CN104088192B - A kind of for overlaying the high definition ink-jet Jie's material at board surface - Google Patents
A kind of for overlaying the high definition ink-jet Jie's material at board surface Download PDFInfo
- Publication number
- CN104088192B CN104088192B CN201410298532.8A CN201410298532A CN104088192B CN 104088192 B CN104088192 B CN 104088192B CN 201410298532 A CN201410298532 A CN 201410298532A CN 104088192 B CN104088192 B CN 104088192B
- Authority
- CN
- China
- Prior art keywords
- high definition
- jie
- jet
- less
- overlaying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of for overlaying the high definition ink-jet Jie's material at board surface, high definition ink-jet Jie's material includes the component of following weight ratio: 1～5% glass fiber, 1～5% carbon fiber chopped silk, 1～5% weak anion resin, 1～15%PVC paste resin, 1～5% aqueous polyurethane emulsion, 1～5% solvent-type acrylic and surplus wood-fibred.The present invention can pass through high definition inkjet printing pattern, good visual effect, and texture is good, and the adhesion strength between plank is high, is not readily separated.
Description
Technical field
The present invention relates to the papery Jie's material technical field for overlaying the carrying pattern at board surface, especially relate to one
Plant for overlaying the high definition ink-jet Jie's material at board surface.
Background technology
In prior art, the surface of plank has overlayed a bristol paper, and the dimensions of plank is 1.2 meters of X2.4 rice, overlays
Bristol paper at board surface has multiple, and bristol paper typically selects spraying paper, spraying paper to be printed with pattern by typography.But
Being that the spraying paper quality of printed patterns is poor, and the bonding strength between plank is poor, spraying paper easily separates with plank, its
Pattern is clear not, and visual effect is poor, and texture is the most poor, it is therefore necessary to improved.
Summary of the invention
The deficiency existed for prior art, it is an object of the invention to provide a kind of for overlaying the high definition at board surface
Ink-jet Jie's material, it can pass through high definition inkjet printing pattern, good visual effect, and texture is good, and the adhesion strength between plank is high,
It is not readily separated.
To achieve these goals, the technical solution adopted in the present invention is.
A kind of for overlaying the high definition ink-jet Jie's material at board surface, high definition ink-jet Jie's material includes the group of following weight ratio
Part:
In the technical scheme of another proportioning of the present invention, high definition ink-jet Jie's material includes the component of following weight ratio:
Further in technical scheme, the length of described wood-fibred is less than 0.2mm, and maximum outside diameter is less than 0.05mm.
Further in technical scheme, described weak anion resin contains primary amine groups, secondary amine or tertiary amine groups.
Further in technical scheme, the length of described glass fiber is less than 10mm, and filament diameter is less than 50 μm.
Further in technical scheme, the length of described carbon fiber chopped silk is less than 0.1mm, and filament diameter is less than 10 μm,
Anti-to stretch modulus be 250～350GPa, and phosphorus content is more than 95%.
Use after said structure, the present invention the most advantageously: the present invention can pass through high definition
Inkjet printing pattern, good visual effect, texture is good, and the adhesion strength between plank is high, is not readily separated.
Detailed description of the invention
The following stated is only presently preferred embodiments of the present invention, the most therefore limits protection scope of the present invention.
Embodiment one
A kind of for overlaying the high definition ink-jet Jie's material at board surface, high definition ink-jet Jie's material includes the group of following weight ratio
Part:
Wherein,
The length of wood-fibred is less than 0.2mm, and maximum outside diameter is less than 0.05mm.
Weak anion resin contains primary amine groups, secondary amine or tertiary amine groups.
The length of glass fiber is less than 10mm, and filament diameter is less than 50 μm.
The length of carbon fiber chopped silk is less than 0.1mm, and filament diameter is less than 10 μm, and anti-to stretch modulus be 250～350GPa, contains
Carbon amounts is more than 95%.
Embodiment two
A kind of for overlaying the high definition ink-jet Jie's material at board surface, high definition ink-jet Jie's material includes the group of following weight ratio
Part:
Wherein,
The length of wood-fibred is less than 0.2mm, and maximum outside diameter is less than 0.05mm.
Weak anion resin contains primary amine groups, secondary amine or tertiary amine groups.
The length of glass fiber is less than 10mm, and filament diameter is less than 50 μm.
The length of carbon fiber chopped silk is less than 0.1mm, and filament diameter is less than 10 μm, and anti-to stretch modulus be 250～350GPa, contains
Carbon amounts is more than 95%.
Above content is only presently preferred embodiments of the present invention, for those of ordinary skill in the art, according to the present invention's
Thought, the most all will change, and this specification content should not be construed as the present invention
Restriction.
Claims (2)
1. one kind is used for overlaying the high definition ink-jet Jie's material at board surface, it is characterised in that high definition ink-jet Jie's material includes following heavy
The component of amount ratio:
Wherein,
The length of described wood-fibred is less than 0.2mm, and maximum outside diameter is less than 0.05mm；
The length of described glass fiber is less than 10mm, and filament diameter is less than 50 μm；
The length of described carbon fiber chopped silk is less than 0.1mm, and filament diameter is less than 10 μm, and anti-to stretch modulus be 250～350GPa, contains
Carbon amounts is more than 95%；
Described weak anion resin contains primary amine groups, secondary amine or tertiary amine groups.
It is the most according to claim 1 a kind of for overlaying the high definition ink-jet Jie's material at board surface, it is characterised in that: described
High definition ink-jet Jie's material includes the component of following weight ratio: