CN104194597A - 一种油包油型醇酸树脂多彩涂料 - Google Patents
一种油包油型醇酸树脂多彩涂料 Download PDFInfo
- Publication number
- CN104194597A CN104194597A CN201410483227.6A CN201410483227A CN104194597A CN 104194597 A CN104194597 A CN 104194597A CN 201410483227 A CN201410483227 A CN 201410483227A CN 104194597 A CN104194597 A CN 104194597A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- synolac
- coating
- alkyd resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种油包油型醇酸树脂多彩涂料,其原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯35-45份;乙二醇乙醚醋酸酯20-40份;氢醌单甲醚10-20份;铬酸钡15-35份;二恶烷1-10份;去离子水80-90份;二甲基乙醇胺25-35份;颜料10-20份;三乙胺30-40份;二戊烯20-30份;过辛酸叔丁酯10-30份;增塑剂6-8份;甲基丙烯酸甲酯25-45份;硅酸铝30-40份;马来酸酐15-25份;涂膜耐擦洗2000-3000次;耐水性好,在水中浸泡60-80d后不起泡、不掉粉;表干1-2h,实干8-10h,耐碱性饱和氢氧化钙溶液30-40d;涂膜花纹独特、装饰效果好,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域,尤其涉及一种油包油型醇酸树脂多彩涂料。
背景技术
涂料,在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面,并能与被涂物形成牢固附着的连续薄膜,通常是以树脂、或油、或乳液为主,添加或不添加颜料、填料,添加相应助剂,用有机溶剂或铬酸钡配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的:“涂料是一种材料,这种材料可以用不同的施工工艺涂覆在物件表面,形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜,又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料,称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称,引进我国后,就一直利用在建筑行业。涂料的作用可以概括为三个方面:保护作用,装饰作用,特殊功能作用。涂料的一般组成:包含成膜物质、颜填料、溶剂、助剂。松香改性醇酸树脂是指在醇酸树脂的制备过程中添加改性剂松香,经化学反应制成的改性树脂。
涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称,建筑涂料是涂料中的一个重要类别,在我国,一般将用于建筑物内墙,外墙,顶棚,地面,卫生间的涂料称为建筑涂料。内墙涂料就是一般装修用的乳胶漆。乳胶漆即是乳液性涂料,按照基材的不同,分为聚醋酸乙烯乳液和丙烯酸乳液两大类。乳胶漆以水为稀释剂,是一种施工方便、安全、耐水洗、透气性好的的涂料,它可根据不同的配色方案调配出不同的色泽。种类:水性内墙漆、油性内墙漆、干粉型内墙漆,属水性涂料,主要由水,乳液,颜料,填料,添加剂五种成分构成。
所谓油包油型醇酸树脂多彩涂料是由不相容的两相成分组成,其中一相分散介质为连续相,另一相为分散相,涂装时,通过一次性喷涂,便可得到豪华、美观、多彩的图案。内墙漆也叫内墙涂料包括液态涂料和粉末涂料,常见的乳胶漆、墙面漆属于液态涂料。内墙涂料的制作成分中基本上由水、颜料、乳液、填充剂和各种助剂组成,这些原材料是不含什么毒性的。作为乳胶漆而言,可能含毒的主要是成膜助剂中的乙二醇和防黴剂中的有机汞。而随着人性化理念的普及,及新型和谐社会的构成,设计一种耐水性、耐擦洗性及耐碱性优异的油包油型醇酸树脂多彩涂料是非常必要的。
发明内容
解决的技术问题:
本申请针对上述技术问题,提供一种油包油型醇酸树脂多彩涂料,解决现有油包油型醇酸树脂多彩涂料耐水性和耐擦洗性差、干燥慢、不耐碱腐蚀等技术问题。
技术方案:
一种油包油型醇酸树脂多彩涂料,所述油包油型醇酸树脂多彩涂料的原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯35-45份;乙二醇乙醚醋酸酯20-40份;氢醌单甲醚10-20份;铬酸钡15-35份;二恶烷1-10份;去离子水80-90份;二甲基乙醇胺25-35份;颜料10-20份;三乙胺30-40份;二戊烯20-30份;过辛酸叔丁酯10-30份;增塑剂6-8份;甲基丙烯酸甲酯25-45份;硅酸铝30-40份;马来酸酐15-25份。
作为本发明的一种优选技术方案:所述油包油型醇酸树脂多彩涂料的原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯40份;乙二醇乙醚醋酸酯30份;氢醌单甲醚15份;铬酸钡25份;二恶烷5份;去离子水85份;二甲基乙醇胺30份;颜料15份;三乙胺35份;二戊烯25份;过辛酸叔丁酯20份;增塑剂7份;甲基丙烯酸甲酯35份;硅酸铝35份;马来酸酐20份。
作为本发明的一种优选技术方案:所述颜料采用氧化铁红、氧化铬绿或中铬黄。
作为本发明的一种优选技术方案:所述增塑剂采用邻苯二甲酸二丁酯。
有益效果:
本发明所述一种油包油型醇酸树脂多彩涂料采用以上技术方案与现有技术相比,具有以下技术效果:1、涂膜耐擦洗2000-3000次;2、耐水性好,在水中浸泡60-80d后不起泡、不掉粉;3、表干1-2h,实干8-10h,耐碱性饱和氢氧化钙溶液30-40d;4、涂膜花纹独特、装饰效果好,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种油包油型醇酸树脂多彩涂料,其原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯35份;乙二醇乙醚醋酸酯20份;氢醌单甲醚10份;铬酸钡15份;二恶烷1份;去离子水80份;二甲基乙醇胺25份;中铬黄10份;三乙胺30份;二戊烯20份;过辛酸叔丁酯10份;邻苯二甲酸二丁酯6份;甲基丙烯酸甲酯25份;硅酸铝30份;马来酸酐15份。
将松香改性醇酸树脂、乙二醇乙醚醋酸酯、氢醌单甲醚、铬酸钡和二恶烷加入去离子水中,加热至40℃搅拌3h,加入二甲基乙醇胺、三乙胺、二戊烯、过辛酸叔丁酯、硅酸铝和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入磷酸三苯酯和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗2000次;在水中浸泡60d后不起泡、不掉粉;表干2h,实干10h,耐碱性饱和氢氧化钙溶液30d。
实施例2:
一种油包油型醇酸树脂多彩涂料,其原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯45份;乙二醇乙醚醋酸酯40份;氢醌单甲醚20份;铬酸钡35份;二恶烷10份;去离子水90份;二甲基乙醇胺35份;氧化铬绿20份;三乙胺40份;二戊烯30份;过辛酸叔丁酯30份;邻苯二甲酸二丁酯8份;甲基丙烯酸甲酯45份;硅酸铝40份;马来酸酐25份。
将松香改性醇酸树脂、乙二醇乙醚醋酸酯、氢醌单甲醚、铬酸钡和二恶烷加入去离子水中,加热至40℃搅拌3h,加入二甲基乙醇胺、三乙胺、二戊烯、过辛酸叔丁酯、硅酸铝和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入磷酸三苯酯和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗2500次;在水中浸泡70d后不起泡、不掉粉;表干1.5h,实干9h,耐碱性饱和氢氧化钙溶液35d。
实施例3:
一种油包油型醇酸树脂多彩涂料,其原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯40份;乙二醇乙醚醋酸酯30份;氢醌单甲醚15份;铬酸钡25份;二恶烷5份;去离子水85份;二甲基乙醇胺30份;氧化铁红15份;三乙胺35份;二戊烯25份;过辛酸叔丁酯20份;邻苯二甲酸二丁酯7份;甲基丙烯酸甲酯35份;硅酸铝35份;马来酸酐20份。
将松香改性醇酸树脂、乙二醇乙醚醋酸酯、氢醌单甲醚、铬酸钡和二恶烷加入去离子水中,加热至40℃搅拌3h,加入二甲基乙醇胺、三乙胺、二戊烯、过辛酸叔丁酯、硅酸铝和邻苯二甲酸二丁酯,升温至50℃用球磨机球磨10min,加入磷酸三苯酯和剩余原料,升温至60℃搅拌10h后既得成品。
涂膜耐擦洗3000次;在水中浸泡80d后不起泡、不掉粉;表干1h,实干8h,耐碱性饱和氢氧化钙溶液40d。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种油包油型醇酸树脂多彩涂料,其特征在于所述油包油型醇酸树脂多彩涂料的原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯35-45份;乙二醇乙醚醋酸酯20-40份;氢醌单甲醚10-20份;铬酸钡15-35份;二恶烷1-10份;去离子水80-90份;二甲基乙醇胺25-35份;颜料10-20份;三乙胺30-40份;二戊烯20-30份;过辛酸叔丁酯10-30份;增塑剂6-8份;甲基丙烯酸甲酯25-45份;硅酸铝30-40份;马来酸酐15-25份。
2.根据权利要求1所述的一种油包油型醇酸树脂多彩涂料,其特征在于所述油包油型醇酸树脂多彩涂料的原料按重量份数配比如下:松香改性醇酸树脂100份;磷酸三苯酯40份;乙二醇乙醚醋酸酯30份;氢醌单甲醚15份;铬酸钡25份;二恶烷5份;去离子水85份;二甲基乙醇胺30份;颜料15份;三乙胺35份;二戊烯25份;过辛酸叔丁酯20份;增塑剂7份;甲基丙烯酸甲酯35份;硅酸铝35份;马来酸酐20份。
3.根据权利要求1所述的一种油包油型醇酸树脂多彩涂料,其特征在于:所述颜料采用氧化铁红、氧化铬绿或中铬黄。
4.根据权利要求1所述的一种油包油型醇酸树脂多彩涂料,其特征在于:所述增塑剂采用邻苯二甲酸二丁酯。