CN104194329A - Transparent PA6 (polyamide 6) composite material - Google Patents
Transparent PA6 (polyamide 6) composite material Download PDFInfo
- Publication number
- CN104194329A CN104194329A CN201410411275.4A CN201410411275A CN104194329A CN 104194329 A CN104194329 A CN 104194329A CN 201410411275 A CN201410411275 A CN 201410411275A CN 104194329 A CN104194329 A CN 104194329A
- Authority
- CN
- China
- Prior art keywords
- parts
- transparent
- composite material
- stearic acid
- polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a transparent PA6 (polyamide 6) composite material which is prepared from the following raw materials in parts by weight: 100-200 parts of PA6, 10-15 parts of stearic acid metal salt, 5-8 parts of inorganic nucleating agent, 1-3 parts of stearic acid, 3-8 parts of polypropylene wax, 10-20 parts of bentonite, 5-15 parts of glass fiber powder and 5-15 parts of glass microsphere. The transparent PA6 composite material has the advantages of favorable transparent effect, low cost and simple production technique, and can not produce transitional products and environmental pollutants.
Description
Technical field
The present invention relates to technical field of polymer materials, be specifically related to a kind of transparent PA6 matrix material.
Background technology
Nylon resin is from since coming out, the history of existing six more than ten years, and it is widely used in the manufacture of synthon, and is acknowledged as the engineering plastics of consumption maximum, and it has experienced from the laboratory of the '30s explores the process of annual sales volume millions of tons up till now.Along with the continuous expansion of nylon resin range of application, some have the nylon kind of property also arises at the historic moment, and nylon monofilament is for fisheries industry, system brush industry and make sewing thread etc.But in order to increase fishing output, improve the outward appearance of brushware, the fabric that sewing thread is applicable to different color and lusters, require nylon resin to there is the good transparency, in addition, the production of some fashionable dress fabrics, also has certain requirement to the transparency of nylon resin.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is that a kind of transparent PA6 matrix material is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of transparent PA6 matrix material, raw material by following parts by weight is made: 100～200 parts of PA6,10～15 parts of Metallic stearates, 5～8 parts of mineral-type nucleators, stearic acid is 1～3 part, 3～8 parts of Poly Propylene Waxes, 10～20 parts of wilkinites, 5～15 parts of glass fiber powders, 5～15 parts of glass microballons.
Beneficial effect of the present invention: transparent effect is good, cost is low, production technique is simple, can not cause transitional product and environmental pollutant.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, and a kind of transparent PA6 matrix material is made by the raw material of following parts by weight: 150 parts of PA6,10 parts of Metallic stearates, 5 parts of mineral-type nucleators, stearic acid is 1 part, 3 parts of Poly Propylene Waxes, 20 parts of wilkinites, 15 parts of glass fiber powders, 5 parts of glass microballons.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a transparent PA6 matrix material, it is characterized in that: the raw material by following parts by weight is made: 100～200 parts of PA6,10～15 parts of Metallic stearates, 5～8 parts of mineral-type nucleators, stearic acid is 1～3 part, 3～8 parts of Poly Propylene Waxes, 10～20 parts of wilkinites, 5～15 parts of glass fiber powders, 5～15 parts of glass microballons.