CN104088196A - Manufacturing method of thermal transfer printing paper raw paper - Google Patents
Manufacturing method of thermal transfer printing paper raw paper Download PDFInfo
- Publication number
- CN104088196A CN104088196A CN201410322135.XA CN201410322135A CN104088196A CN 104088196 A CN104088196 A CN 104088196A CN 201410322135 A CN201410322135 A CN 201410322135A CN 104088196 A CN104088196 A CN 104088196A
- Authority
- CN
- China
- Prior art keywords
- pulp
- paper
- mixing
- transfer printing
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of papermaking and provides a manufacturing method of thermal transfer printing paper raw paper which has strong air permeability, high strength, high elongation and good adsorption performance. The manufacturing method comprises the following steps: step 1, separately pulping needle bush pulp and broadleaf wood pulp by a hydrabrusher and separately beating; step 2, pulping cotton pulp by using the hydrabrusher and beating; beating CTMP (Chemi-Thermo-Mechanical Pulp) to 25-30 degrees SR; step 3, mixing the two types of pulp beaten in the step 1 to obtain first mixed pulp; mixing the two types of pulp beaten in the step 2 to obtain second mixed pulp; mixing the first mixed pulp and the second mixed pulp to obtain general mixed pulp; step 4, feeding the general mixed slurry to a stainless steel mixing tank; adding a wet strength agent, talcum powder and a sizing agent into the stainless steel mixing tank and uniformly agitating to obtain paper pulp; and step 5, putting the paper pulp obtained in the step 4 on a net and controlling dehydration and moulding at the net part; squeezing, carrying out surface sizing and drying to prepare the thermal transfer printing paper raw paper.
Description
Technical field
The present invention relates to field of papermaking, particularly a kind of manufacture method of heat transfer printing paper body paper.
Background technology
At present, paper industry accounts for certain status in national economy, is one of important symbol of weighing modernization level and civilization degree.Heat transfer printing paper is called for short heat-transferring printing paper, claims again hot transfer paper, xylopyrography paper.Heat transfer printing be by pattern printing on a kind of special paper, by applying uniform temperature and pressure, design transfer is upper to stock (as cotton, chemical fibre kind fabric, vessel etc.), form the pattern complete, bright-coloured, stereovision is strong.In this process, play the paper of transfer printing carrier function heat-transferring printing paper.
Heat sublimation transfer printing paper requires that face coat absorbency is good, ink droplet infiltration rate is fast, prints when complete, and image is without obviously heap China ink and diffusion of coloring matter phenomenon.Should meet in common room temperature under environment the curling deformation phenomenon that waits little, heat-resisting quantity will be got well in addition, and temperature is in the time of 250 ℃, and paper is without obviously distortion and carbonization phenomenon.Body paper, except possessing the basic demand of general coated paper, there are certain requirements body paper tightness, air permeability etc.Body paper also needs have good tensile strength and heat resistance, and especially, after heating, body paper still needs to keep some strength.There is the defects such as gas permeability is poor, intensity is low, adsorptivity is not good in existing heat transfer printing paper body paper.
Summary of the invention
Therefore,, for above-mentioned problem, the present invention proposes the manufacture method of the heat transfer printing paper body paper that a kind of gas permeability is strong, intensity is high, percentage elongation is high, absorption property is good.
For solving this technical problem, the present invention takes following scheme: a kind of manufacture method of heat transfer printing paper body paper, comprises the steps:
Step 1, by hydrabrusher difference pulping for the hardwood pulp of the softwood pulp of 30-50 weight portion and 30-50 weight portion, then pulls an oar respectively to 18-25 ° of SR and 16-26 ° of SR with the making beating of series connection double plate mill;
Step 2, with pulper pulping and pull an oar to 21-25 ° of SR, pulls an oar the cotton pulp of 15-30 weight portion to 25-30 ° of SR by the CTMP chemi-mechanical pulp of 20-30 weight portion;
Step 3, two kinds of stock pumps after step 1 making beating are delivered to mixing pit and be fully mixed to get the first mixing slurry, again two kinds of stock pumps after step 2 making beating are delivered to mixing pit and be fully mixed to get the second mixing slurry, and then the first mixing slurry is mixed with second to starch be mixed to get total mixing and starch;
Step 4, sends above-mentioned total mixing slurry into stainless steel mixing pit, adds 0.5-1.5 weight portion PPE wet strength agent, the talcum powder of 10-15 weight portion and the cation colophony glue sizing agent of 1-1.5 weight portion to stainless steel mixing pit and stir obtaining paper pulp;
Step 5, the paper pulp that step 4 is obtained online, controls wet end dehydration forming, then through squeezing, carry out top sizing, dry, makes heat transfer printing paper body paper.
Further, the softwood pulp in described step 1 is bleaching needle chemical pulp.
By adopting aforementioned techniques scheme, the invention has the beneficial effects as follows: by take softwood pulp and hardwood pulp as main fibrous raw material, coordinating cotton pulp and CTMP chemi-mechanical pulp is auxiliary material, add part talcum powder as filler simultaneously, make paper pulp of the present invention in conjunction with the character that has absorbed cotton fiber, it is tough that the heat transfer printing paper body paper of making has absorbability epistasis matter, and tissue is fine and smooth soft, and gas permeability is strong, intensity is high, percentage elongation is high; Talcous interpolation has simultaneously improved the smoothness of paper, make again the adsorbable sicker of paper, by add PPE wet strength agent in slurry, strengthen intensity, deflection and the fineness of heat transfer printing paper, also by optimizing beating degree, made the one-tenth paper various aspects of performance index of heat transfer printing paper body paper of the present invention far beyond existing standard simultaneously.
The specific embodiment
Now in conjunction with the specific embodiment, the present invention is further described.
Embodiment mono-:
A manufacture method for heat transfer printing paper body paper, comprises the steps:
Step 1, by hydrabrusher difference pulping for the hardwood pulp of the softwood pulp of 50 weight portions and 50 weight portions, this softwood pulp is bleaching needle chemical pulp, then pulls an oar and pull an oar respectively to 20 ° of SR and 22 ° of SR with series connection double plate mill;
Step 2, also pulls an oar the cotton pulp of 30 weight portions to 23 ° of SR with pulper pulping, and the CTMP chemi-mechanical pulp of 30 weight portions is pulled an oar to 27 ° of SR;
Step 3, two kinds of stock pumps after step 1 making beating are delivered to mixing pit and be fully mixed to get the first mixing slurry, again two kinds of stock pumps after step 2 making beating are delivered to mixing pit and be fully mixed to get the second mixing slurry, and then the first mixing slurry is mixed with second to starch be mixed to get total mixing and starch;
Step 4, sends above-mentioned total mixing slurry into stainless steel mixing pit, adds 1 weight portion PPE wet strength agent, the talcum powder of 15 weight portions and the cation colophony glue sizing agent of 1.3 weight portions to stainless steel mixing pit and stir obtaining paper pulp;
Step 5, the paper pulp that step 4 is obtained online, controls wet end dehydration forming, then through squeezing, carry out top sizing, dry, makes heat transfer printing paper body paper.
Embodiment bis-:
A manufacture method for heat transfer printing paper body paper, comprises the steps:
Step 1, by hydrabrusher difference pulping for the hardwood pulp of the softwood pulp of 40 weight portions and 35 weight portions, this softwood pulp is bleaching needle chemical pulp, then pulls an oar and pull an oar respectively to 21 ° of SR and 20 ° of SR with series connection double plate mill;
Step 2, also pulls an oar the cotton pulp of 20 weight portions to 22 ° of SR with pulper pulping, and the CTMP chemi-mechanical pulp of 25 weight portions is pulled an oar to 28 ° of SR;
Step 3, two kinds of stock pumps after step 1 making beating are delivered to mixing pit and be fully mixed to get the first mixing slurry, again two kinds of stock pumps after step 2 making beating are delivered to mixing pit and be fully mixed to get the second mixing slurry, and then the first mixing slurry is mixed with second to starch be mixed to get total mixing and starch;
Step 4, sends above-mentioned total mixing slurry into stainless steel mixing pit, adds 1.1 weight portion PPE wet strength agents, the talcum powder of 12 weight portions and the cation colophony glue sizing agent of 1.3 weight portions to stainless steel mixing pit and stir obtaining paper pulp;
Step 5, the paper pulp that step 4 is obtained online, controls wet end dehydration forming, then through squeezing, carry out top sizing, dry, makes heat transfer printing paper body paper.
Embodiment tri-:
A manufacture method for heat transfer printing paper body paper, comprises the steps:
Step 1, by hydrabrusher difference pulping for the hardwood pulp of the softwood pulp of 35 weight portions and 30 weight portions, this softwood pulp is bleaching needle chemical pulp, then pulls an oar and pull an oar respectively to 24 ° of SR and 26 ° of SR with series connection double plate mill;
Step 2, also pulls an oar the cotton pulp of 20 weight portions to 22 ° of SR with pulper pulping, and the CTMP chemi-mechanical pulp of 30 weight portions is pulled an oar to 29 ° of SR;
Step 3, two kinds of stock pumps after step 1 making beating are delivered to mixing pit and be fully mixed to get the first mixing slurry, again two kinds of stock pumps after step 2 making beating are delivered to mixing pit and be fully mixed to get the second mixing slurry, and then the first mixing slurry is mixed with second to starch be mixed to get total mixing and starch;
Step 4, sends above-mentioned total mixing slurry into stainless steel mixing pit, adds 1.3 weight portion PPE wet strength agents, the talcum powder of 43 weight portions and the cation colophony glue sizing agent of 1.1 weight portions to stainless steel mixing pit and stir obtaining paper pulp;
Step 5, the paper pulp that step 4 is obtained online, controls wet end dehydration forming, then through squeezing, carry out top sizing, dry, makes heat transfer printing paper body paper.
In the present invention, each raw material proportioning parts by weight are with softwood pulp 30-50 weight portion, hardwood pulp 30-50 weight portion, cotton pulp 15-30 weight portion, CTMP chemi-mechanical pulp 20-30 weight portion, PPE 0.5-1.5 weight portion, talcum powder 10-15 weight portion, sizing agent 1-1.5 weight portion, for good; Wherein in fibrous raw material, softwood pulp is pulled an oar to 18-25 ° of SR, and hardwood pulp is pulled an oar to 16-26 ° of SR, and Cotton Pulp is to 21-25 ° of SR, and CTMP chemi-mechanical pulp is pulled an oar to 25-30 ° of SR and is advisable.
The present invention is by take softwood pulp and hardwood pulp as main fibrous raw material, coordinating cotton pulp and CTMP chemi-mechanical pulp is auxiliary material, add part talcum powder as filler simultaneously, make paper pulp of the present invention in conjunction with the character that has absorbed cotton fiber, it is tough that the heat transfer printing paper body paper of making has absorbability epistasis matter, tissue is fine and smooth soft, and gas permeability is strong, intensity is high, percentage elongation is high; Talcous interpolation has simultaneously improved the smoothness of paper, make again the adsorbable sicker of paper, by add PPE wet strength agent in slurry, strengthen intensity, deflection and the fineness of heat transfer printing paper, also by optimizing beating degree, made the one-tenth paper various aspects of performance index of heat transfer printing paper body paper of the present invention far beyond existing standard simultaneously.
Although specifically show and introduced the present invention in conjunction with preferred embodiment; but those skilled in the art should be understood that; within not departing from the spirit and scope of the present invention that appended claims limits; can make a variety of changes the present invention in the form and details, be protection scope of the present invention.
Claims (2)
1. a manufacture method for heat transfer printing paper body paper, is characterized in that: comprise the steps:
Step 1, by hydrabrusher difference pulping for the hardwood pulp of the softwood pulp of 30-50 weight portion and 30-50 weight portion, then pulls an oar respectively to 18-25 ° of SR and 16-26 ° of SR with the making beating of series connection double plate mill;
Step 2, with pulper pulping and pull an oar to 21-25 ° of SR, pulls an oar the cotton pulp of 15-30 weight portion to 25-30 ° of SR by the CTMP chemi-mechanical pulp of 20-30 weight portion;
Step 3, two kinds of stock pumps after step 1 making beating are delivered to mixing pit and be fully mixed to get the first mixing slurry, again two kinds of stock pumps after step 2 making beating are delivered to mixing pit and be fully mixed to get the second mixing slurry, and then the first mixing slurry is mixed with second to starch be mixed to get total mixing and starch;
Step 4, sends above-mentioned total mixing slurry into stainless steel mixing pit, adds 0.5-1.5 weight portion PPE wet strength agent, the talcum powder of 10-15 weight portion and the cation colophony glue sizing agent of 1-1.5 weight portion to stainless steel mixing pit and stir obtaining paper pulp;
Step 5, the paper pulp that step 4 is obtained online, controls wet end dehydration forming, then through squeezing, carry out top sizing, dry, makes heat transfer printing paper body paper.
2. the manufacture method of a kind of heat transfer printing paper body paper according to claim 1, is characterized in that: the softwood pulp in described step 1 is bleaching needle chemical pulp.