CN104231651A - Wood-plastic floor - Google Patents
Wood-plastic floor Download PDFInfo
- Publication number
- CN104231651A CN104231651A CN201410551404.XA CN201410551404A CN104231651A CN 104231651 A CN104231651 A CN 104231651A CN 201410551404 A CN201410551404 A CN 201410551404A CN 104231651 A CN104231651 A CN 104231651A
- Authority
- CN
- China
- Prior art keywords
- wood
- plastic floor
- calcium carbonate
- stearic acid
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wood-plastic floor, and the wood-plastic floor is composed of the components in parts by weight: waste plant fibre, talcum powder, light calcium carbonate, acrylate copolymer, modifier, stearic acid, acrylic ester foaming regulator, azodicarbonamide, fire retardant, activated calcium carbonate, chlorinated polyethylene, polyethylene, antiager RD, stearic acid, paraffin wax, stabilizer, antioxygen and plasticizer. The wood-plastic floor has the effect as follows: the strength of the wood-plastic floor is good, the wood does not absorb the water for avoiding swelling deformation, the wood-plastic floor can be recycled and reprocessed for use and also be processed in a biodegradable mode; the wood-plastic floor has wood secondary machining property, as sawed, planed, bonded, fixed through the nail or bolt, the proximate matter is standard and the installation is fast and convenient.
Description
?
technical field
The present invention relates to a kind of floor, particularly a kind of wood-plastic floor board.
Background technology
At present, flooring pavement material is generally various wood floors or compoiste wood floor.The feel of wood floors is pleasant, but easily water-swelling or drying distortions, in use often occurs contraction, dilatational strain, warps, problems of crack, and needs at substantial timber, and the production cycle is longer, and cost is higher.A kind of floor that compoiste wood floor mainly utilizes wood chip and tackiness agent and other additive to be formed through extrusion, its surface color and polish enriches, and cost is low, but there is the problems such as easily water suction distortion.
Wood-plastic floor board is the floor made from wood plastic composite, has the processing characteristics the same with timber, uses common instrument to get final product sawing, boring, upper nail, very convenient, can use as common wood.There is the woodiness touch of timber and the Waterproof corrosion characteristic of plastics simultaneously, make it become a kind of excellent property and the very durable anticorrosion building materials of outdoor water-proof.Prior art wood-plastic floor board is of a great variety, and the selectable leeway of people is very large.
Summary of the invention
The object of the invention is to overcome above-mentioned deficiency existing in prior art, provide a kind of intensity good, do not absorb water, there will not be the wood-plastic floor board of dilatational strain.
In order to realize foregoing invention object, the invention provides following technical scheme:
A kind of wood-plastic floor board, be made up of following composition by weight: discarded vegetable fibre 50-70 part, talcum powder 30-40 part, light calcium carbonate 8-10 part, acrylate copolymer 0.3-0.5 part, properties-correcting agent 0.1-0.7 part, stearic acid 0.2-0.3 part, esters of acrylic acid foaming control agent 4-4.5 part, Cellmic C 121 0.1-0.8 part, fire retardant 0.01-0.02 part, activated Calcium carbonate 3-12 part, chlorinatedpolyethylene 0.5-1.5 part, polyethylene 15-35 part, anti-aging agent RD 2-3 part, stearic acid 0.5-2 part, paraffin 1-2 part, stablizer 2-5 part, oxidation inhibitor 1-1.6 part, softening agent 0.5-1.5 part.
As preferred version of the present invention, described discarded vegetable fibre is waste wood, bamboo.
compared with prior art, beneficial effect of the present invention: wood-plastic floor board intensity of the present invention is good, does not absorb water, there will not be dilatational strain, and recyclable recycling also processes use again, also biodegradable; The present invention has the secondary workability of timber, and as sawed, can dig, bond, fix with nail or screw, various section bar codes and standards, construction and installation are efficient and convenient.
Embodiment
Below in conjunction with test example and embodiment, the present invention is described in further detail.But this should be interpreted as that the scope of the above-mentioned theme of the present invention is only limitted to following embodiment, all technology realized based on content of the present invention all belong to scope of the present invention.
Embodiment 1: a kind of wood-plastic floor board, is made up of following composition by weight: 55 parts discarded, vegetable fibre, talcum powder 32 parts, light calcium carbonate 8 parts, acrylate copolymer 0.3 part, properties-correcting agent 0.15 part, stearic acid 0.2 part, esters of acrylic acid foaming control agent 4.19 parts, Cellmic C 121 0.3 part, fire retardant 0.01 part, activated Calcium carbonate 5 parts, chlorinatedpolyethylene 0.5 part, polyethylene 18 parts, anti-aging agent RD 2-3 part, stearic acid 1.2 parts, 1.1 parts, paraffin, stablizer 2.5 parts, 1.15 parts, oxidation inhibitor, 5 parts, softening agent.
Claims (2)
1. a wood-plastic floor board, it is characterized in that, be made up of following composition by weight: discarded vegetable fibre 50-70 part, talcum powder 30-40 part, light calcium carbonate 8-10 part, acrylate copolymer 0.3-0.5 part, properties-correcting agent 0.1-0.7 part, stearic acid 0.2-0.3 part, esters of acrylic acid foaming control agent 4-4.5 part, Cellmic C 121 0.1-0.8 part, fire retardant 0.01-0.02 part, activated Calcium carbonate 3-12 part, chlorinatedpolyethylene 0.5-1.5 part, polyethylene 15-35 part, anti-aging agent RD 2-3 part, stearic acid 0.5-2 part, paraffin 1-2 part, stablizer 2-5 part, oxidation inhibitor 1-1.6 part, softening agent 0.5-1.5 part.
2. a kind of wood-plastic floor board according to claim 1, it is characterized in that, described discarded vegetable fibre is waste wood, bamboo.