CN104119799A - Non-cured rubber asphalt waterproof paint - Google Patents
Non-cured rubber asphalt waterproof paint Download PDFInfo
- Publication number
- CN104119799A CN104119799A CN201410334998.9A CN201410334998A CN104119799A CN 104119799 A CN104119799 A CN 104119799A CN 201410334998 A CN201410334998 A CN 201410334998A CN 104119799 A CN104119799 A CN 104119799A
- Authority
- CN
- China
- Prior art keywords
- rubber asphalt
- asphalt waterproof
- uncured rubber
- waterproof coating
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a non-cured rubber asphalt waterproof paint. The preparation technology of the paint comprises the following steps: heating the asphalt to 140 DEG C, loading the heated asphalt into a stirring tank, adding a softening agent, rubber powder, and polymer, stirring for 30 minutes, heating to 160 DEG C, delivering the mixture to a colloid mill to grind the two edges, heating to 190 DEG C, adding a special additive, stirring for one hour, cooling to 160 to 170 DEG C, adding an auxiliary agent, stirring for one hour, adding a filling material, stirring for one hour, and finally discharging. The paint solves the problems of waterproof layer fracture due to the cracking stress, which is transferred from the basic layer to the waterproof layer, and the accelerated aging due to the flexural fatigue and high stress state of the waterproof layer. Moreover, because of the cohesiveness of the paint, the capillary pores and cracks in the basic layer can be perfectly sealed by the paint, thus the problem of water leaking in the waterproof layer is solved, and the waterproof reliability is greatly improved.
Description
Technical field
The invention belongs to waterproof paint field, relate in particular to a kind of uncured rubber asphalt waterproof coating.
Background technology
The seepage of building structure is to perplex for a long time a difficult problem of building trade, and building waterproofing technique and water-proof material are the important topics that scientific research personnel puts forth effort research always.China's leakage of buildings situation situation is surprising and severe.
There is following problem in existing water-proof material and waterproof construction technology: rigidity water-proofing material is easily subject to the impact of basic unit distortion and causes the cracking of waterproof layer, directly affects its water-proof function; Flexible waterproof material in use, because construction or external force cause basal plane or water-proof material to damage, can cause intaking between waterproof layer and basal plane, if waterproof roll adopts the mode of some paving or bar paving, after water inlet, be easy to cause channeling water so, once there is leakage of buildings phenomenon, be difficult to find source, maintenance is caused to difficulty.And if the mode of paving is expired in employing, although due to the bonding between water-proof material and basal plane, can play the effect of certain obstruct water, but because material adhesion is in substrate surface, what when base course crack, water-proof material still showed is zero extension: even if material itself has certain unit elongation, but in the time of base course crack, material also destroys thereupon, or only have small extension, and do not possess real anti-base course crack ability.The concept of " zero extends " is in the industry cycle approved.Aspect the bonding of flexible waterproof layer and basic unit, there is a contradiction always.If waterproof layer and basic unit's bonding are firmly, advantage is to have there will not be drum phenomenon, is not also prone to the channeling water phenomenon under waterproof layer.Shortcoming is that waterproof layer is subject to the impact of basic unit's distortion large, once base course crack, when waterproof layer is subject to action of pulling stress, the waterproof layer of both sides, crack does not almost have disbonded ragion, tensile stress cannot be transmitted to both sides and can only concentrate on cracking position, and very little crack just may cause waterproof layer by drawing crack; Even not by drawing crack, the waterproof layer of location of cracks also can be due to for a long time in high-stress state and accelerated deterioration, or because stretching repeatedly produces fatigure failure.Therefore just had and located to take empty paving at predictable location of cracks as plate end seam etc. and process, or waterproof layer all adopts the waterproofing process of the sticky or bar paving of empty paving, point, this is also one of way of current specification recommends.But produce again thus another one problem, once waterproof layer produces tiny cavity or crack at certain position and leaks, under waterproof layer, just there will be channeling water phenomenon, and be difficult to find the source of seepage, brought very large difficulty to patch work.
Summary of the invention
The object of the present invention is to provide a kind of uncured rubber asphalt waterproof coating, be intended to solve because base course crack stress passes to waterproof layer and cause waterproof layer fracture, flexing fatigue to destroy or make the problem of waterproof layer in high-stress state premature aging and the problem of waterproof layer channeling water.
The present invention is achieved in that the each component of a kind of uncured rubber asphalt waterproof coating and mass ratio thereof are: pitch 10%-15%, shoddy 5%-15%, tenderizer 24%-45%, high molecular polymer 5%-10%, specialist additive 4%-10%, auxiliary agent 0.05%-1%, filler 20%-30%.
Further, described pitch is to be selected from a kind of or its mixture of heavily handing in 90# pitch, 10# pitch.
Further, described shoddy is 60-80 object tire tread rubber powder.
Further, described tenderizer is naphthenic oil, aromatic hydrocarbon oil, subtracts a kind of or its several mixtures in third fractional oil.
Further, described high molecular polymer is a kind of or its several mixtures in SBS, SBR, SIS, SEBS, APP, APAO, POE.
Further, described specialist additive is a kind of or its mixture in polyamide hot, modified polyamide.
Further, described auxiliary agent is AClyn lower molecular weight ionomer.
Further, described filler is 400 order coarse whitings or 400 order talcum powder.
Another object of the present invention is to provide a kind of blending process of uncured rubber asphalt waterproof coating as follows:
Step 1, asphalt heating to 140 DEG C is squeezed into stirred pot;
Step 2, add tenderizer, rubber powder, high molecular polymer, stir 30 minutes, temperature is raised to 160 DEG C;
Step 3, enter colloidal mill grind both sides, temperature is raised to 190 DEG C, adds specialist additive, stirs 1 hour;
Step 4, add auxiliary agent while being cooled to 160～170 DEG C, stir 1 hour, add filler to stir 1 hour;
Step 5, discharging.
Another object of the present invention is to provide a kind of constructional method of uncured rubber asphalt waterproof coating as follows:
Full scale construction is carried out at special-shaped position: the detail sections such as the nook of negative and positive angle, plane and facade are first brushed, and thickness is advisable with 2mm, and coiled material is cut into respective shapes enclose after finishing extra play, guarantees the Bulk coat thickness that is consistent;
Big area spraying application:
Step 1, treat that basal plane cleans out after, open heating batch can, in advance material is poured in batch can and heated, reach can spray 150 DEG C of state time until coating bulk temperature, uniformly spray with special coating machine, when spraying, can exchange different spray guns according to different design thicknesss, waterproof layer once shaped, thickness is 2mm;
Step 2, spray after certain area, before paving coiled material, adopted pin survey method to detect coat-thickness, if thickness is not up to standard or local needs strengthened, get some coating with trowel, filled in the manual mode of scraping that is coated with, spraying application should segmentation or district complete, 500-1000m
2be to construct in a region;
After step 3, spraying, cover in time waterproof roll, avoid dust too much in scene to be bonded in coating top layer and reduce the cohesiveness of coating and sealing coat or waterproof roll, after the complete sealing coat of paving or waterproof roll, can go up people and walk.
effect gathers
The beneficial effect of the uncured rubber asphalt waterproof coating of the present invention is as follows:
1, there is random sealing, absorb the characteristic of stress, can fill up basic unit's strain crack, can, because of the frustrating and expand and damage waterproof layer of basic unit, not make building structure remain intact airtight waterproof state.
2, low to Base Smoothness requirement, do not need brushing base treatment agent, can effectively in humidity and submerged structure structure, apply.
3, creep property is good, self-healing ability is strong, touch and glue, be difficult to peel off, even if there is sleeve pipe to penetrate, still can form stable waterproof layer, within the whole durability of waterproof layer, all there is viscosity and self-healing ability, in the time that waterproof layer is subject to External Force Acting and is poked, breakdown point can not expand, and channeling water phenomenon can not occur yet in waterproof layer bottom, and because the creep interaction energy of this coating is gradually by breakdown point reparation, greatly improve the reliability of waterproof layer.
4, convenient and quick construction.Can adopt spread coating construction and spraying method construction, film forming immediately, does not need maintenance, processes without overlap joint, does not affect subsequent handling, and during with coiled material composite water-proof, coiled material can directly be laid on this Project Product surface layer, need not heat, cold construction operation.
5, thermal stability is high, and 70～80 DEG C of slippages of can not trickling are consistent with the thermal stability of self-adhesive coiled material.Creep properties is good and thermal stability is high, and this is its another distinguishing feature.
6, good avidity, can be combined with any material, forms water-proof coating viscosity and stable; Good winter resistance can be constructed under-10 DEG C of low temperature; Easily maintenance management after construction; Not containing solvent, belong to environment-friendly material.
Brief description of the drawings
Fig. 1 is the preparation process figure of the uncured rubber asphalt waterproof coating that provides of the embodiment of the present invention.
Embodiment
In order to make object of the present invention, technical scheme and advantage clearer, below in conjunction with drawings and Examples, the present invention is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
The present invention is achieved in that the each component of a kind of uncured rubber asphalt waterproof coating and mass ratio thereof are: pitch 10%-15%, shoddy 5%-15%, tenderizer 24%-45%, high molecular polymer 5%-10%, specialist additive 4%-10%, auxiliary agent 0.05%-1%, filler 20%-30%.
Further, described pitch is to be selected from a kind of or its mixture of heavily handing in 90# pitch, 10# pitch.
Further, described shoddy is 60-80 object tire tread rubber powder.
Further, described tenderizer is naphthenic oil, aromatic hydrocarbon oil, subtracts a kind of or its several mixtures in third fractional oil.
Further, described high molecular polymer is a kind of or its several mixtures in SBS, SBR, SIS, SEBS, APP, APAO, POE.
Further, described specialist additive is a kind of or its mixture in polyamide hot, modified polyamide.
Further, described auxiliary agent is AClyn lower molecular weight ionomer.
Play the blend solubilizing agent effect of polymkeric substance, form IPN.IPN more can form the mixing of higher degree than simple mixing.Simple description be exactly, and a polymer molecule can be around the molecule of another polymkeric substance in melt stage, once cooling, be just fixed on that place.
Further, described filler is 400 order coarse whitings or 400 order talcum powder.
A kind of blending process of uncured rubber asphalt waterproof coating is as follows:
S101: asphalt heating to 140 DEG C is squeezed into stirred pot;
S102: add tenderizer, rubber powder, high molecular polymer, stir 30 minutes, temperature is raised to 160 DEG C;
S103: enter colloidal mill and grind both sides, temperature is raised to 190 DEG C, adds specialist additive, stirs 1 hour;
S104: add auxiliary agent while being cooled to 160～170 DEG C, stir 1 hour, add filler to stir 1 hour;
S105: discharging.
A kind of constructional method of uncured rubber asphalt waterproof coating is as follows:
Full scale construction is carried out at special-shaped position: the detail sections such as the nook of negative and positive angle, plane and facade are first brushed, and thickness is advisable with 2mm, and coiled material is cut into respective shapes enclose after finishing extra play, guarantees the Bulk coat thickness that is consistent;
Big area spraying application:
Step 1, treat that basal plane cleans out after, open heating batch can, in advance material is poured in batch can and heated, reach can spray 150 DEG C of state time until coating bulk temperature, uniformly spray with special coating machine, when spraying, can exchange different spray guns according to different design thicknesss, waterproof layer once shaped, thickness is 2mm;
Step 2, spray after certain area, before paving coiled material, adopted pin survey method to detect coat-thickness, if thickness is not up to standard or local needs strengthened, get some coating with trowel, filled in the manual mode of scraping that is coated with, spraying application should segmentation or district complete, 500-1000m
2be to construct in a region;
After step 3, spraying, cover in time waterproof roll, avoid dust too much in scene to be bonded in coating top layer and reduce the cohesiveness of coating and sealing coat or waterproof roll, after the complete sealing coat of paving or waterproof roll, can go up people and walk.
Uncured rubber asphalt waterproof coating in the embodiment of the present invention is to be produced by Jiangsu Jin Ming waterproof building material company limited, and by national building materials Industrial buildings water-proof material product quality supervision, inspection center is detected, and detected result is as shown in table 1.
Table 1
By reference to the accompanying drawings the specific embodiment of the present invention is described although above-mentioned; but not limiting the scope of the invention; one of ordinary skill in the art should be understood that; on the basis of technical scheme of the present invention, those skilled in the art do not need to pay various amendments that performing creative labour can make or distortion still within protection scope of the present invention.
Claims (10)
1. a uncured rubber asphalt waterproof coating, it is characterized in that, the described each component of uncured rubber asphalt waterproof coating and mass ratio are: pitch 10%-15%, shoddy 5%-15%, tenderizer 24%-45%, high molecular polymer 5%-10%, specialist additive 4%-10%, auxiliary agent 0.05%-1%, filler 20%-30%.
2. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described pitch is to be selected from a kind of or its mixture of heavily handing in 90# pitch, 10# pitch.
3. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described shoddy is 60-80 object tire tread rubber powder.
4. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described tenderizer is naphthenic oil, aromatic hydrocarbon oil, subtract a kind of or its several mixtures in third fractional oil.
5. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described high molecular polymer is a kind of or its several mixtures in SBS, SBR, SIS, SEBS, APP, APAO, POE.
6. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described specialist additive is a kind of or its mixture in polyamide hot, modified polyamide.
7. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described auxiliary agent is AClyn lower molecular weight ionomer.
8. uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, described filler is 400 order coarse whitings or 400 order talcum powder.
9. a uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, the blending process technique of this uncured rubber asphalt waterproof coating is as follows:
Step 1, asphalt heating to 140 DEG C is squeezed into stirred pot;
Step 2, add tenderizer, rubber powder, high molecular polymer, stir 30 minutes, temperature is raised to 160 DEG C;
Step 3, enter colloidal mill grind both sides, temperature is raised to 190 DEG C, adds specialist additive, stirs 1 hour;
Step 4, add auxiliary agent while being cooled to 160～170 DEG C, stir 1 hour, add filler to stir 1 hour;
Step 5, discharging.
10. a uncured rubber asphalt waterproof coating as claimed in claim 1, is characterized in that, the constructional method of this uncured rubber asphalt waterproof coating is as follows:
Full scale construction is carried out at special-shaped position: the nook detail section of negative and positive angle, plane and facade is first brushed, and thickness is 2mm, and coiled material is cut into respective shapes enclose after finishing extra play, guarantees the Bulk coat thickness that is consistent;
Big area spraying application:
Step 1, treat that basal plane cleans out after, open heating batch can, in advance material is poured in batch can and heated, reach can spray 150 DEG C of state time until coating bulk temperature, uniformly spray with spraying machine, when spraying, can exchange different spray guns according to different design thicknesss, waterproof layer once shaped, thickness is 2mm;
Step 2, spray after certain area, before paving coiled material, adopted pin survey method to detect coat-thickness, if thickness is not up to standard or local needs strengthened, get some coating with trowel, filled in the manual mode of scraping that is coated with, spraying application should segmentation or district complete, 500-1000m
2be to construct in a region;
After step 3, spraying, cover in time waterproof roll, avoid dust too much in scene to be bonded in coating top layer and reduce the cohesiveness of coating and sealing coat or waterproof roll, after the complete sealing coat of paving or waterproof roll, can go up people and walk.