CN104152834B - A kind of manufacture method of surface high connductivity heat zinc coating plate - Google Patents
A kind of manufacture method of surface high connductivity heat zinc coating plate Download PDFInfo
- Publication number
- CN104152834B CN104152834B CN201410392823.3A CN201410392823A CN104152834B CN 104152834 B CN104152834 B CN 104152834B CN 201410392823 A CN201410392823 A CN 201410392823A CN 104152834 B CN104152834 B CN 104152834B
- Authority
- CN
- China
- Prior art keywords
- coating plate
- zinc coating
- heat zinc
- manufacture method
- high connductivity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the manufacture method of a kind of surface high connductivity heat zinc coating plate, including following operation: surface cleaning by degreasing annealing furnace continuous annealing enters zinc pot galvanizing by dipping finishing straightening surface coated treatment;Wherein, in finishing straightening operation, polishing machine working roll is operated under capacitive and carries out hacking, and working roll roll surface roughness controls in 2.0~2.5 μm;The manufacture method of this surface high connductivity heat zinc coating plate, processes the steel band after zinc-plated, improves galvanized sheet process of surface treatment, to obtain extremely low sheet resistance, high guidance quality, the heat zinc coating plate that the rate that is not turned on is extremely low;It is able to ensure that data warehouse data safety, meets the needs of customers.
Description
Technical field
The present invention relates to heat zinc coating plate and manufacture field, be specifically related to the manufacture of a kind of surface high connductivity heat zinc coating plate
Method.
Background technology
Surface high conductivity heat zinc coating plate is generally used for the data warehouse device fabrication that " big data " store, logarithm
According to safety extremely important.The various coating galvanizing productions produced at present, through 16 points/face, two-sided 32 points
Detection, surface conductivity can not all meet requirement.On the one hand globality conduction in surface is bad, sheet resistance
Higher, it is high that surface is not turned on rate, it is impossible to meets user's requirement;On the other hand globality electric conductivity in surface reaches
User requires but close to higher limit, excess room is less, and local surfaces film weight inequality is possible to surmount the upper limit,
User's requirement can not be met.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of sheet resistance is extremely low, has pole
Good surface electric conductivity, can meet the manufacture method of the surface high connductivity heat zinc coating plate of user's request.
To achieve these goals, the technical solution used in the present invention is:
The manufacture method of this surface high connductivity heat zinc coating plate, including following operation: surface cleaning by degreasing---annealing
Stove continuous annealing-------finishing straightening----surface coated treatment that enters zinc pot galvanizing by dipping;Wherein, finishing straightening work
In sequence, polishing machine working roll is operated under capacitive, and working roll roll surface roughness controls in 2.0~2.5 μm.
Surface coated treatment operation, the film of galvanized sheet face coat heavily controls at 1.1g/m2, galvanized sheet surface is coated with
Layer two-sided film weight deviation is ± 0.1g/m2。
Two-sided 6 films weight deviations of galvanized sheet face coat are ± 0.1g/m2。
Two-sided 6 the middle edge of galvanized sheet face coat 2 are 2.5cm from galvanized sheet edge distance, two-sided 6 points
Spacing is equal.
In finishing straightening operation, the finishing liquid lubrication polishing machine using mass percent to be 2.0%-2.5%.
The sheet resistance value of electric heating galvanized sheet is less than 0.2M Ω, and surface is not turned on rate less than 3%.
It is an advantage of the current invention that: the manufacture method of this surface high connductivity heat zinc coating plate, in finishing straightening operation,
By controlling the surface roughness of polishing machine working roll, to control surface roughness and the peak value of heat zinc coating plate,
Improving heat zinc coating plate surface quality, the heat zinc coating plate of production has extremely low resistance, surface has high conductivity,
Disclosure satisfy that user's request.
Further, the manufacture method of this surface high connductivity heat zinc coating plate, surface coated treatment operation, pass through
The film of galvanized sheet face coat is heavily controlled, accurately to control the uniformity of galvanized sheet face coat, with
Reduce heat zinc coating plate sheet resistance, improve heat zinc coating plate surface conductivity;The heat zinc coating plate produced has extremely low
Resistance, surface have high conductivity, it is possible to meet user's request.
Further, two-sided 6 detection modes are used to control double-side membrane weight deviation, with to galvanized sheet face coat
Film be heavily controlled, accurately to control the uniformity of galvanized sheet face coat, to reduce heat zinc coating plate surface
Resistance, improves heat zinc coating plate surface conductivity.
The manufacture method of this surface high connductivity heat zinc coating plate, processes the steel band after zinc-plated, improves zinc-plated
Plate process of surface treatment, to obtain extremely low sheet resistance, high guidance quality, the heat zinc coating plate that the rate that is not turned on is extremely low;
The mass data depot equipment that can be used in " big data " epoch needs manufactures, it is ensured that data warehouse data is pacified
Entirely, meet the needs of customers;And be capable of the yield of 1000 tons/month, and before there is wide market
Scape
Detailed description of the invention
Below against by the description to optimum embodiment, the detailed description of the invention of the present invention is made the most in detail
Thin explanation.
The manufacture method of this surface high connductivity heat zinc coating plate, including following operation: surface cleaning by degreasing---annealing
Stove continuous annealing-------finishing straightening----surface coated treatment that enters zinc pot galvanizing by dipping;Wherein, finishing is drawn
Rectifying in operation, polishing machine working roll is operated under capacitive and carries out hacking, and working roll roll surface roughness controls
In 2.0-2.5 μm, heat zinc coating plate surface roughness is 2.0-2.5 μm.The surface of surface high conductivity heat zinc coating plate
Roughness and peak value thereof control to be one of this production difficult point, in conjunction with finishing prebasal plate surface roughness, light
Complete machine working roll capacitive hacking, controls roller footpath Φ 450mm working roll roll surface roughness in 2.0-2.5 μm
Scope, it is achieved heat zinc coating plate surface low roughness, peak value texturing.Another use mass percent is 2.0%-2.5%
Finishing liquid lubrication polishing machine, strip steel, by the polishing machine through lubrication, can ensure that plate shape is smooth and surface cleaning,
It is further ensured that the finishing effect realizing galvanizing product low roughness, peak value.
The manufacture method of this surface high connductivity heat zinc coating plate, by controlling, to plating surface roughness and peak value
Zinc product surface quality is controlled, and the heat zinc coating plate of production has extremely low resistance, surface has high conductivity.
Meanwhile, surface coated treatment operation, the film of galvanized sheet face coat heavily controls at 1.1g/m2, galvanized sheet
Face coat double interfacial film weight deviation is ± 0.1g/m2.Zinc-plated rear galvanized sheet surface carries out processing roller coating technology, table
The film weight of finishing coat and the control of uniformity are the two of this production difficult points, comprehensive strip steel surface roughness,
Application roll surface roughness, speed and pressure match between feeding roller and application roll, between application roll and strip steel
The influence factor such as pressure, control coated film and focus on 1.1g/m2, galvanized sheet face coat double interfacial film weight deviation
For ± 0.1g/m2, two-sided 6 are detected and control film weight deviation at ± 0.1g/m2, it is ensured that whole plate facial film weight average
Even;Realizing the control effect that film coincidence is fitted, had good uniformity, belt steel surface has excellent electric conductivity,
Surface is not turned on rate less than 3%.
The manufacture method of this surface high connductivity heat zinc coating plate, by heavily controlling the film of galvanized sheet face coat
System, accurately to control the uniformity of galvanized sheet face coat, to reduce heat zinc coating plate sheet resistance, improves heat
Galvanized sheet surface conductivity.
Further, two-sided 6 the middle edge of galvanized sheet face coat 2 from galvanized sheet edge distance are
2.5cm, two-sided six dot spacings are from equal.Six point selection on two-sided: in 6,2 is edge two point, and
Other 4 are equally spaced.The selection of 6 middle edge 2 is the most crucial, owing to edge is in working roll roll-in
Under effect, edge coating uniformity is difficult to control;Steel band width is generally 1.3-1.5 rice, select edge 2 from
Galvanized sheet edge distance is 2.5cm, and edge is consistent with centre position coating uniformity, can be to whole galvanized sheet
Face coat uniformity is controlled, and to reduce heat zinc coating plate sheet resistance, improves heat zinc coating plate surface conductance
Property.
The sheet resistance value of the electric heating galvanized sheet that the manufacture method of this surface high connductivity heat zinc coating plate manufactures is less than 0.2
M Ω, surface is not turned on rate less than 3%.
Specific embodiment: surface conductivity is affected by surface roughness peak value RPc (/cm), table in this embodiment
It is to use general detection equipment, the detection of 32, two sides positive and negative to galvanized sheet that surface resistance and surface are not turned on rate
Obtain.Base plate surface roughness and peak value are mainly controlled by embodiment and face coat film is heavy, uniformly
Property control two aspects and implement.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 75, coated film weight 1.1g/m2, surface
Resistance 0.052m Ω, the rate of being not turned on is 0%.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 90, coated film weight 1.1g/m2, surface electricity
Resistance 0.040m Ω, the rate of being not turned on is 0%.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 115, coated film weight 1.1g/m2, surface
Resistance 0.024m Ω, the rate of being not turned on is 0%.
Embodiment 2: surface conductivity is affected by coated film weight and uniformity.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 90, coated film weight 1.1g/m2, surface
Resistance 0.040m Ω, the rate of being not turned on is 0%.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 90, coated film weight 1.3g/m2, surface electricity
Resistance 0.052m Ω, the rate of being not turned on is 50%.
Base plate surface roughness Ra:1.0 μm, peak value RPc (/cm): 90, coated film weight 1.45g/m2, surface
Resistance 0.058m Ω, the rate of being not turned on is 80%.
Verifying through above example, galvanized sheet surface roughness controls at 2.0~2.5 μm, the film of face coat
Heavily control at 1.1g/m2Time, the sheet resistance value of the electric heating galvanized sheet of the manufacture method manufacture of heat zinc coating plate is less than
0.2M Ω, it is 0 that surface is not turned on rate.
Obviously the present invention implements and is not subject to the restrictions described above, as long as have employed the method structure of the present invention
Think the improvement of the various unsubstantialities carried out with technical scheme, all within protection scope of the present invention.
Claims (4)
1. a manufacture method for surface high connductivity heat zinc coating plate, including following operation: surface cleaning by degreasing---
Annealing furnace continuous annealing-------finishing straightening----surface coated treatment that enters zinc pot galvanizing by dipping;It is characterized in that:
Wherein, in finishing straightening operation, polishing machine working roll is operated under capacitive, working roll roll surface roughness
Control in 2.0~2.5 μm;Surface coated treatment operation, the film of galvanized sheet face coat heavily controls at 1.1g/m2,
Galvanized sheet face coat two-sided film weight deviation be ± 0.1g/m2;Two-sided 6 films weight of galvanized sheet face coat is partially
Difference is ± 0.1g/m2。
2. the manufacture method of surface as claimed in claim 1 high connductivity heat zinc coating plate, it is characterised in that: plating
Two-sided 6 the middle edge of zine plate face coat 2 are 2.5cm from galvanized sheet edge distance, two-sided six dot spacings from
Equal.
3. the manufacture method of surface as claimed in claim 1 high connductivity heat zinc coating plate, it is characterised in that: light
In whole straightening operation, the finishing liquid lubrication polishing machine using mass percent to be 2.0%-2.5%.
4. the manufacture method of the surface high connductivity heat zinc coating plate as described in claim 1 or 2 or 3, its feature
Being: the sheet resistance value of heat zinc coating plate is less than 0.2M Ω, surface is not turned on rate less than 3%.