CN104152003A - 一种陶瓷用环氧树脂粉末涂料 - Google Patents
一种陶瓷用环氧树脂粉末涂料 Download PDFInfo
- Publication number
- CN104152003A CN104152003A CN201410431518.0A CN201410431518A CN104152003A CN 104152003 A CN104152003 A CN 104152003A CN 201410431518 A CN201410431518 A CN 201410431518A CN 104152003 A CN104152003 A CN 104152003A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder coating
- epoxy powder
- acid
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种陶瓷用环氧树脂粉末涂料,原料为:双酚A环氧树脂、松香脂肪酸、聚乙烯醇缩丁醛、苯甲酸、十六烷二油酸二缩水甘油酯、新戊二醇、紫外线吸收剂、间苯二甲酸、二氰基二酰胺、季戊四醇、增塑剂、4,4`-二(苯基异丙基)二苯胺、2-甲基咪唑、聚硅氧烷和己二酸二甲酯;产品光泽度110%-130%,铅笔硬度H-2H;拉伸强度30-50MPa,伸长率200-400%,干燥时间15-20min;附着力1-2级,冲击强度400-500N/cm,水中浸泡40-60d后无起泡、脱落现象,在饱和氢氧化钙中浸泡30-40d不起泡、皱皮,在5%盐酸溶液中浸泡25-35d无异常。
Description
技术领域
本申请属于涂料领域,尤其涉及一种陶瓷用环氧树脂粉末涂料。
背景技术
涂料通常是以树脂或油为主,并加或不加颜、填料,用有机溶剂或水调制而成的粘稠液体,也出现了以固体形态存在的涂料新品种如粉末涂料。各类涂料不论涂料品种的形态(液体或固体)如何,至少应由两种或三种基本成分组成。即分为主要成膜物质;次要成膜物质和辅助成膜物质。涂料能涂敷于底材表面并形成坚韧连续涂膜(漆膜)的液体或固体高分子材料。旧称油漆、漆。主要用来对被涂表面起到装饰与保护作用。有些涂料还具有特定的功能,如耐高温、耐寒、防辐射等。涂料广泛应用于建筑、船舶、车辆、金属制品等方面。新中国成立60年来,伴随着国民经济各行业的发展,作为其配套的涂料工业从一个极不引人注目的小行业逐步发展成为国民经济各领域必不可少的重要行业。经过几代人的顽强拼搏、开拓进取,我国已成为世界第二大涂料生产国和消费国,进入到世界涂料行业发展的主流。
陶瓷工业在我国发展较快,销售市场逐渐转旺。我国是一个陶瓷生产大国,对陶瓷的需求量也越来越大。从国内市场情况看,近年形势喜人,名特优新陶瓷产品供不应求,高档陶瓷和中高档卫生陶瓷十分抢手,质量好的传统产品继续畅销,滞销的只是质量差的产品。迄今为止,陶瓷的界定似可概括地作如下描述:陶瓷是用铝硅酸盐矿物或某些氧化物等为主要原料,依照人的意图通过特定的物理化学工艺在高温下以一定的温度和气氛制成的具有一定型式的工艺岩石。表面可施釉或不施釉,若干瓷质还具有不同程度的半透明度,通体是由一种或多种晶体或与无定形胶结物及气孔或与熟料包裹体等微观结构组成。
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。环氧树脂是泛指分子中含有两个或两个以上环氧基团的有机化合物,除个别外,它们的相对分子质量都不高。环氧树脂的分子结构是以分子链中含有活泼的环氧基团为其特征,环氧基团可以位于分子链的末端、中间或成环状结构。由于分子结构中含有活泼的环氧基团,使它们可与多种类型的固化剂发生交联反应而形成不溶、不熔的具有三向网状结构的高聚物。而随着人性化理念的普及,及新型和谐社会的构成,设计一种附着力好、硬度高、拉伸强度和收缩率高的陶瓷用环氧树脂粉末涂料是非常必要的。
发明内容
解决的技术问题:
本申请针对上述技术问题,提供一种陶瓷用环氧树脂粉末涂料,解决现有陶瓷用环氧树脂粉末涂料附着力差,硬度、拉伸强度和伸长率低等技术问题。
技术方案:
一种陶瓷用环氧树脂粉末涂料,所述陶瓷用环氧树脂粉末涂料的原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸30-50份;聚乙烯醇缩丁醛3.5-5.5份;苯甲酸6-10份;十六烷二油酸二缩水甘油酯40-60份;新戊二醇3-5份;紫外线吸收剂5-15份;间苯二甲酸10-20份;二氰基二酰胺4-8份;季戊四醇20-30份;增塑剂1-10份;4,4`-二(苯基异丙基)二苯胺0.2-0.6份;2-甲基咪唑0.2-0.8份;聚硅氧烷0.4-0.8份;己二酸二甲酯35-45份。
作为本发明的一种优选技术方案:所述陶瓷用环氧树脂粉末涂料的原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸40份;聚乙烯醇缩丁醛4.5份;苯甲酸8份;十六烷二油酸二缩水甘油酯50份;新戊二醇4份;紫外线吸收剂10份;间苯二甲酸15份;二氰基二酰胺6份;季戊四醇25份;增塑剂5份;4,4`-二(苯基异丙基)二苯胺0.4份;2-甲基咪唑0.5份;聚硅氧烷0.6份;己二酸二甲酯40份。
作为本发明的一种优选技术方案:所述紫外线吸收剂采用紫外线吸收剂UV-531或紫外线吸收剂UV-326。
作为本发明的一种优选技术方案:所述增塑剂采用DOP或DBP。
有益效果:
本发明所述一种陶瓷用环氧树脂粉末涂料采用以上技术方案与现有技术相比,具有以下技术效果:1、产品光泽度110%-130%,铅笔硬度H-2H,水中浸泡40-60d后无起泡、脱落现象;2、拉伸强度30-50MPa,伸长率200-400%,干燥时间15-20min;3、附着力1-2级,冲击强度400-500N/cm,在饱和氢氧化钙中浸泡30-40d不起泡、皱皮;4、在5%盐酸溶液中浸泡25-35d无异常,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种陶瓷用环氧树脂粉末涂料,其原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸30份;聚乙烯醇缩丁醛3.5份;苯甲酸6份;十六烷二油酸二缩水甘油酯40份;新戊二醇3份;紫外线吸收剂UV-326为5份;间苯二甲酸10份;二氰基二酰胺4份;季戊四醇20份;DOP1份;4,4`-二(苯基异丙基)二苯胺0.2份;2-甲基咪唑0.2份;聚硅氧烷0.4份;己二酸二甲酯35份。
将上述原料加入反应釜中,升温到110℃,保温反应4h混合均匀,冷却后用粉碎机粉碎,用180mg筛过筛,制得涂料。
产品光泽度110%,铅笔硬度H;拉伸强度30MPa,伸长率200%,干燥时间20min;附着力2级,冲击强度400N/cm,水中浸泡40d后无起泡、脱落现象,在饱和氢氧化钙中浸泡30d不起泡、皱皮,在5%盐酸溶液中浸泡25d无异常。
实施例2:
一种陶瓷用环氧树脂粉末涂料,其原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸50份;聚乙烯醇缩丁醛5.5份;苯甲酸10份;十六烷二油酸二缩水甘油酯60份;新戊二醇5份;紫外线吸收剂UV-531为15份;间苯二甲酸20份;二氰基二酰胺8份;季戊四醇30份;DBP10份;4,4`-二(苯基异丙基)二苯胺0.6份;2-甲基咪唑0.8份;聚硅氧烷0.8份;己二酸二甲酯45份。
将上述原料加入反应釜中,升温到130℃,保温反应6h混合均匀,冷却后用粉碎机粉碎,用200mg筛过筛,制得涂料。
产品光泽度120%,铅笔硬度2H;拉伸强度40MPa,伸长率300%,干燥时间18min;附着力1级,冲击强度450N/cm,水中浸泡50d后无起泡、脱落现象,在饱和氢氧化钙中浸泡35d不起泡、皱皮,在5%盐酸溶液中浸泡30d无异常。
实施例3:
一种陶瓷用环氧树脂粉末涂料,其原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸40份;聚乙烯醇缩丁醛4.5份;苯甲酸8份;十六烷二油酸二缩水甘油酯50份;新戊二醇4份;紫外线吸收剂UV-531为10份;间苯二甲酸15份;二氰基二酰胺6份;季戊四醇25份;DOP5份;4,4`-二(苯基异丙基)二苯胺0.4份;2-甲基咪唑0.5份;聚硅氧烷0.6份;己二酸二甲酯40份。
将上述原料加入反应釜中,升温到120℃,保温反应5h混合均匀,冷却后用粉碎机粉碎,用190mg筛过筛,制得涂料。
产品光泽度130%,铅笔硬度2H;拉伸强度50MPa,伸长率400%,干燥时间15min;附着力1级,冲击强度500N/cm,水中浸泡60d后无起泡、脱落现象,在饱和氢氧化钙中浸泡40d不起泡、皱皮,在5%盐酸溶液中浸泡35d无异常。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种陶瓷用环氧树脂粉末涂料,其特征在于所述陶瓷用环氧树脂粉末涂料的原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸30-50份;聚乙烯醇缩丁醛3.5-5.5份;苯甲酸6-10份;十六烷二油酸二缩水甘油酯40-60份;新戊二醇3-5份;紫外线吸收剂5-15份;间苯二甲酸10-20份;二氰基二酰胺4-8份;季戊四醇20-30份;增塑剂1-10份;4,4`-二(苯基异丙基)二苯胺0.2-0.6份;2-甲基咪唑0.2-0.8份;聚硅氧烷0.4-0.8份;己二酸二甲酯35-45份。
2.根据权利要求1所述的一种陶瓷用环氧树脂粉末涂料,其特征在于所述陶瓷用环氧树脂粉末涂料的原料按重量份数配比如下:双酚A环氧树脂100份;松香脂肪酸40份;聚乙烯醇缩丁醛4.5份;苯甲酸8份;十六烷二油酸二缩水甘油酯50份;新戊二醇4份;紫外线吸收剂10份;间苯二甲酸15份;二氰基二酰胺6份;季戊四醇25份;增塑剂5份;4,4`-二(苯基异丙基)二苯胺0.4份;2-甲基咪唑0.5份;聚硅氧烷0.6份;己二酸二甲酯40份。
3.根据权利要求1所述的一种陶瓷用环氧树脂粉末涂料,其特征在于:所述紫外线吸收剂采用紫外线吸收剂UV-531或紫外线吸收剂UV-326。
4.根据权利要求1所述的一种陶瓷用环氧树脂粉末涂料,其特征在于:所述增塑剂采用DOP或DBP。