CN104120535A

CN104120535A - Real silk elasticity breathable interlaced fabric

Info

Publication number: CN104120535A
Application number: CN201410335352.2A
Authority: CN
Inventors: 谢坤
Original assignee: JIANGSU ZHAOHUA INFORMATION TECHNOLOGY Co Ltd
Current assignee: JIANGSU ZHAOHUA INFORMATION TECHNOLOGY Co Ltd
Priority date: 2014-07-15
Filing date: 2014-07-15
Publication date: 2014-10-29

Abstract

The invention discloses real silk elasticity breathable interlaced fabric. The real silk elasticity breathable interlaced fabric is characterized in that warps are formed by sequentially arraying the A, B and C three sets of real silks with different twist degrees and a D set of polyester filament yarn, and wefts are formed by sequentially arraying the E and F two sets of lustrous rayon with different twist degrees and core-spun yarn formed by compounding dacron and spandex fibers; the A, B and C three sets of warps are all made of 20/22 D*2 real silks, and the twist degrees are 5T/cm, 20T/cm and C28T/cm respectively; the D set of warps is made of 19.8 tex polyester filament yarn, and the twist degree is 3T/cm; the E set of wefts in the wefts is made of 100D lustrous rayon, the twist degree is 18T/cm, the F set of wefts is made of 20/22 D*2 real silks and 20D spandex fibers, and the twist degree is 5T/13T/cm; the fabric is formed by weaving three layers of nested tissue. According to the real silk elasticity breathable interlaced fabric, the rebound resilience, the dimensional stability and the tear resistance of the real silk fabric are improved, and accordingly a concave-convex transformation and alternately dark and bright stereoscopic appearance effect is achieved on the surface of the entire fabric through the arrangement of warp yarn and weft yarn and the fabric weave preparation.

Description

The real silk elastic force MIXED FABRIC of breathing freely

Technical field

The present invention relates to a kind of silk fabric, relate in particular to the ventilative MIXED FABRIC of a kind of real silk elastic force.

Background technology

Real silk belongs to natural protein fibre, in its core " fibroin ", contain 18 seed amino acids, with human body skin structural similarity, the fiber composition that it is special and molecular structure and arrangement, achieved real silk fabric outward appearance elegance, soft smooth, the advantage such as sucting wet air permeability is good.But the specialty fibers composition of real silk and molecular structure and arrangement also make real silk fabric have some obvious defects; its crease-resistant ability; rebound performance is poor with respect to chemical fibre thing; easily produce splitting phenomenon, can not meet people's requirement, these defects make people take in process actual; often have the sense of constraint; this is very limited the application of real silk fabric, Given this needs to provide a kind of resilience good, the silk fabric of anti-splitting.

Summary of the invention

The technical problem to be solved in the present invention is to provide a kind of good springiness, the ventilative MIXED FABRIC of real silk elastic force that anti-splitting moisture absorption is ventilative, and fabric face presents special texture effect.

For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of real silk elastic force MIXED FABRIC of breathing freely, warp thread by tri-groups of different twists of A, B, C and twist with the fingers to real silk and D group polyester filament rearrange in sequence, the cored silk that weft yarn is composited by the bright rayon of E, two groups of different twists of F and terylene and spandex thread is arranged in sequence; Described A, B, tri-groups of warp thread of C all adopt 20/22D × 2 real silk, and wherein, the twist of A group warp thread is 5T/cm, twist with the fingers to being S sth. made by twisting, and the twist of B group warp thread is 20T/cm, twists with the fingers to twisting with the fingers for Z; The twist of C group warp thread is 28T/cm, twists with the fingers to twisting with the fingers for Z; The polyester filament that described D group warp thread is 19.8tex, the twist is 3T/cm, twists with the fingers to twisting with the fingers for S; In described weft yarn, E group weft yarn is 100D bright rayon, and the twist is 18T/cm, twists with the fingers to being S sth. made by twisting, and F group weft yarn is 20/22D × 2 real silk+20D spandex threads, and the twist is 5T/13 T/cm, twists with the fingers to twisting with the fingers for Z; Described fabric adopts three layers of nested tissue to weave, the structure of three layers of described nested tissue is: comprise three layers of elementary organization and fill tissue, these three layers of elementary organizations are respectively the A of elementary organization, the B of elementary organization and the C of elementary organization, in the A of elementary organization is the B of elementary organization through interlacing point, and in the B of elementary organization is the C of elementary organization through interlacing point.

Further, through putting in order as the putting in order as 1A1B1D1C1A of A, B, C, tetra-groups of warp thread of D of weft yarn, the putting in order as 1E1F of E, two groups of weft yarns of F.

Further, the multiple that in three layers of described nested tissue, the Weaving Cycle number of the C of elementary organization is 5, the Weaving Cycle number of the A of elementary organization and the B of elementary organization is selected arbitrarily, the multiple that the Weaving Cycle number of filling tissue is 5.

Further, the described C of elementary organization is twill left to right, and the B of elementary organization is plain weave one on the other, and the A of elementary organization 3 × 3 changes plain weaves, fills and is organized as left twill.

Further, the upper machine of described fabric through close be 126-146 root/10 centimetre, upper machine filling density 72-80 root/10 centimetre.

Further, on described fabric machine through close be 135/10 centimetres, 76/10 centimetres of upper machine filling densities.

Beneficial effect of the present invention:

1) the cored silk that the present invention is composited real silk and bright rayon and real silk and spandex thread interweaves, and artificial silk is as weft yarn and the warp thread formation fabric face that interweaves, can the local moisture permeability that improves fabric face gloss and fabric; The cored silk that real silk and spandex thread are composited interweaves in the larger elasticity of grain cross generation as weft yarn and warp thread, improves resilience and the tear resistance of fabric;

2) utilize the yarn of the different twists to interweave, fabric face can produce the appearance effect of crepe fabrics, and by the cooperation of institutional framework, the appearance effect of crepe fabrics is more outstanding, soft, and sucting wet air permeability is good.

Brief description of the drawings

Fig. 1 is organization chart of the present invention.

Fig. 2 is the organization chart of the A of elementary organization.

Fig. 3 is the organization chart of the B of elementary organization.

Fig. 4 is the organization chart of the C of elementary organization.

Fig. 5 is the organization chart of filling tissue.

Detailed description of the invention

A kind of real silk elastic force of the present invention MIXED FABRIC of breathing freely, warp thread is rearranged in sequence by real silk and the D group polyester filament of tri-groups of different twists of A, B, C, and the cored silk that weft yarn is composited by the bright rayon of E, two groups of different twists of F and terylene and spandex thread is arranged in sequence.

Below in conjunction with the drawings and specific embodiments, technical scheme of the present invention is elaborated.

The ventilative MIXED FABRIC of a kind of real silk elastic force, warp thread by A, B, C, the different twists of tetra-groups of groups of D rearranges in sequence, and the cored silk that weft yarn is composited by the bright rayon of E, two groups of different twists of F and real silk and spandex thread is arranged in sequence.

One, yarn

1.1 warp thread specifications

The present embodiment warp thread uses specification as shown in table 1.

Table 1 warp thread uses specifications parameter

20/22 D real silk is the conventional variety of selling on market, and market ample supply and prompt delivery are purchased commodities convenient and swift, without custom-made, is conducive to reduce cost of material.

The plying twist of A warp thread and D warp thread is respectively 5 T/cm and the 3T/cm twist is little, and yam surface fiber alignment glacing flatness is high, the lustrous surface that is conducive to improve real silk fabric.B, the C warp thread plying twist are respectively 20 T/cm, 28 T/cm, and the twist is larger, forms tight twist yarn, after woven into fabric, the internal stress of fabric is also larger, in rear arrangement process, fabric is in order to discharge this part internal stress, and fabric face can produce the appearance effect of crepe fabrics.

1.2 weft yarn specifications

The present embodiment weft yarn uses specification as shown in table 2.

Table 2 weft yarn specifications parameter

100 D have light people silk to make weft yarn, with the warp thread formation fabric face that interweaves, can locally improve fabric face gloss; In addition, the moisture permeability of people's silk is also fine, contacts with human body, can not reduce the comfortableness of fabric dress; Meanwhile, because there being the price of light people silk lower, can reduce the cost of material of fabric.

The covering filament that 20/22 D × 2 real silk and 20 D spandexs are composited is made weft yarn, its Main Function is to produce larger elasticity at grain cross, again because the sth. made by twisting of this covering filament is to identical with 20/22 D × 2 real silk, and the twist is larger, form tight twist yarn, the fabric being made into, in arrangement process, can utilize finishing technique, accelerate the untwisting of this tight twist yarn, thereby strengthen the particular appearance of fabric face crepe fabrics.

Two, fabric

Fabric tow sides appearance effect is identical.

2.1 fabric tissue

Adopt three layers of nested tissue to weave, be illustrated in figure 1 the structure of three layers of nested tissue, this tissue comprises three layers of elementary organization, the A of elementary organization 3 × 3 changes plain weaves (as shown in Figure 2), the B of elementary organization for plain weave (as shown in Figure 3) one on the other, the C of elementary organization is four bottom right twill-weaves (as shown in Figure 4) on, in the A of elementary organization is the B of elementary organization through interlacing point, and in the B of elementary organization is the C of elementary organization through interlacing point, fills and is organized as three times left twills on two.

2.2 fabric yarns are arranged

The warp thread of fabric is arranged as 1A1B1D1C1A, and weft yarn arrangement is 1E1F.

Three, fabric specification

The main specifications parameter of the ventilative MIXED FABRIC of the present embodiment real silk elastic force is in table 3.

Table 3 fabric main specifications parameter

Through close	Filling density	Fabric weight	Fabric width
				135/10 centimetres	76/10 centimetres	106 grams/meter ²	108cm

Claims

1. the ventilative MIXED FABRIC of real silk elastic force, it is characterized in that: warp thread by tri-groups of different twists of A, B, C and twist with the fingers to real silk and D group polyester filament rearrange in sequence, the cored silk that weft yarn is composited by the bright rayon of E, two groups of different twists of F and terylene and spandex thread is arranged in sequence; Described A, B, tri-groups of warp thread of C all adopt 20/22D × 2 real silk, and wherein, the twist of A group warp thread is 5T/cm, twist with the fingers to being S sth. made by twisting, and the twist of B group warp thread is 20T/cm, twists with the fingers to twisting with the fingers for Z; The twist of C group warp thread is 28T/cm, twists with the fingers to twisting with the fingers for Z; The polyester filament that described D group warp thread is 19.8tex, the twist is 3T/cm, twists with the fingers to twisting with the fingers for S; In described weft yarn, E group weft yarn is 100D bright rayon, and the twist is 18T/cm, twists with the fingers to being S sth. made by twisting, and F group weft yarn is 20/22D × 2 real silk+20D spandex threads, and the twist is 5T/13 T/cm, twists with the fingers to twisting with the fingers for Z; Described fabric adopts three layers of nested tissue to weave, the structure of three layers of described nested tissue is: comprise three layers of elementary organization and fill tissue, these three layers of elementary organizations are respectively the A of elementary organization, the B of elementary organization and the C of elementary organization, in the A of elementary organization is the B of elementary organization through interlacing point, and in the B of elementary organization is the C of elementary organization through interlacing point.

2. the ventilative MIXED FABRIC of a kind of real silk elastic force according to claim 1, is characterized in that: through putting in order as the putting in order as 1A1B1D1C1A of A, B, C, tetra-groups of warp thread of D of weft yarn, and the putting in order as 1E1F of E, two groups of weft yarns of F.

3. the ventilative MIXED FABRIC of a kind of real silk elastic force according to claim 1 and 2, it is characterized in that: the multiple that in three layers of described nested tissue, the Weaving Cycle number of the C of elementary organization is 5, the Weaving Cycle number of the A of elementary organization and the B of elementary organization is selected arbitrarily, the multiple that the Weaving Cycle number of filling tissue is 5.

4. the ventilative MIXED FABRIC of a kind of real silk elastic force according to claim 3, is characterized in that: the described C of elementary organization is twill left to right, and the B of elementary organization is plain weave one on the other, and the A of elementary organization 3 × 3 changes plain weaves, and filling is organized as left twill.

5. the ventilative MIXED FABRIC of a kind of real silk elastic force according to claim 4, is characterized in that: the upper machine of described fabric through close be 126-146 root/10 centimetre, upper machine filling density 72-80 root/10 centimetre.

6. the ventilative MIXED FABRIC of a kind of real silk elastic force according to claim 5, is characterized in that: on described fabric machine through close be 135/10 centimetres, 76/10 centimetres of upper machine filling densities.