CN104109411A - Environment-friendly type waterborne online wet-blasting encarpus tile paint and preparation method thereof - Google Patents
Environment-friendly type waterborne online wet-blasting encarpus tile paint and preparation method thereof Download PDFInfo
- Publication number
- CN104109411A CN104109411A CN201410337138.0A CN201410337138A CN104109411A CN 104109411 A CN104109411 A CN 104109411A CN 201410337138 A CN201410337138 A CN 201410337138A CN 104109411 A CN104109411 A CN 104109411A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- water
- pigment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly type waterborne online wet-blasting encarpus tile paint and a preparation method thereof. The product is prepared from the following raw materials in parts by weight: 30-40 parts of water, 0.5-1.5 parts of dispersing agent, 0.05-0.25 part of controlled-sudsing foam inhibitor, 5-15 parts of pigments, 0-5 parts of filler, 0-3 parts of silicon-containing coupling agent, 0-10 parts of silicon emulsion, 50-100 parts of emulsion, 0.1-0.18 part of fungicide and 0-1.5 parts of coalescing agents. According to the product, water is taken as a solvent, various components are added into water in sequence and then stirring and uniform mixing are performed. As water is taken ad the solvent, the product disclosed by the invention is nontoxic and tasteless, non-combustible and un-explosive, can be used for completely substituting online wet-blasting solvent type acrylic resin which is still in use at home at present and reducing emission of a great deal of poisonous and harmful diluents and has great environment-friendly benefits and social benefits; moreover, the product is very safe in each link such as production and transportation, storage and use.
Description
Technical field
The present invention relates to coating material production technical field, specifically encaustic tile coating of a kind of environment-friendly type aqueous online wet shot and preparation method thereof.
Background technology
At present, the solvent-borne type of the online wet shot of cement encaustic tile is all transparent acrylic resin mostly, and the water soluble acrylic acid of coloured or transparent online wet shot seldom, is mainly that former water-based encarpus tile coating can not solve a wet shot watt body and returns and subtract and the problem such as watt look fresh-keeping.Therefore at present domestic each big-and-middle-sized encaustic tile factory still remains solvent type acrylic resin and solvent-borne type encaustic tile coating at the online wet shot using, these solvent-borne type encaustic tile coatings are used toxic volatile thinner in a large number, the thinner that these are poisonous and other additive easy firings, easily initiation fire even explodes, and causes the processing of cement encaustic tile to have certain risk.Therefore just need to develop a kind of do not have toxicity, also can the not burn water-based encarpus tile coating of the online wet shot that even explodes, eliminate the potential safety hazard in production process in conjunction with practical situation, to meet the needs of modern production.
Summary of the invention
The object of the present invention is to provide encaustic tile coating of a kind of environment-friendly type aqueous online wet shot and preparation method thereof, to solve the problem proposing in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A kind of encaustic tile coating of environment-friendly type aqueous online wet shot, proportioning raw materials by following weight part forms: 30～40 parts, water, 0～1.5 part of dispersion agent, 0.05～0.25 part of foam control suds suppressor, 5～15 parts of pigment, 0～5 part of filler, 0～3 part of silicon-containing coupling reagents, 0～10 part of silicon emulsion, 50～100 parts of emulsions, 0.1～0.18 part, sterilant, 0～1.5 part of film coalescence aid.
As the further scheme of the present invention: described pigment is mineral dye or pigment dyestuff.
As the further scheme of the present invention: described mineral dye is iron oxide pigment or titanium white powder pigment or charcoal blacks, described pigment dyestuff is the blue or green orchid of phthalein or permanent violet etc., described filler is process white, mica powder or coarse whiting salt, and described film coalescence aid is Lauryl Alcohol ester or composite film coalescence aid.
A preparation method for the encaustic tile coating of environment-friendly type aqueous online wet shot, concrete steps are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add again pigment, filler and film coalescence aid, and stir 5～45min; (3) add again cavity suds suppressor, and slowly stir 3～15min; (4) finally add successively emulsion, silicon-containing coupling reagents and silicon emulsion and be slowly stirred to abundant mixing, churning time is 40～50min.
Compared with prior art, the invention has the beneficial effects as follows:
(1) take water completely as solvent, can substitute at present domestic each big-and-middle-sized encaustic tile factory completely and, still at the solvent type acrylic resin of the online wet shot using, both save ample resources, be beneficial to again enterprise employee health, thoroughly eliminate the discharge of poisonous thinner, there is huge environmental benefit and social benefit;
(2) the completely online wet shot of this product, i.e. can be used this product paint spay-coating during the firm moulding of cement encaustic tile, can replace the solvent type acrylic resin of the online wet shot of current cement encaustic tile completely;
(3) can meet the effect of transparent wet shot or coloured wet shot completely; Coloured wet shot can also settle at one go.
(4) this product is nonpoisonous and tasteless, does not fire not quick-friedly, and the links such as production, transportation, storage, use are safety and environmental protection all.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
An encaustic tile coating for environment-friendly type aqueous online wet shot, is formed by the proportioning raw materials of following weight part: 30 parts, water, 0.5 part of dispersion agent, 0.05 part of foam control suds suppressor, 5 parts of iron oxide pigments, 50 parts of emulsions, 0.1～0.18 part, sterilant.
The preparation concrete steps of above-mentioned encaustic tile coating are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add again iron oxide pigment, and stir 30min; (3) add again cavity suds suppressor, and slowly stir 10min; (4) finally add emulsion, and be slowly stirred to abundant mixing, churning time is 40min.
Embodiment 2
A kind of encaustic tile coating of environment-friendly type aqueous online wet shot, proportioning raw materials by following weight part forms: 35 parts, water, 1.0 parts of dispersion agents, 0.15 part of foam control suds suppressor, 10 parts of iron oxide pigments, 2.5 parts of mica powders, 1.5 parts of silicon-containing coupling reagents, 5 parts of silicon emulsions, 75 parts of emulsions, 0.15 part, sterilant, 0.75 part of Lauryl Alcohol ester.
The preparation concrete steps of above-mentioned encaustic tile coating are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add successively again iron oxide pigment, mica powder and Lauryl Alcohol ester, and stir 45min; (3) add again cavity suds suppressor, and slowly stir 15min; (4) finally add successively emulsion, silicon-containing coupling reagents and silicon emulsion, and be slowly stirred to abundant mixing, churning time is 50min.
Embodiment 3
A kind of encaustic tile coating of environment-friendly type aqueous online wet shot, proportioning raw materials by following weight part forms: 40 parts, water, 1.5 parts of dispersion agents, 0.25 part of foam control suds suppressor, 15 parts of titanium white powder pigments, 5 parts of mica powders, 3 parts of silicon-containing coupling reagents, 10 parts of silicon emulsions, 100 parts of emulsions, 0.18 part, sterilant, 1.5 parts of Lauryl Alcohol esters.
The concrete steps of the preparation of above-mentioned encaustic tile coating are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add successively again titanium white powder pigment, mica powder and Lauryl Alcohol ester, and fully stir 45min; (3) add again cavity suds suppressor, and slowly stir 15min; (4) finally add successively emulsion, silicon-containing coupling reagents and silicon emulsion and be slowly stirred to abundant mixing, churning time is 50min.
Embodiment 4(transparent varnish)
A kind of encaustic tile coating of environment-friendly type aqueous online wet shot, proportioning raw materials by following weight part forms: 40 parts, water, 0 part of dispersion agent, 0.25 part of foam control suds suppressor, 0 part of titanium white powder pigment, 0 part of mica powder, 3 parts of silicon-containing coupling reagents, 10 parts of silicon emulsions, 100 parts of emulsions, 0.18 part, sterilant, 0 part of Lauryl Alcohol ester.
The concrete steps of the preparation of above-mentioned encaustic tile coating are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add successively emulsion, silicon-containing coupling reagents and silicon emulsion and be slowly stirred to abundant mixing, churning time is 50min.
In the raw material of above-described embodiment, dispersion agent is the mixture of a kind of dispersion agent or multiple dispersion agent; Pigment can be a kind of pigment or multiple pigment composition; Thickening material is the mixture of a kind of thickening material or multiple thickening material; Film coalescence aid is a kind of film coalescence aid or multiple film coalescence aid mixture, and emulsion is the mixture of a kind of emulsion or multiple emulsion.
Use encaustic tile coating of the present invention, the cooperation consumption paint amount of every cement tile (420mmX330mm) is roughly varnish 10～16g, and colored paint 12～16g, can reach desirable spraying effect.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the situation that not deviating from spirit of the present invention or essential characteristic, can realize the present invention with other specific form.Therefore, no matter from which point, all should regard embodiment as exemplary, and be nonrestrictive, scope of the present invention is limited by claims rather than above-mentioned explanation, is therefore intended to include in the present invention dropping on the implication that is equal to important document of claim and all changes in scope.
Claims (4)
1. the encaustic tile coating of an environment-friendly type aqueous online wet shot, it is characterized in that, by the proportioning raw materials of following weight part, formed: 30～40 parts, water, 0～1.5 part of dispersion agent, 0.05～0.25 part of foam control suds suppressor, 5～15 parts of pigment, 0～5 part of filler, 0～3 part of silicon-containing coupling reagents, 0～10 part of silicon emulsion, 50～100 parts of emulsions, 0.1～0.18 part, sterilant, 0～1.5 part of film coalescence aid.
2. the encaustic tile coating of environment-friendly type aqueous online wet shot according to claim 1, is characterized in that, described pigment is mineral dye or pigment dyestuff.
3. the encaustic tile coating of environment-friendly type aqueous online wet shot according to claim 2, it is characterized in that, described mineral dye is iron oxide pigment or titanium white powder pigment or charcoal blacks etc., described pigment dyestuff is the blue or green orchid of phthalein or permanent violet etc., described filler is process white, mica powder or coarse whiting salt, and described film coalescence aid is Lauryl Alcohol ester or composite film coalescence aid.
4. a preparation method for the encaustic tile coating of the environment-friendly type aqueous online wet shot as described in arbitrary claim 1～3, is characterized in that, concrete steps are as follows: (1) take water as solvent, first dispersion agent, sterilant is dispersed in water, and stirs; (2) add again pigment, filler and film coalescence aid, and stir or grind 5～45min; (3) add again cavity suds suppressor, and slowly stir 3～15min; (4) finally add successively emulsion, silicon-containing coupling reagents and silicon emulsion and be slowly stirred to abundant mixing, churning time is 40～50min.