CN104087161B - 一种透明玻璃隔热涂料 - Google Patents
一种透明玻璃隔热涂料 Download PDFInfo
- Publication number
- CN104087161B CN104087161B CN201410368290.5A CN201410368290A CN104087161B CN 104087161 B CN104087161 B CN 104087161B CN 201410368290 A CN201410368290 A CN 201410368290A CN 104087161 B CN104087161 B CN 104087161B
- Authority
- CN
- China
- Prior art keywords
- parts
- glass
- insulating mold
- mold coating
- transparent glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种透明玻璃隔热涂料，其原料由以下重量份的成分组成：丙烯酸改性有机硅树脂30～50份、低粘度高氯化聚乙烯树脂15～20份、纳米二氧化钛5～10份、纳米氧化锌2～3份、醋酸丁酯20～30份、正丁醇2～5份、环己酮2～5份。本发明涂料在红外光区有较高的屏蔽率，在可见光区有良好的透射率，在紫外光区有显著的吸收功效，可见光透射率＞80%，红外光屏蔽率≥61%，节能效果显著，隔热降温5～10℃，节能20～30%。对玻璃制品表面有良好的附着力。且有自洁功能，表面不带电荷、不沾水和粉尘。可用于门窗玻璃、汽车玻璃、高层建筑的玻璃幕墙等表面的涂装。
Description
技术领域
本发明涉及一种涂料，具体涉及一种透明玻璃隔热涂料。
背景技术
当前全球环境热效应加剧，节能减排是世界建筑行业普遍面临的问题。建筑物节能，就是在保证居室温度舒适的条件下，把建筑物用于采暖和降温的能耗降低。玻璃作为透明材料被广泛应用于建筑中，研究表明，普通玻璃的传热系数是墙体的3.2倍，是屋顶的5倍。此外，由于普通玻璃的透明性，使得光线可以直接从玻璃的一侧到达另一侧，从而使得玻璃内侧的空间受到阳光的照射而升温。由此可见，改善玻璃窗的隔热保温效果是建筑物节能减排中的重要环节。
现有技术中，通常采用贴膜、隔热纸、金属镀膜隔热玻璃等产品来实现玻璃窗的隔热问题，但这些产品通常存在透光率低、隔热效果不佳、工艺复杂等问题。
发明内容
为了解决上述存在的问题，本发明采用先进工艺生产的高性能树脂作基料，使用一种纳米高反射材料，添加自洁功能的纳米助剂与有机溶剂调制而成具有隔热、自洁的透明涂料，该涂料对玻璃制品表面有良好的附着力。
本发明的目的在于提供一种透明玻璃隔热涂料。
本发明所采取的技术方案是：
一种透明玻璃隔热涂料，其原料由以下重量份的成分组成：丙烯酸改性有机硅树脂30～50份、低粘度高氯化聚乙烯树脂15～20份、纳米二氧化钛5～10份、纳米氧化锌2～3份、醋酸丁酯20～30份、正丁醇2～5份、环己酮2～5份。
进一步的，一种透明玻璃隔热涂料，其原料由以下重量份的成分组成：丙烯酸改性有机硅树脂40份、低粘度高氯化聚乙烯树脂18份、纳米二氧化钛7份、纳米氧化锌3份、醋酸丁酯25份、正丁醇4份、环己酮3份。
本发明的有益效果是：
本发明在红外光区有较高的屏蔽率，在可见光区有良好的透射率，在紫外光区有显著的吸收功效，可见光透射率＞80％，红外光屏蔽率≥61％，节能效果显著，隔热降温5～10℃，节能20～30％。对玻璃制品表面有良好的附着力。自洁功能，表面不带电荷、不沾水和粉尘。可用于门窗玻璃、汽车玻璃、高层建筑的玻璃幕墙等表面的涂装。
附图说明
图1为透明隔热涂料喷涂在普通无色玻璃上的效果。
具体实施方式
下面结合具体实施例对本发明作进一步的说明，但并不局限于此。
实施例1：
分别称取以下重量份的原料：丙烯酸改性有机硅树脂40份、低粘度高氯化聚乙烯树脂18份、纳米二氧化钛7份、纳米氧化锌3份、醋酸丁酯25份、正丁醇4份、环己酮3份，将各原料加入搅拌釜中，在200r/min搅速下搅拌50min，充分溶解、混合后，再经过滤去滤渣，即得透明玻璃隔热涂料。
实施例2：
分别称取以下重量份的原料：丙烯酸改性有机硅树脂30份、低粘度高氯化聚乙烯树脂15份、纳米二氧化钛5份、纳米氧化锌3份、醋酸丁酯30份、正丁醇5份、环己酮2份，将各原料加入搅拌釜中，在200r/min搅速下搅拌50min，充分溶解、混合后，再经过滤去滤渣，即得透明玻璃隔热涂料。
实施例3：
分别称取以下重量份的原料：丙烯酸改性有机硅树脂50份、低粘度高氯化聚乙烯树脂15份、纳米二氧化钛10份、纳米氧化锌3份、醋酸丁酯30份、正丁醇5份、环己酮5份，将各原料加入搅拌釜中，在200r/min搅速下搅拌50min，充分溶解、混合后，再经过滤去滤渣，即得透明玻璃隔热涂料。
实施例4：
分别称取以下重量份的原料：丙烯酸改性有机硅树脂45份、低粘度高氯化聚乙烯树脂20份、纳米二氧化钛6份、纳米氧化锌2份、醋酸丁酯20份、正丁醇2份、环己酮3份，将各原料加入搅拌釜中，在200r/min搅速下搅拌50min，充分溶解、混合后，再经过滤去滤渣，即得透明玻璃隔热涂料。
下面对本发明制备的透明玻璃隔热涂料作进一步的效果检测，检测结果如下所述。
在国家建筑材料测试中心对实施例1-4制备的透明玻璃隔热涂料进行相关性能指标测试。将本发明制备的涂料喷涂在普通无色玻璃上，依据GB/T2680-1994建筑玻璃可见光透射比、太阳光直接透射比、太阳能总透射比、紫外线透射比及有关窗玻璃参数的测定。测定结果如表1～3所示，其中表1为紫外线光谱透射比/紫外线光谱反射比/紫外线光谱吸收比的测定结果；表2为可见光光谱透射比/可见光光谱反射比/可见光光谱吸收比的测定结果；表3为太阳光光谱直接透射比/太阳光光谱直接反射比/太阳光光谱直接吸收比的测定结果。
表1紫外线光谱透射比/紫外线光谱反射比/紫外线光谱吸收比的测定结果
表2可见光光谱透射比/可见光光谱反射比/可见光光谱吸收比的测定结果
表3太阳光光谱直接透射比/太阳光光谱直接反射比/太阳光光谱直接吸收比的测定结果
从表1～3的测定数据中可以看出，涂有本发明涂料的普通无色玻璃在在紫外光区有显著的吸收功效，有很高的阻隔率；在可见光区有良好的透射率，可见光透射率＞80％；在红外光区有显著的吸收比，具有较高的屏蔽率，红外光屏蔽率≥61％，节能效果显著，隔热降温5～10℃，节能20～30％。
另外，本发明的透明隔热涂料喷涂在普通无色玻璃上的效果如图1所示，从中可以出喷涂后的玻璃具有很好的透光性，可清晰看见外面的物体，说明本发明的涂料具有很好的透明性。本发明涂料对玻璃制品表面还具有良好的附着力，且具有自洁功能，表面不带电荷、不沾水和粉尘。
Claims (2)
1.一种透明玻璃隔热涂料，其特征在于：其原料由以下重量份的成分组成：丙烯酸改性有机硅树脂30～50份、低粘度高氯化聚乙烯树脂15～20份、纳米二氧化钛5～10份、纳米氧化锌2～3份、醋酸丁酯20～30份、正丁醇2～5份、环己酮2～5份。
2.根据权利要求1所述的一种透明玻璃隔热涂料，其特征在于：其原料由以下重量份的成分组成：丙烯酸改性有机硅树脂40份、低粘度高氯化聚乙烯树脂18份、纳米二氧化钛7份、纳米氧化锌3份、醋酸丁酯25份、正丁醇4份、环己酮3份。