CN104087393B - A kind of lubricant grease for brake system of car and preparation method thereof - Google Patents
A kind of lubricant grease for brake system of car and preparation method thereof Download PDFInfo
- Publication number
- CN104087393B CN104087393B CN201410311787.3A CN201410311787A CN104087393B CN 104087393 B CN104087393 B CN 104087393B CN 201410311787 A CN201410311787 A CN 201410311787A CN 104087393 B CN104087393 B CN 104087393B
- Authority
- CN
- China
- Prior art keywords
- parts
- antioxidant
- lubricant grease
- brake system
- aerosil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of lubricant grease for brake system of car and preparation method thereof, lubricant grease is made up of following component by ratio of weight and the number of copies:50 75 parts of deep refining base oil, 23 parts of aluminium hydroxide, 57 parts of stearic acid, 13 parts of aerosil, 0.2 0.5 parts of nano metal protective agent, 0.5 4 parts of phenolic antioxidant, 0.5 0.8 parts of tackifier, 12 parts of antiwear additive, 0.5 1 parts of antirust agent.Lubricant grease of the present invention has excellent high temperature performance, and dropping point is high, and adhesiveness is good, and loss is few, noncoking, and specialty solves the problems, such as the insufficient lubrication at the positions such as wheel cylinder guide finger, the dirt-proof boot of brakes clamp.
Description
Technical field
The present invention relates to lubricant grease technical field, and in particular to a kind of lubricant grease for brake system of car and its
Preparation method.
Background technology
Brakes clamp wheel cylinder guide finger (alignment pin) and dirt-proof boot can be used general in assembling and maintenance at present
Logical lithium saponify is smeared on these parts.As the heat resistance and abrasion resistance of common lithium saponify are poor, there are the following problems for meeting:
Relatively low using temperature, typically not over 120 DEG C, temperature is slightly higher, and common lithium saponify thinning can be lost in quickly, and wheel cylinder guide finger loses
Lubrication is gone, is caused wheel cylinder guide finger return slow, is extended braking distance, bring serious potential safety hazard.In addition, common lithium saponify
Meeting coking after high temperature, forms the extremely hard oil film of one layer of hardness, and during braking, wheel cylinder guide finger can be stuck, causes wheel cylinder guide finger not return
Position, brake failure are caused serious potential safety hazard, easily cause serious loss to lives and properties.
In the America and Europe that automobile industry is flourishing, brake system of car wheel cylinder guide finger can be all made in assembling and maintenance
Protective agent is carried out with the wheel cylinder guide finger lubricant of specialty, guarantee is brought to the traffic safety of car owner.Numerous braking systems at home
System wheel cylinder guide finger and dirt-proof boot outlet producer, all because the domestic specialty that lacks is used for wheel cylinder guide finger lubricant product, can only
It is forced to use high import wheel cylinder guide finger lubricant product.
According to case above, a kind of professional application is studied in special portions such as brake system of car wheel cylinder guide finger, dirt-proof boots
The lubricant grease of position is to be highly desirable to.
The content of the invention
The present invention provides a kind of lubrication for brake system of car with excellent high temperature performance, high lubricating effect
Grease and preparation method thereof.
A kind of lubricant grease for brake system of car, is made up of following component by ratio of weight and the number of copies:Deep refining base
Plinth oil 50-75 parts, aluminium hydroxide 2-3 parts, stearic acid 5-7 parts, aerosil 1-3 parts, nano metal protective agent 0.2-0.5
Part, phenolic antioxidant 0.5-4 parts, tackifier 0.5-0.8 parts, antiwear additive 1-2 parts, antirust agent 0.5-1 parts.
Preferably, a kind of above-mentioned lubricant grease for brake system of car, is made up of following component by ratio of weight and the number of copies:
60 parts of deep refining base oil, 3 parts of aluminium hydroxide, 6 parts of stearic acid, 2 parts of aerosil, 0.3 part of nano metal protective agent,
2 parts of phenolic antioxidant, 0.7 part of tackifier, 1.5 parts of antiwear additive, 0.7 part of antirust agent.
The saturated hydrocarbon content of the deep refining base oil is 90-99wt%, and sulfur content is 0.001-0.01wt%, viscosity
Index IV >=140.
The nano metal protective agent is close power iron (Militec-1).
The phenolic antioxidant is antioxidant 264, antioxidant 1010, antioxidant 330, antioxidant 1076, antioxidant CA, anti-
One or more in oxygen agent 2246.
The tackifier are polybutene, polyisobutene, polymethacrylates, one or more in ethylene-propylene copolymer.
The antiwear additive is 3- neighbour's isopropoxy carbonyl phenyl boric acids, chlorinated paraffin, sulfide isobutene, tricresol phosphate
One or more in ester, di-n-butyl phosphite, triphenyl phosphate, lead naphthenate.
The antirust agent is BTA, barium mahogany sulfonate, lanolin magnesium soap, natrium nitrosum, dialkyl dithio phosphorus
One or more in sour zinc.
A kind of preparation method of above-mentioned lubricant grease for brake system of car, is characterized in that:Carry out according to the following steps:
(1) by deep refining base oil, stearic acid, aerosil input saponification kettle, pressure 0.1MPa, heating rise
Temperature is sufficiently stirred for 30min to 100-120 DEG C;
(2) aluminium hydroxide is put in saponification kettle, pressure 0.1MPa, temperature 100-120 DEG C are sufficiently stirred for 30min, carry out
Saponification;
(3) be heated to 180-200 DEG C carry out the compound refining 30min of high temperature after, kettle cover addition is opened when being cooled to 100 DEG C
Phenolic antioxidant, tackifier, antiwear additive, antirust agent and nano metal protective agent, are stirred 30-40min;
(4) after in kettle, raw material cools, homogeneous, degassing, filter after obtain finished product.
Preferably, in step (4), filtration treatment is using 120 mesh filter screen filtrations.
It is after using above-mentioned technical proposal, of the invention compared with existing background technology, have the advantage that:
The lubricant grease of the present invention has excellent resistance to elevated temperatures and antiseptic property, while having good extreme-pressure anti-wear
Property, excellent cryogenic property, dropping point be high, and adhesiveness is good, and loss is few, noncoking.Specialty solves the wheel cylinder of brakes clamp and leads
To the problem of the insufficient lubrication at the positions such as pin, dirt-proof boot, the purposes such as protection dirt-proof boot, lubrication wheel cylinder guide finger are played, system is improved
The sensitivity of dynamic system, shortens braking distance, greatly promotes braking safety, extends dirt-proof boot service life, it can also be used to its
During his type device requires higher bearing lubrication.
Specific embodiment
Some embodiments of the present invention presented below, to help further understanding the present invention, but protection scope of the present invention
It is not limited in these embodiments.
Embodiment one
A kind of lubricant grease for brake system of car, is made up of following component by ratio of weight and the number of copies:
60 parts of deep refining base oil, 3 parts of aluminium hydroxide, 6 parts of stearic acid, 2 parts of aerosil, 0.3 part of close power iron,
2 parts of antioxidant 264,0.7 part of polybutene, 1.5 parts of 3- neighbour's isopropoxy carbonyls phenyl boric acid, 0.7 part of barium mahogany sulfonate.
A kind of preparation method of above-mentioned lubricant grease for brake system of car, is carried out according to the following steps:
(1) by deep refining base oil, stearic acid, aerosil input saponification kettle, pressure 0.1MPa, heating rise
Temperature is sufficiently stirred for 30min to 100 DEG C;
(2) aluminium hydroxide is put in saponification kettle, pressure 0.1MPa, 100 DEG C of temperature are sufficiently stirred for 30min, carry out saponification
Reaction;
(3) be heated to 190 DEG C carry out the compound refining 30min of high temperature after, kettle cover is opened when being cooled to 100 DEG C and adds close power
Iron (Militec-1), antioxidant 264, polybutene, 3- neighbour's isopropoxy carbonyl phenyl boric acids and barium mahogany sulfonate, are stirred
35min;
(4) after raw material cools in kettle, homogeneous, degassing, finished product is obtained using 120 mesh filter screen filtrations.
Embodiment two
50 parts of deep refining base oil, 2 parts of aluminium hydroxide, 7 parts of stearic acid, 1 part of aerosil, 0.5 part of close power iron,
0.2 part of antioxidant 1010,0.3 part of antioxidant 2246,0.5 part of polymethacrylates, 1 part of di-n-butyl phosphite, phosphoric acid
1 part of triphenylmethyl methacrylate, 0.3 part of BTA, 0.2 part of lanolin magnesium soap.
A kind of preparation method of above-mentioned lubricant grease for brake system of car, is carried out according to the following steps:
(1) by deep refining base oil, stearic acid, aerosil input saponification kettle, pressure 0.1MPa, heating rise
Temperature is sufficiently stirred for 30min to 110 DEG C;
(2) aluminium hydroxide is put in saponification kettle, pressure 0.1MPa, 110 DEG C of temperature are sufficiently stirred for 30min, carry out saponification
Reaction;
(3) be heated to 200 DEG C carry out the compound refining 30min of high temperature after, kettle cover is opened when being cooled to 100 DEG C and adds close power
Iron (Militec-1), antioxidant 1010, antioxidant 2246, polymethacrylates, di-n-butyl phosphite, triphenyl phosphate,
BTA and lanolin magnesium soap, are stirred 30min;
(4) after in kettle, raw material cools, homogeneous, degassing, using obtaining finished product after 120 mesh filter screen filtrations.
Embodiment three
75 parts of deep refining base oil, 2.5 parts of aluminium hydroxide, 5 parts of stearic acid, 3 parts of aerosil, close power iron 0.2
Part, 2 parts of antioxidant 330,2 parts of antioxidant CA, 0.3 part of polyisobutene, 0.5 part of ethylene-propylene copolymer, tricresyl phosphate 0.5
Part, 0.5 part of lead naphthenate, 1 part of zinc dialkyl dithiophosphate.
A kind of preparation method of above-mentioned lubricant grease for brake system of car, is carried out according to the following steps:
(1) by deep refining base oil, stearic acid, aerosil input saponification kettle, pressure 0.1MPa, heating rise
Temperature is sufficiently stirred for 30min to 120 DEG C;
(2) aluminium hydroxide is put in saponification kettle, pressure 0.1MPa, 120 DEG C of temperature are sufficiently stirred for 30min, carry out saponification
Reaction;
(3) be heated to 180 DEG C carry out the compound refining 30min of high temperature after, kettle cover is opened when being cooled to 100 DEG C and adds close power
Iron (Militec-1), antioxidant 330, antioxidant CA, polyisobutene, ethylene-propylene copolymer, tricresyl phosphate, lead naphthenate and
Zinc dialkyl dithiophosphate, is stirred 40min;
(4) after raw material cools in kettle, homogeneous, degassing, finished product is obtained using 120 mesh filter screen filtrations.
In above-described embodiment 1-3, the saturated hydrocarbon content of deep refining base oil (UHVIS) is 90-99%wt, and sulfur content is
0.001-0.01%wt, viscosity index (VI) IV >=140.Deep refining base oil is provided by British Petroleum Company (PB).
Close power iron (MILITEC-1) is by AMT companies of the U.S. (ADAPTIVE MOLECULARTECHNOLOGY
INCORPERATED) produce.Close power iron is a kind of homozygosis into hydrocarbon, uniform, stable, pure environmental protection, harmless.
Close power iron can merge completely, and make carrier using which with machine oil, lubricating oil, refrigeration oil, cutting oil, the iundustrial oil such as hydraulic oil
Each position of close power sheet iron strip to parts, and the protection parts that react (when temperature reaches 38-66 DEG C, chemically reactive infiltration
Become metal surface molecular structure to metal surface, make metal skin hardness strengthen about 17 times), it is industrial without changing these
Oily physical property and the property changed.
The particle diameter of aerosil is 7-40 nanometers, and specific surface area is 200-400m2/g。
The quality index of lubricant grease obtained in embodiment 1-3 is tested, test result is listed in table 1.
Lubricant grease quality index test data obtained in 1 embodiment 1-3 of table
From 1 test data of table, lubricant grease of the present invention has excellent high temperature performance, and dropping point is high, and adhesiveness is good, damages
Lose few, noncoking.Specialty solves the problems, such as the insufficient lubrication at the positions such as wheel cylinder guide finger, the dirt-proof boot of brakes clamp.
Above-described embodiment is the present invention preferably embodiment, but embodiments of the present invention not by above-described embodiment
Limit, other any Spirit Essences without departing from the present invention and the change, modification, replacement made under principle, combine, simplification,
Equivalent substitute mode is should be, is included within protection scope of the present invention.
Claims (7)
1. a kind of lubricant grease for brake system of car, is characterized in that:It is made up of following component by ratio of weight and the number of copies:Depth
Refined base oil 50-75 parts, aluminium hydroxide 2-3 parts, stearic acid 5-7 parts, aerosil 1-3 parts, nano metal protective agent
0.2-0.5 parts, phenolic antioxidant 0.5-4 parts, tackifier 0.5-0.8 parts, antiwear additive 1-2 parts, antirust agent 0.5-1 parts;
The saturated hydrocarbon content of the deep refining base oil is 90-99wt%, and sulfur content is 0.001-0.01wt%, viscosity index (VI)
IV≥140;
The antiwear additive be 3- neighbour's isopropoxy carbonyl phenyl boric acids, chlorinated paraffin, sulfide isobutene, tricresyl phosphate,
One or more in di-n-butyl phosphite, triphenyl phosphate, lead naphthenate;
The particle diameter of the aerosil is 7-40 nanometers, and specific surface area is 200-400m2/g;
The nano metal protective agent is close power iron.
2. a kind of lubricant grease for brake system of car according to claim 1, is characterized in that:By ratio of weight and the number of copies
It is made up of following component:60 parts of deep refining base oil, 3 parts of aluminium hydroxide, 6 parts of stearic acid, aerosil 2 part, nanometer
0.3 part of metal coating agent, 2 parts of phenolic antioxidant, 0.7 part of tackifier, 1.5 parts of antiwear additive, 0.7 part of antirust agent.
3. a kind of lubricant grease for brake system of car according to claim 1 and 2, is characterized in that:The phenols
Antioxidant is antioxidant 264, antioxidant 1010, antioxidant 330, antioxidant 1076, antioxidant CA, the one kind in antioxidant 2246
Or it is several.
4. a kind of lubricant grease for brake system of car according to claim 3, is characterized in that:The tackifier are
One or more in polybutene, polyisobutene, polymethacrylates, ethylene-propylene copolymer.
5. a kind of lubricant grease for brake system of car according to claim 4, is characterized in that:The antirust agent is
One or more in BTA, barium mahogany sulfonate, lanolin magnesium soap, natrium nitrosum, zinc dialkyl dithiophosphate.
6. the preparation method of a kind of lubricant grease for brake system of car according to any one of claim 1 to 5, its
It is characterized in that:Carry out according to the following steps:
(1) by deep refining base oil, stearic acid, aerosil input saponification kettle, pressure 0.1MPa is heated to
100-120 DEG C, it is sufficiently stirred for 30min;
(2) aluminium hydroxide is put in saponification kettle, pressure 0.1MPa, temperature 100-120 DEG C are sufficiently stirred for 30min, carry out saponification
Reaction;
(3) be heated to 180-200 DEG C carry out the compound refining 30min of high temperature after, kettle cover is opened when being cooled to 100 DEG C and adds phenols
Antioxidant, tackifier, antiwear additive, antirust agent and nano metal protective agent, are stirred 30-40min;
(4) after in kettle, raw material cools, homogeneous, degassing, filter after obtain finished product.
7. a kind of preparation method of lubricant grease for brake system of car according to claim 6, is characterized in that:Step
Suddenly in (4), filtration treatment is using 120 mesh filter screen filtrations.