CN104087102A - Antifouling paint for ships - Google Patents
Antifouling paint for ships Download PDFInfo
- Publication number
- CN104087102A CN104087102A CN201410363084.5A CN201410363084A CN104087102A CN 104087102 A CN104087102 A CN 104087102A CN 201410363084 A CN201410363084 A CN 201410363084A CN 104087102 A CN104087102 A CN 104087102A
- Authority
- CN
- China
- Prior art keywords
- parts
- antifouling
- paint
- ships
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antifouling paint for ships, relating to the technical field of paints. The paint is prepared from the following raw materials in parts by weight: 10-15 parts of acrylic resin, 15-25 parts of zinc acrylate resin, 10-15 parts of ceramide, 5-8 parts of 1-methyl adenine, 2-5 parts of talcum powder, 6-8 parts of zinc oxide, 10-15 parts of butanol, 0.2-0.5 part of sodium silicate and 1-2.5 parts of bentonite. Compared with the prior art, the antifouling paint for ships has excellent environment-friendly characteristic, can effectively prevent the large-size algae sea lettuce from adhesion and prevent the marine bacteria from growth, has the advantages of favorable antifouling effect and long antifouling time (36-40 months), reduces the ship resistance and lowers the oil consumption.
Description
Technical field
The present invention relates to technical field of coatings, especially a kind of anti-fouling ship paint.
Background technology
Boats and ships are immersed in seawater for a long time, the hull outside surface contacting with water can adhere to a lot of marine organisms, these marine organisms also can be on hull growth and breeding, make hull surface become coarse, increase running resistance, cause fuel consumption to increase, running cost raises, and the marine organisms and the bacterium that are accumulated in hull bottom can cause boats and ships outside surface stained, need often boats and ships to be carried out to touch-up paint, at present, be to apply antifouling paint at the outside surface of boats and ships for preventing that marine organisms from adhering to most economical effective measures.But traditional antifouling paint contains the stain control agent that organotin or Red copper oxide etc. are poisonous, when use, can discharge poisonous pigment, can work the mischief to environment, its anti-fouling effect is not lasting yet, can only maintain 18-24 month to the protective effect of ocean dirt, and can breed bacteria.
Summary of the invention
The object of this invention is to provide a kind of anti-fouling ship paint, this coating can solve environmental influence greatly and the unabiding problem of anti-fouling effect.
In order to address the above problem, the technical solution used in the present invention is: this anti-fouling ship paint comprises the raw material of following parts by weight: acrylic resin 10-15 part, zinc acrylate resin 15-25 part, Cer EOS 0-15 part, 1-methyladenine 5-8 part, talcum powder 2-5 part, zinc oxide 6-8 part, butanols 10-15 part, water glass 0.2-0.5 part, wilkinite 1-2.5 part.
In the technical scheme of above-mentioned anti-fouling ship paint, technical scheme can also be more specifically: 12 parts of acrylic resins, 18 parts of zinc acrylate resin, 2 parts of Cer EOSs, 6 parts of 1-methyladenines, 4 parts of talcum powder, 7 parts, zinc oxide, 12 parts, butanols, 0.3 part of water glass, 2 parts of wilkinites.
Owing to having adopted technique scheme, the present invention compared with prior art has following beneficial effect:
1, not containing toxic raw materials such as existing antifouling paint conventional Red copper oxide, organotin and dimethylbenzene, there is good environmental protection characteristic;
2, can effectively prevent adhering to and stoping marine bacteria growth of large-scale algae sea lettuce, anti-fouling effect is good, has lowered running resistance, reduces oil consumption, and the antifouling time is lasting, can maintain 36-40 month.
Embodiment
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
The raw material of the antifouling paint of the present embodiment is: 10 kilograms of acrylic resins, 15 kilograms of zinc acrylate resin, 0 kilogram of Cer EOS, 5 kilograms of 1-methyladenines, 2 kilograms of talcum powder, 6 kilograms, zinc oxide, 10 kilograms, butanols, 0.2 kilogram of water glass, 1 kilogram of wilkinite.
Preparation method is:
Acrylic resin and zinc acrylate resin are dissolved in after butanols, add ceramide, 1-methyladenine, talcum powder, zinc oxide, water glass, wilkinite, carry out high-speed stirring and obtain slurry, when stirring, controlling mixing speed is 500 revs/min, stir 5 minutes, slurry is ground to the fineness of 40 microns, regulate grind after slurry viscosity to be coated with-4 glasss 60 seconds.
The antifouling varnish product that this embodiment makes meets the indices of GB/T6822-2007 standard.This antifouling paint product is carried out to antifouling property test, and product effectively prevented stained in 36 months, there is no adhesion loss, foaming and slabbing.
Embodiment 2
The raw material of the antifouling paint of the present embodiment is: 12 kilograms of acrylic resins, 18 kilograms of zinc acrylate resin, 2 kilograms of Cer EOSs, 6 kilograms of 1-methyladenines, 4 kilograms of talcum powder, 7 kilograms, zinc oxide, 12 kilograms, butanols, 0.3 kilogram of water glass, 2 kilograms of wilkinites.
Preparation method is:
Acrylic resin and zinc acrylate resin are dissolved in after butanols, add ceramide, 1-methyladenine, talcum powder, zinc oxide, water glass, wilkinite, carry out high-speed stirring and obtain slurry, when stirring, controlling mixing speed is 600 revs/min, stir 5 minutes, slurry is ground to the fineness of 50 microns, regulate grind after slurry viscosity to be coated with-4 glasss 70 seconds.
The antifouling varnish product that this embodiment makes meets the indices of GB/T6822-2007 standard.This antifouling paint product is carried out to antifouling property test, and product effectively prevented stained in 40 months, there is no adhesion loss, foaming and slabbing.
Embodiment 3
The raw material of the antifouling paint of the present embodiment is: 15 kilograms of acrylic resins, 25 kilograms of zinc acrylate resin, 5 kilograms of Cer EOSs, 8 kilograms of 1-methyladenines, 5 kilograms of talcum powder, 8 kilograms, zinc oxide, 15 kilograms, butanols, 0.5 kilogram of water glass, 2.5 kilograms of wilkinites.
Preparation method is:
Acrylic resin and zinc acrylate resin are dissolved in after butanols, add ceramide, 1-methyladenine, talcum powder, zinc oxide, water glass, wilkinite, carry out high-speed stirring and obtain slurry, when stirring, controlling mixing speed is 500 revs/min, stir 5 minutes, slurry is ground to the fineness of 60 microns, regulate grind after slurry viscosity to be coated with-4 glasss 80 seconds.
The antifouling varnish product that this embodiment makes meets the indices of GB/T6822-2007 standard.This antifouling paint product is carried out to antifouling property test, and product effectively prevented stained in 38 months, there is no adhesion loss, foaming and slabbing.
Claims (2)
1. an anti-fouling ship paint, it is characterized in that comprising the raw material of following parts by weight: acrylic resin 10-15 part, zinc acrylate resin 15-25 part, Cer EOS 0-15 part, 1-methyladenine 5-8 part, talcum powder 2-5 part, zinc oxide 6-8 part, butanols 10-15 part, water glass 0.2-0.5 part, wilkinite 1-2.5 part.
2. anti-fouling ship paint according to claim 1, is characterized in that: 12 parts of acrylic resins, 18 parts of zinc acrylate resin, 2 parts of Cer EOSs, 6 parts of 1-methyladenines, 4 parts of talcum powder, 7 parts, zinc oxide, 12 parts, butanols, 0.3 part of water glass, 2 parts of wilkinites.