CN104164083A - Magnetic modified plastic cement material - Google Patents
Magnetic modified plastic cement material Download PDFInfo
- Publication number
- CN104164083A CN104164083A CN201410368996.1A CN201410368996A CN104164083A CN 104164083 A CN104164083 A CN 104164083A CN 201410368996 A CN201410368996 A CN 201410368996A CN 104164083 A CN104164083 A CN 104164083A
- Authority
- CN
- China
- Prior art keywords
- parts
- iron
- magnetic
- plastic cement
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A disclosed magnetic modified plastic cement material is characterized by comprising the following substances in parts by weight: 25-30 parts of nylon 6 powder, 14-20 parts of thermoplastic resin, 3-9 parts of iron-iron-boron magnetic powder, 5-9 parts of carboxymethyl cellulose, 3-8 parts of a composite substrate material, 4-8 parts of 6-aminocaproic acid, 5-7 parts of butyl methacrylate, 1-6 parts of maleic anhydride, 1-2 parts of magnesium, 2-6 parts of a composite adhesive, 3-6 parts of nanometer level silicon dioxide, 1-2 parts of a silane coupling agent, and 3-9 parts of stearic acid. The iron-iron-boron magnetic powder in the plastic cement material is uniform in distribution, is relatively easily dispersed during fusion extrusion, and helps to increase the strength of the composite material.
Description
Technical field
The present invention relates to a kind of magnetic modified plastic rubber material.
Background technology
Magnetic plastics can be divided into structure-type and compound two kinds, wherein, structure-type magnetic plastics refers to that polymkeric substance itself has ferromagnetic magnet, and compound magnetic plastics refer to taking plastics or rubber as binding agent and magnetic powder tear closes the magnet magnetic plastics that bonding is processed into.
The most magnetic plasticses that use in prior art all belong to compound, by inorganic magnetic powder and polymer plastic glue material are blended into matrix material, then excite the magnetic of the inorganic magnetic material in matrix material through magnetizing.The magnetic being filled in plastics is mainly ferrite class magnetic and iron iron boron class magnetic.On market, magnetic plastics is mainly filled ferrite class magnetic, and this type of magnetic is with low cost, easily processing, but magnetic a little less than, its use range is limited.And the iron coin friend class magnetic of admiring is mainly used in sintering magnetic material, this type of magnetic material adopts the method for powder metallurgy, magnetic and macromolecular material are mixed to bonding, by compression molding product, then through removing plastic components sinter molding again, this product structure is simple, rotproofness is poor, tooling cost is high, and intensity is lower, is not suitable for the complicated meticulous product of processing structure.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of magnetic modified plastic rubber material.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of magnetic modified plastic rubber material, is characterized in that, comprises the material of following parts by weight: nylon 6 powder 25-30 parts, thermoplastic resin 14-20 part, iron iron boron magnetic powder 3-9 part, carboxy methyl cellulose 5-9 part, composite base material 3-8 part, six hexosamine 4-8 parts, n-BMA 5-7 part, maleic anhydride 1-6 part, magnesium 1-2 part, composite adhesive 2-6 part, nanometer grade silica 3-6 part, silane coupling agent 1-2 part, stearic acid 3-9 part.
The iron boron magnetic powder of admiring in plastic material of the present invention is evenly distributed, and in the process melt extruding, more easily disperses, and has increased the intensity of matrix material.
Embodiment
Embodiment 1
A kind of magnetic modified plastic rubber material, is characterized in that, comprises the material of following parts by weight: nylon 6 powder 25-30 parts, thermoplastic resin 14-20 part, iron iron boron magnetic powder 3-9 part, carboxy methyl cellulose 5-9 part, composite base material 3-8 part, six hexosamine 4-8 parts, n-BMA 5-7 part, maleic anhydride 1-6 part, magnesium 1-2 part, composite adhesive 2-6 part, nanometer grade silica 3-6 part, silane coupling agent 1-2 part, stearic acid 3-9 part.
Claims (1)
1. a magnetic modified plastic rubber material, is characterized in that, comprises the material of following parts by weight: nylon 6 powder 25-30 parts, thermoplastic resin 14-20 part, iron iron boron magnetic powder 3-9 part, carboxy methyl cellulose 5-9 part, composite base material 3-8 part, six hexosamine 4-8 parts, n-BMA 5-7 part, maleic anhydride 1-6 part, magnesium 1-2 part, composite adhesive 2-6 part, nanometer grade silica 3-6 part, silane coupling agent 1-2 part, stearic acid 3-9 part.