CN104098959A - Process method for manufacturing paint through waste plastic - Google Patents
Process method for manufacturing paint through waste plastic Download PDFInfo
- Publication number
- CN104098959A CN104098959A CN201410361736.1A CN201410361736A CN104098959A CN 104098959 A CN104098959 A CN 104098959A CN 201410361736 A CN201410361736 A CN 201410361736A CN 104098959 A CN104098959 A CN 104098959A
- Authority
- CN
- China
- Prior art keywords
- container
- added
- waste
- certain amount
- weight parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing paint through waste plastic and relates to the field of paint manufacturing technology. The method comprises the following steps: A, a certain amount of cleaned waste plastic is added into a container A, then a certain amount of benzene is added into the container A, and a stirring rod is used for stirring fully until the waste plastic is dissolved completely; B, a certain amount of xylene is added into a container B, then a certain amount of gasoline is added into the container B and the xylene and the gasoline are mixed uniformly and fully; C, solutions obtained in the steps A and B are poured into a large container C to be mixed uniformly, a certain amount of rosin solution is added, and a certain amount of oil-soluble pigment is added after full dissolution, and uniform mixing is performed; D, a certain amount of zinc stearate is added finally, and the mixture is poured into a filtering device for filtering after full mixing, so that the paint is obtained. The method provided by the invention can solve the problem of recycling of waste plastic.
Description
Technical field
The present invention relates to paint manufacturing technology field, especially a kind of processing method of utilizing waste or used plastics to make paint.
Background technology
Plastics are as one of three large synthetic materialss, oneself is widely used in the industry-by-industry of China, because plastics are materials of a kind of hard degradation, its chemical stability is fine, along with the continuous increase of plastics consumption, waste plastic is also on the increase, and oneself has caused serious pollution and harm to the mankind's living environment waste or used plastics, oneself reaches tens million of tons own this pollutant through existing of China, and increases in the speed with annual approximately 6,000,000 tons; The raw material of plastics is oil and natural gas, is all non-renewable resource, and in recent years, effective mine reserves of oil declines rapidly, and the recycling of waste or used plastics, as the measure of a save energy, protection of the environment, generally comes into one's own.At present, waste or used plastics processing is three kinds of modes substantially: one, landfill disposal; Two, burning disposal; Three, evaporating method; Also do not find that there is the method for making raw material making paint of waste or used plastics.
Summary of the invention
The object of this invention is to provide a kind of processing method of utilizing waste or used plastics to make paint, it can not only can solve the problem that waste or used plastics recycles, and can also reduce the production cost of paint.
In order to address the above problem, the technical solution used in the present invention is:
This processing method of utilizing waste or used plastics to make paint, comprises the following steps:
A, will join in container through 40 ~ 45 weight part waste or used plastics of clean, then the benzene that 35 ~ 40 weight parts are housed is added to this container, fully stir by stirring rod, until waste or used plastics all dissolves;
B, pack the dimethylbenzene of 40 ~ 45 weight parts into another container, then in this container, add the gasoline of 10 ~ 20 weight parts, fully mix;
After C, the solution that A step, B step are obtained are poured a large container into and mixed, then add the rosin solution of 15 ~ 20 weight parts, after fully dissolving, add the oil color of 10 ~ 15 weight parts to mix;
D, finally add the Zinic stearas of 0.5 ~ 0.8 weight part, after fully mixing, pour filtration unit into and filter, painted.
Further: described waste or used plastics is any in polyvinyl chloride or polyethylene or polypropylene or nylon or ABS engineering plastics.
Owing to having adopted technique scheme, the present invention compared with prior art has following beneficial effect:
1, raw materials cost of the present invention is low, only account for ordinary process method produce oil paint this 1/3rd;
2, equipment required for the present invention is less, and technological process is simple.
Embodiment
Below in conjunction with embodiment, the present invention is further described:
This processing method of utilizing waste or used plastics to make paint,
One, formula (with listed as parts by weight): waste or used plastics is taking polyethylene as example:
40 ~ 45 parts of polyethylene, 35 ~ 40 parts of benzene, 40 ~ 45 parts of dimethylbenzene, 10 ~ 20 parts, gasoline, 5 ~ 20 parts of 1 rosin, 10 ~ 15 parts of oil colors, 0.5 ~ 0.8 part of zinc stearate.
Two, making method
A, waste or used plastics is carried out to sorting, then it is clean that the polyethylene sub-electing is carried out to clean, then the polyethylene airing of cleaning is removed to moisture, the polyethylene that weighs up 40 ~ 45 weight parts joins in container first; The benzene that takes again 35 ~ 40 weight parts adds this container first, fully stirs by stirring rod, until polyethylene all dissolves, it is gluey that the liquid in container is now;
B, the dimethylbenzene that takes 40 ~ 45 weight parts pack in another container second, then in this container, add the gasoline of 10 ~ 20 weight parts, fully mix;
After C, the solution that A step, B step are obtained are poured into and mixed in a large container third, then add the rosin solution of 15 ~ 20 weight parts, after fully dissolving, add again the oil color of 10 ~ 15 weight parts to mix;
D, finally add the Zinic stearas of 0.5 ~ 0.8 weight part, after fully mixing, pour filtration unit into and filter, painted.
Waste or used plastics of the present invention can also be with any in polyvinyl chloride or polypropylene or nylon or ABS engineering plastics.
Claims (2)
1. utilize waste or used plastics to make a processing method for paint, it is characterized in that: comprise the following steps:
A, will join in container through 40 ~ 45 weight part waste or used plastics of clean, then the benzene that 35 ~ 40 weight parts are housed is added to this container, fully stir by stirring rod, until waste or used plastics all dissolves;
B, pack the dimethylbenzene of 40 ~ 45 weight parts into another container, then in this container, add the gasoline of 10 ~ 20 weight parts, fully mix;
After C, the solution that A step, B step are obtained are poured a large container into and mixed, then add the rosin solution of 15 ~ 20 weight parts, after fully dissolving, add the oil color of 10 ~ 15 weight parts to mix;
D, finally add the Zinic stearas of 0.5 ~ 0.8 weight part, after fully mixing, pour filtration unit into and filter, painted.
2. the processing method of utilizing waste or used plastics to make paint according to claim 1, is characterized in that: described waste or used plastics is any in polyvinyl chloride or polyethylene or polypropylene or nylon or ABS engineering plastics.