CN104152753A - 一种led用含改性树木灰的铝基复合散热材料 - Google Patents

一种led用含改性树木灰的铝基复合散热材料 Download PDF

Info

Publication number
CN104152753A
CN104152753A CN201410321991.3A CN201410321991A CN104152753A CN 104152753 A CN104152753 A CN 104152753A CN 201410321991 A CN201410321991 A CN 201410321991A CN 104152753 A CN104152753 A CN 104152753A
Authority
CN
China
Prior art keywords
parts
aluminium
heat dissipation
led
dissipation material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410321991.3A
Other languages
English (en)
Other versions
CN104152753B (zh
Inventor
刘孝峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Nantong haizhisheng e-commerce Co., Ltd
Original Assignee
BENGBU YINGLU PHOTOELECTRIC CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU YINGLU PHOTOELECTRIC CO LTD filed Critical BENGBU YINGLU PHOTOELECTRIC CO LTD
Priority to CN201410321991.3A priority Critical patent/CN104152753B/zh
Publication of CN104152753A publication Critical patent/CN104152753A/zh
Application granted granted Critical
Publication of CN104152753B publication Critical patent/CN104152753B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及灯具散热材料，具体涉及一种LED用含改性树木灰的铝基复合散热材料及其生产方法，该散热材料由以下重量份的原料制成：铝88-90、氮化铝13-15、漂珠5-6、蓝晶石2-4、莫来石3-5、酒石酸1-3、导热碳纤维10-12、硅酸钠9-10、淀粉4-6、树木灰15-18、矿渣8-10、钨酸铵1-3、助剂4-5；本发明的散热材料综合了铝、氮化铝、导热碳纤维、树木灰等成分的优点，兼具良好的导热和绝缘性能，并将树木灰经酒石酸和钨酸铵的混合溶液浸泡改性，再结合硅酸钠、助剂等原料的使用，使得该材料易于成型，烧结效果良好，材料表面光洁致密，轻质坚韧，耐热稳定，且生产成本得到控制，其良好的散热能力能够快速的降低LED灯具温度，有效的延长了使用寿命。

Description

一种LED用含改性树木灰的铝基复合散热材料
技术领域
本发明涉及灯具散热材料，具体涉及一种LED用含改性树木灰的铝基复合散热材料及其生产方法。
背景技术
LED被称为第四代光源，具有节能、环保、安全、低能耗、高亮度等优点，在日常生活中被广泛使用，LED灯体本身的散热性能至关重要，直接影响到灯具的使用寿命和照明效果。现有的LED散热材料主要是由铝、铜等金属材料制成，在实际使用中存在成本限制、绝缘性能不够等缺点，因此很有必要改进材料的配方，使材料达到更为良好的散热效果，改善灯具的使用性能，延长使用寿命。
发明内容
本发明的目的在于，提供一种LED用含改性树木灰的铝基复合散热材料，以改善材料的使用性能，提高灯具的使用寿命，为了实现上述目的，本发明采用的技术方案如下：
一种LED用含改性树木灰的铝基复合散热材料，其特征在于，本发明材料由以下重量份的原料制成：铝88-90、氮化铝13-15、漂珠5-6、蓝晶石2-4、莫来石3-5、酒石酸1-3、导热碳纤维10-12、硅酸钠9-10、淀粉4-6、树木灰15-18、矿渣8-10、钨酸铵1-3、助剂4-5。
所述的助剂由以下重量份的原料制成：桐油6-8、苯基硅油1-2、氧化锌纳米线4-5、硝酸银1-2、碳纳米管6-8、微细二氧化硅气凝胶8-10，制备方法为：先将硝酸银溶于适量的水中，配制成浓度为6-8%的水溶液，并将氧化锌纳米线、碳纳米管、微细二氧化硅气凝胶投入溶液中，搅拌分散均匀后静置5-8h后干燥，所得的物料再与其它剩余成分混合，搅拌分散2-3h后浓缩干燥，研磨成400-500目细粉，即得。
所述的一种LED用含改性树木灰的铝基复合散热材料，其制作工艺包含以下步骤：
（1）先将酒石酸、钨酸铵溶于10倍于其总重量份的水中，并将树木灰投入溶液中浸泡10-12h后水洗至中性，并低温烘干，所得物料备用；
（2）将步骤（1）所得物料与其它剩余成分一起混合搅拌1-2h后，投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（3）将步骤（2）所得的物料送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结4-6h后，经自然冷却至室温即得。
本发明的优点在于：较传统铝质散热材料在原料上综合了铝、氮化铝、漂珠、导热碳纤维、硅酸钠、树木灰等成分的优点，兼具良好的导热和绝缘性能，并将树木灰经酒石酸和钨酸铵的混合溶液浸泡改性，增进其与其它金属粉末间的相容性，再结合硅酸钠、助剂等原料的使用，使得本发明制备的散热材料易于成型，烧结效果良好，材料表面光洁致密，轻质坚韧，耐热稳定，且生产成本得到控制，其良好的散热能力能够快速的降低LED灯具温度，从而有效的延长了使用寿命。
具体实施方式
实施例
本实施例LED散热材料由以下重量份原料制成：铝88、氮化铝15、漂珠6、蓝晶石2、莫来石5、酒石酸3、导热碳纤维12、硅酸钠10、淀粉6、树木灰18、矿渣10、钨酸铵3、助剂5。
所述的助剂由以下重量份的原料制成：桐油6、苯基硅油2、氧化锌纳米线5、硝酸银2、碳纳米管8、微细二氧化硅气凝胶10，制备方法为：先将硝酸银溶于适量的水中，配制成浓度为7.0%的水溶液，并将氧化锌纳米线、碳纳米管、微细二氧化硅气凝胶投入溶液中，搅拌分散均匀后静置8h后干燥，所得的物料再与其它剩余成分混合，搅拌分散3h后浓缩干燥，研磨成500目细粉，即得。
所述的一种LED用含改性树木灰的铝基复合散热材料，其制作工艺包含以下步骤：
（1）先将酒石酸、钨酸铵溶于10倍于其总重量份的水中，并将树木灰投入溶液中浸泡12h后水洗至中性，并低温烘干，所得物料备用；
（2）将步骤（1）所得物料与其它剩余成分一起混合搅拌2h后，投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（3）将步骤（2）所得的物料送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结6h后，经自然冷却至室温即得。
本实施例所制得的散热材料较常规LED用散热材料较常规铝基散热材料的导热系数提高23.4%，热扩散率提高26.2%，热平衡时间平均缩短145min，灯具使用寿命提高27.5%。

Claims (2)

1.一种LED用含改性树木灰的铝基复合散热材料，其特征在于，该散热由以下重量份的原料制成：铝88-90、氮化铝13-15、漂珠5-6、蓝晶石2-4、莫来石3-5、酒石酸1-3、导热碳纤维10-12、硅酸钠9-10、淀粉4-6、树木灰15-18、矿渣8-10、钨酸铵1-3、助剂4-5；
所述的助剂由以下重量份的原料制成：桐油6-8、苯基硅油1-2、氧化锌纳米线4-5、硝酸银1-2、碳纳米管6-8、微细二氧化硅气凝胶8-10，制备方法为：先将硝酸银溶于适量的水中，配制成浓度为6-8%的水溶液，并将氧化锌纳米线、碳纳米管、微细二氧化硅气凝胶投入溶液中，搅拌分散均匀后静置5-8h后干燥，所得的物料再与其它剩余成分混合，搅拌分散2-3h后浓缩干燥，研磨成400-500目细粉，即得。
2.如权利要求1所述的一种LED用含改性树木灰的铝基复合散热材料，其生产方法如下：
（1）先将酒石酸、钨酸铵溶于10倍于其总重量份的水中，并将树木灰投入溶液中浸泡10-12h后水洗至中性，并低温烘干，所得物料备用；
（2）将步骤（1）所得物料与其它剩余成分一起混合搅拌1-2h后，投入球磨机中球磨处理，使所得物料的万孔筛余量≤0.05%；
（3）将步骤（2）所得的物料送入模具中压制成型，在氮气氛围下以650-700℃的温度烧结4-6h后，经自然冷却至室温即得。
CN201410321991.3A 2014-07-08 2014-07-08 一种led用含改性树木灰的铝基复合散热材料 Active CN104152753B (zh)