CN104213585A - Plane and facade construction method for APF self-adhibiting waterproof roll - Google Patents
Plane and facade construction method for APF self-adhibiting waterproof roll Download PDFInfo
- Publication number
- CN104213585A CN104213585A CN201410325259.3A CN201410325259A CN104213585A CN 104213585 A CN104213585 A CN 104213585A CN 201410325259 A CN201410325259 A CN 201410325259A CN 104213585 A CN104213585 A CN 104213585A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- self
- apf
- adhesive
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plane and facade construction method for an APF self-adhibiting waterproof roll. The unique construction process-pre-adhibiting method (border adhibiting method) is adopted; in the aspect of innovative construction method selection, dry adhibiting, wet adhibiting, border adhibiting, pre-adhibiting anti-stick methods can be adopted for construction, so that the labor strength is reduced, and the base layer requirement can be met; roll width can be selected from 1m to 2m, so that lap joint reduced, the construction is faster, and the plane and facade construction method is especially suitable for large-area construction; the plane and facade construction method is safe and environmentally friendly; construction on the APF self-adhibiting roll is cold construction, so that the plane and facade construction method is friendly to the environment, and the potential safety hazard of a construction site is eliminated.
Description
Technical field
The present invention relates to APE adhesive waterproof coil plane and elevation construction method.
Background technology
Current waterproofing material is varied, along with the progress in epoch, waterproofing materials, way are also constantly weeded out the old and bring forth the new, safer, environmental protection, construction are convenient, wherein APF adhesive waterproof coil is exactly one of the new material being applied in basement, roofing, this waterproofing materials way, construction technology standard also more imperfect at present and engineering method.
APF adhesive waterproof coil material has following characteristic
(1) solid and reliable, the easy construction of wet paving way bonding, quick, APF self-adhesive coiled material can directly be constructed on wet base, the effective adhesive that has of polymer cement mortar and basic unit and APF self-adhesive coiled material makes waterproofing system and structure form entirety, prevents " channeling water " seepage.
(2) set up defences flexibly, during the thickness≤3mm of polymer cement mortar, can be used as adhesive linkage; As the thickness >=6mm of polymer cement mortar, APF coiled material just can form the twice waterproofing course of tempering toughness with gentleness.
(3) APF coiled material can with any self-adhesive coiled material compound use, composition mixes completely, bonding firmly, setting up defences requires high waterproofing system.The self-adhesion of coiled material also can form composite waterproof system with the synthesized polymer material such as Ethylene Propylene Terpolymer, high density polyethylene (HDPE), meets the needs of high-grade waterproofing.
(4) specially designed APF self-adhesive coiled material not only bonds with polymer cement mortar layer firmly, can also form effective connection with concrete structure, forms the Trinitarian water proof structure of polymer cement mortar--APF self-adhesive coiled material--deck.
(5) cold construction, safety, environmental protection, APF coiled material composite waterproof system directly uses polymer cement mortar to paste, and preparation is simple, free from environmental pollution, without disaster hidden-trouble.
(6) good integrity, the seam between coiled material is tightly reliable, and adjacent web lap side seam is that self-adhesion face is bonding with glue face, self-adhesion face, and joint strength is high, has certain flexible and extendable performance simultaneously, stability of material is good, corrosion resistance is strong, long service life.
Summary of the invention
For above-mentioned technological deficiency, the present invention proposes APE adhesive waterproof coil plane and elevation construction method.
In order to solve the problems of the technologies described above, technical scheme of the present invention is as follows:
APE adhesive waterproof coil plane construction, comprises the steps:
11) contrast basic level requirement by conventional procedures process, reach basal plane requirement, then play installation of membrane reference line;
12) prepared polymer cement mortar step: cement adopts the Portland cement prepared polymer cement mortar of more than 32.5R level, by mixture and polymer master batch: Portland cement is that 1:10 is put and stirred in a reservoir according to weight ratio, then water ash be by weight 0.40 add water after, mixture in container will be contained in electric mixer and stir 1 ~ 2 minute to evenly, leave standstill for subsequent use after 5 ~ 8 minutes;
13) node processing step: first sheared by additional self-adhesive coiled material by thin portion shape detail section, paste in thin portion, after apparent size, shape are suitable, then will add self-adhesive coiled material stickup;
14) APF self-adhesive coiled material step is overlay: be layered on basal plane by APF self-adhesive coiled material view picture by snap the line location sky, the antiseized barrier film of coiled material, is then rolled from two ends to centre down;
15) be coated with and scrape polymer cement mortar step: the polymer cement mortar mixed is poured in basic unit, with trowel or scraper plate polymer cement mortar good for mixing is evenly coated with and scrapes in basic unit;
16) paving self-adhesive coiled material step: cut barrier paper by overlaying the APF self-adhesive coiled material spooled, while smear mortar limit to roll paving, a width APF self-adhesive coiled material successively sequentially rolls paving from centre respectively to two ends;
17) step is overlapped: adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam APF self-adhesive coiled material face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting;
18) calandering steps: after APF self-adhesive coiled material every paving two width, slowly flattens compacting by the special pressure roller of a width coiled material of first paving;
19) closing in step: do edge sealing process in the solid rear APF waterproof coiled material system-specific sealing compound of tack coat.
APE adhesive waterproof coil elevation construction engineering method, comprises the steps:
21) contrast basic level requirement by conventional procedures process, reach basal plane requirement, then play installation of membrane reference line;
22) brushing base treatment agent step: brushing base treatment agent in the basic unit handled well, requires that scumbling is not show-through, must not have packing phenomenon;
23) node processing step: to detail section by designing requirement process, for exterior wall self-adhesive coiled material closing in way: underground construction self-adhesive coiled material end is received head and dehisced to adopt encapsulation process for preventing coiled material, end is received head place polyurethane water-proof paint and is brushed, and sealed width is not less than 10mm;
24) paving self-adhesive coiled material step: after base treatment agent is dry, the height of APF self-adhesive coiled material by designing requirement is cut out, be aligned in basic unit by snap the line, the antiseized barrier film of coiled material is towards basic unit, cut barrier paper, while tear barrier paper off, simultaneously be directly pasted onto to be coated with and brush on the basal plane of base treatment agent;
25) step is overlapped: adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam APF self-adhesive coiled material face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting;
26) calandering steps: after APF self-adhesive coiled material every paving two width, slowly flattens compacting by the special pressure roller of a width coiled material of first paving;
27) closing in step: do edge sealing process in the solid rear APF waterproof coiled material system-specific sealing compound of tack coat.
Beneficial effect of the present invention is: started unique construction technology---pre-laid process (empty laid process).Innovation engineering method is selected, and can adopt dry paving, wet paving, empty paving and pre-laid method construction, reduce labour intensity, more adapt to basic level requirement.Wide cut has 1m-2m available, reduces overlap joint, and construction is faster, is particularly suitable for large-area construction.Safety and environmental protection, the construction of APF self-adhesive coiled material is cold construction, environmentally friendly, eliminates job site potential safety hazard.
Accompanying drawing explanation
Fig. 1 is the flow chart of plane of the present invention construction;
Fig. 2 is the flow chart of elevation construction of the present invention.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the present invention is described further.
Embodiment one
Plane is constructed: as shown in Figure 1,
(1) basic level requirement is contrasted by step process, until reach basal plane requirement.Play installation of membrane reference line again.
(2) prepared polymer cement mortar
Cement adopts the Portland cement prepared polymer cement mortar of more than 32.5R level, to mix and close thing ﹛ polymer master batch: Portland cement=1:10 (weight ratio) ﹜ will be put and stirred in a reservoir, then be after 0.40 (weight ratio) adds water by water/binder ratio, mixture in container will be contained in electric mixer and stir 1 ~ 2 minute to evenly, leave standstill for subsequent use after 5 ~ 8 minutes.
(3) node processing
Thin portion to carry out at positions such as two sides corner, three negative and positive angles additionally strengthening process with dedicated additional layer self-adhesive coiled material and the negative and positive angle self-adhesive coiled material that cuts in such as negative and positive angle, pipe root position etc., and flat facade on average launches.Method is first sheared by coiled material by thin portion shape, pastes in thin portion, after apparent size, shape are suitable, then pasted by self-adhesive coiled material, every hem width degree 250mm.
(4) APF self-adhesive coiled material is overlay
Be layered on basal plane by APF self-adhesive coiled material view picture by snap the line location sky, the antiseized barrier film of coiled material down, is then rolled from two ends to centre.
(5) polymer cement mortar is scraped in painting
The polymer cement mortar mixed is poured in basic unit, is evenly coated with trowel or the scraper plate polymer cement mortar that just mixing is good and scrapes in basic unit.
(6) paving self-adhesive coiled material
Cut open barrier paper by overlaying the APF self-adhesive coiled material cutter spooled, while smear mortar limit to roll paving, a width coiled material successively sequentially rolls paving from centre respectively to two ends.(general workman can divide group, one group of three people, and a people spreads coiled material, and a people smears polymer mortar, people's spice.It is moistening that dry basal plane should spread water, accomplish basal plane moistening and without open fire)
(7) overlap
Adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam self-adhesion face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting.
(8) roll-in
After APF self-adhesive coiled material every paving two width, the special pressure roller of a width coiled material of first paving is slowly flattened compacting.
(9) close up
Edge sealing process is done in the solid rear APF waterproof coiled material system-specific sealing compound of tack coat.
(10) when the paving of APF self-adhesive coiled material waterproofing course complete qualified by inspection after, the construction of next process can be carried out.
Embodiment two
Elevation construction: as shown in Figure 2,
(1) base treatment:
Contrast basic level requirement, by step process, until reach basal plane requirement, then plays installation of membrane reference line.
(2) brushing base treatment agent:
Brushing base treatment agent in the basic unit handled well, requires that scumbling is not show-through, must not have packing phenomenon.
(3) node processing:
Additional enhancement layer and negative and positive angle various pipes mouth etc. are by designing requirement process.Exterior wall self-adhesive coiled material closing in way: underground construction self-adhesive coiled material end is received head and dehisced to adopt encapsulation process for preventing coiled material.End is received head place polyurethane water-proof paint and is brushed, and sealed width is not less than 10mm.Under the prerequisite of security performance ensureing waterproofing system, great help is played to the safe operating life extending waterproofing system.
(4) installation of membrane
After base treatment agent is dry, be advisable with tack-free, the height of APF self-adhesive coiled material by designing requirement is cut out, be aligned in basic unit by snap the line, the antiseized barrier film of coiled material is towards basic unit, cut open barrier paper with cutter, tear barrier paper off, simultaneously be directly pasted onto to be coated with and brush on the basal plane of base treatment agent.
(5) overlap
Adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam self-adhesion face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting.
(6) roll-in
After APF self-adhesive coiled material every paving two width, the special pressure roller of a width coiled material of first paving is slowly flattened compacting.
(7) close up
Edge sealing process is done in APF self-adhesive coiled material closing in place APF waterproof coiled material system-specific sealing compound.
(8) when the paving of APF self-adhesive coiled material waterproofing course complete qualified by inspection after, the construction of next process can be carried out.
The principle of above-mentioned engineering is: APF coiled material composite waterproof system directly uses polymer cement mortar to paste, preparation is simple, utilize cement polymer mortar to do tack coat, can fast paving on the concrete base layer of humidity, also can directly paving on the concrete surface of drying.Good integrity, the seam between coiled material is tightly reliable, and adjacent web lap side seam is that self-adhesion face is bonding with glue face, self-adhesion face, and joint strength is high, has certain flexible and extendable performance simultaneously, stability of material is good, corrosion resistance is strong, long service life.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, without departing from the inventive concept of the premise; can also make some improvements and modifications, these improvements and modifications also should be considered as in scope.
Claims (2)
1.APE adhesive waterproof coil plane construction method, is characterized in that, comprise the steps:
11) contrast basic level requirement by conventional procedures process, reach basal plane requirement, then play installation of membrane reference line;
12) prepared polymer cement mortar step: cement adopts the Portland cement prepared polymer cement mortar of more than 32.5R level, by mixture and polymer master batch: Portland cement is that 1:10 is put and stirred in a reservoir according to weight ratio, then water ash be by weight 0.40 add water after, mixture in container will be contained in electric mixer and stir 1 ~ 2 minute to evenly, leave standstill for subsequent use after 5 ~ 8 minutes;
13) node processing step: first sheared by additional self-adhesive coiled material by thin portion shape detail section, paste in thin portion, after apparent size, shape are suitable, then will add self-adhesive coiled material stickup;
14) APF self-adhesive coiled material step is overlay: be layered on basal plane by APF self-adhesive coiled material view picture by snap the line location sky, the antiseized barrier film of coiled material, is then rolled from two ends to centre down;
15) be coated with and scrape polymer cement mortar step: the polymer cement mortar mixed is poured in basic unit, with trowel or scraper plate polymer cement mortar good for mixing is evenly coated with and scrapes in basic unit;
16) paving self-adhesive coiled material step: cut barrier paper by overlaying the APF self-adhesive coiled material spooled, while smear mortar limit to roll paving, a width APF self-adhesive coiled material successively sequentially rolls paving from centre respectively to two ends;
17) step is overlapped: adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam APF self-adhesive coiled material face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting;
18) calandering steps: after APF self-adhesive coiled material every paving two width, slowly flattens compacting by the special pressure roller of a width coiled material of first paving;
19) closing in step: do edge sealing process in the solid rear APF waterproof coiled material system-specific sealing compound of tack coat.
2.APE adhesive waterproof coil elevation construction method, is characterized in that, comprise the steps:
21) contrast basic level requirement by conventional procedures process, reach basal plane requirement, then play installation of membrane reference line;
22) brushing base treatment agent step: brushing base treatment agent in the basic unit handled well, requires that scumbling is not show-through, must not have packing phenomenon;
23) node processing step: to detail section by designing requirement process, for exterior wall self-adhesive coiled material closing in way: underground construction self-adhesive coiled material end is received head and dehisced to adopt encapsulation process for preventing coiled material, end is received head place polyurethane water-proof paint and is brushed, and sealed width is not less than 10mm;
24) paving self-adhesive coiled material step: after base treatment agent is dry, the height of APF self-adhesive coiled material by designing requirement is cut out, be aligned in basic unit by snap the line, the antiseized barrier film of coiled material is towards basic unit, cut barrier paper, while tear barrier paper off, simultaneously be directly pasted onto to be coated with and brush on the basal plane of base treatment agent;
25) step is overlapped: adjacent two width APF self-adhesive coiled material seams adopt overlapping mode, overlap joint control line should be aimed at during mutual overlap joint, lap width have designing requirement by designing requirement, can by long limit 100mm without designing requirement, minor face 100mm, tear the reserved barrier paper in seam APF self-adhesive coiled material face during construction off, ensure that lap-joint is clean, drying does not have dust, then directly paste compacting;
26) calandering steps: after APF self-adhesive coiled material every paving two width, slowly flattens compacting by the special pressure roller of a width coiled material of first paving;
27) closing in step: do edge sealing process in the solid rear APF waterproof coiled material system-specific sealing compound of tack coat.