CN104097240A - Timber decoration material and preparing method thereof - Google Patents
Timber decoration material and preparing method thereof Download PDFInfo
- Publication number
- CN104097240A CN104097240A CN201410294122.6A CN201410294122A CN104097240A CN 104097240 A CN104097240 A CN 104097240A CN 201410294122 A CN201410294122 A CN 201410294122A CN 104097240 A CN104097240 A CN 104097240A
- Authority
- CN
- China
- Prior art keywords
- wood
- cork
- bending
- timber
- high frequency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a timber decoration material, comprising at least two timber layers; the first timber layer is softwood; the second timber layer is bent wood; the softwood and the bent wood are connected and adhered. Correspondingly, the invention also discloses a method for preparing the timber decoration material. The method comprises the steps of placing a softwood slice onto the bent wood, and injecting glue between the softwood slice and the bent wood to obtain a primary finished product; placing the primary finished product into a high frequency hot press and laminating the softwood slice onto the bent wood by the high frequency hot press to obtain a finished product. The softwood and the bent wood are combined for the first time to form a novel timber decoration material, and the timber formed by combining the softwood and the bent wood is good in quality and is not easily broken during bending.
Description
Technical field
The present invention relates to decorative materials technology, relate in particular to a kind of decorative wood material and preparation method thereof.
Background technology
Cork, is commonly called as cork, cork, the crust product of the very flourishing seeds of plant phellem layer, the surface protection tissue after stem and root diameter increment.General cork article has: 1. natural cork goods: through boiling, softening, dry after, directly cut, the method such as punching press, rotary cut makes finished product as plug, pad, handicraft etc.2. cure cork article: the surplus material of natural cork goods recompresses moulding through pulverizing, in the baker of 260～316 DEG C, bake 1～1.5 hour, after letting cool, for low temperature is heat insulation with cork brick, also can use the manufacture of superheated steam heating means.3. cementing cork article: cork particulate and powder, adhesive (as resin, rubber) are pressed into cementing cork article after mixing, and as floor surfacing, sound panel, thermal insulation board etc., are widely used in the aspects such as space flight, boats and ships, machinery, building.4. cork-rubber goods: taking cork powder as raw material, rubber consumption approximately 70% is made.There is the compressibility of cork and the elasticity of rubber, mainly, as low, middle pressure static sealing materials of high-quality such as engines, also can be used as antidetonation, sound insulation, friction material etc.
But existing cork is bending easy to be broken, be not well positioned to meet the performance requirement of ornament materials.
In prior art not by the precedent of cork 1 and bending-wood 2 combinations.Compared with prior art, the present invention by cork 1 and bending-wood 2 combinations, forms a kind of novel decorative wood material first, provides a kind of new selection to consumer.And described cork 1 and bending-wood 2 are in conjunction with the timber forming, its quality is good, non-friable, has overcome the shortcoming of cork.
In above-mentioned arbitrary embodiment, described cork 1 and described bending-wood 2 are preferably by glue bonding connection.Better, described glue is Polyvinylacetate Emulsion Adhesive.Adopt Polyvinylacetate Emulsion Adhesive, can be by cork 1 and bending-wood 2 secure bond, difficult drop-off.
Further, described cork 1 and described bending-wood 2 are compounded to form described decorative wood material by hot press with high frequency.That is to say, it adopts hot press with high frequency to process processing can obtain finished product, and therefore, the equipment that decorative wood material of the present invention adopts is simple, and exploitativeness is strong, is suitable for large application scope.Wherein, the power of described hot press with high frequency is 10-100kw.Preferably, the power of described hot press with high frequency is 20-26 kw.
Accordingly, referring to Fig. 4, the present invention also provides a kind of method of preparing above-mentioned decorative wood material, comprising:
S101, is placed in cork section on bending-wood, and injects glue between cork section and bending-wood, obtains just finished product.
Wherein, the thickness of cork section can be 0.8-80mm, concrete, the thickness of described cork section is 0.8mm, 1mm, 2mm, 3mm, 5mm, 7mm, 10mm, 15mm, 20mm, 25mm, 30mm, 35mm, 40mm, 45mm, 50mm, 60mm, 70mm, 78mm, but is not limited to this.
Described glue is preferably Polyvinylacetate Emulsion Adhesive, but is not limited to this.Adopt Polyvinylacetate Emulsion Adhesive, can be by cork and bending-wood secure bond, difficult drop-off.
S102, puts into hot press with high frequency by first finished product, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Wherein, the power of described hot press with high frequency is 10-100kw; The temperature of described hot press with high frequency is 35-200 DEG C.
Preferably, the power of described hot press with high frequency is 20-26 kw; The temperature of described hot press with high frequency is 60-145 DEG C.
As the detailed description of the invention of hot press with high frequency, the power of described hot press with high frequency can be 20 kw, 22 kw, 24 kw, 25 kw, 26 kw, 30 kw, 32 kw, 35 kw, 42 kw, but is not limited to this;
The temperature of described hot press with high frequency can be 45 DEG C, 55 DEG C, 65 DEG C, 70 DEG C, 75 DEG C, 80 DEG C, 85 DEG C, 90 DEG C, 95 DEG C, 100 DEG C, 102 DEG C, 105 DEG C, 108 DEG C, 110 DEG C, 115 DEG C, 120 DEG C, 122 DEG C, 125 DEG C, 128 DEG C, 132 DEG C, 135 DEG C, 140 DEG C, 145 DEG C, but is not limited to this.
Just finished product is put into hot press with high frequency, within 1-5 minute under the effect of high-frequency heating, can complete solidifying of glue, makes cork section firmly cover and be added on bending-wood.
It should be noted that, the described heatronic time can determine according to the demand of the character of actual timber and product, can be specifically 1.5 minutes, 2 minutes, 2.5 minutes, 3 minutes, 3.5 minutes, 4 minutes, 4.5 minutes etc.
Further set forth the preparation method of decorative wood material of the present invention below with specific embodiment
Summary of the invention
Technical problem to be solved by this invention is, non-friable decorative wood material of a kind of bending and preparation method thereof is provided.
In order to solve the problems of the technologies described above, the invention provides a kind of decorative wood material, at least comprise two-layer timber, ground floor timber is cork, second layer timber is bending-wood, described cork and described bending-wood bonding connection; Described cork is located at the top of described bending-wood.
As the improvement of such scheme, described timber is made up of multilayer timber, and wherein, the timber of ground floor is cork, and the timber of other except ground floor layer is bending-wood; Described cork is located at the top of described bending-wood.
As the improvement of such scheme, described timber is made up of two-layer timber, and the timber on upper strata is cork, and the timber of lower floor is bending-wood.
As the improvement of such scheme, described cork and described bending-wood are by glue bonding connection.
As the improvement of such scheme, described glue is Polyvinylacetate Emulsion Adhesive.
Accordingly, the present invention also provides a kind of method of preparing above-mentioned decorative wood material, comprising:
Cork section is placed on bending-wood, and injects glue between cork section and bending-wood, obtain just finished product;
First finished product is put into hot press with high frequency, by high-frequency heating, cork section is covered and be added on bending-wood, obtain finished product.
As the improvement of such scheme, the power of described hot press with high frequency is 10-100kw.
As the improvement of such scheme, the power of described hot press with high frequency is 20-26kw.
As the improvement of such scheme, the temperature of described hot press with high frequency is 35-200 DEG C.
As the improvement of such scheme, described glue is Polyvinylacetate Emulsion Adhesive.
Implement the present invention, there is following beneficial effect:
The invention provides a kind of decorative wood material, at least comprise two-layer timber, ground floor timber is cork, and second layer timber is bending-wood, cork and bending-wood bonding connection.The present invention is by covering cork on bending-wood, and bending-wood provides support to cork, and like this, cork is just non-friable in the time of bending, can meet well the performance requirement of ornament materials.
Compared with prior art, the present invention, first by cork and bending-wood combination, forms a kind of novel decorative wood material, provides a kind of new selection to consumer.And described cork and bending-wood are in conjunction with the timber forming, its quality is good, non-friable, has overcome the shortcoming of cork.
Accordingly, the invention provides a kind of preparation method of decorative wood material, comprise cork section is placed on bending-wood, and inject glue between cork section and bending-wood, obtain just finished product; First finished product is put into hot press with high frequency, by high-frequency heating, cork section is covered and be added on bending-wood, obtain finished product.That is to say, it adopts hot press with high frequency to process to process and can obtain finished product, therefore, prepares that the technique that decorative wood material of the present invention adopts is simple, equipment is simple, and exploitativeness is strong, is suitable for large application scope.
Brief description of the drawings
Fig. 1 is the schematic diagram of a kind of decorative wood material one embodiment of the present invention;
Fig. 2 is the schematic diagram of the another embodiment of a kind of decorative wood material of the present invention;
Fig. 3 is the schematic diagram of a kind of another embodiment of decorative wood material of the present invention;
Fig. 4 is the preparation method's of a kind of decorative wood material of the present invention flow chart.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, below in conjunction with accompanying drawing, the present invention is described in further detail.
Existing cork is bending easy to be broken, be not well positioned to meet the performance requirement of ornament materials, for solving the frangible technical problem of existing cork, the invention provides a kind of decorative wood material, at least comprise two-layer timber, ground floor timber is cork, and second layer timber is bending-wood, described cork and described bending-wood bonding connection.Described cork is located at the top of described bending-wood.
Wherein, described cork refers to by cork particulate and powder, adhesive (as resin, rubber) and is pressed into cementing cork article after mixing.
Described bending-wood refer to by usual wood be converted into curve or other anything, the mode of main making is that the wooden skin of multilayer is put into mould, using glue as adhesive, and multiple-layer stacked, the drawing method that adopts HTHP, makes wooden skin bend to the radian that designer wants.Material mainly uses material to have Manchurian ash, birch, beech, poplar of toughness etc. as inner core material, and surface can be in conjunction with the relatively good Manchurian ash of decorative pattern, birch, beech etc. as exterior trim.
Described decorative wood material has numerous embodiments, below in conjunction with Fig. 1-3, is further elaborated with specific embodiment:
Referring to Fig. 1, Fig. 1 provides an a kind of embodiment of decorative wood material, and described timber is made up of multilayer timber, wherein, the timber of ground floor is cork 1, and the timber of other except ground floor layer is bending-wood 2, and described cork 1 is located at the top of described bending-wood 2.
Referring to Fig. 2, Fig. 2 provides a kind of another embodiment of decorative wood material, and described timber is made up of two-layer timber, and the timber on upper strata is cork 1, and the timber of lower floor is bending-wood 2.
Referring to Fig. 3, Fig. 3 provides another embodiment of a kind of decorative wood material, and described timber is made up of multilayer timber, and wherein, the timber of ground floor is cork 1, and the second layer is bending-wood 2, and the timber of other except first and second layer layer is common wood 3.Wherein, the cork 1 of ground floor is located at the top.
It should be noted that, common wood 3 can be selected other any timber except cork, bending-wood.
The present invention is by cork 1 is covered on bending-wood 2, and bending-wood 2 provides support to cork 1, and like this, cork 1 is just non-friable in the time of bending, can meet well the performance requirement of ornament materials.
Embodiment 1
Choose cork section and the bending-wood of 1mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 26W, and temperature is 75 DEG C, and the processing time is 3min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 2
Choose cork section and the bending-wood of 10mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 24W, and temperature is 85 DEG C, and the processing time is 5min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 3
Choose cork section and the bending-wood of 15mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 25W, and temperature is 90 DEG C, and the processing time is 2.5min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 4
Choose cork section and the bending-wood of 20mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 28W, and temperature is 100 DEG C, and the processing time is 2min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 5
Choose cork section and the bending-wood of 30mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 35W, and temperature is 75 DEG C, and the processing time is 4min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 6
Choose cork section and the bending-wood of 40mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 20W, and temperature is 120 DEG C, and the processing time is 3min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 7
Choose cork section and the bending-wood of 50mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 22W, and temperature is 150 DEG C, and the processing time is 1min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
Embodiment 8
Choose cork section and the bending-wood of 80mm, reduce according to actual needs size, and cork section is placed on bending-wood, between cork section and bending-wood, inject Polyvinylacetate Emulsion Adhesive simultaneously, obtain head product;
Head product is placed in and puts into hot press with high frequency, and the power of hot press with high frequency is 26W, and temperature is 200 DEG C, and the processing time is 2min, by high-frequency heating, cork section is covered and is added on bending-wood, obtains finished product.
To sum up, the invention provides a kind of preparation method of decorative wood material, it utilizes High frequency heating technology, cork section is placed on bending-wood, and injects glue between cork section and bending-wood, obtains just finished product; First finished product is put into hot press with high frequency, by high-frequency heating, cork section is covered and be added on bending-wood, obtain finished product.That is to say, it adopts hot press with high frequency to process to process and can obtain finished product, therefore, prepares that the technique that decorative wood material of the present invention adopts is simple, equipment is simple, and exploitativeness is strong, is suitable for large application scope.
Above disclosed is only optimal way of the present invention, certainly can not limit with this interest field of the present invention, therefore the equivalent variations of doing according to the claims in the present invention, or some improvements and modifications of doing under the premise without departing from the principles of the invention, still belong to the scope that the present invention is contained.
Claims (10)
1. a decorative wood material, at least comprises two-layer timber, it is characterized in that, ground floor timber is cork, and second layer timber is bending-wood, described cork and described bending-wood bonding connection;
Described cork is located at the top of described bending-wood.
2. decorative wood material as claimed in claim 1, is characterized in that, described timber is made up of multilayer timber, and wherein, the timber of ground floor is cork, and the timber of other except ground floor layer is bending-wood;
Described cork is located at the top of described bending-wood.
3. decorative wood material as claimed in claim 1, is characterized in that, described timber is made up of two-layer timber, and the timber on upper strata is cork, and the timber of lower floor is bending-wood.
4. the decorative wood material as described in claim 1-3 any one, is characterized in that, described cork and described bending-wood are by glue bonding connection.
5. decorative wood material as claimed in claim 4, is characterized in that, described glue is Polyvinylacetate Emulsion Adhesive.
6. a method of preparing the decorative wood material described in claim 1-5 any one, is characterized in that, comprising:
Cork section is placed on bending-wood, and injects glue between cork section and bending-wood, obtain just finished product;
First finished product is put into hot press with high frequency, by high-frequency heating, cork section is covered and be added on bending-wood, obtain finished product.
7. the preparation method of decorative wood material as claimed in claim 6, is characterized in that, the power of described hot press with high frequency is 10-100kw.
8. the preparation method of decorative wood material as claimed in claim 7, is characterized in that, the power of described hot press with high frequency is 20-26 kw.
9. the preparation method of decorative wood material as claimed in claim 6, is characterized in that, the temperature of described hot press with high frequency is 35-200 DEG C.
10. the preparation method of decorative wood material as claimed in claim 6, is characterized in that, described glue is Polyvinylacetate Emulsion Adhesive.