CN104165818A - 采用溶胀度判断复合绝缘子老化程度的方法 - Google Patents
采用溶胀度判断复合绝缘子老化程度的方法 Download PDFInfo
- Publication number
- CN104165818A CN104165818A CN201410319855.0A CN201410319855A CN104165818A CN 104165818 A CN104165818 A CN 104165818A CN 201410319855 A CN201410319855 A CN 201410319855A CN 104165818 A CN104165818 A CN 104165818A
- Authority
- CN
- China
- Prior art keywords
- composite insulator
- swellbility
- aging
- degree
- umbrella skirt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种采用溶胀度判断复合绝缘子老化程度的方法，其技术特点包括以下步骤：采集复合绝缘子伞裙样品；将复合绝缘子伞裙样品浸泡在有机溶剂中，充分浸泡后进行质量测量；将测完质量的复合绝缘子伞裙样品充分干燥后再次进行质量测量；对复合绝缘子溶胀度进行计算：根据溶胀度对复合绝缘子老化程度进行判断。本发明设计合理，将复合绝缘子伞裙浸泡在有机溶剂中，根据复合绝缘子伞裙浸泡后的质量增加程度评估其中有机高分子含量的变化情况，进而判断复合绝缘子材料的老化程度，实现了对复合绝缘子老化程度的有效评估功能，保证了复合绝缘子的正常工作。
Description
技术领域
本发明属于复合绝缘子技术领域，尤其是一种采用溶胀度判断复合绝缘子老化程度的方法。
背景技术
复合绝缘子在电力系统中起到支撑导线和绝缘的作用，随着复合绝缘子运行时间的积累，在高电压电磁场和紫外线等环境因素的综合作用下，复合绝缘子伞裙会发生不同程度的老化。由于复合绝缘子伞裙材料为高温固化硅橡胶，其主要成分为有机硅氧高分子链和无机填料，随着复合绝缘子的不断老化，伞裙材料中的硅氧高分子链断裂，有机高分子含量逐渐减少，伴随着复合绝缘子的机械性能和电气性能逐渐下降，当老化严重到不能承受高电压时，复合绝缘子便发生闪络击穿，造成大范围的停电事故。因此，如何对复合绝缘子老化程度进行评估以保证复合证绝缘子的可靠工作是迫切需要解决的问题。
发明内容
本发明的目的在于克服现有技术的不足，提供一种采用溶胀度判断复合绝缘子老化程度的方法，解决复合绝缘子老化程度的判断问题。
本发明解决其技术问题是采取以下技术方案实现的：
一种采用溶胀度判断复合绝缘子老化程度的方法，包括以下步骤：
步骤1、采集复合绝缘子伞裙样品；
步骤2、将复合绝缘子伞裙样品浸泡在有机溶剂中，充分浸泡后进行质量测量；
步骤3、将测完质量的复合绝缘子伞裙样品充分干燥后再次进行质量测量；
步骤4、按照以下公式对复合绝缘子溶胀度进行计算：溶胀度＝充分溶胀后的质量/原始质量
步骤5、根据溶胀度对复合绝缘子老化程度进行判断。
而且，所述复合绝缘子伞裙样品包含有伞裙上表面、下表面和边沿。
而且，所述的有机溶剂为120号汽油。
而且，步骤2所述侵泡的时间为24小时。
而且，步骤3所述充分干燥的方法采用将样品置于空气中晾晒24小时来实现。
而且，所述步骤5的判断方法为：
(1)当溶胀度大于等于165％时，复合绝缘子运行良好；
(2)当溶胀度大于等于155％且小于165％时，复合绝缘子轻度老化；
(3)当溶胀度小于155％时，复合绝缘子严重老化。
本发明的优点和积极效果是：
1、本发明根据相似相容的原理，将复合绝缘子伞裙浸泡在有机溶剂中，根据复合绝缘子伞裙浸泡后的质量增加程度评估其中有机高分子含量的变化情况，进而判断复合绝缘子材料的老化程度，实现了对复合绝缘子老化程度的有效评估功能。
2、本发明根据试验结果提出了复合绝缘子处于不同老化阶段时溶胀度的特征阈值，在复合绝缘子满足运行要求的前提下，对其运行寿命进一步做出分析评价，给出其运行寿命的指导意见，为输电线路状态检修提供决策依据。
附图说明
图1是本发明的处理流程图。
具体实施方式
以下结合附图对本发明做进一步详述：
一种采用溶胀度判断复合绝缘子老化程度的方法，如图1所示，包括以下步骤：
步骤1、采集复合绝缘子伞裙样品。
在采集复合绝缘子伞裙样品时，对复合绝缘子伞裙进行切块，所有样品均从伞裙边沿开始切割，保证所有样品均包含有伞裙上表面、下表面和边沿。
步骤2、将复合绝缘子伞裙样品浸泡在有机溶剂中，浸泡24小时后进行质量测量。
在本实施例，有机溶剂采用120号汽油，将样品浸泡在120好汽油中，对复合绝缘子伞裙样品进行溶胀性分析。
步骤3、将测完质量的复合绝缘子伞裙样品置于空气中晾干，24小时后再次进行质量测量。
步骤4、按照以下公式对复合绝缘子溶胀度进行计算：
溶胀度＝充分溶胀后的质量/原始质量
步骤5、根据溶胀度对复合绝缘子伞裙样品老化程度进行判断。
通过大量试验，将不同老化程度复合绝缘子的溶胀度值与其材料硬度、表面绝缘电阻、耐漏电起痕性能等进行相关性分析，分析结果表明运用溶胀度可以有效表征复合绝缘子的不同老化程度。具体判断方法为：
(1)当溶胀度大于等于165％时，复合绝缘子运行良好。
(2)当溶胀度大于等于155％且小于165％时，复合绝缘子轻度老化。
(3)当溶胀度小于155％时，复合绝缘子严重老化。
本发明的工作原理为：由于有机高分子材料在有机溶剂中浸泡时会发生溶胀现象，体积、质量均会上升，高温硫化硅橡胶也不例外。当硅橡胶发生老化、体系交联度上升以后，伞裙材料中的硅氧高分子链断裂，有机高分子含量逐渐减少，分子间隙减小，宏观表现为硅橡胶材料在有机溶液中的溶胀度降低。本发明便是根据复合绝缘子伞裙浸泡后的质量增加程度评估其中有机高分子含量的变化情况，进而判断复合绝缘子材料的老化程度。
需要强调的是，本发明所述的实施例是说明性的，而不是限定性的，因此本发明包括并不限于具体实施方式中所述的实施例，凡是由本领域技术人员根据本发明的技术方案得出的其他实施方式，同样属于本发明保护的范围。
Claims (6)
1.一种采用溶胀度判断复合绝缘子老化程度的方法，其特征在于包括以下步骤：
步骤1、采集复合绝缘子伞裙样品；
步骤2、将复合绝缘子伞裙样品浸泡在有机溶剂中，充分浸泡后进行质量测量；
步骤3、将测完质量的复合绝缘子伞裙样品充分干燥后再次进行质量测量；
步骤4、按照以下公式对复合绝缘子溶胀度进行计算：溶胀度＝充分溶胀后的质量/原始质量
步骤5、根据溶胀度对复合绝缘子老化程度进行判断。
2.根据权利要求1所述的采用溶胀度判断复合绝缘子老化程度的方法，其特征在于：所述复合绝缘子伞裙样品包含有伞裙上表面、下表面和边沿。
3.根据权利要求1所述的采用溶胀度判断复合绝缘子老化程度的方法，其特征在于：所述的有机溶剂为120号汽油。
4.根据权利要求1所述的采用溶胀度判断复合绝缘子老化程度的方法，其特征在于：步骤2所述侵泡的时间为24小时。
5.根据权利要求1所述的采用溶胀度判断复合绝缘子老化程度的方法，其特征在于：步骤3所述充分干燥的方法采用将样品置于空气中晾晒24小时来实现。
6.根据权利要求1所述的采用溶胀度判断复合绝缘子老化程度的方法，其特征在于：所述步骤5的判断方法为：
(1)当溶胀度大于等于165％时，复合绝缘子运行良好；
(2)当溶胀度大于等于155％且小于165％时，复合绝缘子轻度老化；
(3)当溶胀度小于155％时，复合绝缘子严重老化。