CN104178020B - 一种陶瓷用紫外光固化涂料 - Google Patents

一种陶瓷用紫外光固化涂料 Download PDF

Info

Publication number
CN104178020B
CN104178020B CN201410453433.2A CN201410453433A CN104178020B CN 104178020 B CN104178020 B CN 104178020B CN 201410453433 A CN201410453433 A CN 201410453433A CN 104178020 B CN104178020 B CN 104178020B
Authority
CN
China
Prior art keywords
parts
curing paint
ultraviolet
water
pottery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410453433.2A
Other languages
English (en)
Other versions
CN104178020A (zh
Inventor
费金华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinzhou Tao Hua Dao Ceramics Co., Ltd.
Original Assignee
Suzhou Shengpula New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Shengpula New Material Technology Co Ltd filed Critical Suzhou Shengpula New Material Technology Co Ltd
Priority to CN201410453433.2A priority Critical patent/CN104178020B/zh
Publication of CN104178020A publication Critical patent/CN104178020A/zh
Application granted granted Critical
Publication of CN104178020B publication Critical patent/CN104178020B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种陶瓷用紫外光固化涂料，其原料如下：聚氨酯丙烯酸酯、二氧化钛、三羟甲基丙烷三丙烯酸酯、立德粉、水、滑石粉、着色颜料、轻质碳酸钙、丙烯酸乙酯、硫酸钡、交联剂、安息香乙醚、二甲基丙烷羧酸酯、二苯甲酮和三甲氧基硅烷；产品光泽度120％-130％，表干时间20-60s，实干30-40min；水中浸泡40-60d后无起泡、脱落现象；在饱和氢氧化钙中浸泡20-30d不起泡、皱皮；产品耐95％乙醇浸棉球摩擦8-12h，可以广泛生产并不断代替现有材料。

Description

一种陶瓷用紫外光固化涂料
技术领域
本申请属于涂料领域，尤其涉及一种陶瓷用紫外光固化涂料。
背景技术
陶瓷涂料耐候性和加工性能优异，耐脏而且耐损伤。以往的陶瓷涂料虽然耐损伤，但是如果对涂装后的部件进行弯曲加工，容易产生裂纹，而且含氟树脂涂料和有机涂料，容易被沙石、灰尘等损坏。因此，陶瓷涂料的问世，受到了陶瓷行业的青睐，并正向其他行业渗透，前景看好。而随着人性化理念的普及，及新型和谐社会的构成，设计一种光泽度好、干燥快、抗化学品与抗水性良好的陶瓷用紫外光固化涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种陶瓷用紫外光固化涂料，解决现有陶瓷用紫外光固化涂料光泽度、干燥慢、抗化学品与抗水性差等技术问题。
技术方案：
一种陶瓷用紫外光固化涂料，所述陶瓷用紫外光固化涂料的原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛1-10份；三羟甲基丙烷三丙烯酸酯20-30份；立德粉15-25份；水80-100份；滑石粉10-20份；着色颜料5-15份；轻质碳酸钙20-40份；丙烯酸乙酯5-25份；硫酸钡30-40份；交联剂3-5份；安息香乙醚1-10份；二甲基丙烷羧酸酯25-35份；二苯甲酮5-10份；三甲氧基硅烷35-45份。
作为本发明的一种优选技术方案：所述陶瓷用紫外光固化涂料的原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛5份；三羟甲基丙烷三丙烯酸酯25份；立德粉20份；水90份；滑石粉15份；着色颜料10份；轻质碳酸钙30份；丙烯酸乙酯15份；硫酸钡35份；交联剂4份；安息香乙醚5份；二甲基丙烷羧酸酯30份；二苯甲酮8份；三甲氧基硅烷40份。
作为本发明的一种优选技术方案：所述着色颜料采用氧化铁红或中铬黄。
作为本发明的一种优选技术方案：所述交联剂采用苯乙烯。
有益效果：
本发明所述一种陶瓷用紫外光固化涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品光泽度120％-130％，表干时间20-60s，实干30-40min；2、水中浸泡40-60d后无起泡、脱落现象；3、在饱和氢氧化钙中浸泡20-30d不起泡、皱皮；4、产品耐95％乙醇浸棉球摩擦8-12h，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种陶瓷用紫外光固化涂料，其原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛1份；三羟甲基丙烷三丙烯酸酯20份；立德粉15份；水80份；滑石粉10份；中铬黄5份；轻质碳酸钙20份；丙烯酸乙酯5份；硫酸钡30份；苯乙烯3份；安息香乙醚1份；二甲基丙烷羧酸酯25份；二苯甲酮5份；三甲氧基硅烷35份。
将上述原料在反应釜中加热至70℃，混合12h后，涂覆于陶瓷上，用紫外线照射固化即可。
产品光泽度120％，表干时间60s，实干40min；水中浸泡40d后无起泡、脱落现象；在饱和氢氧化钙中浸泡20d不起泡、皱皮；产品耐95％乙醇浸棉球摩擦8h。
实施例2:
一种陶瓷用紫外光固化涂料，其原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛10份；三羟甲基丙烷三丙烯酸酯30份；立德粉25份；水100份；滑石粉20份；氧化铁红15份；轻质碳酸钙40份；丙烯酸乙酯25份；硫酸钡40份；苯乙烯5份；安息香乙醚10份；二甲基丙烷羧酸酯35份；二苯甲酮10份；三甲氧基硅烷45份。
将上述原料在反应釜中加热至70℃，混合16h后，涂覆于陶瓷上，用紫外线照射固化即可。
产品光泽度125％，表干时间40s，实干35min；水中浸泡50d后无起泡、脱落现象；在饱和氢氧化钙中浸泡25d不起泡、皱皮；产品耐95％乙醇浸棉球摩擦10h。
实施例3:
一种陶瓷用紫外光固化涂料，其原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛5份；三羟甲基丙烷三丙烯酸酯25份；立德粉20份；水90份；滑石粉15份；氧化铁红10份；轻质碳酸钙30份；丙烯酸乙酯15份；硫酸钡35份；苯乙烯4份；安息香乙醚5份；二甲基丙烷羧酸酯30份；二苯甲酮8份；三甲氧基硅烷40份。
将上述原料在反应釜中加热至70℃，混合14h后，涂覆于陶瓷上，用紫外线照射固化即可。
产品光泽度130％，表干时间20s，实干30min；水中浸泡60d后无起泡、脱落现象；在饱和氢氧化钙中浸泡30d不起泡、皱皮；产品耐95％乙醇浸棉球摩擦12h。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。

Claims (2)

1.一种陶瓷用紫外光固化涂料，其特征在于所述陶瓷用紫外光固化涂料的原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛1-10份；三羟甲基丙烷三丙烯酸酯20-30份；立德粉15-25份；水80-100份；滑石粉10-20份；着色颜料5-15份；轻质碳酸钙20-40份；丙烯酸乙酯5-25份；硫酸钡30-40份；交联剂3-5份；安息香乙醚1-10份；二甲基丙烷羧酸酯25-35份；二苯甲酮5-10份；三甲氧基硅烷35-45份；
所述着色颜料采用氧化铁红或中铬黄；
所述交联剂采用苯乙烯。
2.根据权利要求1所述的一种陶瓷用紫外光固化涂料，其特征在于所述陶瓷用紫外光固化涂料的原料按重量份数配比如下：聚氨酯丙烯酸酯100份；二氧化钛5份；三羟甲基丙烷三丙烯酸酯25份；立德粉20份；水90份；滑石粉15份；着色颜料10份；轻质碳酸钙30份；丙烯酸乙酯15份；硫酸钡35份；交联剂4份；安息香乙醚5份；二甲基丙烷羧酸酯30份；二苯甲酮8份；三甲氧基硅烷40份。
CN201410453433.2A 2014-09-09 2014-09-09 一种陶瓷用紫外光固化涂料 Active CN104178020B (zh)