CN104195446A - 用于泵阀产品上的超级奥氏体不锈钢 - Google Patents
用于泵阀产品上的超级奥氏体不锈钢 Download PDFInfo
- Publication number
- CN104195446A CN104195446A CN201410381275.4A CN201410381275A CN104195446A CN 104195446 A CN104195446 A CN 104195446A CN 201410381275 A CN201410381275 A CN 201410381275A CN 104195446 A CN104195446 A CN 104195446A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- pump valve
- valve products
- equal
- superaustenitic stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：17.5%～18.5%，铬：19.5%～20.5%，钼：6%～6.5%，铜：0.5%～1%，氮：0.18%～0.22%，碳：≤0.02%，猛：≤1%，硅≤0.8%，磷：≤0.03%，硫：≤0.01%，余量为铁。本发明的优点是：耐点腐蚀、耐缝隙腐蚀、抗应力腐蚀破裂等形式的耐腐蚀性能好，其抗点蚀性能Pl≥40，在保持奥氏体不锈钢可锻性和韧性的同时，还能大大提高强度、塑性、耐腐蚀等性能，其屈服强度比普通奥氏体不锈钢的屈服强度高出至少50%，延伸率、低温性能、抗撞击及抗断裂性能也提高了，大大延长了泵阀产品的使用寿命，降低了使用成本。
Description
技术领域
本发明涉及奥氏体不锈钢，特别涉及一种用于泵阀产品上的超级奥氏体不锈钢。
背景技术
随着我国现代化工业的迅速发展，各种具有强酸特性的流体的应用使得对泵阀产品的制造材料的要求越来越高，泵阀产品在工作时不仅要承受流体的液压冲击，而且还要承受各种具有强酸特性的流体的侵蚀。目前大部分的泵阀产品的制造材料一般采用奥氏体不锈钢，奥氏体不锈钢制造的泵阀产品易被各种具有强酸特性的流体以点腐蚀、缝隙腐蚀、应力腐蚀破裂等腐蚀形式侵蚀，大大降低了泵阀产品的使用寿命，因而需要经常对其进行维护和更换，大大提高了使用成本。为了适应现代化工业的发展，需要开发一种耐腐蚀性好的用于泵阀产品上的超级奥氏体不锈钢。
发明内容
本发明所需解决的技术问题是：提供一种耐腐蚀性能好的用于泵阀产品上的超级奥氏体不锈钢。
为解决上述问题，本发明采用的技术方案是：所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：17.5%～18.5%，铬：19.5%～20.5%，钼：6%～6.5%，铜：0.5%～1%，氮：0.18%～0.22%，碳：≤0.02%，猛：≤1%，硅≤0.8%，磷：≤0.03%，硫：≤0.01%，余量为铁。
进一步地，前述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：18.1%～18.5%，铬：20%～20.3%，钼：6.0%～6.3%，铜：0.7%～0.9%，氮：0.2%～0.22%，碳：＜0.02%，猛：≤0.9%，硅≤0.8%，磷：＜0.03%，硫：≤0.01%，余量为铁。
本发明的有益效果是：上述用于泵阀产品上的超级奥氏体不锈钢，耐腐蚀性能好，其抗点蚀性能Pl(Pl为点蚀指数)≥40,而且在保持奥氏体不锈钢可锻性和韧性的同时，还能大大提高其强度、塑性、耐腐蚀等性能，其屈服强度比普通奥氏体不锈钢的屈服强度高出至少50%，大大延长了泵阀产品的使用寿命，降低了使用成本。
具体实施方式
下面结合优选实施例对本发明所述的技术方案作进一步详细的说明。
实施例一
本实施例所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：17.5%，铬：20.3%，钼：6%，铜：0.7%，氮：0.18%，碳：≤0.02%，猛：≤1%，硅：≤0.8%，磷：＜0.03%，硫：≤0.01%，余量为铁。由上述各组成成分组成的超级奥氏体不锈钢的密度为8.0g/cm3,熔点为1320～1390℃，抗拉强度Rm为660Mpa，屈服强度RP0.2为310Mpa，定倍数A5的延伸率δ为36.3%，其中定倍数A5是指比例试样原始标距与直径比为5。
实施例二
本实施例所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：18.1%，铬：20.5%，钼：6.3%，铜：0.5%，氮：0.2%，碳：≤0.01%，猛：≤1%，硅：≤0.8%，磷：≤0.03%，硫：≤0.01%，余量为铁。由上述各组成成分组成的超级奥氏体不锈钢的密度为8.0g/cm3,熔点为1320～1390℃，抗拉强度Rm为654Mpa，屈服强度RP0.2为305Mpa，定倍数A5的延伸率δ为35.1%。
实施例三
本实施例所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：18.3%，铬：20.1%，钼： 6.0%，铜：0.9%，氮：0.22%，碳：≤0.01%，猛：≤0.08%，硅：≤0.7%，磷：≤0.02%，硫：≤0.01%，余量为铁。由上述各组成成分组成的超级奥氏体不锈钢的密度为8.0g/cm3,熔点为1320～1390℃，抗拉强度Rm为690Mpa，屈服强度RP0.2为345Mpa，定倍数A5的延伸率δ为40.2%。
实施例四
本实施例所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍： 18.5%，铬： 20%，钼： 6.2%，铜： 1%，氮： 0.21%，碳：≤0.02%，猛：≤1%，硅≤0.8%，磷：＜0.03%，硫：≤0.01%，余量为铁。由上述各组成成分组成的超级奥氏体不锈钢的密度为8.0g/cm3,熔点为1320～1390℃，抗拉强度Rm为680Mpa，屈服强度RP0.2为339Mpa，定倍数A5的延伸率δ为38.2%。
实施例五
本实施例所述的用于泵阀产品上的超级奥氏体不锈钢，其组成成分及各成分重量百分比如下：镍：18.5%，铬：19.5%，钼：6.5%，铜：0.8%，氮：0.22%，碳：＜0.02%，猛：≤1%，硅：≤0.8%，磷：≤0.03%，硫：≤0.01%，余量为铁。由上述各组成成分组成的超级奥氏体不锈钢的密度为8.0g/cm3,熔点为1320～1390℃，抗拉强度Rm为672Mpa，屈服强度RP0.2为322Mpa，，定倍数A5的延伸率δ为37.4%。
上述用于泵阀产品上的超级奥氏体不锈钢，耐点腐蚀、耐缝隙腐蚀、抗应力腐蚀破裂等形式的耐腐蚀性能好，其抗点蚀性能Pl≥40,在保持奥氏体不锈钢可锻性和韧性的同时，还能大大提高强度、塑性、耐腐蚀等性能，其屈服强度比普通奥氏体不锈钢的屈服强度高出至少50%，延伸率、低温性能、抗撞击及抗断裂性能也提高了，大大延长了泵阀产品的使用寿命，降低了使用成本。在实验时将该超级奥氏体不锈钢放置在600～1000℃温度下经过一小时敏化处理后仍能通过施特劳斯晶间腐蚀试验，因而该类超级奥氏体不锈钢在焊接时不会出现晶界腐蚀现象。该类超级奥氏体不锈钢除了能应用到泵阀产品上，还能应用于烟气脱硫装置、建筑等用于恶劣环境的产品上。
Claims (2)
1.用于泵阀产品上的超级奥氏体不锈钢，其特征在于：其组成成分及各成分重量百分比如下：镍：17.5%～18.5%，铬：19.5%～20.5%，钼：6%～6.5%，铜：0.5%～1%，氮：0.18%～0.22%，碳：≤0.02%，猛：≤1%，硅≤0.8%，磷：≤0.03%，硫：≤0.01%，余量为铁。
2.按照权利要求1所述的用于泵阀产品上的超级奥氏体不锈钢，其特征在于：其组成成分及各成分重量百分比如下：镍：18.1%～18.5%，铬：20%～20.3%，钼：6.0%～6.3%，铜：0.7%～0.9%，氮：0.2%～0.22%，碳：＜0.02%，猛：≤0.9%，硅≤0.8%，磷：＜0.03%，硫：≤0.01%，余量为铁。