CN104231763B - A kind of fibre board use fireproof paint and preparation method thereof - Google Patents
A kind of fibre board use fireproof paint and preparation method thereof Download PDFInfo
- Publication number
- CN104231763B CN104231763B CN201410480886.4A CN201410480886A CN104231763B CN 104231763 B CN104231763 B CN 104231763B CN 201410480886 A CN201410480886 A CN 201410480886A CN 104231763 B CN104231763 B CN 104231763B
- Authority
- CN
- China
- Prior art keywords
- parts
- fibre board
- board use
- fireproof paint
- epoxychloropropane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of fibre board use fireproof paint and preparation method thereof, this coating contains following composition in mass parts: 5～15 parts of Corvics, 15～30 parts of polyisobutene, 10～20 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 10～20 parts of esters, 1～5 part of melamine pyrophosphate, 3～8 parts, glass dust, 2～6 parts, decabromodiphenyl ether, 0.3～1.2 part of calgon, 0.5～1 part of epoxychloropropane, 1～4 part of copper chloride. Coating provided by the invention has excellent fire-resistant and water resistance, to the strong adhesion of fiberboard, can protect well fiberboard, extends the service life of fiberboard.
Description
Technical field
The present invention relates to paint field, relate in particular to a kind of fibre board use fireproof paint and preparation method thereof.
Background technology
Fiberboard is taking wood fibre or other plant cellulose fiber as raw material, applies the wood-based plate that Lauxite or other applicable adhesive are made. Fiberboard such as has a material intensity difference is little, not easy to crack evenly, in length and breadth at the advantage, of many uses. Development Fibreboard Production is the effective way of timber resources comprehensive utilization.
At present, the coating type that fiberboard surface applies has a lot, but their fire-resistant and water resistance is poor, can not play protective effect well.
Summary of the invention
The technical problem solving: the fire-resistant and poor shortcoming of water resistance for existing fibre board use coating, the invention provides a kind of fibre board use fireproof paint and preparation method thereof.
Technical scheme: a kind of fibre board use fireproof paint, contain following composition in mass parts: 5～15 parts of Corvics, 15～30 parts of polyisobutene, 10～20 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 10～20 parts of esters, 1～5 part of melamine pyrophosphate, 3～8 parts, glass dust, 2～6 parts, decabromodiphenyl ether, 0.3～1.2 part of calgon, 0.5～1 part of epoxychloropropane, 1～4 part of copper chloride.
A kind of fibre board use fireproof paint described above, contain following composition in mass parts: 7～12 parts of Corvics, 20～25 parts of polyisobutene, 13～17 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 14～18 parts of esters, 2～4 parts of melamine pyrophosphates, 4～6 parts, glass dust, 3～5 parts, decabromodiphenyl ether, 0.5～0.8 part of calgon, 0.6～0.9 part of epoxychloropropane, 1.5～3 parts of copper chlorides.
The preparation process of a kind of fibre board use fireproof paint described above is as follows: first Corvic, polyisobutene and chlorinated rubber are dropped in ceramic still, be uniformly mixed, obtain resin solution; Separately by tricresyl phosphate-(2,3-dibromopropyl) ester, melamine pyrophosphate, glass dust, decabromodiphenyl ether, calgon, epoxychloropropane and copper chloride grind after mixing, be ground to fineness≤50 μ m, then mix with resin solution, get product.
Beneficial effect: a kind of fibre board use fireproof paint provided by the invention and preparation method thereof, this coating has excellent fire-resistant and water resistance, to the strong adhesion of fiberboard, can protect well fiberboard, extends the service life of fiberboard.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail.
Embodiment 1
The present embodiment provides a kind of fibre board use fireproof paint, contain following composition in mass parts: 5 parts of Corvics, 15 parts of polyisobutene, 10 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 10 parts of esters, 1 part of melamine pyrophosphate, 3 parts, glass dust, 2 parts, decabromodiphenyl ether, 0.3 part of calgon, 0.5 part of epoxychloropropane, 1 part of copper chloride.
A kind of preparation process of fibre board use fireproof paint is as follows: first Corvic, polyisobutene and chlorinated rubber are dropped in ceramic still, be uniformly mixed, obtain resin solution; Separately by tricresyl phosphate-(2,3-dibromopropyl) ester, melamine pyrophosphate, glass dust, decabromodiphenyl ether, calgon, epoxychloropropane and copper chloride grind after mixing, be ground to fineness≤50 μ m, then mix with resin solution, get product.
Embodiment 2
The present embodiment provides a kind of fibre board use fireproof paint, contain following composition in mass parts: 7 parts of Corvics, 20 parts of polyisobutene, 13 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 14 parts of esters, 2 parts of melamine pyrophosphates, 4 parts, glass dust, 3 parts, decabromodiphenyl ether, 0.5 part of calgon, 0.6 part of epoxychloropropane, 1.5 parts of copper chlorides.
A kind of preparation process of fibre board use fireproof paint is as follows: first Corvic, polyisobutene and chlorinated rubber are dropped in ceramic still, be uniformly mixed, obtain resin solution; Separately by tricresyl phosphate-(2,3-dibromopropyl) ester, melamine pyrophosphate, glass dust, decabromodiphenyl ether, calgon, epoxychloropropane and copper chloride grind after mixing, be ground to fineness≤50 μ m, then mix with resin solution, get product.
Embodiment 3
The present embodiment provides a kind of fibre board use fireproof paint, contain following composition in mass parts: 12 parts of Corvics, 25 parts of polyisobutene, 17 parts of chlorinated rubbers, tricresyl phosphate-(2,3-dibromopropyl) 18 parts of esters, 4 parts of melamine pyrophosphates, 6 parts, glass dust, 5 parts, decabromodiphenyl ether, 0.8 part of calgon, 0.9 part of epoxychloropropane, 3 parts of copper chlorides.
A kind of preparation process of fibre board use fireproof paint is as follows: first Corvic, polyisobutene and chlorinated rubber are dropped in ceramic still, be uniformly mixed, obtain resin solution; Separately by tricresyl phosphate-(2,3-dibromopropyl) ester, melamine pyrophosphate, glass dust, decabromodiphenyl ether, calgon, epoxychloropropane and copper chloride grind after mixing, be ground to fineness≤50 μ m, then mix with resin solution, get product.
The technical performance index of a kind of fibre board use fireproof paint of above-described embodiment 1～embodiment 3, its testing result is as follows:
Testing result
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (2)
1. a fibre board use fireproof paint, is characterized in that, contains following composition in mass parts: 5～15 parts of Corvics, 15～30 parts of polyisobutene, 10～20 parts of chlorinated rubbers, tricresyl phosphate-10～20 parts of (2,3-dibromopropyl) esters, 1～5 part of melamine pyrophosphate, 3～8 parts, glass dust, 2～6 parts, decabromodiphenyl ether, 0.3～1.2 part of calgon, 0.5～1 part of epoxychloropropane, 1～4 part of copper chloride;
The preparation method of described a kind of fibre board use fireproof paint, the preparation process of the method is as follows: first Corvic, polyisobutene and chlorinated rubber are dropped in ceramic still, be uniformly mixed, obtain resin solution; Separately by tricresyl phosphate-(2,3-dibromopropyl) ester, melamine pyrophosphate, glass dust, decabromodiphenyl ether, calgon, epoxychloropropane and copper chloride grind after mixing, be ground to fineness≤50 μ m, then mix with resin solution, get product.
2. a kind of fibre board use fireproof paint according to claim 1, is characterized in that, contains following composition in mass parts: 7～12 parts of Corvics, 20～25 parts of polyisobutene, 13～17 parts of chlorinated rubbers, tricresyl phosphate-14～18 parts of (2,3-dibromopropyl) esters, 2～4 parts of melamine pyrophosphates, 4～6 parts, glass dust, 3～5 parts, decabromodiphenyl ether, 0.5～0.8 part of calgon, 0.6～0.9 part of epoxychloropropane, 1.5～3 parts of copper chlorides.