CG: 0.3 ~ 0.6, Potassium tripolyphosphate: 0.1 ~ 0.5, water glass: 4 ~ 8,
Sodium alkyl sulfate: 2 ~ 6, ethylene glycol: 20 ~ 30, Calucium Silicate powder: 20 ~ 30,
Alcohol ester-12: 5 ~ 8, rutile: 100 ~ 200, pure aluminium silicate: 50 ~ 80,
Calcium carbonate: 100 ~ 200, water: 400 ~ 500.
The preparation method of described Vinyl Acetate Copolymer ester paint is: said components is added high speed dispersor respectively, high speed dispersion 20 ~ 30 minutes, qualified to fineness; Discharging, filters, packaging, warehouse-in.
Compared with prior art, the present invention has following beneficial effect:
1, salient features: total solids divides/% (quality): 50.4, total solids divides/% (volume): 30.6, viscosity/KU:82.88, PVC/%:68.9; 2, water-tolerant, to soak after 24h without bubbling, obscission in water; 3, sticking power is good, without avalanche; 4, appearance of film even uniform, thermotolerance, erasibility are good, the widespread production not division of history into periods can replace current material.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
For a high-grade Vinyl Acetate Copolymer ester paint for upholstery, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 3, polyvinyl acetate emulsion: 120,
Kathon CG: 0.3, Potassium tripolyphosphate: 0.1, water glass: 4,
Sodium alkyl sulfate: 2, ethylene glycol: 20, Calucium Silicate powder: 20, alcohol ester-12: 5,
Rutile: 100, pure aluminium silicate: 50, calcium carbonate: 100, water: 400.
Embodiment 2
For a high-grade Vinyl Acetate Copolymer ester paint for upholstery, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 5, polyvinyl acetate emulsion: 180,
Kathon CG: 0.6, Potassium tripolyphosphate: 0.5, water glass: 8,
Sodium alkyl sulfate: 6, ethylene glycol: 30, Calucium Silicate powder: 30, alcohol ester-12: 8,
Rutile: 200, pure aluminium silicate: 80, calcium carbonate: 200, water: 500.
Embodiment 3
For a high-grade Vinyl Acetate Copolymer ester paint for upholstery, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 4, polyvinyl acetate emulsion: 160,
Kathon CG: 0.5, Potassium tripolyphosphate: 0.4, water glass: 6,
Sodium alkyl sulfate: 4, ethylene glycol: 25, Calucium Silicate powder: 26, alcohol ester-12: 6,
Rutile: 160, pure aluminium silicate: 60, calcium carbonate: 150, water: 450.
Claims (4)
1., for a high-grade Vinyl Acetate Copolymer ester paint for upholstery, it is characterized in that, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 3 ~ 5, polyvinyl acetate emulsion: 120 ~ 180,
Kathon CG: 0.3 ~ 0.6, Potassium tripolyphosphate: 0.1 ~ 0.5, water glass: 4 ~ 8,
Sodium alkyl sulfate: 2 ~ 6, ethylene glycol: 20 ~ 30, Calucium Silicate powder: 20 ~ 30,
Alcohol ester-12: 5 ~ 8, rutile: 100 ~ 200, pure aluminium silicate: 50 ~ 80,
Calcium carbonate: 100 ~ 200, water: 400 ~ 500.
2. a kind of high-grade Vinyl Acetate Copolymer ester paint for upholstery according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 3, polyvinyl acetate emulsion: 120,
Kathon CG: 0.3, Potassium tripolyphosphate: 0.1, water glass: 4,
Sodium alkyl sulfate: 2, ethylene glycol: 20, Calucium Silicate powder: 20, alcohol ester-12: 5,
Rutile: 100, pure aluminium silicate: 50, calcium carbonate: 100, water: 400.
3. a kind of high-grade Vinyl Acetate Copolymer ester paint for upholstery according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 5, polyvinyl acetate emulsion: 180,
Kathon CG: 0.6, Potassium tripolyphosphate: 0.5, water glass: 8,
Sodium alkyl sulfate: 6, ethylene glycol: 30, Calucium Silicate powder: 30, alcohol ester-12: 8,
Rutile: 200, pure aluminium silicate: 80, calcium carbonate: 200, water: 500.
4. a kind of high-grade Vinyl Acetate Copolymer ester paint for upholstery according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Ethoxylated alkyl sodium sulphite: 4, polyvinyl acetate emulsion: 160,
Kathon CG: 0.5, Potassium tripolyphosphate: 0.4, water glass: 6,
Sodium alkyl sulfate: 4, ethylene glycol: 25, Calucium Silicate powder: 26, alcohol ester-12: 6,
Rutile: 160, pure aluminium silicate: 60, calcium carbonate: 150, water: 450.