A kind of nano diatomite that adds reduces fragrance cork paper body paper of flue gas content and preparation method thereof
Technical field
The present invention relates to cigarette technical field, particularly a kind of nano diatomite that adds reduces fragrance cork paper body paper of flue gas content and preparation method thereof.
Background technology
Cigarette tipping paper plays a part to connect pipe tobacco and filter tip.Utilizing the permeability of cork paper to dilute flue gas is a kind of important means reducing harmful substance in cigarette smoke.Existing filter-tip, due to the concrete condition consideration that work principle of filter is single, filter process does not press flue gas, cannot reach fully desirable filter effect.As disposable filtering cigarette holder is too simplified, making it most of harmful substance can not dispose.Along with the raising day by day of people's quality of life, society constantly strengthens the concern of smoking and health problem, and minimizing bitting midges has become the responsibilities and obligations that tobacco business must be born.In this context, tobacco business actively develops the research of cigarette filter, is especially strengthening in the filtration of filter tip, adsorption function and smoke perfume.Just wish now that a kind of cork paper of invention is wrapped in filter tip skin, can play filtration suction-operated, both can not block, can know again and fall harmful substance.
Summary of the invention
The object of this invention is to provide a kind of nano diatomite that adds and reduce fragrance cork paper body paper of flue gas content and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
Add the fragrance cork paper body paper that nano diatomite reduces flue gas content, be made up of the raw material of following weight portion: softwood pulp 125-140, bleaching rice straw pulp 68-80, acid fiber by polylactic 1-2, anhydrous sodium pyrophosphate 0.3-0.5, yellow cinnamon leaf 3-4, kiwi fruit leaf 2-3, lignin 0.6-1, nano diatomite 1.5-2, stonewort essential oil 1-2, spirulina powder 1.5-2, algin 0.9-1.2, alkyl ketene dimer 0.8-1, potpourri 3-4;
Described potpourri is prepared from by the raw material of following weight portion: nanmu 1-2, vanilla 3-5, lemonlike citrus leaf 4-6, horseradish 2.5-4, the positive leaves of pulse plants flower 1.5-2, mushroom 3-5, Pu'er 3-4, rhizoma nelumbinis 5-7, apple skin 6-8, watermelon peel 4-6, peach blossom 4-5; Preparation method is that to obtain squeezeding juice through cold press after first mushroom, rhizoma nelumbinis, apple skin, watermelon peel being cleaned up stand-by, and all the other residual componentss put into 8-10 soak by water 1-1.5 hour doubly, filter cleaner, and it is stand-by to get filtrate; By the mixing of two kinds of liquid, put into centrifugation apparatus, with the centrifugation 5-10 minute of 3500-5000 rev/min, then upper strata centrifugate utilized aperture to be the ultrafiltration membrance filter of 1 micron, remove the large molecular impurity in centrifugate, be concentrated into medicinal extract and get final product.
A kind of fragrance cork paper body paper adding nano diatomite reduction flue gas content of the present invention, be made up of following concrete steps:
(1) yellow cinnamon leaf, kiwi fruit leaf are cleaned up, put into baking oven, under 55 DEG C of-60 DEG C of conditions, dry 1.5-2.5 hour, then pulverizes, and makes 100-150 object mixed-powder, stand-by;
(2) algin is added in the water of 10 times amount, then add alkyl ketene dimer, nano diatomite, spirulina powder, be heated to 55 DEG C-60 DEG C, stirring reaction 1-2 hour, form mixture stand-by;
(3) add in beater by softwood pulp, bleaching rice straw pulp, acid fiber by polylactic and all the other residual componentss except potpourri, add suitable quantity of water making beating, control beating consistency at 3.6-4.3%, beating degree is 68 ~ 75
0sR, obtained slurry, then all adds mixed-powder and mixture in slurry, is heated to 55 DEG C-60 DEG C, insulated and stirred 1.5-2 hour;
(4) by the slurry that mixes up after wet end and press section are shaped dehydration, at the aqueous solution of the potpourri of l Water Paper page frame table even brushing half amount, then under 100 DEG C of-120 DEG C of conditions, electric heating air blast was taken out after 2-3 minute, continue the aqueous solution of brushing residue potpourri, dry 3-5 minute again, finally on calender, carry out press polish, after taking-up, namely obtain cork paper body paper.
The invention has the beneficial effects as follows: the present invention is by adding in paper making raw material by nano diatomite, play an important role in reduction flue gas, increase adsorptivity, by adding potpourri, natural delicate fragrance, improves pungent flue gas and the peculiar smell of cigarette, keep oral cavity refreshing, the cork paper body paper coating that the present invention obtains is even, good waterproof performance, good permeability, tensile strength is high, is applicable to the use of high-quality cigarette.
Specific embodiments
Below by instantiation, the present invention is described in detail.
Add the fragrance cork paper body paper that nano diatomite reduces flue gas content, be made up of the raw material of following weight portion (kilogram): softwood pulp 125, bleaching rice straw pulp 68, acid fiber by polylactic 1, anhydrous sodium pyrophosphate 0.3, yellow cinnamon leaf 3, kiwi fruit leaf 2, lignin 0.6, nano diatomite 1.5, stonewort essential oil 1, spirulina powder 1.5, algin 0.9, alkyl ketene dimer 0.8, potpourri 3;
Described potpourri is prepared from by the raw material of following weight portion (kilogram): nanmu 1, vanilla 3, lemonlike citrus leaf 4, horseradish 2.5, the positive leaves of pulse plants spend 1.5, mushroom 3, Pu'er 3, rhizoma nelumbinis 5, apple skin 6, watermelon peel 4, peach blossom 4; Preparation method is that to obtain squeezeding juice through cold press after first mushroom, rhizoma nelumbinis, apple skin, watermelon peel being cleaned up stand-by, and all the other residual componentss put into 8-10 soak by water 1-1.5 hour doubly, filter cleaner, and it is stand-by to get filtrate; By the mixing of two kinds of liquid, put into centrifugation apparatus, with the centrifugation 5-10 minute of 3500-5000 rev/min, then upper strata centrifugate utilized aperture to be the ultrafiltration membrance filter of 1 micron, remove the large molecular impurity in centrifugate, be concentrated into medicinal extract and get final product.
A kind of fragrance cork paper body paper adding nano diatomite reduction flue gas content of the present invention, be made up of following concrete steps:
(1) yellow cinnamon leaf, kiwi fruit leaf are cleaned up, put into baking oven, under 55 DEG C of-60 DEG C of conditions, dry 1.5-2.5 hour, then pulverizes, and makes 100-150 object mixed-powder, stand-by;
(2) algin is added in the water of 10 times amount, then add alkyl ketene dimer, nano diatomite, spirulina powder, be heated to 55 DEG C-60 DEG C, stirring reaction 1-2 hour, form mixture stand-by;
(3) add in beater by softwood pulp, bleaching rice straw pulp, acid fiber by polylactic and all the other residual componentss except potpourri, add suitable quantity of water making beating, control beating consistency at 3.6-4.3%, beating degree is 68 ~ 75
0sR, obtained slurry, then all adds mixed-powder and mixture in slurry, is heated to 55 DEG C-60 DEG C, insulated and stirred 1.5-2 hour;
(4) by the slurry that mixes up after wet end and press section are shaped dehydration, at the aqueous solution of the potpourri of l Water Paper page frame table even brushing half amount, then under 100 DEG C of-120 DEG C of conditions, electric heating air blast was taken out after 2-3 minute, continue the aqueous solution of brushing residue potpourri, dry 3-5 minute again, finally on calender, carry out press polish, after taking-up, namely obtain cork paper body paper.
After testing, the machine direction tensile strength of the cork paper body paper that the present invention obtains is 1.67KN/m, and air permeability is 72CU.