CN104194596B - 一种橘纹涂料 - Google Patents
一种橘纹涂料 Download PDFInfo
- Publication number
- CN104194596B CN104194596B CN201410437069.0A CN201410437069A CN104194596B CN 104194596 B CN104194596 B CN 104194596B CN 201410437069 A CN201410437069 A CN 201410437069A CN 104194596 B CN104194596 B CN 104194596B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- fructus citri
- citri tangerinae
- vagina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种橘纹涂料,其原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯15-25份;钛白粉35-45份;二甲苯20-30份;碳酸钙30-40份;氢醌单甲醚5-15份;硫酸钡15-35份;一缩二乙二醇25-35份;颜填料20-30份;丙三醇单烯丙基醚5-25份;苯乙烯10-30份;甲基四氢苯酐10-20份;增韧剂30-40份;邻苯二甲酸酐20-40份;甲苯35-45份;DBP1-10份;涂膜柔韧性1mm,光泽度12-18%;硬度0.4-0.5,冲击强度60-70kg·cm;附着力2级,耐水性10-20d,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域,尤其涉及一种橘纹涂料。
背景技术
涂料,在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面,并能与被涂物形成牢固附着的连续薄膜,通常是以树脂、或油、或乳液为主,添加或不添加颜填料、填料,添加相应助剂,用有机溶剂或碳酸钙配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的:“涂料是一种材料,这种材料可以用不同的施工工艺涂覆在物件表面,形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜,又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料,称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称,引进我国后,就一直利用在建筑行业。涂料的作用可以概括为三个方面:保护作用,装饰作用,特殊功能作用。涂料的一般组成:包含成膜物质、颜填料、溶剂、助剂。涂料是指应用于物体表面而能结成坚韧保护膜的物料的总称,建筑涂料是涂料中的一个重要类别,在我国,一般将用于建筑物内墙,外墙,顶棚,地面,卫生间的涂料称为建筑涂料。
桔纹漆是装饰性涂料:由特种树脂、颜料、助剂和稀释剂经特殊工艺制成;桔纹清晰、立体感强,装饰性能好;干燥快,附着力强,硬度好,机械性能好。橘纹涂料又叫橘纹漆、橘纹油漆;橘纹涂料是由特种涂料构成的具有特殊效能的涂料品种,是一种工业用漆,与其他涂料一样,将这种涂料涂在物体表面会起到对各种物体的保护作用,不同的是其涂料成膜后,涂面会自然形成和出现自然的各种美丽图案花纹,如锤纹、皱纹、橘纹、石纹、斑纹、晶纹、裂纹、木纹等。而随着人性化理念的普及,及新型和谐社会的构成,设计一种光泽度高、冲击强度及附着力高的橘纹涂料是非常必要的。
发明内容
解决的技术问题:
本申请针对上述技术问题,提供一种橘纹涂料,解决现有橘纹涂料光泽度和冲击强度低、耐水性差、附着力低等技术问题。
技术方案:
一种橘纹涂料,所述橘纹涂料的原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯15-25份;钛白粉35-45份;二甲苯20-30份;碳酸钙30-40份;氢醌单甲醚5-15份;硫酸钡15-35份;一缩二乙二醇25-35份;颜填料20-30份;丙三醇单烯丙基醚5-25份;苯乙烯10-30份;甲基四氢苯酐10-20份;增韧剂30-40份;邻苯二甲酸酐20-40份;甲苯35-45份;DBP1-10份。
作为本发明的一种优选技术方案:所述橘纹涂料的原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯20份;钛白粉40份;二甲苯25份;碳酸钙35份;氢醌单甲醚10份;硫酸钡25份;一缩二乙二醇30份;颜填料25份;丙三醇单烯丙基醚15份;苯乙烯20份;甲基四氢苯酐15份;增韧剂35份;邻苯二甲酸酐30份;甲苯40份;DBP5份。
作为本发明的一种优选技术方案:所述颜填料采用柠檬黄、酞菁蓝或炭黑。
作为本发明的一种优选技术方案:所述增韧剂采用苯乙烯-丁二烯-苯乙烯。
有益效果:
本发明所述一种橘纹涂料采用以上技术方案与现有技术相比,具有以下技术效果:1、涂膜柔韧性1mm,光泽度12-18%;2、硬度0.4-0.5,冲击强度60-70kg·cm;3、附着力2级,耐水性10-20d,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种橘纹涂料,其原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯15份;钛白粉35份;二甲苯20份;碳酸钙30份;氢醌单甲醚5份;硫酸钡15份;一缩二乙二醇25份;炭黑20份;丙三醇单烯丙基醚5份;苯乙烯10份;甲基四氢苯酐10份;苯乙烯-丁二烯-苯乙烯30份;邻苯二甲酸酐20份;甲苯35份;DBP1份。
常温下,将醇酸树脂、二缩三丙二醇二丙烯酸酯、钛白粉和二甲苯加入反应釜中,搅拌10min后加入碳酸钙、氢醌单甲醚和硫酸钡,搅拌20min后升温至90℃加入剩余原料,搅拌均匀后投入砂磨机研磨30min,冷却并过滤后既得成品。
涂膜光泽度12%;硬度0.4,冲击强度60kg·cm;耐水性10d。
实施例2:
一种橘纹涂料,其原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯25份;钛白粉45份;二甲苯30份;碳酸钙40份;氢醌单甲醚15份;硫酸钡35份;一缩二乙二醇35份;酞菁蓝30份;丙三醇单烯丙基醚25份;苯乙烯30份;甲基四氢苯酐20份;苯乙烯-丁二烯-苯乙烯40份;邻苯二甲酸酐40份;甲苯45份;DBP10份。
常温下,将醇酸树脂、二缩三丙二醇二丙烯酸酯、钛白粉和二甲苯加入反应釜中,搅拌10min后加入碳酸钙、氢醌单甲醚和硫酸钡,搅拌20min后升温至90℃加入剩余原料,搅拌均匀后投入砂磨机研磨30min,冷却并过滤后既得成品。
涂膜光泽度15%;硬度0.45,冲击强度65kg·cm;耐水性15d。实施例3:
一种橘纹涂料,其原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯20份;钛白粉40份;二甲苯25份;碳酸钙35份;氢醌单甲醚10份;硫酸钡25份;一缩二乙二醇30份;柠檬黄25份;丙三醇单烯丙基醚15份;苯乙烯20份;甲基四氢苯酐15份;苯乙烯-丁二烯-苯乙烯35份;邻苯二甲酸酐30份;甲苯40份;DBP5份。
常温下,将醇酸树脂、二缩三丙二醇二丙烯酸酯、钛白粉和二甲苯加入反应釜中,搅拌10min后加入碳酸钙、氢醌单甲醚和硫酸钡,搅拌20min后升温至90℃加入剩余原料,搅拌均匀后投入砂磨机研磨30min,冷却并过滤后既得成品。
涂膜光泽度18%;硬度0.5,冲击强度70kg·cm;耐水性20d。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (1)
1.一种橘纹涂料,其特征在于所述橘纹涂料的原料按重量份数配比如下:醇酸树脂100份;二缩三丙二醇二丙烯酸酯20份;钛白粉40份;二甲苯25份;碳酸钙35份;氢醌单甲醚10份;硫酸钡25份;一缩二乙二醇30份;颜填料25份;丙三醇单烯丙基醚15份;苯乙烯20份;甲基四氢苯酐15份;增韧剂35份;邻苯二甲酸酐30份;甲苯40份;DBP5份;
所述颜填料采用柠檬黄、酞菁蓝或炭黑;
所述增韧剂采用苯乙烯-丁二烯-苯乙烯。