CN104074068B - A kind of acid fluorescent staining technique for COTTON FABRIC - Google Patents
A kind of acid fluorescent staining technique for COTTON FABRIC Download PDFInfo
- Publication number
- CN104074068B CN104074068B CN201410256937.5A CN201410256937A CN104074068B CN 104074068 B CN104074068 B CN 104074068B CN 201410256937 A CN201410256937 A CN 201410256937A CN 104074068 B CN104074068 B CN 104074068B
- Authority
- CN
- China
- Prior art keywords
- woven fabric
- fluorescent dye
- knitted cloth
- cotton fabric
- acid fluorescent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to textile technology field, specifically a kind of acid fluorescent staining technique for COTTON FABRIC.For an acid fluorescent staining technique for COTTON FABRIC, it is characterized in that concrete staining procedure processes as follows: the proportioning that (a) gets modifier and fluorescent dye is 1:10, and mixed solution is warming up to 50 ~ 100 DEG C of maintenance constant temperature; B knitted cloth or woven fabric or yarn are contaminated in mixed solution by (); C knitted cloth after dyeing or woven fabric or yarn take out by (), and wash by normal-temperature water; (d) normal temperature is washed after knitted cloth or woven fabric or yarn take out, then to wash in the hot water entering to 100 DEG C; E knitted cloth after hot wash or woven fabric or yarn take out by (), dry.Compared with the existing technology, COTTON FABRIC is replaced traditional chemical fibre and the material of nylon, and cotton fabric is carried out modification before dyeing, make it more easily dye.
Description
Technical field
The present invention relates to textile technology field, specifically a kind of acid fluorescent staining technique for COTTON FABRIC.
Background technology
Along with the progress in epoch, people are not only confined to warming for the requirement of clothes, the field that increasing consumer more follows the fashion, the clothes of fluorescence, due to the bright eye of its color, very popular.
But fluorescence clothes occurred in the market, the water-fast character of its fluorescent dye itself, therefore has to adopt adhesive to be bonded on fabric by fluorescent dye, so just makes clothes sultry, airtight in the process of dyeing; And traditional fluorescence clothes mostly adopt the material such as chemical fibre, nylon, long-time dress can become very uncomfortable.
Summary of the invention
The present invention is for overcoming the deficiencies in the prior art, COTTON FABRIC is replaced traditional chemical fibre and the material of nylon, but because cotton fabric itself can not well by fluorescent staining, therefore cotton fabric is carried out modification before dyeing, it is made more easily to dye, such cotton fabric, being had again the comfort of cotton fabric itself while well dyeing, improves the overall quality of fluorescence dress ornament.
For achieving the above object, design a kind of acid fluorescent staining technique for COTTON FABRIC, it is characterized in that concrete staining procedure processes as follows:
A () gets modifier 70 ~ 100g/L, be 1:10 with the proportioning of fluorescent dye, and mixed solution is warming up to 50 ~ 100 DEG C of maintenance constant temperature;
B knitted cloth or woven fabric or yarn are contaminated in mixed solution by (), continue 30 ~ 60 minutes;
C knitted cloth after dyeing or woven fabric or yarn take out by (), and carry out washing 15 minutes by normal-temperature water;
(d) normal temperature is washed after knitted cloth or woven fabric or yarn take out, then carry out washing 15 minutes in the hot water entering to 100 DEG C;
E knitted cloth after hot wash or woven fabric or yarn take out by (), dry.
For an acid fluorescent staining technique for COTTON FABRIC, it is characterized in that concrete staining procedure processes as follows:
A () gets modifier 70 ~ 100g/L, be 1:10 with the proportioning of fluorescent dye;
B woven fabric is contaminated in mixed solution by (), the time is 40 ~ 80 minutes;
C woven fabric after dyeing takes out by (), and pad, and makes water retention rate remain on 20%;
D woven fabric after padding carries out baking 2 minutes by () in the dryer of 120 ~ 150 DEG C;
E woven fabric after baking takes out by ().
Described modifier is the solution be made up of cation polyurethane emulsion and water.
Described fluorescent dye is the acid fluorescent dye of KayanolBrillFlavineFL or the acid fluorescent dye of KayacylPhodamineFB.
The present invention compared with the existing technology, COTTON FABRIC is replaced traditional chemical fibre and the material of nylon, and cotton fabric is carried out modification before dyeing, it is made more easily to dye, such cotton fabric, being had again the comfort of cotton fabric itself while well dyeing, improves the overall quality of fluorescence dress ornament.
Detailed description of the invention
Embodiment one
The acid fluorescent staining of COTTON FABRIC, concrete staining procedure processes as follows:
A () gets modifier 75g/L, be 1:10 with the proportioning of fluorescent dye, and mixed solution is warming up to 50 ~ 100 DEG C of maintenance constant temperature;
B knitted cloth or woven fabric or yarn are contaminated in mixed solution by (), continue 30 ~ 60 minutes;
C knitted cloth after dyeing or woven fabric or yarn take out by (), and carry out washing 15 minutes by normal-temperature water;
(d) normal temperature is washed after knitted cloth or woven fabric or yarn take out, then carry out washing 15 minutes in the hot water entering to 100 DEG C;
E knitted cloth after hot wash or woven fabric or yarn take out by (), dry.
Described modifier is the solution be made up of cation polyurethane emulsion and water.
Described fluorescent dye is the acid fluorescent dye of the KayanolBrillFlavineFL that provided by Japanese chemical drug or the acid fluorescent dye of KayacylPhodamineFB.
Embodiment two
The acid fluorescent staining of COTTON FABRIC, concrete staining procedure processes as follows:
A () gets modifier 70 ~ 100g/L, be 1:10 with the proportioning of fluorescent dye;
B woven fabric is contaminated in mixed solution by (), the time is 40 ~ 80 minutes;
C woven fabric after dyeing takes out by (), and pad, and makes water retention rate remain on 20%;
D woven fabric after padding carries out baking 2 minutes by () in the dryer of 120 ~ 150 DEG C;
E woven fabric after baking takes out by ().
Described modifier is the solution be made up of cation polyurethane emulsion and water.
Described fluorescent dye is the acid fluorescent dye of the KayanolBrillFlavineFL that provided by Japanese chemical drug or the acid fluorescent dye of KayacylPhodamineFB.
Claims (2)
1., for an acid fluorescent staining technique for COTTON FABRIC, it is characterized in that concrete staining procedure processes as follows:
A () gets modifier 70 ~ 100g/L, be 1:10 with the proportioning of fluorescent dye, and mixed solution is warming up to 50 ~ 100 DEG C of maintenance constant temperature;
B knitted cloth or woven fabric or yarn are contaminated in mixed solution by (), continue 30 ~ 60 minutes;
C knitted cloth after dyeing or woven fabric or yarn take out by (), and carry out washing 15 minutes by normal-temperature water;
(d) normal temperature is washed after knitted cloth or woven fabric or yarn take out, then carry out washing 15 minutes in the hot water entering to 100 DEG C;
E knitted cloth after hot wash or woven fabric or yarn take out by (), dry;
Described modifier is the solution be made up of cation polyurethane emulsion and water;
Described fluorescent dye is the acid fluorescent dye of KayanolBrillFlavineFL or the acid fluorescent dye of KayacylPhodamineFB.
2., for an acid fluorescent staining technique for COTTON FABRIC, it is characterized in that concrete staining procedure processes as follows:
A () gets modifier 70 ~ 100g/L, be 1:10 with the proportioning of fluorescent dye;
B woven fabric is contaminated in mixed solution by (), the time is 40 ~ 80 minutes;
C woven fabric after dyeing takes out by (), and pad, and makes water retention rate remain on 20%;
D woven fabric after padding carries out baking 2 minutes by () in the dryer of 120 ~ 150 DEG C;
E woven fabric after baking takes out by ();
Described modifier is the solution be made up of cation polyurethane emulsion and water;
Described fluorescent dye is the acid fluorescent dye of KayanolBrillFlavineFL or the acid fluorescent dye of KayacylPhodamineFB.