CN104212348B - A kind of water-fast finish paint and preparation method thereof for boats and ships - Google Patents

A kind of water-fast finish paint and preparation method thereof for boats and ships Download PDF

Info

Publication number
CN104212348B
CN104212348B CN201410456380.XA CN201410456380A CN104212348B CN 104212348 B CN104212348 B CN 104212348B CN 201410456380 A CN201410456380 A CN 201410456380A CN 104212348 B CN104212348 B CN 104212348B
Authority
CN
China
Prior art keywords
parts
water
floating type
boats
ships
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410456380.XA
Other languages
Chinese (zh)
Other versions
CN104212348A (en
Inventor
戴晓宸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Yunshu New Material Technology Co Ltd
Original Assignee
Suzhou Yunshu New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Yunshu New Material Technology Co Ltd filed Critical Suzhou Yunshu New Material Technology Co Ltd
Priority to CN201410456380.XA priority Critical patent/CN104212348B/en
Publication of CN104212348A publication Critical patent/CN104212348A/en
Application granted granted Critical
Publication of CN104212348B publication Critical patent/CN104212348B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a kind of water-fast finish paint and preparation method thereof for boats and ships, this finish paint contains following composition in mass parts: 20~30 parts of coal tar pitches, 10~15 parts of cyclohexanone, 10~15 parts of dimethylbenzene, 40~60 parts of boiled wood oils, 5~10 parts, non-floating type silver powder, 5~12 parts of non-floating type aluminum pastes, 2~5 parts of tetraethylthiuram disulfides, 8~16 parts, cuprous oxide. Finish paint provided by the invention has good protection and decorative effect to boats and ships, and water-fast, the water resistant with excellence permeated, corrosion-resistant, UV resistant performance, and can effectively suppress algae and microbial growth.

Description

A kind of water-fast finish paint and preparation method thereof for boats and ships
Technical field
The present invention relates to paint field, relate in particular to a kind of water-fast finish paint and preparation method thereof for boats and ships.
Background technology
Along with social development, paint is widely used every field. At ship domain, paint, in playing boats and ships attractive in appearance, also has the effect of protection to boats and ships, the effects such as such as corrosion-resistant, weatherability, UV resistant. But water-fast, the water resistant of existing boats and ships use coating permeated, UV resistant performance is not high, and do not have the effect that suppresses algae and growth of microorganism.
Summary of the invention
The technical problem solving: for the shortcomings such as the infiltration of water-fast, water resistant, the UV resistant performance of coating is not high for spot ship, the invention provides a kind of water-fast finish paint and preparation method thereof for boats and ships.
Technical scheme: the water-fast finish paint of a kind of boats and ships, contain following composition in mass parts: 20~30 parts of coal tar pitches, 10~15 parts of cyclohexanone, 10~15 parts of dimethylbenzene, 40~60 parts of boiled wood oils, 5~10 parts, non-floating type silver powder, 5~12 parts of non-floating type aluminum pastes, 2~5 parts of tetraethylthiuram disulfides, 8~16 parts, cuprous oxide.
Further, described a kind of boats and ships contain following composition with water-fast finish paint in mass parts: 25 parts of coal tar pitches, 12 parts of cyclohexanone, 13 parts of dimethylbenzene, 50 parts of boiled wood oils, 8 parts, non-floating type silver powder, 8 parts of non-floating type aluminum pastes, 3.5 parts of tetraethylthiuram disulfides, 12 parts, cuprous oxide.
The preparation method of water-fast finish paint for a kind of boats and ships, the preparation process of the method is as follows: in the equipment with stirring and condensation reflux unit, add coal tar pitch, be heated to 100~120 DEG C, add again cyclohexanone and dimethylbenzene, be uniformly mixed to coal tar pitch and dissolve completely, after being cooled to room temperature, cross 400 mesh sieves, and then mix with boiled wood oil, non-floating type silver powder, non-floating type aluminum paste, tetraethylthiuram disulfide and cuprous oxide, get product.
Beneficial effect: a kind of water-fast finish paint and preparation method thereof for boats and ships provided by the invention; this finish paint has good protection and decorative effect to boats and ships; water-fast, the water resistant with excellence permeated, corrosion-resistant, UV resistant performance, and can effectively suppress algae and microbial growth.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail.
Embodiment 1
The present embodiment provides a kind of boats and ships water-fast finish paint, contains following composition in mass parts: 20 parts of coal tar pitches, 10 parts of cyclohexanone, 10 parts of dimethylbenzene, 40 parts of boiled wood oils, 5 parts, non-floating type silver powder, 5 parts of non-floating type aluminum pastes, 2 parts of tetraethylthiuram disulfides, 8 parts, cuprous oxide.
A kind of boats and ships are as follows by the preparation process of water-fast finish paint: in the equipment with stirring and condensation reflux unit, add coal tar pitch, be heated to 100 DEG C, add again cyclohexanone and dimethylbenzene, be uniformly mixed to coal tar pitch and dissolve completely, after being cooled to room temperature, cross 400 mesh sieves, and then mix with boiled wood oil, non-floating type silver powder, non-floating type aluminum paste, tetraethylthiuram disulfide and cuprous oxide, get product.
Embodiment 2
The present embodiment provides a kind of boats and ships water-fast finish paint, contains following composition in mass parts: 30 parts of coal tar pitches, 15 parts of cyclohexanone, 15 parts of dimethylbenzene, 60 parts of boiled wood oils, 10 parts, non-floating type silver powder, 12 parts of non-floating type aluminum pastes, 5 parts of tetraethylthiuram disulfides, 16 parts, cuprous oxide.
A kind of boats and ships are as follows by the preparation process of water-fast finish paint: in the equipment with stirring and condensation reflux unit, add coal tar pitch, be heated to 120 DEG C, add again cyclohexanone and dimethylbenzene, be uniformly mixed to coal tar pitch and dissolve completely, after being cooled to room temperature, cross 400 mesh sieves, and then mix with boiled wood oil, non-floating type silver powder, non-floating type aluminum paste, tetraethylthiuram disulfide and cuprous oxide, get product.
Embodiment 3
The present embodiment provides a kind of boats and ships water-fast finish paint, contains following composition in mass parts: 25 parts of coal tar pitches, 12 parts of cyclohexanone, 13 parts of dimethylbenzene, 50 parts of boiled wood oils, 8 parts, non-floating type silver powder, 8 parts of non-floating type aluminum pastes, 3.5 parts of tetraethylthiuram disulfides, 12 parts, cuprous oxide.
A kind of boats and ships are as follows by the preparation process of water-fast finish paint: in the equipment with stirring and condensation reflux unit, add coal tar pitch, be heated to 110 DEG C, add again cyclohexanone and dimethylbenzene, be uniformly mixed to coal tar pitch and dissolve completely, after being cooled to room temperature, cross 400 mesh sieves, and then mix with boiled wood oil, non-floating type silver powder, non-floating type aluminum paste, tetraethylthiuram disulfide and cuprous oxide, get product.
The technical performance index of the above-mentioned water-fast finish paint of a kind of boats and ships of stating embodiment 1~embodiment 3, its testing result is as follows:
Testing result
Test item Test index Embodiment 1 Embodiment 2 Embodiment 3
Freeze-thaw resistance (circulating 5 times) GB/T 9268-2008 Well Well Well
Salt tolerant 15d.h >= GB/T10834-89 245 245 252
Artificial weathering ageing resistance 30d(25 DEG C) >= GB/T1865 212h 215h 220h
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.

Claims (2)

1. the water-fast finish paint of boats and ships, it is characterized in that, contain following composition in mass parts: 20~30 parts of coal tar pitches, 10~15 parts of cyclohexanone, 10~15 parts of dimethylbenzene, 40~60 parts of boiled wood oils, 5~10 parts, non-floating type silver powder, 5~12 parts of non-floating type aluminum pastes, 2~5 parts of tetraethylthiuram disulfides, 8~16 parts, cuprous oxide;
The preparation method of water-fast finish paint for described a kind of boats and ships, the preparation process of the method is as follows: in the equipment with stirring and condensation reflux unit, add coal tar pitch, be heated to 100~120 DEG C, add again cyclohexanone and dimethylbenzene, be uniformly mixed to coal tar pitch and dissolve completely, after being cooled to room temperature, cross 400 mesh sieves, and then mix with boiled wood oil, non-floating type silver powder, non-floating type aluminum paste, tetraethylthiuram disulfide and cuprous oxide, get product.
2. the water-fast finish paint of a kind of boats and ships according to claim 1, it is characterized in that, contain following composition in mass parts: 25 parts of coal tar pitches, 12 parts of cyclohexanone, 13 parts of dimethylbenzene, 50 parts of boiled wood oils, 8 parts, non-floating type silver powder, 8 parts of non-floating type aluminum pastes, 3.5 parts of tetraethylthiuram disulfides, 12 parts, cuprous oxide.
CN201410456380.XA 2014-09-10 2014-09-10 A kind of water-fast finish paint and preparation method thereof for boats and ships Expired - Fee Related CN104212348B (en)