CN104231478A - Polyvinyl chloride plastic colloidal particle formula - Google Patents
Polyvinyl chloride plastic colloidal particle formula Download PDFInfo
- Publication number
- CN104231478A CN104231478A CN201410458765.XA CN201410458765A CN104231478A CN 104231478 A CN104231478 A CN 104231478A CN 201410458765 A CN201410458765 A CN 201410458765A CN 104231478 A CN104231478 A CN 104231478A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- parts
- wax
- igelite
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyvinyl chloride plastic colloidal particle formula which comprises the following components: 1.5-4 parts of stabilizer, 0.1-0.5 part of lubricating agent, 0.1-0.3 part of PE wax, 8-12 parts of nitrogen and phosphorus flame retardants, 8-12 parts of bromide epoxy resin, 20-25 parts of plasticizer and 50-58 parts of resin powder. The polyvinyl chloride plastic colloidal particle formula prepared by the invention is low in price, high in yield, excellent in performance, environmentally friendly and antistatic and meets different requirements of customers.
Description
Technical field
The present invention relates to a kind of igelite micelle formula.
Background technology
The thermoplastic resin that polyvinyl chloride is polymerized under the effect of initiator by vinylchlorid, be the homopolymer of chloroethene, ryuron and vinyl chloride copolymer are referred to as vinyl chloride resin.Polyvinyl chloride has good mechanical property, about tensile strength 60mpa, shock strength 5-10kj/m
2, have excellent dielectric properties, but a poor stability to light and heat, more than 100 DEG C or will decompose through long-time solar exposure and produce hydrogenchloride, and autocatalytically decomposition causes variable color further, and physicals also declines rapidly.Stablizer must be added in actual applications to improve the stability to light and heat.In embody rule, rigid polyvinyl chloride and soft PVC can be divided into according to the major traits of polyvinyl chloride product, wherein rigid polyvinyl chloride is mainly used in the material of construction such as tubing, section bar aspect, and soft PVC is mainly used in the aspects such as cable, flexible pipe, electrical equipment.The hybrid technique comparative maturity of China's igelite micelle, particularly use opening rubber mixing machine quite perfect as the hybrid technique of major equipment, the igelite micelle formula of general property is also mature on the whole.Along with the raising of human environment protection consciousness and the concern to own health, many countries and tissue formulate strict standard and statute one after another, the use of restriction objectionable impurities on various product.
Summary of the invention
The present invention seeks to: provide that a kind of low price, yield rate are high, excellent property, meet client's difference and require and the igelite micelle formula of environmental protection, anti-electrostatic.
A technical scheme of the present invention is: a kind of igelite micelle formula, it comprises the composition of following weight part: stablizer 1.5-4 part, lubricant 0.1-0.5 part, PE wax 0.1-0.3 part, nitrogen phosphorus fire retardant 8-12 part, Australia epoxy resin 8-12 part, softening agent 20-25 part, resin-oatmeal 50-58 part.
Preferably, the number of described lubricant is greater than the number of wax.
Another technical scheme of the present invention is: a kind of preparation method of igelite micelle formula, first stablizer, lubricant, wax, nitrogen phosphorus fire retardant, Australia's epoxy resin, softening agent, resin-oatmeal are added homogenizer Inner and stir, then add twin screw extruder Inner extruding pelletization by spring charging machine.
Advantage of the present invention is: low price, yield rate are high, excellent property, meet client difference require and environmental protection, anti-electrostatic.
Embodiment
Embodiment: the specific embodiment that the invention provides a kind of igelite micelle formula, it comprises the composition of following weight part: stablizer 1.5-4 part, lubricant 0.1-0.5 part, PE wax 0.1-0.3 part, nitrogen phosphorus fire retardant 8-12 part, Australia epoxy resin 8-12 part, softening agent 20-25 part, resin-oatmeal 50-58 part.
Resin-oatmeal is the base mateiral of plastics micelle, the present invention selects S-65 type polyvinyl chloride (PVC) RESINS as the base resin powder of formula, softening agent can control polyvinyl chloride soft durometer, increase gloss, stablizer has stability to polyvinyl chloride, and it can slow down reaction, keeps chemical equilibrium, reduce surface tension, prevent the effects such as light, thermolysis or oxygenolysis.PE wax is compared with fats lubricant, and it can not bring disadvantageous effect to melt tension and Vicat softening point, and provides know clearly excellent resistance to bond and control mobilization.Nitrogen phosphorus fire retardant as a kind of environment friendly flame retardant, thus instead of traditional fire retardant better.ST can increase mobility and the oilness of product.Australia's epoxy resin has excellent physical and mechanical properties, electrical insulating property, drug-resistant performance and adhesive property.Adding coarse whiting is to increase viscosity and reducing cost.
Preferably, 2.6kg stablizer, 0.3kg lubricant, 0.2kgPE wax, 10kg nitrogen phosphorus fire retardant, 10kg Australia epoxy resin, 20kg softening agent, 50kg resin-oatmeal are added in homogenizer and stirs, then add extruding pelletization in twin screw extruder by spring charging machine.Thus obtained plastics micelle has flame-retarding characteristic, can reach about 50 ° through Shore durometer test.
The invention has the beneficial effects as follows: low price, yield rate are high, excellent property, environmental protection, anti-electrostatic.
Certain above-described embodiment, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalent transformations of doing according to the spirit of main technical schemes of the present invention or modification, all should be encompassed within protection scope of the present invention.
Claims (3)
1. an igelite micelle formula, is characterized in that it comprises the composition of following weight part: stablizer 1.5-4 part, lubricant 0.1-0.5 part, PE wax 0.1-0.3 part, nitrogen phosphorus fire retardant 8-12 part, Australia epoxy resin 8-12 part, softening agent 20-25 part, resin-oatmeal 50-58 part.
2. a kind of igelite micelle formula as claimed in claim 1, is characterized in that: the number of described lubricant is greater than the number of wax.
3. one kind adopts the preparation method of igelite micelle formula as claimed in claim 1, it is characterized in that: first stablizer, lubricant, wax, nitrogen phosphorus fire retardant, Australia's epoxy resin, softening agent, resin-oatmeal are added homogenizer Inner and stir, then add twin screw extruder Inner extruding pelletization by spring charging machine.