CN104194570A - 一种低voc高固含uv喷涂面漆 - Google Patents
一种低voc高固含uv喷涂面漆 Download PDFInfo
- Publication number
- CN104194570A CN104194570A CN201410484962.9A CN201410484962A CN104194570A CN 104194570 A CN104194570 A CN 104194570A CN 201410484962 A CN201410484962 A CN 201410484962A CN 104194570 A CN104194570 A CN 104194570A
- Authority
- CN
- China
- Prior art keywords
- spray paint
- low
- low voc
- paint according
- height
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于化工领域中的紫外光固化涂料,涉及应用于电子工业3C电子产品的一种低VOC高固含UV喷涂面漆:它由下列质量份的原料制成:聚氨酯丙烯酸酯树酯10~20%;环氧丙烯酸酯树酯15~25%;四氢呋喃单丙烯酸酯10~20%;己二醇双丙烯酸酯10~20%;丙烯酸丁酯10~20%;引发剂3~8%;流平剂0.1~5%;消泡剂0.1~1%;有机溶剂5~15%;涂膜结构坚韧,抗划伤,高丰满度,耐侯耐腐蚀。较低的粘度能直接喷涂于3C电子制键和制品上,是一种能长期有效的保防3C电子产品制键和制品表面的涂料产品,并提供优良的装饰效果,而且在生产过程中低VOC排放,固化速度快、效率高、更加环保。
Description
技术领域
本发明属于化工领域中的紫外光固化涂料,为一种低VOC高固含UV喷涂面漆,是一种UV树脂、UV单体、UV光引发剂及各种助剂所组成的单组份型紫外光固化涂料,施工时采用喷涂方式进行施工。
背景技术
UV涂料的固化属于化学方法,它是UV引发化学反应的结果。与其他的固化方式的涂料比较,UV涂料具有速率快、费用低、污染少的特点。
全世界每年消耗涂料2000多万吨,其中有机溶剂约占40%,就是说每年大约有800多万吨溶剂进入大气。进入大气的有机物可以形成比二氧化碳更严重的温室效应,而且在阳光照射下可形成氧化物和光化学烟雾,从而造成环境污染和对操作工人身体健康的损害。
现阶段应用于电子工业3C电子产品外壳保护的无溶剂UV喷涂涂料普遍存在粘度较高,不利于喷涂操作和施工。而溶剂型的UV涂料虽然解决了粘度带来的施工问题,但为了达到喷涂施工的要求还必须添加大量挥发性有机溶剂来降低粘度。在喷涂施工和操作过程中造成大量VOC排放,不但污染环境也不利于环保和健康。
发明内容
本发明的目的是:提供一种应用于电子工业3C电子产品外壳保护的低VOC高固含UV喷涂面漆,喷涂后经UV固化在制品或制键上形成一层性能优异保护膜,并提供优良的装饰效果。其粘度低、VOC排放低,可使用喷涂的方法进行作业,提高生产效率、减少排放,达到快捷、高效、环保。
1、本发明是这样实现的:一种低VOC高固含UV喷涂面漆,使用喷涂方式进行喷涂施工,它由下列重量份的原料制成:
聚氨酯丙烯酸酯10~20%;
环氧丙烯酸酯15~25%;
四氢呋喃单丙烯酸酯10~20%;
己二醇双丙烯酸酯10~20%;
丙烯酸丁酯10~20%;
光引发剂3~8%;
流平剂0.1~5%;
消泡剂0.1~1%;
有机溶剂5~15%。
2、所述的一种低VOC高固含UV喷涂面漆,所述的聚氨酯丙烯酸酯为6 官能度脂肪族聚氨酯丙烯酸树酯,其粘度低,具有耐侯性好,附着力佳,柔韧性佳,增加涂层表面硬度,固化速度快,反应活性强。
3、所述的一种低VOC高固含UV喷涂面漆,所述的环氧丙烯酸酯其成份为含80%双酚A型环氧丙烯酸酯,20%TPGDA单体组成,其低色数、高光泽、耐化学性,硬度佳。
4、所述的一种低VOC高固含UV喷涂面漆,所述的四氢呋喃单丙烯酸酯为单官能度丙烯酸酯类单体,具有很强的稀释性、良好的增柔效果,优越的抗水性及耐化妆品性。
5、所述的一种低VOC高固含UV喷涂面漆,所述的己二醇二丙烯酸酯单体为2 官能度丙烯酸酯类单体,具有稀释能力强,低收缩,固化速度快,高硬度、极好的附着力。
6、所述的一种低VOC高固含UV喷涂面漆,所述的丙烯酸丁酯为单官能丙烯酸酯类单体,具有很好的稀释能力并具有长链的丁基,使分子结构易旋转使涂层容易释放内应力有利于附着力的保持。
7、所述的一种低VOC高固含UV喷涂面漆,所述的光引发剂为芳香酮类、苯偶姻及其衍生物或它们的混合物。
8、所述的一种低VOC高固含UV喷涂面漆,所述的流平剂为丙烯酸酯类溶液。
9、所述的一种低VOC高固含UV喷涂面漆,所述消泡剂为非硅酮高分子聚合物。
10、所述的一种低VOC高固含UV喷涂面漆,所述有机溶剂为醋酸丁酯、异丙醇、丁酮一种或二种以上。
具体实施方式
下面结合实施例对本发明进行详细的说明,实施例仅是本发明的优选实施方式,不是对本发明的限定。
本发明的制备方法为本技术领域的常规方法,因此在此不再详细描述。
实施例1
一种低VOC高固含UV喷涂面漆,使用喷涂方式进行喷涂施工,它由下列重量份的原料制成:
聚氨酯丙烯酸酯10%;
环氧丙烯酸酯20%;
四氢呋喃单丙烯酸酯8%;
己二醇双丙烯酸酯20%;
丙烯酸丁酯8%;
光引发剂5%;
流平剂0.4%;
消泡剂0.2%;
有机溶剂8%。
实施例2
一种低VOC高固含UV喷涂面漆,使用喷涂方式进行喷涂施工,它由下列重量份的原料制成:
聚氨酯丙烯酸酯10%;
环氧丙烯酸酯15%;
四氢呋喃单丙烯酸酯8%;
己二醇双丙烯酸酯20%;
丙烯酸丁酯13%;
光引发剂5%;
流平剂0.4%;
消泡剂0.2%;
有机溶剂13%。
3、上述实施组份中:所述聚氨酯丙烯酸酯可采用台湾长兴公司6150-100、6145-100,SARTOMER公司CN9103或它们的混合物。
4、所述环氧丙烯酸酯可采台湾长兴公司621A-80。
5、所述四氢呋喃单丙烯酸酯、己二醇双丙烯酸酯、丙烯酸丁酯可采用CYTEC公司、SARTOMER公司、长兴公司或它们的混合物。
6、所述的光引发剂为芳香酮类、苯偶姻及其衍生物或它们的混合物,如BASF生产的BP、1173、184或它们的混合物。
7、所述的流平剂为丙烯酸酯类溶液,如台湾德谦公司生产的德谦3600、德谦835,荷兰EFKA助剂公司生产的EFKA 3777或它们的混合物。
8、所述的消泡剂为非硅酮高分子聚合物,如荷兰EFKA助剂公司生产的EFKA-2721、台湾德谦公司生产的德谦3100或它们的混合物。
9、所述的有机溶剂为醋酸丁酯、异丙醇、二甲苯、丁酮混合溶液,可采用中山市鑫汇化工、广州市俱辉化工有限公司、东莞市百建化工有限公司或它们的混合物。
10、配制时,将聚氨酯丙烯酸酯、环氧丙烯酸树酯、四氢呋喃单丙烯酸酯、己二醇双丙烯酸酯、丙烯酸丁酯、流平剂、消泡剂、有机溶剂依次加入并分散后,加入光引发剂充分分散均匀,控制涂料温度不超过60℃。
11、涂料施工时,可根据具体情况加入适当UV单体或溶剂,或控制涂料温度来调节施工粘度,通过喷涂的方式将漆涂布于产品制品或制键上,置于50℃烘箱内流平3-5分钟即可UV固化。
12、经检测,使用本发明涂装的基板的技术指标如下:
实例一 | 实例二 | 检测标准 | |
固含量 | 91% | 86% | 热挥发125℃×1h/ASTM D1644 |
漆膜外观 | 平整光滑 | 平整光滑 | 目视/ASTM D1729 |
硬度 | HB | H | 中华铅笔(1KG)/ASTM D3363-74 |
光泽 | 98 | 98 | WGG-4 光泽仪60°/ASTMD1003 |
耐候性 | 漆膜无明显外观不良 | 漆膜无明显外观不良 | QUV 加速老化机 48h/ASTM G53 |
耐化学品 | 漆膜无明显外观不良 | 漆膜无明显外观不良 | 剃须膏、洗手液、碳酸饮料、食醋、奶油、咖啡、香水、酒(35~40%乙醇)×35℃×72h |
附着力 | 4B | 4B | 划格法600# (次)/ASTMD3359-95 |
耐热水 | 漆膜无明显外观不良 | 漆膜无明显外观不良 | 85℃×0.5h |
耐盐雾性 | 漆膜无明显外观不良 | 漆膜无明显外观不良 | 盐雾试验机 5%氯化钠 48h |
Claims (10)
1.一种低VOC高固含UV喷涂面漆,使用喷涂方式进行喷涂施工;其特征在于:它由下列质量份的原料制成:
聚氨酯丙烯酸酯10~20%;
环氧丙烯酸酯15~25%;
四氢呋喃单丙烯酸酯10~20%;
己二醇双丙烯酸酯 10~20%;
丙烯酸丁酯10~20%;
光引发剂3~8%;
流平剂0.1~5%;
消泡剂0.1~1%;
有机溶剂5~15%。
2.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的聚氨酯丙烯酸酯为6 官能度脂肪族聚氨酯丙烯酸树酯,其粘度低,具有耐侯性好,附着力佳,柔韧性佳,增加涂层表面硬度,固化速度快,反应活性强。
3.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的环氧丙烯酸酯其成份为含80%双酚A型环氧丙烯酸酯,20%TPGDA单体组成,其低色数、高光泽、耐化学性,硬度佳。
4.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的四氢呋喃单丙烯酸酯为单官能度丙烯酸酯类单体,具有很强的稀释性、良好的增柔效果,优越的抗水性及耐化妆品性。
5.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的己二醇二丙烯酸酯单体为2 官能度丙烯酸酯类单体,具有稀释能力强,低收缩,固化速度快,高硬度、极好的附着力。
6.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的丙烯酸丁酯为单官能丙烯酸酯类单体,具有很好的稀释能力并具有长链的丁基,使分子结构易旋转使涂层容易释放内应力有利于附着力的保持。
7.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的光引发剂为芳香酮类、苯偶姻及其衍生物或它们的混合物。
8.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述的流平剂为丙烯酸酯类溶液。
9.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述消泡剂为非硅酮高分子聚合物。
10.根据权利要求1 所述的一种低VOC高固含UV喷涂面漆,其特征在于:所述有机溶剂为醋酸丁酯、异丙醇、丁酮一种或二种以上。