CN104131292B - Etch-proof composite polishing liquid of a kind of easy to clean and preparation method thereof - Google Patents
Etch-proof composite polishing liquid of a kind of easy to clean and preparation method thereof Download PDFInfo
- Publication number
- CN104131292B CN104131292B CN201410308876.2A CN201410308876A CN104131292B CN 104131292 B CN104131292 B CN 104131292B CN 201410308876 A CN201410308876 A CN 201410308876A CN 104131292 B CN104131292 B CN 104131292B
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- easy
- etch
- clean
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the etch-proof composite polishing liquid of a kind of easy to clean, it is characterized in that, be made up of the raw material of following weight part: cerium oxide 11-14, titanium dioxide 5-7, rust-preventive agent T747? 3-4, ethanol 5-7, phosphoric acid ester 2-4, Virahol 5-7, Dioctyl Sodium Sulfosuccinate 4-7, sodium stearate 3-5, sodium alginate 2-4, auxiliary agent 5-7, deionized water 300; The present invention adds the tensio-active agents such as Dioctyl Sodium Sulfosuccinate, the physical adsorption top layer of long-term easy cleaning is formed on processing metal surface, to improve condition of surface, add auxiliary agent, there is good wear-resisting, dispersion, lubrication, film-forming properties, add rust-preventive agent, rustproof layer can be formed in metallic surface; Mixed polishing solution of the present invention, safety non-toxic, manufacture craft is simple, two-forty, easy cleaning, is applicable to Stainless Steel Products polishing.
Description
Technical field
The present invention relates to technical field of surface, particularly etch-proof composite polishing liquid of a kind of easy to clean and preparation method thereof.
Background technology
Stainless steel refers to the steel of the chemical etching dielectric corrosions such as the weak corrosive medium such as resistance to air, steam, water and acid, alkali, salt.The product of current stainless material is very many, and part shape complexity is various, and operation is more in the course of processing.Stainless steel in use inevitably produces scuffing, damages, thus stainless steel product can not normally be used.Shape size etc. due to stainless steel part is complicated various, and therefore traditional mechanical polishing mode can not meet the requirement of product, and the method for electropolishing also cannot meet for the product with certain size, and the homogeneity of electropolishing is relatively poor simultaneously.
Chemical rightenning process is not by the shape of part, the restriction of size, do not need special instrument, and disposablely can process more part, chemical rightenning utilizes the chemical solution of definite composition to the surface of microcosmic injustice, make the metal rapid solution at outstanding position, thus smooth microcosmic not plane surface, reach the effect of light.Hardware shapes rear surface can adhere to one deck greasy dirt or other chemicals usually; utensil uses the corrosion by environment for use after for some time; rusty stain can be produced on surface; in order to attractive in appearance and increase the service life; the dirt on surface cleared up by conventional special metal cleaner or rumbling compound, but existing rumbling compound product exist return fast, the applicable metal species of rust narrow, clean halfway problem.
Summary of the invention
The object of this invention is to provide etch-proof composite polishing liquid of a kind of easy to clean and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
The etch-proof composite polishing liquid of a kind of easy to clean, is made up of the raw material of following weight part: cerium oxide 11-14, titanium dioxide 5-7, rust-preventive agent T747 3-4, ethanol 5-7, phosphoric acid ester 2-4, Virahol 5-7, Dioctyl Sodium Sulfosuccinate 4-7, sodium stearate 3-5, sodium alginate 2-4, auxiliary agent 5-7, deionized water 300;
Described auxiliary agent is made up of the raw material of following weight part: aluminium sesquioxide 4-6, nano titanium oxide 5-7, water glass 1-2,1-Methoxy-2-propyl acetate 3-4, Lauryl Alcohol ester 2-3, methyl acrylate 2-4, croscarmellose sodium 2-3, emulsifier BP 4-5, water 50-54; First aluminium sesquioxide, nano titanium oxide, croscarmellose sodium, emulsifier BP add in the water of half amount by preparation method, grinding 1-2 hour, then all the other remaining components are slowly added, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The etch-proof composite polishing liquid of a kind of easy to clean of the present invention, be made up of following concrete steps:
(1) cerium oxide, titanium dioxide, Dioctyl Sodium Sulfosuccinate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grinding 25-35 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 35 DEG C-45 DEG C, insulation 1-1.5 hour, obtain mixing B material;
(3) the mixing B of insulation material is slowly joined in mixing A material while stirring, after fully stirring, add auxiliary agent, continue to stir 25-35 minute, be cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention adds the tensio-active agents such as Dioctyl Sodium Sulfosuccinate, the physical adsorption top layer of long-term easy cleaning is formed on processing metal surface, to improve condition of surface, add auxiliary agent, there is good wear-resisting, dispersion, lubrication, film-forming properties, add rust-preventive agent, rustproof layer can be formed in metallic surface; Mixed polishing solution of the present invention, safety non-toxic, manufacture craft is simple, two-forty, easy cleaning, is applicable to Stainless Steel Products polishing.
Embodiment
Below by specific examples, the present invention is described in detail.
The etch-proof composite polishing liquid of a kind of easy to clean, is made up of the raw material of following weight part (kilogram): cerium oxide 11, titanium dioxide 5, rust-preventive agent T747 3, ethanol 5, phosphoric acid ester 2, Virahol 5, Dioctyl Sodium Sulfosuccinate 4, sodium stearate 3, sodium alginate 2, auxiliary agent 5, deionized water 300;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): aluminium sesquioxide 4, nano titanium oxide 5, water glass 1,1-Methoxy-2-propyl acetate 3, Lauryl Alcohol ester 2, methyl acrylate 2, croscarmellose sodium 2, emulsifier BP 4, water 50; First aluminium sesquioxide, nano titanium oxide, croscarmellose sodium, emulsifier BP add in the water of half amount by preparation method, grinding 1-2 hour, then all the other remaining components are slowly added, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The etch-proof composite polishing liquid of a kind of easy to clean of the present invention, be made up of following concrete steps:
(1) cerium oxide, titanium dioxide, Dioctyl Sodium Sulfosuccinate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grinding 25-35 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 35 DEG C-45 DEG C, insulation 1-1.5 hour, obtain mixing B material;
(3) the mixing B of insulation material is slowly joined in mixing A material while stirring, after fully stirring, add auxiliary agent, continue to stir 25-35 minute, be cooled to room temperature and get final product.
Laboratory test results: the surface of each stainless steel work-piece of visual inspection, workpiece surface appearance uniform, without heterochromatic or have slight color differences and without snowflake; Adopt BYK company of miniature glossometer A-4430(Germany) test the glossiness of each polishing stainless steel workpiece surface, glossiness is 48 Gu.
Claims (2)
1. the etch-proof composite polishing liquid of easy to clean, it is characterized in that, be made up of the raw material of following weight part: cerium oxide 11-14, titanium dioxide 5-7, rust-preventive agent T747 3-4, ethanol 5-7, phosphoric acid ester 2-4, Virahol 5-7, Dioctyl Sodium Sulfosuccinate 4-7, sodium stearate 3-5, sodium alginate 2-4, auxiliary agent 5-7, deionized water 300;
Described auxiliary agent is made up of the raw material of following weight part: aluminium sesquioxide 4-6, nano titanium oxide 5-7, water glass 1-2,1-Methoxy-2-propyl acetate 3-4, Lauryl Alcohol ester 2-3, methyl acrylate 2-4, croscarmellose sodium 2-3, emulsifier BP 4-5, water 50-54; First aluminium sesquioxide, nano titanium oxide, croscarmellose sodium, emulsifier BP add in the water of half amount by preparation method, grinding 1-2 hour, then all the other remaining components are slowly added, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. the etch-proof composite polishing liquid of a kind of easy to clean according to claim 1, is characterized in that, be made up of following concrete steps:
(1) cerium oxide, titanium dioxide, Dioctyl Sodium Sulfosuccinate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grinding 25-35 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 35 DEG C-45 DEG C, insulation 1-1.5 hour, obtain mixing B material;
(3) the mixing B of insulation material is slowly joined in mixing A material while stirring, after fully stirring, add auxiliary agent, continue to stir 25-35 minute, be cooled to room temperature and get final product.