CN104194125A - Magnetic wood-plastic material and preparing method thereof - Google Patents
Magnetic wood-plastic material and preparing method thereof Download PDFInfo
- Publication number
- CN104194125A CN104194125A CN201410464397.XA CN201410464397A CN104194125A CN 104194125 A CN104194125 A CN 104194125A CN 201410464397 A CN201410464397 A CN 201410464397A CN 104194125 A CN104194125 A CN 104194125A
- Authority
- CN
- China
- Prior art keywords
- plastic material
- wood
- parts
- magnetic
- magnetic wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a magnetic wood-plastic material. The magnetic wood-plastic material comprises the following ingredients in parts by weight: 0.1-20 parts of rare earth magnetic powder, 0.5-5 parts of pigment, 10-70 parts of wood fibers, 20-85 parts of plastic, 2-5 parts of a lubricant and 1-5 parts of a compatilizer. The invention further discloses a preparing method of the magnetic wood-plastic material. Through the addition of the rare earth magnetic powder into the magnetic wood-plastic material, the finally prepared wood-plastic material has the functions of the magnetic material, and the application range of the wood-plastic material is greatly enlarged.
Description
Technical field
The present invention relates to a kind of Wood-plastic material and preparation method thereof, especially relate to a kind of magnetic Wood-plastic material and preparation method thereof, belong to Wood-plastic material formula and preparation method's technical field.
Background technology
Wood-plastic material is that a kind of waste or used plastics and vegetable fibre of utilizing is mixed into new material, then through extruding, the advanced composite material that processes such as mold pressing, injection molding.It is widely used in gardens, garden, plank road, wayside pavilion, fence etc.
Have no at present the report of magnetic Wood-plastic material, magnetic Wood-plastic material the advantage such as the wood appearance that normal wood moulds is good, environment-protecting asepsis, also has the dramatic benefit of magneticsubstance except having, and can widen the range of application of Wood-plastic material, as can be applicable to toy, stationery etc.
Summary of the invention
The object of the present invention is to provide a kind of applied range attractive in appearance, there is magnetic Wood-plastic material of magneticsubstance advantage and preparation method thereof.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A magnetic Wood-plastic material, is characterized in that, comprises that the parts by weight of following component and each component are:
Rare earth magnet powders: 0.1-20 part;
Pigment: 0.5-5 part;
Xylon: 10-70 part;
Plastics: 20-85 part;
Lubricant: 2-5 part;
Compatilizer: 1-5 part.
Further, described rare earth magnet powders is SmCo
5, Sm
2co
17, Sm
2fe
17, Sm
2cu
17, Sm
2zr
17, Sm
2nb
17, Sm
2ni
17, Sm
2mn
17in at least one.
And described plastics are at least one in PE, PP, PA, ABS, PET, PVC.
And described pigment is red iron oxide, iron oxide yellow, carbon black, titanium dioxide at least one.
A preparation method for magnetic Wood-plastic material, is characterized in that, concrete steps are as follows: by rare earth magnet powders: 0.1-20 part; Pigment: 0.5-5 part; Xylon: 10-70 part; Plastics: 20-85 part; Lubricant: 2-5 part; Compatilizer: after 1-5 part batch mixing, granulation, then by extruding or injection moulding obtains magnetic Wood-plastic material.
Beneficial effect of the present invention is: the present invention, by add rare earth magnet powders in Wood-plastic material, makes the final Wood-plastic material of preparing have the function of magneticsubstance, has greatly expanded the range of application of Wood-plastic material.
Embodiment
Below in conjunction with specific embodiment, describe the present invention in detail.
embodiment 1:
By SmCo
5: 20 parts; 3 parts of red iron oxides; Xylon: 41 parts; PP:30 part; Lubricant: 3 parts; Compatilizer: after 3 parts of batch mixings, granulation, then by extruding or injection moulding obtains magnetic Wood-plastic material.
The magnetic Wood-plastic material that embodiment 1 prepares is according to the standard test methods test of the saturation magnetization of ASTM A 894/A 894M-2000 nonmetal magnetic material or magnetic conductance, its saturation magnetization 15.645emu/g, residual magnetization 8.689emu/g, MOR 30.5MPa.
embodiment 2:
By Sm
2mn
17: 10 parts; 3 parts of red iron oxides; Xylon: 51 parts; PE:30 part; Lubricant: 3 parts; Compatilizer: after 3 parts of batch mixings, granulation, then by extruding or injection moulding obtains magnetic Wood-plastic material.
The magnetic Wood-plastic material that embodiment 2 prepares after tested, its saturation magnetization 11.423emu/g, residual magnetization 5.211emu/g, MOR 28.7MPa.
embodiment 3:
By Sm
2co
17: 5 parts; 5 parts of iron oxide yellow; Xylon: 25 parts; PA6:60 part; Lubricant: 2 parts; Compatilizer: after 3 parts of batch mixings, granulation, then obtain magnetic Wood-plastic material by injection moulding.
The magnetic Wood-plastic material that embodiment 3 prepares after tested, its saturation magnetization 6.471emu/g, residual magnetization 3.652emu/g, MOR 48.6MPa.
embodiment 4:
By Sm
2cu
17: 0.2 part; 3 parts of titanium dioxides; Xylon: 70 parts; PVC:20 part; Lubricant: 2 parts; Compatilizer: after 4.8 parts of batch mixings, granulation, then obtain magnetic Wood-plastic material by extrusion moulding.
The magnetic Wood-plastic material that embodiment 4 prepares after tested, its saturation magnetization 0.352emu/g, residual magnetization 0.056emu/g, MOR 21.3MPa.
The present invention is illustrated and should be appreciated that above-described embodiment does not limit the present invention in any form according to above-described embodiment, and all employings are equal to replaces or technical scheme that equivalent transformation mode obtains, within all dropping on protection scope of the present invention.
Claims (5)
1. a magnetic Wood-plastic material, is characterized in that, comprises that the parts by weight of following component and each component are:
Rare earth magnet powders: 0.1-20 part;
Pigment: 0.5-5 part;
Xylon: 10-70 part;
Plastics: 20-85 part;
Lubricant: 2-5 part;
Compatilizer: 1-5 part.
2. a kind of magnetic Wood-plastic material according to claim 1, is characterized in that, described rare earth magnet powders is SmCo
5, Sm
2co
17, Sm
2fe
17, Sm
2cu
17, Sm
2zr
17, Sm
2nb
17, Sm
2ni
17, Sm
2mn
17in at least one.
3. a kind of magnetic Wood-plastic material according to claim 1, is characterized in that, described plastics are at least one in PE, PP, PA, ABS, PET, PVC.
4. a kind of magnetic Wood-plastic material according to claim 1, is characterized in that, described pigment is at least one of red iron oxide, iron oxide yellow, carbon black, titanium dioxide.
5. a preparation method for magnetic Wood-plastic material, is characterized in that, concrete steps are as follows: by rare earth magnet powders: 0.1-20 part; Pigment: 0.5-5 part; Xylon: 10.70 parts; Plastics: 20-85 part; Lubricant: 2-5 part; Compatilizer: after 1-5 part batch mixing, granulation, then by extruding or injection moulding obtains magnetic Wood-plastic material.