CN104087365B - A kind of wear-resisting automobile oil and preparation method thereof - Google Patents

A kind of wear-resisting automobile oil and preparation method thereof Download PDF

Info

Publication number
CN104087365B
CN104087365B CN201410313292.4A CN201410313292A CN104087365B CN 104087365 B CN104087365 B CN 104087365B CN 201410313292 A CN201410313292 A CN 201410313292A CN 104087365 B CN104087365 B CN 104087365B
Authority
CN
China
Prior art keywords
parts
oil
wear
automobile oil
resisting automobile
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410313292.4A
Other languages
Chinese (zh)
Other versions
CN104087365A (en
Inventor
李勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Precious Prompt Lubricating Oil Zhenjiang Co Ltd
Original Assignee
Precious Prompt Lubricating Oil Zhenjiang Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Precious Prompt Lubricating Oil Zhenjiang Co Ltd filed Critical Precious Prompt Lubricating Oil Zhenjiang Co Ltd
Priority to CN201410313292.4A priority Critical patent/CN104087365B/en
Publication of CN104087365A publication Critical patent/CN104087365A/en
Application granted granted Critical
Publication of CN104087365B publication Critical patent/CN104087365B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of wear-resisting automobile oil, include that following components is made according to parts by weight: modified Nano diamond 25~40 parts, base oil 40~80 parts, organic-molybdenum mixture 20~30 parts, antiwear additive 10~20 parts, preservative 20~30 parts.The invention also discloses the preparation method of above-mentioned wear-resisting automobile oil.Antiwear additive is used in automobile oil reducing friction and wear by the present invention, also can improve oil viscosity index.The present invention is also added into preservative simultaneously, is possible to prevent metal parts to get rusty, and extends the service life of car.

Description

A kind of wear-resisting automobile oil and preparation method thereof
Technical field
The present invention relates to automobile oil technical field, particularly to a kind of wear-resisting automobile oil and preparation method thereof.
Background technology
Current has the performance of many kollags very well, but owing to density can not be suspended in oil greatly, coarse size is entered not Removing friction pair, mass deposition is serious, has used blocking oil circuit long, it is impossible to apply in lubricating oil.Pole in conventional lubrication oil Pressure antiwear additive is often a little sulfur, phosphorus, chloride, generates metal compound by boundary lubrication TRANSIENT HIGH TEMPERATURE high pressure with friction pair Thing, improves hardness and wear resistence.Though this compound is hard but the most crisp, constantly comes off at friction process and constantly formed, Both having corroded parts, and consumed again additive, machinery or the service life of lubricating oil are the shortest.Conventional lubrication oil In wear-resistant composition such as zinc dialkyl dithiophosphate (T202 oxidation and corrosion inhibitor) etc., sulfur-bearing, phosphorus, zinc, not only corrode silver Bearing, poisons waste gas conversion equipment catalyst, goes back pollutant atmosphere.Lube product generally will be in the lowest environment temperature Degree is lower to be used, the most in the winter time and under cold car state, therefore it is required that the lubricating oil used has good low temperature flow Can, so not only contribute to the normal startup optimization of machine, it is also possible to reduce machine abrasion in start-up course.
Summary of the invention
Goal of the invention: for problem of the prior art, first technical problem to be solved by this invention there is provided one Plant wear-resisting automobile oil.Second technical problem to be solved by this invention there is provided the preparation of wear-resistant wagon lubricating oil Method.
Technical scheme: in order to solve above-mentioned technical problem, the invention provides a kind of wear-resisting automobile oil, according to weight Number includes that following components is made: modified Nano diamond 25~40 parts, base oil 40~80 parts, organic-molybdenum mixture 20~30 parts, antiwear additive 10~20 parts, preservative 20~30 parts.
Wherein, above-mentioned modified Nano diamond is to obtain by CTM1 and CTM2 is modified.
Wherein, above-mentioned base oil be viscosity index (VI) 110~120 base oil.
Wherein, during above-mentioned organic-molybdenum mixture is dialkyl dithiophosphoric acid oxygen molybdenum, D2EHDTPA molybdenum salt or organic acid molybdenum salt One or more.
Wherein, above-mentioned antiwear additive be ZDDP and phosphorus, sulfur, chlorine compound in one or more.
Wherein, one or both during foregoing preservatives is fatty acid or amine.
Wherein, above-mentioned modified Nano diamond particle diameter is 2~20nm.
The preparation method of above-mentioned wear-resisting automobile oil, comprises the following steps: by base oil, organic-molybdenum mixture, resist Grinding agent, modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and are warming up to by heat-conducting oil heating 150-160 DEG C so that above-mentioned raw materials is completely dissolved, continue constant temperature stirring, the simultaneously material of dissolution kettle pump circulation height Speed flows through pipeline clipper and shears 1~2h, controls the degradation temperature wear-resistant wagon lubrication at 55~65 DEG C of available required viscositys Oil.
Wherein, above-mentioned lubrication oil viscosity is 14~16mm2/s。
Beneficial effect: the present invention, relative to prior art, has the advantage that antiwear additive is used for automobile-used lubrication by the present invention Oil can reduce friction and wear, also can improve oil viscosity index.The present invention is also added into preservative simultaneously, permissible Prevent metal parts from getting rusty, extend the service life of car.Meanwhile, due to the fact that modified Nano diamond surface is long-pending big, Activity is high, can pass through coupling, be esterified, connects the methods such as skill and carry out surface modification, it is easy to be suspended in oil, not reprecipitation Layering and blocking oil circuit;Having excellent adsorptivity and chemical reactivity, in the related oil of energy, other additive is adsorbed onto together On friction pair, the effect of various additive is made to be fully played most;Lubricant is worked into nanoscale, its crystallization temperature Spend only 600 DEG C-700 DEG C, can utilize completely the instantaneous pressure seeping at high temperature of boundary lubrication to metal lattice, hardened surface, Improve its abrasion resistance;Friction pair real contact area diffuses into maximum, continues friction and will more grind more light, and specific load is little, Frictional resistance and oil temperature are the lowest, and the service life of machinery and oil all can greatly extend;Lubriation material is some metals, metal Oxide or inorganic compound, not only evaporate, aoxidize, heat resisting temperature high, and do not pollute.
Detailed description of the invention
Below in conjunction with specific embodiment, it is further elucidated with the present invention, but the invention is not restricted to this.
Embodiment 1:
According to parts by weight, a kind of wear-resisting automobile oil, includes that following components is made: 25 parts of modified Nano diamond, Base oil 40 parts, 20 parts of organic-molybdenum mixture, antiwear additive 10 parts, preservative 20 parts.Modified Nano diamond is logical Cross that CTM1 and CTM2 is modified to be obtained.Base oil be viscosity index (VI) 110 base oil.Organic-molybdenum mixture is Dialkyl dithiophosphoric acid oxygen molybdenum.Antiwear additive is ZDDP.Preservative is fatty acid.Modified Nano diamond particle diameter is 2nm.
The preparation method of wear-resisting automobile oil, comprises the following steps: by base oil, organic-molybdenum mixture, antiwear additive, Modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and are warming up to 150 DEG C by heat-conducting oil heating, Above-mentioned raw materials being completely dissolved, continues constant temperature stirring, the circulation of material pump the high speed of dissolution kettle flows through pipeline and cuts simultaneously Cutter shears 1h, controls the degradation temperature wear-resisting automobile oil at 55 DEG C of available required viscositys.Lubrication oil viscosity For 14mm2/s。
Embodiment 2:
According to parts by weight, a kind of wear-resisting automobile oil, includes that following components is made: 40 parts of modified Nano diamond, Base oil 80 parts, 30 parts of organic-molybdenum mixture, antiwear additive 20 parts, preservative 30 parts.Modified Nano diamond is logical Cross that CTM1 and CTM2 is modified to be obtained.Base oil be viscosity index (VI) 120 base oil.Organic-molybdenum mixture is D2EHDTPA molybdenum salt.Antiwear additive is the compound of phosphorus, sulfur.Preservative is amine.Modified Nano diamond particle diameter is 20nm.
The preparation method of wear-resisting automobile oil, comprises the following steps: by base oil, organic-molybdenum mixture, antiwear additive, Modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and are warming up to 160 DEG C by heat-conducting oil heating, Above-mentioned raw materials being completely dissolved, continues constant temperature stirring, the circulation of material pump the high speed of dissolution kettle flows through pipeline and cuts simultaneously Cutter shears 2h, controls the degradation temperature wear-resisting automobile oil at 65 DEG C of available required viscositys.Lubrication oil viscosity For 16mm2/s。
Embodiment 3:
According to parts by weight, a kind of wear-resisting automobile oil, includes that following components is made: 30 parts of modified Nano diamond, Base oil 60 parts, 25 parts of organic-molybdenum mixture, antiwear additive 15 parts, preservative 25 parts.Modified Nano diamond is logical Cross that CTM1 and CTM2 is modified to be obtained.Base oil be viscosity index (VI) 115 base oil.Organic-molybdenum mixture is Organic acid molybdenum salt.Antiwear additive is the compound of sulfur, chlorine.Preservative is fatty acid and amine.Modified Nano diamond particle diameter is 11nm。
The preparation method of wear-resisting automobile oil, comprises the following steps: by base oil, organic-molybdenum mixture, antiwear additive, Modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and are warming up to 155 DEG C by heat-conducting oil heating, Above-mentioned raw materials being completely dissolved, continues constant temperature stirring, the circulation of material pump the high speed of dissolution kettle flows through pipeline and cuts simultaneously Cutter shears 1.5h, controls the degradation temperature wear-resisting automobile oil at 60 DEG C of available required viscositys.Lubrication oil viscosity For 15mm2/s。
Experimental example:
The automobile oil of embodiment 1~3 is carried out the mensuration of extreme pressure and antiwear behavior: this test is to agree on testing machine at ladder nurse Carry out, lubricating oil is added in certain flow between becket and the friction pair of metal derby of the certain rotating speed of certain load.Warp The polishing scratch observed on metal derby after crossing the operating of certain time represents to the extreme pressure property OK value judging lubricating oil.
Result data is as follows:
Embodiment 1 Embodiment 2 Embodiment 3
Ladder nurse agree OK value 456 466 442
Low-temperature dynamic viscosity-30 DEG C, mPa.s 650 640 650
Borderline pumping temperature-35 DEG C, mPa.s 32000 32200 31200
Resistance to corrosion Good Good Good
HTHS 4.5 4.5 5.0
Base number 7.8 7.6 7.2
N-pentane insoluble substance 0.5 0.4 0.5
The above is only the preferred embodiment of the present invention, it should be pointed out that: for those skilled in the art For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also Should be regarded as protection scope of the present invention.

Claims (4)

1. a wear-resisting automobile oil, it is characterized in that, include that following components is made according to parts by weight: modified Nano diamond 25~40 parts, base oil 40~80 parts, organic-molybdenum mixture 20~30 parts, antiwear additive 10~20 parts, preservative 20~30 parts, described base oil be viscosity index (VI) 110 ~ 120 base oil, described organic-molybdenum mixture is two kinds in dialkyl dithiophosphoric acid oxygen molybdenum, D2EHDTPA molybdenum salt, described antiwear additive is ZDDP and phosphorus, sulfur, chlorine compound in one or more, described preservative is one or both in fatty acid or amine;The preparation method of described wear-resisting automobile oil, comprise the following steps: base oil, organic-molybdenum mixture, antiwear additive, modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and it is warming up to 150-160 DEG C by heat-conducting oil heating, above-mentioned raw materials is completely dissolved, continue constant temperature stirring, the circulation of material pump the high speed of dissolution kettle flows through pipeline clipper and shears 1 ~ 2h simultaneously, controls the degradation temperature wear-resisting automobile oil at 55 ~ 65 DEG C of available required viscositys.
The wear-resisting automobile oil of one the most according to claim 1, it is characterised in that described modified Nano diamond particle diameter is 2 ~ 20nm.
3. the preparation method of the wear-resisting automobile oil described in any one of claim 1 ~ 2, it is characterized in that, comprise the following steps: base oil, organic-molybdenum mixture, antiwear additive, modified Nano diamond and preservative are added in dissolution kettle by above-mentioned parts by weight, and it is warming up to 150-160 DEG C by heat-conducting oil heating, above-mentioned raw materials is completely dissolved, continue constant temperature stirring, the circulation of material pump the high speed of dissolution kettle flows through pipeline clipper and shears 1 ~ 2h simultaneously, controls the degradation temperature wear-resisting automobile oil at 55 ~ 65 DEG C of available required viscositys.
The preparation method of wear-resisting automobile oil the most according to claim 3, it is characterised in that described lubrication oil viscosity is 14 ~ 16 mm2/s。
CN201410313292.4A 2014-07-02 2014-07-02 A kind of wear-resisting automobile oil and preparation method thereof Active CN104087365B (en)