CN104148828B - Stainless steel welding stick processing technology - Google Patents
Stainless steel welding stick processing technology Download PDFInfo
- Publication number
- CN104148828B CN104148828B CN201410229023.XA CN201410229023A CN104148828B CN 104148828 B CN104148828 B CN 104148828B CN 201410229023 A CN201410229023 A CN 201410229023A CN 104148828 B CN104148828 B CN 104148828B
- Authority
- CN
- China
- Prior art keywords
- wind
- water
- finished product
- wire
- cut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of stainless steel welding stick processing technology, comprise following processing step: annealing, wire drawing, Ultrasonic Cleaning, the first wind are cut, hot water rinsing, the second wind are cut, oiling, the 3rd wind, take-up packaging, improve the cleannes of welding wire surface by original running water rinsing being changed into Ultrasonic Cleaning, apply lubricating oil by oiling technique at welding wire surface in addition and can prevent that plug wire phenomenon from use appearring in welding wire.
Description
Technical field
The present invention relates to a kind of stainless steel welding stick processing technology.
Background technology
Stainless steel welding stick, is widely used, and the control point of most critical is in process of production: the composition of mother metal, and finished productThe cleannes on surface, selected cannot adjustment of the composition of mother metal in the cold-drawing technology of Shen Xian factory, in surface cleanness controlSpecial aobvious important, require the clean free from admixture of bonding wire surface requirements pollution-free, with avoided impurity enter welding bead affect finished product character orBe to cause surface abnormalities, in stainless steel welding stick production engineering, the use of powdered lubricant lubricating oil must need, at present stainless steelThe cleaning of welding wire only carrys out rinsing by running water, therefore cannot remove the finely ground particles and the oil that remain in product surfaceDirt, causes product cleannes lower, and welding wire surface all do not pass through oiling processing, causes client in use to cause plug wireThe generation of phenomenon.
Summary of the invention
The object of the invention is to overcome the defect existing in prior art, a kind of stainless steel welding stick processing technology be provided,The cleannes that improve welding wire surface prevent that it from plug wire in use occurring.
For achieving the above object, technical scheme of the present invention has been to provide a kind of stainless steel welding stick processing technology, comprise withLower processing step:
S1: annealing process, the semi-finished product that are 1.9mm by diameter by wire-sending device pass through annealing with the speed of 11 ms/minStove carries out annealing in process, and furnace temperature is 1080 DEG C;
S2: drawing process, draws with the speed of 150 ms/min the semi-finished product after annealing by gantry pay off rack by six roadsWire process carries out wire drawing processing, 30 DEG C of diaphragm capsule water temperatures, and after wire drawing, product specification is followed successively by 1.65mm-1.45mm-1.28mm-1.18mm-1.08mm-1.0mm；
S3: ultrasonic cleaning process, the greasy dirt of the finished product after wire drawing being removed to finished surface by supersonic wave cleaning machine withAnd fine particle thing, hyperacoustic general power is 18KW, and wherein the ratio of water-soluble washing agent and water is 1:40, and water temperature is 70℃；
S4: the first wind cutting process, carries out wind by the finished product after Ultrasonic Cleaning through wind cutting apparatus and cuts processing, blastFor 2kgf/c ㎡, wind speed is 200m/s;
S5: hot water rinsing process, enters the finished product after the first wind is cut to carry out warm water filtration, water in heating water tank-washerTemperature is 70 DEG C;
S6: the second wind cutting process, the finished product after superheated water rinsing is carried out to wind through wind cutting apparatus and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S7: oiling technique, the finished product after the second wind is cut is entered in heating water tank-washer and is coated with oil processing, water-solubleThe ratio of lubricating oil and clear water is 1:3, and water temperature is 70 DEG C;
S8: the 3rd wind cutting process, will carry out wind through wind cutting apparatus through oiling finished product after treatment and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S9: take-up packaging, by spool take-up, the finished product after the 3rd wind is cut is carried out to take-up, then wrapDress is processed.
As preferably, in step S2, six road wire-drawing process Zhong Qian tetra-road wire-drawing process are that powder draws, rear twice wire-drawing processFor sky draws, wherein wire drawing powder is powder for receiving.
As preferably, in step S3, water-soluble washing agent is by natrium citricum, sodium carbonate, sodium metasilicate, fatty alcohol ethoxyBase compound composition.
As preferably, in step S7, water-soluble lubricating oil is made up of oiliness improver, EP agent, water-soluble drawing oil.
Advantage of the present invention and beneficial effect are: improve weldering by original running water rinsing being changed into Ultrasonic CleaningThe cleannes on silk surface, apply lubricating oil by oiling technique at welding wire surface in addition and can prevent that welding wire from use going outExisting plug wire phenomenon.
Detailed description of the invention
Below in conjunction with drawings and Examples, the specific embodiment of the present invention is further described. Following examples onlyFor technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
A kind of stainless steel welding stick processing technology, comprises following processing step:
S1: annealing process, the semi-finished product that are 1.9mm by diameter by wire-sending device pass through annealing with the speed of 11 ms/minStove carries out annealing in process, and furnace temperature is 1080 DEG C;
S2: drawing process, draws with the speed of 150 ms/min the semi-finished product after annealing by gantry pay off rack by six roadsWire process carries out wire drawing processing, 30 DEG C of diaphragm capsule water temperatures, and after wire drawing, product specification is followed successively by 1.65mm-1.45mm-1.28mm-1.18mm-1.08mm-1.0mm；
S3: ultrasonic cleaning process, the greasy dirt of the finished product after wire drawing being removed to finished surface by supersonic wave cleaning machine withAnd fine particle thing, hyperacoustic general power is 18KW, and wherein the ratio of water-soluble washing agent and water is 1:40, and water temperature is 70℃；
S4: the first wind cutting process, carries out wind by the finished product after Ultrasonic Cleaning through wind cutting apparatus and cuts processing, blastFor 2kgf/c ㎡, wind speed is 200m/s;
S5: hot water rinsing process, enters the finished product after the first wind is cut to carry out warm water filtration, water in heating water tank-washerTemperature is 70 DEG C;
S6: the second wind cutting process, the finished product after superheated water rinsing is carried out to wind through wind cutting apparatus and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S7: oiling technique, the finished product after the second wind is cut is entered in heating water tank-washer and is coated with oil processing, water-solubleThe ratio of lubricating oil and clear water is 1:3, and water temperature is 70 DEG C;
S8: the 3rd wind cutting process, will carry out wind through wind cutting apparatus through oiling finished product after treatment and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S9: take-up packaging, by spool take-up, the finished product after the 3rd wind is cut is carried out to take-up, then wrapDress is processed.
In step S2, six road wire-drawing process Zhong Qian tetra-road wire-drawing process are that powder draws, and rear twice wire-drawing process is that sky draws, whereinWire drawing powder is powder for receiving.
In step S3, water-soluble washing agent is made up of natrium citricum, sodium carbonate, sodium metasilicate, alcohol ethoxylate.
In step S7, water-soluble lubricating oil is made up of oiliness improver, EP agent, water-soluble drawing oil.
Improve the cleannes of welding wire surface by original running water rinsing being changed into Ultrasonic Cleaning, in addition by oilingTechnique applies lubricating oil at welding wire surface can prevent that plug wire phenomenon from use appearring in welding wire.
The above is only the preferred embodiment of the present invention, it should be pointed out that the ordinary skill people for the artMember, not departing under the prerequisite of the technology of the present invention principle, can also make some improvements and modifications, these improvements and modificationsAlso should be considered as protection scope of the present invention.
Claims (4)
1. a stainless steel welding stick processing technology, is characterized in that: comprise following processing step:
S1: annealing process, the semi-finished product that are 1.9mm by diameter by wire-sending device enter by annealing furnace with the speed of 11 ms/minRow annealing in process, furnace temperature is 1080 DEG C;
S2: drawing process, passes through six road wire drawers by the semi-finished product after annealing with the speed of 150 ms/min by gantry pay off rackOrder is carried out wire drawing processing, 30 DEG C of diaphragm capsule water temperatures, and after wire drawing, product specification is followed successively by 1.65mm-1.45mm-1.28mm-1.18mm-1.08mm-1.0mm；
S3: ultrasonic cleaning process, the finished product after wire drawing is removed to the greasy dirt of finished surface and thin by supersonic wave cleaning machineSmall particle, hyperacoustic general power is 18KW, and wherein the ratio of water-soluble washing agent and water is 1:40, and water temperature is 70 DEG C;
S4: the first wind cutting process, the finished product after Ultrasonic Cleaning is carried out to wind through wind cutting apparatus and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S5: hot water rinsing process, the finished product after the first wind is cut is entered in heating water tank-washer and carries out warm water filtration, water temperature is70℃；
S6: the second wind cutting process, the finished product after superheated water rinsing is carried out to wind through wind cutting apparatus and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S7: oiling technique, enters the finished product after the second wind is cut in heating water tank-washer and be coated with oil processing, water-soluble lubricatingOil is 1:3 with the ratio of clear water, and water temperature is 70 DEG C;
S8: the 3rd wind cutting process, will carry out wind through wind cutting apparatus through oiling finished product after treatment and cut processing, blast is2kgf/c ㎡, wind speed is 200m/s;
S9: take-up packaging, by spool take-up, the finished product after the 3rd wind is cut is carried out to take-up, then carry out packaging placeReason.
2. stainless steel welding stick processing technology as claimed in claim 1, is characterized in that: in step S2, in six road wire-drawing processQian Si road wire-drawing process is that powder draws, and rear twice wire-drawing process is that sky draws, and wherein wire drawing powder is powder for receiving.
3. stainless steel welding stick processing technology as claimed in claim 1, is characterized in that: in step S3, water-soluble washing agent byNatrium citricum, sodium carbonate, sodium metasilicate, alcohol ethoxylate composition.
4. stainless steel welding stick processing technology as claimed in claim 1, is characterized in that: in step S7, water-soluble lubricating oil byOiliness improver, EP agent, water-soluble drawing oil composition.