CN1040887A - Fuse quartz sand filler - Google Patents
Fuse quartz sand filler Download PDFInfo
- Publication number
- CN1040887A CN1040887A CN 88106230 CN88106230A CN1040887A CN 1040887 A CN1040887 A CN 1040887A CN 88106230 CN88106230 CN 88106230 CN 88106230 A CN88106230 A CN 88106230A CN 1040887 A CN1040887 A CN 1040887A
- Authority
- CN
- China
- Prior art keywords
- quartz sand
- filler
- fuse
- orders
- arc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of quartz sand filler that is used for fuse is characterized in that dioxide-containing silica between 98.2%～99.6%, and ferric oxide content is between 0.02%～0.15%, and the order number is 20 orders～60 orders, and the dihedral coefficient is less than 1.30.Adopt the fuse of this filler, have good breaking capacity (500V, 120KA), lower I
2(mean value during 820V/39KA is 189 * 10 to the t value
3A
2S).
Description
The utility model relates to and is used for the quartz sand filler that fuse is made arc-extinguishing medium.
Filler is the important component part of fuse, when melt fuses, absorbs arc energy by filler, makes arc extinction.Quartz sand has good arc-extinguishing property, thereby obtains extensive use as the fuse filler.Yet, obtain desirable arc extinction performance, still need natural siliceous sand (or quartzite) is carried out various processed, make granular size, grain shape and the chemical composition of quartz sand meet certain requirement.When particle size was big, the quartz sand of loading in the same fuse shell was just few, and the absorbent arc energy of institute is also few, thereby is unfavorable for arc extinguishing; Particle size hour, the plasma that the melt gasification produces quartz sand around the fusing when flowing is easy to form the liquid metal bridge, stop plasma to enter the quartz sand filler periphery, electric arc is longer, and the arcing time is also longer, the pressure of electric arc is also bigger, is unfavorable for arc extinguishing equally.Grain shape, promptly particle De Roll circularity also is the key factor that influences the filler arc extinction performance, it is very big to the influence of breaking capacity.The quartz sand packed density of circular granular is bigger, and particle surface contact is for the some contact, and from integral body, it is uniform that the space distributes; And the packed density of the tangible quartz sand particle of corner angle is less, and gap between particles varies, skewness.When melt fusing produced electric arc, if circular granular, the plasma of arc channel can be by the space to evenly conduction all around, and electric arc fully contacts with circular quartz sand particle, helps arc extinguishing.Otherwise the tangible quartz sand of corner angle is unfavorable for arc extinguishing.Say from chemical composition, the content height of silicon dioxide, favourable to arc extinguishing, and the content of di-iron trioxide is few more good more.
Existing a kind of quartz sand filler through processed, the content of its silicon dioxide is not less than 99.6%, and the content of di-iron trioxide is not more than 0.02%, and its particle size is between 30 orders～120 orders.Though this quartz sand filler has arc extinction performance preferably, because to the having relatively high expectations of chemical composition, thereby the production cost of quartz sand filler is improved greatly.
The purpose of this utility model is to provide a kind of and has good arc-extinguishing property and the quartz sand filler of low production cost.
The quartz sand filler that the process processed that the utility model provides obtains, the content of its silicon dioxide is lower than 99.6%, and the content of di-iron trioxide is much higher than 0.02%.Thereby can reduce production costs significantly.Its order number is-20 orders～+ 60 orders, and the dihedral coefficient is less than 1.30.The dihedral coefficient is the coefficient that characterizes Ke Li Roll circularity.
The dioxide-containing silica of an embodiment of the utility model is lower than 99.6% and be greater than or equal to 98.2%, and the content of di-iron trioxide is higher than 0.02% and be less than or equal to 0.15%, and the order number is-20 orders～+ 60 orders, and the dihedral coefficient is less than 1.30.
Adopt the fuse of the foregoing description filler, (500V, 120KA), it cut-offs I to have good breaking capacity
2The t value is lower, and (mean value during 820V/39KA is 189 * 10
3A
2S), lower by 10% than above-mentioned prior art, and have good current limiting performance.
Claims (1)
1, a kind of fuse quartz sand filler that obtains through processed is characterized in that:
The content of a, silicon dioxide is lower than 99.6% and be greater than or equal to 98.2%;
The content of b, di-iron trioxide is higher than 0.02% and be less than or equal to 0.15%;
C, order number are-20 orders～+ 60 orders;
D, dihedral coefficient are less than 1.30.