CN104142097A - Fireworks outer barrel mechanically molded by hydraulic mold at high temperature and manufacturing process of fireworks outer barrel - Google Patents
Fireworks outer barrel mechanically molded by hydraulic mold at high temperature and manufacturing process of fireworks outer barrel Download PDFInfo
- Publication number
- CN104142097A CN104142097A CN201310166825.6A CN201310166825A CN104142097A CN 104142097 A CN104142097 A CN 104142097A CN 201310166825 A CN201310166825 A CN 201310166825A CN 104142097 A CN104142097 A CN 104142097A
- Authority
- CN
- China
- Prior art keywords
- outer barrel
- mould
- fireworks
- temperature
- external cylinder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a fireworks outer barrel mechanically molded by a hydraulic mold at high temperature. The fireworks outer barrel is characterized in that the fireworks outer barrel is made of materials which include, by weight, 6-30 parts of starch, 4-50 parts of plant fibers, 20-60 parts of filling mixture, 1-12 parts of catalyst and 4-25 parts of stabilizer by the steps of mixing and high-temperature molding by the hydraulic mold. A manufacturing process of the fireworks outer barrel has high production efficiency and can realize flow-line production of the fireworks outer barrels. As compared with conventional paper outer barrels, the fireworks outer barrel need short time for drying, and especially in seasons with rainy days, the advantage in drying time is much more remarkable. In addition, the materials for making the fireworks outer barrel are degradable materials, the outer barrel of fireworks which are set off can be used as fertilizer after being degraded, and safety in setting off is guaranteed.
Description
Technical field
The invention belongs to a kind of fireworks and firecrackers device, relate in particular to a kind of urceolus and manufacturing process thereof of fireworks and firecrackers.
Background technology
Traditional fireworks and firecrackers urceolus mainly adopts moulding paper, by rotary machine, is rolled into paper web or multiple moulding paper are bonded as and have certain thickness cardboard, then by molding press, this millboard is made for to urceolus, or manually rolls.This traditional handicraft and materials process are complicated, and production efficiency is low, contaminated environment, set off that security incident occurs frequently, can not produce rainy day, easily fried cylinder is dangerous, the production cycle is long, the high management of manufacturing cost is loaded down with trivial details, large to amount of labour demanded.
Summary of the invention
The invention provides a kind of mechanization hydraulic die high-temperature molding firework external cylinder and manufacturing process thereof, its object solves the shortcoming that prior art exists, and firework external cylinder is easily degraded, environmental protection, and production technology is simple, and production efficiency is high.
The technical solution adopted for the present invention to solve the technical problems is:
A mechanization hydraulic die high-temperature molding firework external cylinder, is characterized in that:
Its material composition comprises the raw material of following weight portion proportioning:
Described plant amylum is for selecting one or more in farina, sweet potato starch, chestnut starch, cornstarch, Job's tears, tapioca, konjak starch to mix with arbitrary proportion;
Described natural fiber mixes with arbitrary proportion through one or more in broken string, waste paper, plant seed, fruit, stem, leaf for selecting;
Described filling mixture is for selecting one or more in calcite, calcium-magnesium powder, magnesium silicate superfine powder, rich magnesium silicate, lithopone to mix with arbitrary proportion;
Described catalyst is for selecting one or more in fatty oil mixture, octadecanoid acid, silicone compounds to mix with arbitrary proportion;
Described stabilizing agent is for selecting one or more in montmorillonite or gypsum to mix with arbitrary proportion.
The manufacturing process of above-mentioned mechanization hydraulic die high-temperature molding firework external cylinder
It is characterized in that, comprise the following steps:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Usefulness of the present invention is:
Production technology of the present invention, production efficiency is high, can streamline produces, and the papery urceolus than traditional, has reduced oven dry equal time, and in rainy weather too much season, effect is just more obvious; Material of the present invention is easy degradable material, after the urceolus degraded after setting off, can work as fertilizer, sets off safety.
The specific embodiment
Embodiment 1:
Following raw material is mixed (unit: kilogram)
Mixed raw material obtains mechanization hydraulic die high-temperature molding firework external cylinder with following steps processing above:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Embodiment 2:
Following raw material is mixed (unit: kilogram)
Mixed raw material obtains mechanization hydraulic die high-temperature molding firework external cylinder with following steps processing above:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Embodiment 3:
Following raw material is mixed (unit: kilogram)
Mixed raw material obtains mechanization hydraulic die high-temperature molding firework external cylinder with following steps processing above:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Embodiment 4:
Following raw material is mixed (unit: kilogram)
Mixed raw material obtains mechanization hydraulic die high-temperature molding firework external cylinder with following steps processing above:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Embodiment 5:
Following raw material is mixed (unit: kilogram)
Mixed raw material obtains mechanization hydraulic die high-temperature molding firework external cylinder with following steps processing above:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.
Adopt after the present invention, fireworks manufacturer, using mechanization mould high-temperature molding to obtain after firework external cylinder, only needs to install the making that lead-in wire has just completed fireworks cylinder, natural environmental-protective, green regenerating; And because material of the present invention is easy degradable material, after the urceolus degraded after setting off, can work as fertilizer, set off safety; Production technology of the present invention is simple, and operation is few, and production efficiency is high, can produce by streamline, has refreshed the history that firework mechanical automation is produced, and produces the product of same specification quantity and can save 75% manpower.
Claims (7)
1. a mechanization hydraulic die high-temperature molding firework external cylinder, is characterized in that:
Its material composition comprises the raw material of following weight portion proportioning:
2. mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that: described plant amylum is for selecting one or more in farina, sweet potato starch, chestnut starch, cornstarch, Job's tears, tapioca, konjak starch to mix with arbitrary proportion.
3. mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that: described natural fiber mixes with arbitrary proportion through one or more in broken string, waste paper, plant seed, fruit, stem, leaf for selecting.
4. mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that: described filling mixture is for selecting one or more in calcite, calcium-magnesium powder, magnesium silicate superfine powder, rich magnesium silicate, lithopone to mix with arbitrary proportion.
5. mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that: described catalyst is for selecting one or more in fatty oil mixture, octadecanoid acid, silicone compounds to mix with arbitrary proportion.
6. mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that: described stabilizing agent is for selecting one or more in montmorillonite or gypsum to mix with arbitrary proportion.
7. the manufacturing process of mechanization hydraulic die high-temperature molding firework external cylinder as claimed in claim 1, is characterized in that, comprises the following steps:
The first step: and material: employing and material machine will add the stirring of proper amount of normal-temperature boiling water with mixer after raw material mixing;
Second step: high-temperature liquid compression mould moulding: according to the first step and the raw material of having expected, with cutting plate, pour in the oil pressure mold cavity of hydraulic press, hydraulic press matched moulds, heat-conducting oil furnace is sent conduction oil into circulating-heating in die of hydraulic machine simultaneously, making temperature in mould is 120-320 degree, until the outer dry-steam of mould is emerged, last hydraulic press is opened mould and with cutting plate, the product on mould is taken out.