CN104086853A - Noise-reducing muted drainpipe - Google Patents
Noise-reducing muted drainpipe Download PDFInfo
- Publication number
- CN104086853A CN104086853A CN201410233807.XA CN201410233807A CN104086853A CN 104086853 A CN104086853 A CN 104086853A CN 201410233807 A CN201410233807 A CN 201410233807A CN 104086853 A CN104086853 A CN 104086853A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- minute
- mixed
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A disclosed noise-reducing muted drainpipe is composed of the following raw materials in parts by weight: 2-3 parts of propolis, 1-2 parts of guanidine sulfamate, 4-6 parts of hollow glass bead, 0.2-0.5 parts of ammonium paratungstate, 1-2 parts of docusate sodium, 1-2 parts of N-ethyl-o/p-toluenesulfonamide, 1-2 parts of calcium fluoride, 1-2 parts of polyvinyl butyral, 0.5-1 parts of cyclohexanehexol, 1-2 parts of decabromodiphenylethane, 2-3 parts of vinyl acetate, 10-13 parts of precipitate barium sulfate, 93-100 parts of polypropylene and 7-10 parts of a composite auxiliary agent. The drainpipe has the mute effect obviously better than the mute effect of other pipes, has the routine draining noise value low to 45 decibel or less, is good in environment-protection property, and also is good in impact resistance, high in toughness and strong in weatherability.
Description
Technical field
The present invention relates generally to tubing field, relates in particular to a kind of noise reduction mute drainage pipe and preparation method thereof.
Background technology
Polyacrylic degree of crystallinity is high, compound with regular structure, thereby there is good mechanical property.The absolute value of Mechanical Properties of PP is higher than polyethylene, but in plastic material, still belongs to kind on the low side, and its tensile strength only can reach 30 MPa or slightly high level.The polypropylene that isotactic index is larger has higher tensile strength, but with the raising of isotactic index, the shock strength of material declines to some extent, but no longer changes after dropping to a certain numerical value.
Temperature and loading rate are very large to polyacrylic Toughness.When temperature is during higher than second-order transition temperature, impact fracture is ductile rupture, is brittle rupture lower than second-order transition temperature, and impact value significantly declines.Improve loading rate, the temperature rise that can make ductile rupture change to brittle rupture.Polypropylene has excellent counter-bending fatigability, its goods bent 106 times and do not damage at normal temperatures;
Polyacrylic chemical stability is fine, outside decapacitation is corroded by the vitriol oil, concentrated nitric acid, all more stable to other various chemical reagent, but low-molecular-weight aliphatic hydrocarbon, aromatic hydrocarbon and chlorinated hydrocarbon etc. can make polypropylene softening and swelling, its chemical stability also increases with the increase of degree of crystallinity simultaneously, so polypropylene is applicable to making various chemical pipelines and accessory, anticorrosion ability is good; Preparing aspect corrugated tube, polypropylene has the features such as higher Young's modulus and lower density, can meet the performance requriements of corrugated tube completely.
Summary of the invention
The object of the invention is just to provide a kind of noise reduction mute drainage pipe and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of noise reduction mute drainage pipe, is characterized in that what it was made up of the raw material of following weight parts:
Propolis 2-3, Guanidine Sulfamate 99 1-2, hollow glass micropearl 4-6, ammonium metawolframate 0.2-0.5, succinate sodium 2-ethylhexyl 1-2, N-ethyl-adjacency pair toluol sulfonamide 1-2, Calcium Fluoride (Fluorspan) 1-2, polyvinyl butyral acetal ester 1-2, nucite 0.5-1, TDE 1-2, vinyl acetate 2-3, process white 10-13, polypropylene 93-100, composite assistant 7-10;
Described composite assistant is made up of the raw material of following weight parts:
Polypropylene 20-30, poly(vinylidene fluoride) 10-20, titanium nitride 1-2, silica gel silicon oil 1-2, sepiolite powder 20-30, dithiocyano-methane 0.1-0.2, the different monooctyl ester 2-3 of polyacrylic acid, ammonium octamolybdate 0.5-1,2,6 ditertiary butyl p cresol 0.4-1;
Above-mentioned polypropylene is mixed with poly(vinylidene fluoride), and at 100-120 DEG C, Heat preservation 20-30 minute, adds titanium nitride, grinds evenly, adds dithiocyano-methane, and 200-300 rev/min of dispersed with stirring 3-5 minute, must expect a;
Sepiolite powder is calcined to 2-3 hour at 600-700 DEG C, after discharging is cooling, add ammonium octamolybdate, add after different polyacrylic acid monooctyl ester is heated to 50-60 DEG C, under agitation condition, drip silica gel silicon oil, after dropwising, mix with material a and the each raw material of residue, fully ball milling, obtains described composite assistant.
A preparation method for noise reduction mute drainage pipe, comprises the following steps:
(1) above-mentioned process white is mixed with Calcium Fluoride (Fluorspan), ammonium metawolframate, at 50-70 DEG C, insulated and stirred 20-30 minute, is cooled to normal temperature, adds Guanidine Sulfamate 99,200-300 rev/min of dispersed with stirring 15-20 minute;
(2) polyvinyl butyral acetal ester is mixed with propolis, be uniformly mixed 3-5 minute at 40-50 DEG C;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, adopt twin screw granulation, by pellet extruding pipe material on twin screw extruder, tubing is pipe finished through cooling, cutting, hole enlargement, packaging etc.
Advantage of the present invention is:
Water shoot muting function of the present invention is obviously better than other pipelines, and conventional draining noise value can be low to moderate below 45 decibels, and the feature of environmental protection is good, and it also has good shock resistance, and toughness is high, and weathering resistance is strong.
Embodiment
Embodiment 1
A kind of noise reduction mute drainage pipe, it is made up of the raw material of following weight parts:
Propolis 2, Guanidine Sulfamate 99 2, hollow glass micropearl 4, ammonium metawolframate 0.5, succinate sodium 2-ethylhexyl 2, N-ethyl-adjacency pair toluol sulfonamide 1, Calcium Fluoride (Fluorspan) 1, polyvinyl butyral acetal ester 1, nucite 0.5, TDE 1, vinyl acetate 3, process white 13, polypropylene 100, composite assistant 10;
Described composite assistant is made up of the raw material of following weight parts:
Polypropylene 30, poly(vinylidene fluoride) 20, titanium nitride 1, silica gel silicon oil 2, sepiolite powder 30, dithiocyano-methane 0.2, the different monooctyl ester 3 of polyacrylic acid, ammonium octamolybdate 0.5,2,6 ditertiary butyl p cresol 0.4;
Above-mentioned polypropylene is mixed with poly(vinylidene fluoride), and at 120 DEG C, Heat preservation 30 minutes, adds titanium nitride, grinds evenly, adds dithiocyano-methane, and 300 revs/min of dispersed with stirring 5 minutes, must expect a;
Sepiolite powder is calcined 3 hours at 700 DEG C, after discharging is cooling, added ammonium octamolybdate, add after different polyacrylic acid monooctyl ester is heated to 60 DEG C, under agitation condition, drip silica gel silicon oil, after dropwising, mix with material a and the each raw material of residue, fully ball milling, obtains described composite assistant.
A preparation method for noise reduction mute drainage pipe, comprises the following steps:
(1) above-mentioned process white is mixed with Calcium Fluoride (Fluorspan), ammonium metawolframate, at 50 DEG C, insulated and stirred 30 minutes, is cooled to normal temperature, adds Guanidine Sulfamate 99,300 revs/min of dispersed with stirring 20 minutes;
(2) polyvinyl butyral acetal ester is mixed with propolis, be uniformly mixed 5 minutes at 50 DEG C;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, adopt twin screw granulation, by pellet extruding pipe material on twin screw extruder, tubing is pipe finished through cooling, cutting, hole enlargement, packaging etc.
Performance test:
Dimension card heat-resisting (10N, 50 DEG C/h): 159;
Drop impact (0 DEG C): qualified;
Degree of corrosion (60% hydrochloric acid, 60 DEG C, 165h): without layering, without cracked;
Degree of corrosion (40% sodium hydroxide, 60 DEG C, 165h): without layering, without cracked;
Ring is flexible: sample is round and smooth, without reverse bending, and crack-free.
Claims (2)
1. a noise reduction mute drainage pipe, is characterized in that what it was made up of the raw material of following weight parts:
Propolis 2-3, Guanidine Sulfamate 99 1-2, hollow glass micropearl 4-6, ammonium metawolframate 0.2-0.5, succinate sodium 2-ethylhexyl 1-2, N-ethyl-adjacency pair toluol sulfonamide 1-2, Calcium Fluoride (Fluorspan) 1-2, polyvinyl butyral acetal ester 1-2, nucite 0.5-1, TDE 1-2, vinyl acetate 2-3, process white 10-13, polypropylene 93-100, composite assistant 7-10;
Described composite assistant is made up of the raw material of following weight parts:
Polypropylene 20-30, poly(vinylidene fluoride) 10-20, titanium nitride 1-2, silica gel silicon oil 1-2, sepiolite powder 20-30, dithiocyano-methane 0.1-0.2, the different monooctyl ester 2-3 of polyacrylic acid, ammonium octamolybdate 0.5-1,2,6 ditertiary butyl p cresol 0.4-1;
Above-mentioned polypropylene is mixed with poly(vinylidene fluoride), and at 100-120 DEG C, Heat preservation 20-30 minute, adds titanium nitride, grinds evenly, adds dithiocyano-methane, and 200-300 rev/min of dispersed with stirring 3-5 minute, must expect a;
Sepiolite powder is calcined to 2-3 hour at 600-700 DEG C, after discharging is cooling, add ammonium octamolybdate, add after different polyacrylic acid monooctyl ester is heated to 50-60 DEG C, under agitation condition, drip silica gel silicon oil, after dropwising, mix with material a and the each raw material of residue, fully ball milling, obtains described composite assistant.
2. a preparation method for noise reduction mute drainage pipe as claimed in claim 1, is characterized in that comprising the following steps:
(1) above-mentioned process white is mixed with Calcium Fluoride (Fluorspan), ammonium metawolframate, at 50-70 DEG C, insulated and stirred 20-30 minute, is cooled to normal temperature, adds Guanidine Sulfamate 99,200-300 rev/min of dispersed with stirring 15-20 minute;
(2) polyvinyl butyral acetal ester is mixed with propolis, be uniformly mixed 3-5 minute at 40-50 DEG C;
(3) above-mentioned each raw material after treatment is mixed with the each raw material of residue, adopt twin screw granulation, by pellet extruding pipe material on twin screw extruder, tubing is pipe finished through cooling, cutting, hole enlargement, packaging etc.