Summary of the invention
The object of the invention is the defect for prior art, a kind of method of basic metal rod and manufacture basic metal rod is provided, in use can neutralize the acidity of a part of food, the acidity burden in ameliorate body, and can be by contact stripping.
For achieving the above object, first aspect, the invention provides a kind of basic metal rod, and the weight ratio of the component in described basic metal bar matter is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Further, the weight ratio of the component in described basic metal bar matter is: Zn is 1.0-6.0%, and Zr is 0.02-2%, and Na is 0.01-0.1%, and K is 0.01-0.1%, and Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Further, the weight ratio of the component in described basic metal bar matter is: Zn is 3.5-5%, and Zr is 0.8-1.5%, and Na is 1-5%, and K is 1-5%, and Ca is 0.9-1.5%, and Sn is 0.001-7%, and surplus is magnesium.
Further, the weight ratio of the component in described basic metal bar matter is: Zn is that 3%, Zr is that 0.1%, Na is that 0.1%, K is that 0.1%, Ca is 0.2%, Sn5%, and surplus is magnesium.
Second aspect, the invention provides a kind of method for the manufacture of basic metal rod, and described method comprises:
The alloy material that is main material by bases metal is made alloy pole, and the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium;
By extrusion principle, described alloy pole is processed as to rough basic metal rod;
Utilize machining that described rough basic metal rod is processed as to meticulous basic metal rod.
The third aspect, the invention provides a kind of method for the manufacture of basic metal rod, and described method comprises:
The alloy material that is main material by bases metal is made sheet alloy, and the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium;
Described sheet alloy is cut into bar;
Utilize machining that described bar is processed as to basic metal rod.
Fourth aspect, the invention provides a kind of method for the manufacture of basic metal rod, and described method comprises:
Utilizing the alloy material die cast that mould is main material by bases metal is rough basic metal rod, and the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium;
Utilize machining that described rough basic metal rod is processed as to meticulous basic metal rod.
The method basic metal rod of the present invention of basic metal rod of the present invention and manufacture basic metal rod is containing harmful element, can or serve as chopsticks for the stirring of tap water, coffee, tea, when meeting manufacture and use properties, in use can neutralize the acidity of a part of water and food, acidity burden in ameliorate body, and can, by contact stripping, supplement the bases element of needed by human.
Embodiment
Below by drawings and Examples, technical scheme of the present invention is described in further detail.
The present invention is used to provide a kind of basic metal rod, can be used for the alkalescence rod that tap water stirred or served as chopsticks, make it when meeting manufacture and use properties, in use can neutralize the acidity of a part of food, acidity burden in ameliorate body, and can, by contact stripping, supplement the bases element (including but not limited to calcium, magnesium, potassium, sodium) of needed by human.
The weight ratio of the component in the material of basic metal rod of the present invention is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferably, the weight ratio of the component in the material of basic metal rod is: Zn is 1.0-6.0%, and Zr is 0.02-2%, and Na is 0.01-0.1%, and K is 0.01-0.1%, and Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferred again, the weight ratio of the component in basic metal bar matter is: Zn is 3.5-5%, and Zr is 0.8-1.5%, and Na is 1-5%, and K is 1-5%, and Ca is 0.9-1.5%, and Sn is 0.001-7%, and surplus is magnesium.
Concrete, the weight ratio of the component in basic metal bar matter is: Zn is that 3%, Zr is that 0.1%, Na is that 0.1%, K is that 0.1%, Ca is 0.2%, Sn5%, and surplus is magnesium.
Magnesium alloy of the present invention, because have specific purposes, is used for processing for the edible basic metal rod of processing, and is therefore directly to contact with processed food, thus the content of essential strict control heavy metal, as Pb, Cd, Cr, As, Ni.
And will control equally the content of Al, this is harmful because of aluminium element and is very easily dissolved in medium.
Fig. 1 is the schema of basic metal rod of the present invention the first embodiment, and as shown in the figure, the present embodiment specifically comprises the steps:
Step 101, the alloy material that is main material by bases metal is made alloy pole, and the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, surplus is magnesium.
Preferably, the weight ratio of the component in the material of basic metal rod is: Zn is 1.0-6.0%, and Zr is 0.02-2%, and Na is 0.01-0.1%, and K is 0.01-0.1%, and Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferred again, the weight ratio of the component in basic metal bar matter is: Zn is 3.5-5%, and Zr is 0.8-1.5%, and Na is 1-5%, and K is 1-5%, and Ca is 0.9-1.5%, and Sn is 0.001-7%, and surplus is magnesium.
Concrete, the weight ratio of the component in basic metal bar matter is: Zn is that 3%, Zr is that 0.1%, Na is that 0.1%, K is that 0.1%, Ca is 0.2%, Sn5%, and surplus is magnesium.
Step 102, by extrusion principle, is processed as rough basic metal rod by described alloy pole;
Step 103, utilizes machining that described rough basic metal rod is processed as to meticulous basic metal rod.
Fig. 2 is the schema of basic metal rod of the present invention the second embodiment, and as shown in the figure, the present embodiment specifically comprises the steps:
Step 201, the alloy material that is main material by bases metal is made sheet alloy, and the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, and Zr is that≤2%, Na is that≤10%, K is that≤10%, Ca is 0.2-2%, Sn≤15%, surplus is magnesium.
Preferably, the weight ratio of the component in the material of basic metal rod is: Zn is 1.0-6.0%, and Zr is 0.02-2%, and Na is 0.01-0.1%, and K is 0.01-0.1%, and Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferred again, the weight ratio of the component in basic metal bar matter is: Zn is 3.5-5%, and Zr is 0.8-1.5%, and Na is 1-5%, and K is 1-5%, and Ca is 0.9-1.5%, and Sn is 0.001-7%, and surplus is magnesium.
Concrete, the weight ratio of the component in basic metal bar matter is: Zn is that 3%, Zr is that 0.1%, Na is that 0.1%, K is that 0.1%, Ca is 0.2%, Sn5%, and surplus is magnesium.
Step 202, cuts into bar by described sheet alloy;
Step 203, utilizes machining that described bar is processed as to basic metal rod.
Fig. 3 is the schema of basic metal rod of the present invention the 3rd embodiment, and as shown in the figure, the present embodiment specifically comprises the steps:
Step 301, utilizing the alloy material die cast that mould is main material by bases metal is rough basic metal rod, the weight ratio of the component of described alloy material is: Zn is 1.0-6.0%, Zr is that≤2%, Na is that≤10%, K is≤10%, Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferably, the weight ratio of the component in the material of basic metal rod is: Zn is 1.0-6.0%, and Zr is 0.02-2%, and Na is 0.01-0.1%, and K is 0.01-0.1%, and Ca is 0.2-2%, Sn≤15%, and surplus is magnesium.
Preferred again, the weight ratio of the component in basic metal bar matter is: Zn is 3.5-5%, and Zr is 0.8-1.5%, and Na is 1-5%, and K is 1-5%, and Ca is 0.9-1.5%, and Sn is 0.001-7%, and surplus is magnesium.
Concrete, the weight ratio of the component in basic metal bar matter is: Zn is that 3%, Zr is that 0.1%, Na is that 0.1%, K is that 0.1%, Ca is 0.2%, Sn5%, and surplus is magnesium.
Step 302, utilizes machining that described rough basic metal rod is processed as to meticulous basic metal rod.
The result of embodiment shows, basic metal rod provided by the invention is not containing harmful element, can or serve as chopsticks for tap water stirring, when meeting manufacture and use properties, in use can neutralize the acidity of a part of food, acidity burden in ameliorate body, and can, by contact stripping, supplement the bases element (including but not limited to calcium, magnesium, potassium, sodium) of needed by human.Basic metal rod of the present invention is not containing harmful element, can or serve as chopsticks for the stirring of tap water, coffee, tea, when meeting manufacture and use properties, in use can neutralize the acidity of a part of water and food, acidity burden in ameliorate body, and can, by contact stripping, supplement the bases element of needed by human.
Above-described embodiment; object of the present invention, technical scheme and beneficial effect are further described; institute is understood that; the foregoing is only the specific embodiment of the present invention; the protection domain being not intended to limit the present invention; within the spirit and principles in the present invention all, any modification of making, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.