CN104119470A - Preparation methods of modified acrylic resin for anticorrosion paints and copper surface anticorrosion paint - Google Patents
Preparation methods of modified acrylic resin for anticorrosion paints and copper surface anticorrosion paint Download PDFInfo
- Publication number
- CN104119470A CN104119470A CN201410325648.6A CN201410325648A CN104119470A CN 104119470 A CN104119470 A CN 104119470A CN 201410325648 A CN201410325648 A CN 201410325648A CN 104119470 A CN104119470 A CN 104119470A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- copper
- preparation
- copper surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Project | Index | Remarks |
Solid part | 58-62.0% | ? |
Viscosity | 30-60 second | Form pipe, 25 ℃ |
Acid number | 6-18 | ? |
Hydroxy radical content | 2.0-3.3% | By 100% solid, calculate |
Raw material | Weight (g) | Remarks |
Acrylic resin modified | 70 | Embodiment 1 preparation |
Flatting silica SYLOID ED50 | 6 | GRACE company produces |
Antisettling agent DeuRheo211 | 2 | ELEMENTIS produces |
Defoamer Defom5400 | 0.2 | ELEMENTIS produces |
Levelling Levaslip466 | 0.2 | ELEMENTIS produces |
1-Methoxy-2-propyl acetate | 5 | ? |
N-BUTYL ACETATE | 9 | ? |
Dimethylbenzene | 7.6 | Adjust viscosity |
Raw material | Weight (g) | Remarks |
Acrylic resin modified | 65 | Embodiment 1 preparation |
Flatting silica SYLOID ED50 | 6 | GRACE company produces |
Antisettling agent DeuRheo211 | 3 | ELEMENTIS produces |
Defoamer Defom5400 | 0.1 | ELEMENTIS produces |
Levelling Levaslip466 | 0.1 | ELEMENTIS produces |
1-Methoxy-2-propyl acetate | 6 | ? |
N-BUTYL ACETATE | 9 | ? |
Dimethylbenzene | 10.8 | Adjust viscosity |
Raw material | Weight (g) | Remarks |
Acrylic resin modified | 75 | Embodiment 1 preparation |
Flatting silica SYLOID ED50 | 6 | GRACE company produces |
Antisettling agent DeuRheo211 | 1 | ELEMENTIS produces |
Defoamer Defom5400 | 0.3 | ELEMENTIS produces |
Levelling Levaslip466 | 0.3 | ELEMENTIS produces |
1-Methoxy-2-propyl acetate | 3 | ? |
N-BUTYL ACETATE | 8 | ? |
Dimethylbenzene | 6.4 | Adjust viscosity |
Claims (7)
- One kind acrylic resin modified, it is characterized in that being made by A, B and tri-kinds of components of C, in weight part, each component raw material is as follows:
- 2. an acrylic resin modified preparation method as claimed in claim 1, it is characterized in that: first A component is placed in to reaction vessel and is heated to reflux, then B component is dropped in reaction vessel, drip off and keep refluxing at least 1h, finally C component is added to reaction vessel, insulation reaction is 1h at least, cooling discharge.
- 3. a utilization matte varnish for acrylic resin modified preparation as claimed in claim 1, is characterized in that being made by the raw material of following weight part:
- 4. the preparation method of matte varnish as claimed in claim 3, it is characterized in that: in whipping appts, first add acrylic resin modified and dimethylbenzene, under stirring, slowly add antisettling agent, be dispersed to homogeneous, add defoamer, stir, add flatting silica, flow agent, 1-Methoxy-2-propyl acetate and N-BUTYL ACETATE, stirring, be uniformly dispersed to fineness is less than 25 μ m, filters.
- 5. utilize the copper surface anticorrosion coating that as claimed in claim 3 prepared by matte varnish, it is characterized in that being made by the raw material of following weight part:80~120 parts of matte varnish;10~20 parts, solidifying agent;20~40 parts of thinners.
- 6. copper surface anticorrosion coating as claimed in claim 5, is characterized in that described thinner is comprised of the raw material of following weight part:45~55 parts of dimethylbenzene;27~42 parts of N-BUTYL ACETATEs;10~22 parts of 1-Methoxy-2-propyl acetates.
- 7. a preparation method for copper surface anticorrosion coating as described in claim 5 or 6, is characterized in that: matte varnish is mixed with solidifying agent, then add thinner to stir allotment evenly.