CN104209816B - A kind of marble surface polishing method of sedimentary rock attribute - Google Patents
A kind of marble surface polishing method of sedimentary rock attribute Download PDFInfo
- Publication number
- CN104209816B CN104209816B CN201410379621.5A CN201410379621A CN104209816B CN 104209816 B CN104209816 B CN 104209816B CN 201410379621 A CN201410379621 A CN 201410379621A CN 104209816 B CN104209816 B CN 104209816B
- Authority
- CN
- China
- Prior art keywords
- stone
- polishing
- mesh
- marble
- sedimentary rock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to building material technical field, especially a kind of marble surface polishing method of sedimentary rock attribute, by in bruting process, appropriate control to technological parameter and processing step, the marble of sedimentary rock attribute enable by the source as conventional marble and granite TERRAZZO raw material, and the marble of sedimentary rock attribute is generally existing in each province and each area, so reduce the cost of ornament materials carrying, with significant economic benefit, and also improve the marmorean value of exploiting and utilizing of sedimentary rock attribute；By the use of multistage resin abrasive disc, and the material added during stone material of polishing resin abrasive disc is controlled so that the classic charm of the TERRAZZO polished is full, the generous beauty of outward appearance of TERRAZZO, can promote the purchase of Market Consumer.
Description
Technical field
The present invention relates to building material technical field, especially a kind of marble surface polishing method of sedimentary rock attribute.
Background technology
It is more stronger than granitic hardness for the marble (being commonly called as bluestone board) of sedimentary rock attribute, but stone structure density is fine and smooth
With high-grade marmorean value, marble one kind is fallen within, is studied through long-time, proves and is processed by a variety of methods repeatedly
Polishing and marble, the polishing technical finesse of granite traditional handicraft can not all reach the luminosity of this marble shiny side and embody stone
Material primary colors, and then it is difficult to reach purpose attractive in appearance.
Meanwhile marble polishing of the technology to sedimentary rock attribute is polished using marble of the prior art and handled, its into
This is larger, and polishing effect is undesirable, it is difficult to which meeting to turn into the Marble processing of sedimentary rock attribute has classic charm, can allow people
Feel elegant, generous TERRAZZO, and then influence the selling market of stone material.
Also, according to literature search and research, in the prior art in the processing technology of stone material, being more by cement etc.
The technology that kind raw material make artificial stone is more, and for using raw material stone burnish and fabricate the technical literature of stone material
It is less, simply in the technology of conventional operation, the smoothness of stone material can be strengthened according to constantly polishing stone, improved
The quality of TERRAZZO and the principle of quality, and then stone material is processed, system of such processing technology for TERRAZZO
It is made for this, consumptive material is larger, the difficult choosing of stone raw material, and cost is larger.
Therefore, this researcher is by effort and trial for many years, by the marble of sedimentary rock attribute, this generally existing
Stone raw material produces and processes as the raw material of TERRAZZO so that the TERRAZZO made disclosure satisfy that other stone materials original
Expect that elegant, the beautiful, generous and classic charm made is stronger, be sedimentary rock attribute marmorean popularization and application with
And the marble polishing technology of sedimentary rock attribute provides a kind of new approaches.
The content of the invention
In order to solve above-mentioned technical problem present in prior art, present invention offer is a kind of can be by sedimentary rock attribute
The classic charm that marble is polished into the TERRAZZO produced with traditional marble and granite as raw material is strong, attractive in appearance, big
Side, and the raw material sources of TERRAZZO are widened, the marble market development value of sedimentary rock attribute is improved, reduces TERRAZZO
Cost sedimentary rock attribute marble surface polishing method.
It is achieved particular by following technical scheme：
A kind of marble surface polishing method of sedimentary rock attribute, using grinding to marble stone according to traditional grinding technics
It is ground, and in process of lapping, is ground first using iron and marble stone cuts into 30-40cm is wide, and 4-5cm is thick, 40-
The stone of 50cm length, and after surface is added into water mill 1-2h；Resin abrasive disc polishing block faces 3- of the specification for 50 mesh is used again
6min, and add water in polishing so that the humidity of block faces is 100%；And then specification is used to be ground for the resin of 150 mesh
The humidity that piece adds water to block faces is 100% polishing block faces 3-6min；Use 300 mesh, 500 mesh, 1000 mesh instead successively again
Resin abrasive disc continue according to the method described above successively plus water polishing 3-6min after, then using 2000 mesh resin abrasive disc and be not added with water
Abrasive material polishing stone is added, and stone is subjected to heat treatment simultaneously, makes the temperature of stone and abrasive material while heats to 60-80 DEG C
When, continue to polish, until the luminosity of stone reaches 65-75 °, stop the polishing of the resin abrasive disc of 2000 mesh, use 4000 purposes instead
After resin abrasive disc adds water to carry out polishing 15-20min, then using the mesh of polished silicon wafer 4000 of oxalic acid property it is processed by shot blasting,
The marble surface polishing of sedimentary rock attribute can be completed.
The polished silicon wafer of described oxalic acid property is that the abrasive material containing oxalic acid is added on stone, then is entered using polished silicon wafer
Row polishing.
Mesh is a kind of unit value of grinding or polished silicon wafer, i.e. its smaller rugosity of mesh number is bigger, and mesh number is bigger, and its rugosity is got over
It is small, and then by the marble of sedimentary rock attribute, using the resin abrasive disc of the resin abrasive disc from 50 mesh to 2000 mesh change and beat
Mill, and during to the resin abrasive disc for adding water to 1000 mesh in bruting process, use 2000 mesh resin abrasive discs instead and add abrasive material to polish, and increase
Add abrasive material and stone to certain temperature so that during polishing, abrasive material and the calcium ion of block faces or other gold
Microcosmic biochemical reaction occurs for category, nonmetallic ion, and then forms in block faces that more classic and charm is full, attractive in appearance
Generous apparent condition, then add water to polish certain time using the resin abrasive disc of 4000 mesh, and then ensure to be formed has allusion
Charm, the luminosity of TERRAZZO attractive in appearance are more preferable.Finally TERRAZZO surface is thrown with the abrasive material of the property containing oxalic acid
Light processing, further improve the luminosity on TERRAZZO surface.
Abrasive material when 2000 mesh resin abrasive discs add abrasive material to polish is resinous abrasive materials.
Compared with prior art, the present invention has following technique effect：
1. by the use of multistage resin abrasive disc, and the material added during stone material of polishing resin abrasive disc is controlled
System so that the classic charm of the TERRAZZO polished is full, the generous beauty of outward appearance of TERRAZZO, market can be promoted to disappear
The purchase of the person of expense, there is significant economic benefit.
2. by regarding the marble of sedimentary rock attribute as traditional marble or granite ornament materials to be processed,
Increase the raw material sources of marble and granite as TERRAZZO, reduce the cost of TERRAZZO.
3. by bruting process, the appropriate control to technological parameter and processing step so that sedimentary rock attribute it is big
Reason stone can be by the source as conventional marble and granite TERRAZZO raw material, and the marble of sedimentary rock attribute is each
Province and each area are generally existings, so reduce the cost of ornament materials carrying, have significant economic benefit,
And also improve the marmorean value of exploiting and utilizing of sedimentary rock attribute.
Embodiment
Limited with reference to specific embodiment technical scheme is further, but claimed
Scope is not only limited to made description.
Embodiment 1
A kind of marble surface polishing method of sedimentary rock attribute, using grinding to marble stone according to traditional grinding technics
It is ground, and in process of lapping, is ground first using iron and marble stone cuts into 40cm is wide, and 5cm is thick, 50cm length
Stone, and after surface is added into water mill 2h；Resin abrasive disc polishing block faces 6min of the specification for 50 mesh is used again, and in polishing
Add water so that the humidity of block faces is 100%；And then specification is used to add water to block faces for the resin abrasive disc of 150 mesh
Humidity be 100% polishing block faces 6min；Use instead successively again 300 mesh, 500 mesh, 1000 mesh resin abrasive disc continue according to
The above method add successively water polishing 6min after, then using 2000 mesh resin abrasive disc and be not added with water addition resinous abrasive materials polishing stone
Block, and stone is subjected to heat treatment simultaneously, when making the temperature of stone and resinous abrasive materials while heating to 80 DEG C, continue to polish,
Until the luminosity of stone reaches 75 °, the polishing of the resin abrasive disc of 2000 mesh of stopping, the resin abrasive disc for using 4000 mesh instead adds water to carry out
Polish after 20min, then using the mesh of polished silicon wafer 4000 of oxalic acid property it is processed by shot blasting, you can complete sedimentary rock attribute
Marble surface polishes.
The polished silicon wafer of oxalic acid property is that the abrasive material containing oxalic acid is added on stone, then is polished using polished silicon wafer
Processing.
Embodiment 2
A kind of marble surface polishing method of sedimentary rock attribute, using grinding to marble stone according to traditional grinding technics
It is ground, and in process of lapping, is ground first using iron and marble stone cuts into 30cm is wide, and 4cm is thick, 40cm length
Stone, and after surface is added into water mill 1h；Resin abrasive disc polishing block faces 3min of the specification for 50 mesh is used again, and in polishing
Add water so that the humidity of block faces is 100%；And then specification is used to add water to block faces for the resin abrasive disc of 150 mesh
Humidity be 100% polishing block faces 3min；Use instead successively again 300 mesh, 500 mesh, 1000 mesh resin abrasive disc continue according to
The above method add successively water polishing 3min after, then using 2000 mesh resin abrasive disc and be not added with water addition resinous abrasive materials polishing stone
Block, and stone is subjected to heat treatment simultaneously, when making the temperature of stone and resinous abrasive materials while heating to 60 DEG C, continue to polish,
Until the luminosity of stone reaches 65 °, the polishing of the resin abrasive disc of 2000 mesh of stopping, the resin abrasive disc for using 4000 mesh instead adds water to carry out
Polish after 15min, then using the mesh of polished silicon wafer 4000 of oxalic acid property it is processed by shot blasting, you can complete sedimentary rock attribute
Marble surface polishes.
The polished silicon wafer of oxalic acid property is that the abrasive material containing oxalic acid is added on stone, then is polished using polished silicon wafer
Processing.
Claims (1)
1. a kind of marble surface polishing method of sedimentary rock attribute, it is characterised in that using grinding to marble stone according to biography
System grinding technics is ground, and in process of lapping, is ground that marble stone cut into 30-40cm is wide using iron first,
4-5cm is thick, the stone of 40-50cm length, and after surface is added into water mill 1-2h；Resin abrasive disc polishing stone of the specification for 50 mesh is used again
Block surface 3-6min, and add water in polishing so that the humidity of block faces is 100%；And then specification is used as 150 mesh
Resin abrasive disc add water to the humidity of block faces as 100% polishing block faces 3-6min；Use 300 mesh, 500 instead successively again
Mesh, the resin abrasive disc of 1000 mesh are continued according to the method described above successively plus after water polishing 3-6min, then ground using the resin of 2000 mesh
Piece is simultaneously not added with water addition abrasive material polishing stone, and stone is carried out into heat treatment simultaneously, makes the temperature of stone and abrasive material while increases
When temperature is to 60-80 DEG C, continue to polish, until the luminosity of stone reaches 65-75 °, stop the polishing of the resin abrasive disc of 2000 mesh, change
After adding water to carry out polishing 15-20min with the resin abrasive disc of 4000 mesh, then using the mesh of polished silicon wafer 4000 of oxalic acid property it is carried out
Polishing, you can complete the marble surface polishing of sedimentary rock attribute；
The polished silicon wafer of described oxalic acid property is that the abrasive material containing oxalic acid is added on stone, then is thrown using polished silicon wafer
Light processing.