CN104073314A - Solid fuel production method - Google Patents
Solid fuel production method Download PDFInfo
- Publication number
- CN104073314A CN104073314A CN201310111437.8A CN201310111437A CN104073314A CN 104073314 A CN104073314 A CN 104073314A CN 201310111437 A CN201310111437 A CN 201310111437A CN 104073314 A CN104073314 A CN 104073314A
- Authority
- CN
- China
- Prior art keywords
- paraffin
- quality
- parts
- mass
- putting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a solid fuel production method which is simple in process and low in cost. The method comprises the following steps: 1) preparing 1 part by mass of paraffin, heating in a jacketed kettle till paraffin is completely fused; then adding 6 parts by mass of carbon powder and 1.2 parts by mass of sawdust powder while uniformly stirring; stirring for 5-8 minutes at 60 DEG C so that the materials are mixed uniformly, and cooling for later use; 2) when the uniformly mixed material is cooled to below 25 DEG C, spraying 0.8 part by mass of alcohol into the mixed material by a sprayer while uniformly stirring; putting into a container, covering the container with a plastic film to prevent alcohol volatilization; (3) putting the obtained mixed material into a mould and pressing the mould for compression moulding; and 4) preparing 10 parts by mass of paraffin, putting the paraffin on the jacketed kettle and heating till the paraffin is complete fused, putting the material block molded in the step 3) into the fused paraffin so that the material block is coated with a thin paraffin layer, and cooling and packaging.
Description
Technical field
The present invention relates to a kind of solid fuel production method.
Background technology
Solid fuel is a kind of novel fuel, with once lighting according to match, can heated food, and the honeybee pot coal that ignites, easy to carry, use range is very wide.In current all kinds of solid fuel, composition various kinds, but most more open, take up room greatly, deposit and transport inconvenience, be also not easy to for heated food, or use at special Space, Place.
Summary of the invention
The problem that the present invention is directed to prior art existence provides a kind of technique simple, the solid fuel production method that cost is low.
The object of the present invention is achieved like this, a kind of solid fuel production method, comprise the steps: 1) get 1 part of quality of paraffin, be placed in jacketed kettle and be heated to melt completely, then evenly add while stirring the powdered carbon of 6 parts of quality, the sawdust powder of 1.2 parts of quality, and remain on 60 DEG C of stirrings 5～8 minutes, make the even combination cooling of above-mentioned materials for subsequent use;
2) when the above-mentioned material mixing is cooled to below 25 DEG C, the alcohol of 0.8 part of quality is sprayed in said mixture material with atomizer, simultaneously uniform stirring is to entering in a container, and covers with anti-spillage essence volatilization with plastics film;
3) by step 2) mixture of gained packs in mould and uses compacting tool set compression moulding;
4) get the paraffin of 10 parts of quality, be placed on jacketed kettle and be heated to and melt completely, by step 3) in the material piece of moulding put into paraffin after melting and make the wax layer of its parcel thin layer, cooling rear packaging.
The present invention produces solid-fuelled method, process is simple, practical, and present method is not high to matching requirements, be applicable to many normalized production or extensive centralization production on a small scale, and can suppress by mould the finished product of different size according to solid-fuelled field of employment.And in the present invention, solid-fuelled raw materials cost is low, and the products of combustion of fuel is harmless, and environmentally safe suitability is strong.
For further realizing the present invention, the granularity of described powdered carbon raw material is 80～100 orders, and the granularity of described sawdust is 40～50 orders, and melting point of paraffin wax is 54 DEG C～60 DEG C, and the degree of depth of described alcohol is greater than 95%.
For making solid fuel finished product solid, be convenient to packaging and storing transport, described step 3) in forming pressure be 80
～double centner power/cm
2.
Embodiment
For further illustrating the present invention, below in conjunction with embodiment, the present invention is elaborated.
A kind of solid fuel production method, comprises the steps:
1) get 1 kilogram, paraffin, be placed in jacketed kettle and be heated to melt completely, then evenly add while stirring the powdered carbon of 6 kilograms, the sawdust powder of 1.2 kilograms, and remain on 60 DEG C of stirrings 5～8 minutes, make the even combination cooling of above-mentioned materials for subsequent use;
2) when the above-mentioned material mixing is cooled to below 25 DEG C, the alcohol of 0.8 kilogram is sprayed in said mixture material with atomizer, simultaneously uniform stirring is to entering in a container, and covers with anti-spillage essence volatilization with plastics film;
3) by step 2) mixture of gained packs in mould with 80～double centner power/cm
2it is 5cm that pressing force is pressed into diameter, and thick is the finished product of 2cm;
4) get the paraffin of 10 kilograms, be placed on jacketed kettle and be heated to and melt completely, by step 3) in the material piece of moulding put into paraffin after melting and make the wax layer of its parcel thin layer, cooling rear packaging.
The present invention produces solid-fuelled method, process is simple, practical, and present method is not high to matching requirements, be applicable to many normalized production or extensive centralization production on a small scale, and can suppress by mould the finished product of different size according to solid-fuelled field of employment.And in the present invention, solid-fuelled raw materials cost is low, and the products of combustion of fuel is harmless, and environmentally safe suitability is strong.
Claims (3)
1. a solid fuel production method, comprises the steps:
1) get 1 part of quality of paraffin, be placed in jacketed kettle and be heated to melt completely, then evenly add while stirring the powdered carbon of 6 parts of quality, the sawdust powder of 1.2 parts of quality, and remain on 60 DEG C of stirrings 5～8 minutes, make the even combination cooling of above-mentioned materials for subsequent use;
2) when the above-mentioned material mixing is cooled to below 25 DEG C, the alcohol of 0.8 part of quality is sprayed in said mixture material with atomizer, simultaneously uniform stirring is to entering in a container, and covers with anti-spillage essence volatilization with plastics film;
3) by step 2) mixture of gained packs in mould and uses compacting tool set compression moulding;
4) get the paraffin of 10 parts of quality, be placed on jacketed kettle and be heated to and melt completely, by step 3) in the material piece of moulding put into paraffin after melting and make the wax layer of its parcel thin layer, cooling rear packaging.
2. method according to claim 1, is characterized in that, the granularity of described powdered carbon raw material is 80～100 orders, and the granularity of described sawdust is 40～50 orders, and melting point of paraffin wax is 54 DEG C～60 DEG C, and the degree of depth of described alcohol is greater than 95%.
3. method according to claim 1, is characterized in that, described step 3) in forming pressure be 80～double centner power/cm
2.