CN104059740A - Lubricating agent for special-shaped steel tube cold-drawing production - Google Patents
Lubricating agent for special-shaped steel tube cold-drawing production Download PDFInfo
- Publication number
- CN104059740A CN104059740A CN201410302151.2A CN201410302151A CN104059740A CN 104059740 A CN104059740 A CN 104059740A CN 201410302151 A CN201410302151 A CN 201410302151A CN 104059740 A CN104059740 A CN 104059740A
- Authority
- CN
- China
- Prior art keywords
- lubricator
- drawn
- percent
- steel tubes
- lubricating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of special-shaped steel tubes and in particular relates to a lubricating agent for special-shaped steel tube cold-drawing production. The lubricating agent comprises the following components in percentage by weight: 8-10 percent of industrial beef tallow, 20-30 percent of graphite, 30-40 percent of triformate phosphate, 20-30 percent of borax, 0.05-0.1 percent of dimethyl silicon oil and 1-2 percent of zinc butyl octyl dithiophosphate. The lubricating agent for special-shaped steel tube cold-drawing production is good in lubricating performance and does not have corrosion on the inner wall of the steel tube, the lubricating agent can keep the oil film strength and stable thickness performance in the drawing process, the wear resistance is high, the viscosity-temperature performance is good, the wear of drawing tools and drawing dies can be effectively reduced, the lubricating agent has low flow shear stress, and the metal surface quality is improved.
Description
Technical field
The present invention relates to steel tubes technical field, especially relate to a kind of steel tubes cold-drawn and produce with lubricator.
Background technology
Drawing is one of main production method of tubing, bar, section bar and wire rod.Press goods cross-sectional shape, drawing can be divided into: solid material drawing and the large class of hollow material drawing two.Steel pipe drawing is that steel tube blank is imposed to pulling force, makes it by nib to obtain and the plastic processing method of nib sectional dimension, goods that shape is identical.
In drawing process, the friction except between material, drawing-die and steel core, on contact surface, because drawing speed improves, will occurrence temperature sharply rise.In drawing process, to there is heavy wear or sintering in order reducing, thereby to require lubricant to play antifriction and wear prevention, cooling, lubricated effect; Be improved drawing speed and section reduction rate simultaneously, to improve output and the quality of drawing process processing, prevent the generation of the defects such as surface tear, fold, bending, bias, crackle, broken end, metal are pressed into.
And the factor that affects steel pipe drawing has conventionally: steel pipe character (hardness, degree of cleaning, condition of surface); The material kind of drawing and drawing-die; The adaptability of drawing compound.Due to the difference of mode, condition and the range of product of drawing, the requirement of lubricant is also had to difference.And lubricating method generally adopt immersion, brush, roll be stained with, traction or circulation etc.Therefore, drawing compound should meet many-sided requirements such as drawing process condition, industrial safety, economy, environmental friendliness, energy-conservation, reduction of discharging.
Summary of the invention
The technical problem to be solved in the present invention is: in order to overcome the problems of the prior art, provide a kind of steel tubes cold-drawn to produce with lubricator, lubricity is good, corrosion-free to steel pipe inner wall, has improved steel pipe inner wall quality.
The technical solution adopted for the present invention to solve the technical problems is: a kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Industry butter 8-10%
Graphite 20-30%
Phosphoric acid salt 30-40%
Borax 20-30%
Dimethyl silicone oil 0.05-0.1%
Sulphur phosphorus fourth octyl group zinc salt 1-2%
As preferably, described phosphoric acid salt is tripotassium phosphate acid esters.
As preferably, described graphite can substitute with one or both in mica and talcum powder.
As preferably, described borax useable glass powder substitutes.
As preferably, described industrial butter can substitute with industrial lard.
As preferably, described industrial butter can substitute with stearic acid.
As preferably, described industrial butter can substitute with palm fibre oil.
The invention has the beneficial effects as follows: the invention provides a kind of steel tubes cold-drawn and produce with lubricator, lubricity is good, corrosion-free to steel pipe inner wall, in drawing process, lubricant can keep oil film strength and thickness stable performance, resistance to abrasion, viscosity temperature characteristic can effectively reduce well the wearing and tearing of drawing device and drawing-die, have less mobile shear-stress, have improved metallic surface quality.
Embodiment
Below in conjunction with specific embodiment, further the present invention is set forth, should be understood that and quote embodiment only for the present invention is described, limit the scope of the invention and be not used in.
Embodiment 1
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Industry butter 8%
Graphite 20.9%
Tripotassium phosphate acid esters 40%
Glass powder, borax 30%
Dimethyl silicone oil 0.1%
Sulphur phosphorus fourth octyl group zinc salt 1%.
Embodiment 2
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Industrial lard 10%
Mica 27.95%
Tripotassium phosphate acid esters 30%
Borax 30%
Dimethyl silicone oil 0.05%
Sulphur phosphorus fourth octyl group zinc salt 2%.
Embodiment 3
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Stearic acid 9%
Mica and talcum powder, graphite 30%
Tripotassium phosphate acid esters 39%
Glass powder 20%
Dimethyl silicone oil 0.05%
Sulphur phosphorus fourth octyl group zinc salt 1.95%.
Embodiment 4
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Palm fibre oil 10%
Mica and talcum powder 20%
Tripotassium phosphate acid esters 40%
Glass powder, borax 27.9%
Dimethyl silicone oil 0.1%
Sulphur phosphorus fourth octyl group zinc salt 2%.
Embodiment 5
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Palm fibre oil 8%
Mica 25%
Tripotassium phosphate acid esters 35%
Glass powder, borax 30%
Dimethyl silicone oil 0.05%
Sulphur phosphorus fourth octyl group zinc salt 1.95%.
Embodiment 6
A kind of steel tubes cold-drawn is produced with lubricator, and each component and each component weight percent content are:
Industry butter 10%
Talcum powder 28.4%
Tripotassium phosphate acid esters 35%
Glass powder, borax 25%
Dimethyl silicone oil 0.1%
Sulphur phosphorus fourth octyl group zinc salt 1.5%.
Taking above-mentioned foundation desirable embodiment of the present invention as enlightenment, by above-mentioned description, relevant staff can, not departing from the scope of this invention technological thought, carry out various change and amendment completely.The technical scope of this invention is not limited to the content on specification sheets, must determine its technical scope according to claim scope.
Claims (7)
1. a steel tubes cold-drawn is produced with lubricator, it is characterized in that each component and each component weight percent content are:
Industry butter 8-10%
Graphite 20-30%
Phosphoric acid salt 30-40%
Borax 20-30%
Dimethyl silicone oil 0.05-0.1%
Sulphur phosphorus fourth octyl group zinc salt 1-2%.
2. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described phosphoric acid salt is tripotassium phosphate acid esters.
3. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described graphite can substitute with one or both in mica and talcum powder.
4. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described borax useable glass powder substitutes.
5. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described industrial butter can substitute with industrial lard.
6. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described industrial butter can substitute with stearic acid.
7. steel tubes cold-drawn as claimed in claim 1 is produced with lubricator, it is characterized in that: described industrial butter can substitute with palm fibre oil.