A kind of aquaculture private cable
Technical field
The present invention relates to a kind of cable, particularly relate to a kind of aquaculture private cable being applied to the relevant place of sea water.
Background technology
Cable application is in every field, and the cable of the cable, particularly aquaculture for sea water association area, just require that cable has the resistance to salt water of excellence, thermostability, ozone resistance, additionally must there is the elasticity of excellence, resistance to pull, it is ensured that be not damaged by when fishing boat impacts or stretches being subject to.
And currently without producing the cable of specialty for culture fishery, major part user directly adopts general three-core cable for aquaculture, its insulation adopts a small amount of ethylene propylene diene rubber to be used for insulating barrier after mixing with chlorinated polyethylene mostly, restrictive coating then all adopts chlorinated polyethylene to make, although such cable weatherability is also good, but because chlorinated polyethylene polarity is relatively big, in use water suction is serious, and its poor flexibility, so service life is shorter.
Summary of the invention
It is an object of the invention to overcome the defect of prior art, it is provided that a kind of aquaculture private cable being specifically designed for aquaculture requirement.
For achieving the above object, the present invention proposes following technical scheme:
A kind of aquaculture private cable, including sheath and be located at the steel cable within described sheath and complex conduction core, steel wire rope sheath it is coated with outside described steel wire rope, being coated with insulating barrier, described sheath and steel wire rope sheath outside described conductor wire core is that EP rubbers is by EPR, vulcanizing agent, reinforcing agent, filler, age resistor, softening agent and Pb3O4Being proportionally that 100: 3~4: 50~60: 50~60: 3~4: 8~10: 3~5 proportionings prepare, described insulating barrier is that EP rubbers is by EPDM, vulcanizing agent, age resistor, 2280 paraffin oil, modified potter's clay, Pulvis Talci and Pb3O4It is proportionally that 100: 3~4: 2~3: 6~10: 80~90: 50~60: 3~6 proportionings prepare.
Described steel wire rope is the stranded zinc-coated wire of 1*19, and diameter of section is 1.5~2.0mm, and pulling apart pulling force is 1.27~3.82KN.
Described vulcanizing agent is DCP or TAIC.
Reinforcing agent in described sheath and steel wire rope sheath is white carbon black 550 or strong prestige powder.
Filler in described sheath and steel wire rope sheath is modified potter's clay or Pulvis Talci.
In described insulating barrier, age resistor is RD age resistor or MB age resistor.
In described sheath and steel wire rope sheath, age resistor is RD age resistor or MB age resistor or paraffin.
In described sheath and steel wire rope sheath, softening agent is 2280 paraffin oil or di-n-octyl sebacate.
Compared with prior art; a kind of aquaculture private cable that the present invention discloses; one is added with the steel wire rope that can pull in the middle of conductor wire core; ensure that what aquaculture cable can be random in laying or other processes pulls without damaging conductor wire core; insulating barrier and sheath simultaneously; all adopt EP rubbers as base material; ensure that material can have the weather resistance of excellence; nonpolar EP rubbers is few with water suction in contact with sea water process; water-swellable coefficient is very little, it is possible to ensure insulating properties in use and the protective value to cable.
Accompanying drawing explanation
Fig. 1 is the structural representation of aquaculture private cable of the present invention.
Detailed description of the invention
Below in conjunction with the accompanying drawing of the present invention, the technical scheme of the embodiment of the present invention is carried out clear, complete description.
As shown in Figure 1, disclosed a kind of aquaculture private cable, including sheath 1 and be located at the steel cable 2 within described sheath 1 and complex conduction core 3, described steel wire rope 2 is outside is coated with steel wire rope sheath 4, and described conductor wire core 3 is outside is coated with insulating barrier 5, described sheath 1 and steel wire rope sheath 4 are that EP rubbers is by EPR, vulcanizing agent, reinforcing agent, filler, age resistor, softening agent and Pb3O4Being proportionally that 100: 3~4: 50~60: 50~60: 3~4: 8~10: 3~5 proportionings prepare, described insulating barrier 5 is that EP rubbers is by EPDM, vulcanizing agent, age resistor, 2280 paraffin oil, modified potter's clay, Pulvis Talci and Pb3O4It is proportionally that 100: 3~4: 2~3: 6~10: 80~90: 50~60: 3~6 proportionings prepare.
Wherein, the diameter of section of described conductor wire core 3 is 1.5~6mm, and described steel wire rope 2 is the stranded zinc-coated wire of 1*19, and diameter of section is 1.5~2.0mm, and the pulling force that fractures is 1.27~3.82KN.
Described vulcanizing agent is DCP or TAIC.
Reinforcing agent in described sheath 1 and steel wire rope sheath 4 is white carbon black 550 or strong prestige powder, and filler is modified potter's clay or Pulvis Talci, and age resistor is RD age resistor or MB age resistor or paraffin, and softening agent is 2280 paraffin oil or di-n-octyl sebacate.
In described insulating barrier 5, age resistor is RD age resistor or MB age resistor.
The technology contents of the present invention and technical characteristic have revealed that as above; but those of ordinary skill in the art are still potentially based on teachings of the present invention and announcement and do all replacements without departing substantially from spirit of the present invention and modification; therefore; scope should be not limited to the content that embodiment is disclosed; and the various replacement without departing substantially from the present invention and modification should be included, and contained by present patent application claim.